Modulation magnesium-doping in AlGaN/GaN superlattices

Low resistivity of p-type Mg-doped AlGaN/GaN superlattices (SLs) is demonstrated. The resistivity of the SLs is less than 0.6 Omega .cm. and the measured hole concentration is higher than 1x10(18)cm(-3). The resistivity of SLs is much lower, and the hole concentration of SLs is much higher, than that of bulk GaN and AlGaN, The electrical properties of the SLs are less sensitive than the conventional bulk lavers.

The content calculation of hexagonal phase inclusions in cubic GaN films on GaAs(001) substrates grown by metalorganic chemical vapor deposition

Cubic GaN(c-GaN) films are grown on GaAs(001) substrates by metalorganic chemical vapor deposition (MOCVD). Two GaN samples were grown with different buffer layer, the deposition time of each was 1 and 3 min, respectively. 4-circle X-ray double crystal diffraction (XRDCD) was used to study the secondary crystallographic phases presented in the c-GaN films. The phase composition of the epilayers was determined by X-ray reciprocal space mapping. The intensities of the c-GaN(002) and h-GaN(10 (1) over bar 1) planes detected in the mapping were investigated by omega scans. The content of the hexagonal phase inclusions in the c-GaN films was calculated to about 1.6 and 7.9%, respectively. The thicker buffer layer is not preferable for growing high quality pure c-GaN films. (C) 2000 Elsevier Science S.A. All rights reserved.