Epitaxial crystallization in the sPP/nylon-12 semicrystalline polymer system

The epitaxial crystallization behaviour of syndiotactic polypropylene (sPP) on highly oriented nylon-12 substrates has been investigated by means of transmission electron microscopy. The results obtained from bright field electron microscopy and electron diffraction indicate that sPP crystals grow epitaxially on the oriented nylon-12 substrate with their c-axes +/- 37 degrees apart from the chain axis of the nylon-12 substrate. The contact planes of the sPP crystals are the (100) lattice planes. Moreover, the epitaxial crystallization of nylon-12 on highly oriented sPP substrates from a dilute solution in cyclohexanone has also been studied using optical microscopy. The results show that the nylon-12 crystals grow epitaxially on the oriented sPP substrate with the oriented nylon-12 lamellae forming large, anisotropic domains. Copyright (C) 1996 Elsevier Science Ltd.

Studies on water-swellable elastomer .1. Synthesis and characterization of amphiphilic polymer

A new amphiphilic polymer i.e., polyethylene glycol (PEG) grafted crystalline neoprene, which was used as compatibilizer to improve the compatibility of elastomer and water-absorbent resin, has been investigated. The synthesis was based on the reaction between chlorine in neoprene and sodium salts of PEG. PEGs with molecular weights of 600 and 2000 were used. The grafting percent and the PEG content were calculated through elemental analysis of chlorine in the resulted copolymers. The maximum grafting percent of copolymers was ca. 24.80%. The molecular parameters such as number-average molecular weight and the average number of grafting chains on one CR backbone were also calculated and discussed. (C) 1996 John Wiley & Sons, Inc.

Ionic conductivity of polymer gel electrolytes based on poly(polyethylene glycol dimethacrylate)

Gel electrolytes have been prepared by thermal polymerization of poly(polyethylene glycol dimethacrylate) (P(PEGD)) in the presence of propylene carbonate (PC) and alkali metal salts, such as LiClO4, LICF(3)SO(3) and LiBF4. The conductivity was studied by means of impedance spectroscopy, and it is found that the temperature dependence of conductivities follow a Arrhenius relationship when the molar percentage of PC is higher than 75% or LiClO4 concentration is lower than 0.9 mol/l. However, when LiCF3SO3 or LiBF4 is used instead of LiClO4 as the salt, the situation is different. For LICF(3)SO(3), the Arrhenius relationship almost holds true for all the salt concentrations studied; while for LiBF4, the Arrhenius equation hardly fits for any salt concentration. The dependence of activation energy on salt concentration is also examined, both for LiClO4 and LiCF3SO3, the values of E(a) tend to reach a minimum value with increasing salt concentration. Copyright (C) 1996 Elsevier Science Ltd.

Synthesis and characterization of interpenetrating polymer networks based on polyacrylate and epoxy

The synthesis and properties of simultaneously interpenetrating networks (SINs) based on poly(polyethylene glycol diacrylate) (PEGDA) and epoxy (diglycidyl ether of bisphenol A, DGEBA) were studied. The effect of compositional variation on the morphology and properties of products was investigated. The swelling coefficient, densities, glass transition behavior, and thermal stability of these interpenetrating networks (IPNs) are discussed. Microphase separation morphological structures were found in all PEGDA/DGEBA IPNs. Decreased swelling ratios compared to the calculated swelling coefficients based on the weight additivity of the components were obtained after the formation of IPNs. Increased density and thermal stability were also obtained in these IPNs, implying the existence of interpenetration (topological entanglements) among the component networks.

A study of the dependence of ferrocene diffusion on electrolyte concentration and size in a polymer medium using non-steady-state chronoamperometry

This article describes a quantitative study of the diffusion rate of ferrocene(Fc) dissolved in ploy(ethylene glycol)(PEG) medium containing MClO(4)(M = Li+, Na+, Bu(4)N(+), Hx(4)N(+)). The apparent diffusion coefficient D-app and the active concentration c(a) of Fc were simultaneously measured by using non-steady-state chronoamperometry. The D-app and c(a) of Fc have been estimated in PEG containing different concentrations and sizes of supporting electrolyte, and the dependence of D-app on ferrocene concentrations has been observed. The values of D-app decrease with increasing concentrations of Fc, increasing concentrations of LiClO4 or the ratio (O:Li) and also with 4 decreasing cation radius of the electrolyte. The temperature dependencies conform to a simple free volume model. The concentration and size of the counterion dependencies of the diffusion rate are similar to the behavior of their dependencies of ionic conductivity in polyelectrolyte.

An investigation on ion solvation and ion association in a gel-type solid state polymer electrolyte

Ion salvation and ion association in polytriethylene glycol dimethacrylate (PTREGD)-LiClO4 gel-type polymer electrolytes were investigated. It was found that the fraction of solute existing as single ions (alpha(i)) decreases and that of triple ions (alpha(i)) increases linearly with increasing LiClO4 concentration, while for ion pairs, as the salt concentration increases, its fraction (alpha(p)) increases first and then falls down. The findings can be rationalized by the fact that the ionic conductance of the polymer electrolyte may be mainly contributed by triple ions and higher ionic aggregates with unequal numbers of positive and negative charges in the salt concentration range of practical significance, i.e. in the range of 0.5-1.5 mol/l. The temperature dependence of these fractions was also examined. In the case of tetraethylene glycol as the solvent, alpha(i) and alpha(p) increase as the temperature is raised, but alpha(t) decreases as the temperature increases from 25 degrees C to 85 degrees C. It seems that the increase of alpha(i) and alpha(p) results from the redissociation of triple ions at higher temperature, The same changing trend of those fractions is also observed when PEG(400) is used as the solvent.

Kinetics of electrocatalytic ascorbic acid at ultramicroelectrode modified by Eastman-AQ polymer containing tris(2,2-'-bipyridine) osmium(III/II) complexes as electron-transfer centers

The theoretical model[17] of an ultramicroelectrode modified with a redox species film is used as the diagnostic tool to characterize the catalytic oxidation of ascorbic acid at carbon fiber ultramicrodisk electrodes coated with an Eastman-AQ-Os(bpy)(3)(2+) film. The electrocatalytic behavior of ascorbic acid at the ultramicroelectrode modified by an Eastman-AQ polymer containing tris(2,2'-bipyridine) osmium(III/II) as mediators is described. In order to determine the five characteristic currents quantitatively, the radius of the ultramicroelectrode and the concentration of ascorbic acid are varied systematically. The kinetic zone diagram has been used to study the electrocatalytic system. This system with 0.5-2.75 mM ascorbic acid belongs to SR + E case, and the concentration profiles of the catalyst in the film are given in detail. Finally, optimizing the design of catalytic system is discussed.

Toughening mechanism of polymer blends: Influence of voiding ability of dispersed-phase particles

The parameters which effect the cavitation strain of polymer blends toughened with a shear yield mechanism have been studied by analysis of the stress acted on the equatorial plane of dispersed-phase particles. As a result, the cavitation strain of polymer blends depends on the Young's modulus and the Poisson's ratio of the dispersed-phase particles and the matrix and also on the break stress of dispersed-phase particles. We tried to provide a criterion for selecting the materials used as dispersed-phase particles which can effectively enhance the toughness of polymer blends. (C) 1996 John Wiley & Sons, Inc.

Preparation and characterization of polymer-supported rare earth complexes

The polymers containing different ligand groups of atoms (mainly O, N, and S) and their rare earth complexes were prepared, characterized and classified based on the type of metal-ligand tending. The catalytic activities of the complexes are briefly discussed. The polymer-supported rare earth complexes showed much greater activities than the corresponding complexes with a low molecular weight.

SYNTHESIS AND CHARACTERIZATION OF A NEW COMB-LIKE POLYMER-BASED ON POLY(VINYL METHYL ETHER-ALT-MALEIC ANHYDRIDE) BACKBONE

A new comblike polymer host for polymer electrolyte was synthesized by reacting monomethyl ether of poly(ethylene glycol) with poly(vinyl methyl ether-alt-maleic anhydride) and endcapping the residual carboxylic acid with methanol. Butanone was selected as a solvent for the esterification in order to obtain a completely soluble product. The synthesis process was traced through by LR. Compared with the model compounds, the presumed structure of this comblike polymer has been proved to be valid by C-13 NMR The comb polymer is a white rubbery solid. It can be dissolved in butanone and THF, and manifests good film forming ability.

IONIC-CONDUCTION OF A NOVEL COMB POLYMER ELECTROLYTE BASED ON MALEIC-ANHYDRIDE COPOLYMER WITH OLIGO-OXYETHYLENE SIDE-CHAINS

A comb-shaped polymer (BM350) with oligo-oxyethylene side chains of the type -O(CH2CH2O)(7)CH3 was prepared from methyl vinyl ether/maleic anhydride copolymer. Homogeneous amorphous polymer electrolyte complexes were made from the comb polymer and LICF(3)SO(3) by solvent casting from acetone, and their conductivities were measured as a function of temperature and salt concentration. Maximum conductivity close to 5.08 X 10(-5) Scm(-1) was obtained at room temperature and at a [Li]/[EO] ratio of about 0.12. The conductivity which displayed non-Arrhenius behaviour was analyzed using the Vogel-Tammann-Fulcher equation and interpreted on the basis of the configurational entropy model. The results of mid-IR showed that the coordination of Li+ to side chains made the C-O-C band become broader and shift slightly. X-ray photoelectron spectroscopy analysis indicated that the oxygen atoms in the two situations could coordinate to Li+ and this coordination resulted in the reduction of the electron orbit binding energy of F and S.

EFFECT OF PARTICLE-SIZE ON IMPACT STRENGTH OF POLYMER BLENDS

The effect of particle size on impact strength of polymer blends with ductile fracture was studied. The results are in agreement with the experiments. (C) 1995 John Wiley & Sons, Inc.

ELECTROACTIVE COATINGS OF DICYANO-BIS(1,10-PHENANTHROLINE)IRON(II) ATTACHED TO NAFION POLYMER FILM-MODIFIED ELECTRODES VIA ADSORPTION

A dicyano-bis(1,10-phenanthroline)iron(II) modified elecrode was prepared. The voltammetric and the spectroelectrochemical behavior of this electrode were investigated. The influence of pH and the amount of Nafion and dicyano-bis(1,10-phenanthroline) iron(II) (DBPI) used in the electrode preparation on the electrochemical behavior is presented.

AN EXTENSION OF THE METHOD FOR PREDICTING PERMEABILITY THROUGH POLYMER MEMBRANES FROM SIMPLE GASES TO WATER-VAPOR

It is found that there is a linear relationship between log P-w, and the parameter term V-f/0.5 E(coh) [1+(delta(w) - delta(p))(2)/delta(p)(2), from the water permeability (P-w) data of 21 polymers covering 4 orders of magnitude. This correlation may be useful in choosing membrane materials for dehumidification of gases.