Synergistic extraction and recovery of Cerium(IV) and Fluorin from sulfuric solutions with Cyanex 923 and di-2-ethylhexyl phosphoric acid

Synergistic extraction and recovery of Cerium(IV) (Ce(IV)) and Fluorin (F) from sulfuric solutions using mixture of Cyanex 923 and di-2-ethylhexyl phosphoric acid (D2EHPA) in n-heptane have been carried out. in order to investigate the synergistic extraction of Cyanex 923 + D2EHPA, extraction Ce(IV), F, Ce(III) and Ce-F mixture solution using D2EHPA or Cyanex 923 as extractant alone were studied firstly, and then Synergistic extraction of Ce(IV), F and Ce(IV)-F mixture solution with D2EHPA + Cyanex 923 were carried out. The largest synergistic coefficient of Ce(IV) is obtained at the mole fraction X-Cyanex (923) = 0.8. The synergistic enhancement coefficients (R-max) obtained for Ce(IV) are 23.12 in Ce(IV) solution, and in Ce-F mixed solution R-max for Ce(IV) and F are 2.24 and 3.25 respectively.

The separation of Cerium(IV) from nitric acid solutions containing Thorium(IV) and Lanthanides(III) using pure [C(8)mim]PF6 as extracting phase

The extraction behavior of Ce(IV) along with Th(IV) and Ln(III) (Ln = Ce, Gd, Yb) nitrate by pure ionic liquid, [C(8)mim]PF6, was investigated. [C(8)mim]PF6 alone showed good extraction ability for Ce(IV), while it was slight for Th(IV) and negligible for Ln(III). The extraction behavior of Ce(IV) by [C(8)mim]PF6 was particularly studied, and the most probable extraction mechanism proposed was the anion exchange mechanism. Moreover, the stripping of Ce(IV) from IL phase was also investigated. The Ce(IV) in IL phase can be quantitatively recovered by water.

Biosorption of Cd2+, Cu2+, Ni2+ and Zn2+ ions from aqueous solutions by pretreated biomass of brown algae

In this paper, marine brown algae Laminaria japonica was chemically modified by crosslinking with epichlorohydrin (EC1 and EC2), or oxidizing by potassium permanganate (PC), or crosslinking with glutaraldehyde (GA), or only washed by distilled water (DW). They were used for equilibrium sorption uptake studies with Cd2+, Cu2+, Ni2+ and Zn2+. The experimental data have been analyzed using Langmuir, Freundlich and Redlich-Peterson isotherms. The results showed that the biosorption equilibrium was well described by both the Langmuir and Redlich-Peterson isotherms.

ZnO Nanorods as Scatterers for Random Lasing Emission from Dye Doped Polymer Films

A random lasing emission from 4-(dicy-anomethylene)-2-t-butyl-6(1,1,7,7-tetramethyljulolidyl-9-enyl)-4H-pyran (DCJTB) doped polystyrene (PS) thin films was realized by the scattering role of ZnO nanorods. The device was fabricated by spin-coating DCJTB doped PS on ZnO nanorods. The ZnO nanorods were grown on indium-tin-oxide (ITO) glass substrate by hydrothermal synthesis method. It can be seen that the device emits a resonance multimode peak at center wavelength of 630 nm with a mode line-width of less than 0.23 nm and exhibits threshold excitation intensity as low as 0.375 mJ pulse(-1) cm(-2). The agreement of the dependence of threshold pumped intensity on the excitation area with the random laser theory indicates that the lasing emission realized here is random laser. Our results demonstrate that the nanostructured ZnO nanorods are promising candidate as alternative sources of coherent light emission to realize organic lasers.

Pressure effects on thermodynamics of phase behavior in polystyrene/methylcyclohexane solutions

The calculations presented in this paper are based on the Sanchez-Lacombe (SL) lattice fluid theory. The interaction energy parameter, g*(12)/k, required in this approach was obtained by fitting the cloud points of polystyrene (PS) /methyleyclohexane (MCH) polymer solutions under pressure. The SL lattice fluid theory was used to calculate the spinodals, the binodals, and the Flory-Huggins (FH) interaction parameter of the solutions. The calculated results show that the SL lattice fluid theory can describe the dependences of thermodynamics of PS/MCH solutions on temperature and pressure very well. However, the calculated enthalpy and the excess volume changes indicate that the Clausius-Clapeyron equation cannot be suitable to describe pressure effect on PS/MCH solutions. Further analysis on the thermodynamics of this system under pressure shows that the role of entropy is more important than the excess volume in the present case.

Cathodic electrochemiluminescence in aqueous solutions at bismuth electrodes

The high hydrogen evolution overpotential of a bismuth electrode makes it a powerful electrode for cathodic electro-chemiluminescence studies in aqueous solutions.

Biodegradable polyurethane based on random copolymer of L-lactide and epsilon-caprolactone and its shape-memory property

A series of biodegradable polyurethanes (PUs) are synthesized from the copolymer diols prepared from L-lactide and epsilon-caprolactone (CL), 2,4-toluene diisocyanate, and 1,4-butanediol. Their thermal and mechanical properties are characterized via FTIR, DSC, and tensile tests. Their T(g)s are in the range of 28-53 degrees C. They have high modulus, tensile strength, and elongation ratio at break. With increasing CL content, the PU changes from semicrystalline to completely amorphous. Thermal mechanical analysis is used to determine their shape-memory property. When they are deformed and fixed at proper temperatures, their shape-recovery is almost complete for a tensile elongation of 150% or a compression of 2-folds. By changing the content of CL and the hard-to-soft ratio, their T(g)s and their shape-recovery temperature can be adjusted. Therefore, they may find wide applications.

Polyelectrolyte-functionalized ionic liquid for electrochemistry in supporting electrolyte-free aqueous solutions and application in amperometric flow injection analysis

As a green process, electrochemistry in aqueous solution without a supporting electrolyte has been described based on a simple polyelectrolyte-functionalized ionic liquid (PFIL)-modified electrode. The studied PFIL material combines features of ionic liquids and traditional polyelectrolytes. The ionic liquid part provides a high ionic conductivity and affinity to many different compounds. The polyelectrolyte part has a good stability in aqueous solution and a capability of being immobilized on different substrates. The electrochemical properties of such a PFIL-modified electrode assembly in a supporting electrolyte-free solution have been investigated by using an electrically neutral electroactive species, hydroquinone ( HQ) as the model compound. The partition coefficient and diffusion coefficient of HQ in the PFIL film were calculated to be 0.346 and 4.74 X 10(-6) cm(2) s(-1), respectively. Electrochemistry in PFIL is similar to electrochemistry in a solution of traditional supporting electrolytes, except that the electrochemical reaction takes place in a thin film on the surface of the electrode. PFILs are easily immobilized on solid substrates, are inexpensive and electrochemically stable. A PFIL-modified electrode assembly is successfully used in the flow analysis of HQ by amperometric detection in solution without a supporting electrolyte.

Preparation, structure and oxide ion conductivity in Ce6-xYxMoO15-delta (x=0.1-1.4) solid solutions

The Ce6-xYxMoO15-delta solid solution with fluorite-related structure have been characterized by differential thermal analysis/thermogravimetry (DTA/TG), X-ray diffraction (XRD), IR, Raman, scanning electric microscopy (SEM) and X-ray photoelectron spectroscopy (XPS) methods. The electric conductivity of samples is investigated by Ac impedance spectroscopy. An essentially pure oxide-ion conductivity of the oxygen-deficiency was observed in pure argon, oxygen and air. The highest oxygen-ion conductivity was found in Ce5.5Y0.5MoO15-delta ranging from 5.9 X 10(-5)(S cm(-1)) at 300 degrees C to 1.3 X 10(-2)(S cm(-1)) at 650 degrees C, respectively. The oxide-ion conductivities remained stable over 80 h-long test at 800 degrees C. These properties suggested that significant oxide-ionic conductivity exists in these materials at moderately elevated temperatures.

Random lasing emission from a red fluorescent dye doped polystyrene film containing dispersed polystyrene nanoparticles

The authors report a random lasing emission from 4-(dicy-anomethylene)-2-t-butyl-6(1,1,7,7-tetramethyljulolidyl-9-enyl)-4H-pyran doped polystyrene thin films by introducing polystyrene nanoparticles. The aspects of concentration and diameter of polystyrene nanoparticles have been intensively investigated and found that the lasing occurs due to the scattering role of polystyrene nanoparticles. The devices emit a resonance multimode peak centered at a wavelength of 630 nm with a mode linewidth of less than 0.35 nm and exhibit threshold excitation intensity of as low as 0.06 mJ pulse(-1) cm(-2). The microscopic laser cavities formed by multiple scattering have been captured. The demonstration of random laser opens up the possibility of using organic scattering as alternative sources of coherent light emission.

Conformation studies on sol-gel transition in triblock copolymer solutions

The gelation of physically associating triblock copolymers in a good solvent was investigated by means of the Monte Carlo simulation and a gelation process based on the conformation transition of the copolymer that was described in detail. In our simulative system, it has been found that the gelation is closely related with chain conformations, and there exist four types of chains defined as free, dangling, loop, and bridge conformations. The copolymer chains with different conformations contribute to the formation of gel in different ways. We proposed a conformational transition model, by which we evaluated the role of these four types of chains in sol-gel transition. It was concluded that the free chains keeping the conformation transition equilibrium and the dangling conformation being the hinge of conformation transition, while the chain with loop conformation enlarges the size of the congeries and the chain with bridge conformations binds the congeries consisted of the copolymer chains. In addition, the effects of temperature and concentration on the physical gelation, the association of the copolymer congeries, and the copolymer chain conformations' distribution were discussed.

Extraction and separation of cadmium(II), iron(III), zinc(II), and europium(III) by Cyanex302 solutions using hollow fiber membrane modules

The mass transfer behaviors of Cd(II), Fe(III), Zn(II), and Eu(III) in sulfuric acid solution using microporous hollow fiber membrane (HFM) containing bis(2,4,4-trimethylpentyl)monothiophosphinic acid (commercial name Cyanex302) were investigated in this paper. The experimental results showed that the values of the mass transfer coefficients (K-w) decreased with an increase of H+ concentration and increased with an increase of extractant Cyanex302 concentration. The mass transfer resistance of Eu3+ was the largest because K-w value of Eu3+ was the smallest. The order of mass transfer rate of metal ions at low pH was Cd > Zn > Fe > Eu. Mixtures of Zn2+ and Eu3+ or of Zn2+ and Cd2+ were well separated in a counter-current circulation experiment using two modules connected in series at different initial acidity and concentration ratio. These results indicate that a hollow fiber membrane extractor is capable of separating the mixture compounds by controlling the acidity of the aqueous solution and by exploiting different mass transfer kinetics. The interfacial activity of Cyanex302 in sulfuric acid solution was measured and interfacial parameters were obtained according to Gibbs adsorption equation.

Solvent extraction of scandium(III), yttrium(III), lanthanum(III) and gadolinium(III) using Cyanex 302 in heptane from hydrochloric acid solutions

The extractions of the selected rare earths (Sc, Y, La and Gd) from hydrochloric acid solutions have been investigated using bis(2,4,4-trimethylpentyl)-mono thiophosphinic acid (Cyanex 302, HL) in heptane as an extractant. The results demonstrate that the extractions of rare earths occur via the following reaction: Sc(OH)(2+) + 2[(HL)(2)]((O)) double left right arrow [Sc(OH)L-2 (.) 2(HL)]((O)) + 2H(+) Y3+ + 3[(HL)(2)]((O)) double left right arrow [Y(HL2)(3)]((O)) + 3H(+) La(OH)(2)(+) + 3[(HL)(2)](O) double left right arrow [La(OH)(2)L (.) 5(HL)]((O)) + H+ Gd(OH)(2+) + 3[(HL)(2)]((O)) double left right arrow [Gd(OH)L-2 (.) 4(HL)]((O)) + 2H(+) The pH(1/2) values and equilibrium constants of the extracted complexes have been deduced by taking into account the aqueous phase complexation of the metal ion with hydroxyl ligands and plausible complexes extracted into the organic phase. According to the pH(1/2) values, it is possible to realize mutual separation among Sc(III), Y(III), La(III) and Gd(III) with Cyanex 302 by controlling aqueous acidity.

Extraction and separation of cerium(IV) from nitric acid solutions containing thorium(IV) and rare earths(III) by DEHEHP

The extraction behaviour of Ce(IV), Th(IV) and part of RE(III), viz., La, Ce, Nd and Yb, has been investigated using di(2-ethylhexyl) 2-ethylhexyl phosphonate (DEHEHP,B) in heptane as an extractant. Results show that extractability varies in the order: Ce(IV) > Th(IV) much greater than RE(III). Therefore, it is possible to find the appropriate conditions under which Ce(IV) can be effectively separated from Th(IV) and RE(III). Furthermore, stripping Ce(IV) from the loaded organic phase can be carried out by dilute H2SO4 with an aliquot of H2O2.Roasted bastnasite made in Baotou (China) by Na2CO3 and leached by HNO3, there is about 50% Ce mainly as tetravalent nitrate along with other RE(III) and Th(IV) in the leachings. Through fractional extraction, taking nitric acid leachings of roasted Bastnasite as feed and DEHEHP as an extractant, we can obtain the CeO2 products with high purity of 99.9-99.99%, with a yield of >85%, in which ThO2/CeO2 < 10(-4).