The purpose of this study was to determine if storage for up to 4 h in human saliva results in a decrease of erosive tooth wear (ETW) and in an increase of surface microhardness (SMH) of enamel samples after an erosive attack with subsequent abrasion. Furthermore, we determined the impact of individual salivary parameters on ETW and SMH. Enamel samples were distributed into five groups: group 1 had neither erosion nor saliva treatment; groups 2-5 were treated with erosion, then group 2 was placed in a humid chamber and groups 3-5 were incubated in saliva for 30 min, 2 h, and 4 h, respectively. After erosion and saliva treatments, all groups were treated with abrasion. Surface microhardness and ETW were measured before and after erosion, incubation in saliva, and abrasion. Surface microhardness and ETW showed significant changes throughout the experiment: SMH decreased and ETW increased in groups 2-5, regardless of the length of incubation in saliva. The results of groups 3-5 (exposed to saliva) were not significantly different from those of group 2 (not exposed to saliva). Exposure of eroded enamel to saliva for up to 4 h was not able to increase SMH or reduce ETW. However, additional experiments with artificial saliva without proteins showed protection from erosive tooth wear. The recommendation to postpone toothbrushing of enamel after an erosive attack should be reconsidered.

The histological features and physical properties of eroded dental hard tissues.

Erosive demineralisation causes characteristic histological features. In enamel, mineral is dissolved from the surface, resulting in a roughened structure similar to an etching pattern. If the acid impact continues, the initial surface mineral loss turns into bulk tissue loss and with time a visible defect can develop. The microhardness of the remaining surface is reduced, increasing the susceptibility to physical wear. The histology of eroded dentine is much more complex because the mineral component of the tissue is dissolved by acids whereas the organic part is remaining. At least in experimental erosion, a distinct zone of demineralised organic material develops, the thickness of which depends on the acid impact. This structure is of importance for many aspects, e.g. the progression rate or the interaction with active agents and physical impacts, and needs to be considered when quantifying mineral loss. The histology of experimental erosion is increasingly well understood, but there is lack of knowledge about the histology of in vivo lesions. For enamel erosion, it is reasonable to assume that the principal features may be similar, but the fate of the demineralised dentine matrix in the oral cavity is unclear. As dentine lesions normally appear hard clinically, it can be assumed that it is degraded by the variety of enzymes present in the oral cavity. Erosive tooth wear may lead to the formation of reactionary or reparative dentine.

Effectiveness of fluorescence-based methods to detect in situ demineralization and remineralization on smooth surfaces.

This study aimed to evaluate the effectiveness of fluorescence-based methods (DIAGNOdent, LF; DIAGNOdent pen, LFpen, and VistaProof fluorescence camera, FC) in detecting demineralization and remineralization on smooth surfaces in situ. Ten volunteers wore acrylic palatal appliances, each containing 6 enamel blocks that were demineralized for 14 days by exposure to a 20% sucrose solution and 3 of them were remineralized for 7 days with fluoride dentifrice. Sixty enamel blocks were evaluated at baseline, after demineralization and 30 blocks after remineralization by two examiners using LF, LFpen and FC. They were submitted to surface microhardness (SMH) and cross-sectional microhardness analysis. The integrated loss of surface hardness (ΔKHN) was calculated. The intraclass correlation coefficient for interexaminer reproducibility ranged from 0.21 (FC) to 0.86 (LFpen). SMH, LF and LFpen values presented significant differences among the three phases. However, FC fluorescence values showed no significant differences between the demineralization and remineralization phases. Fluorescence values for baseline, demineralized and remineralized enamel were, respectively, 5.4 ± 1.0, 9.2 ± 2.2 and 7.0 ± 1.5 for LF; 10.5 ± 2.0, 15.0 ± 3.2 and 12.5 ± 2.9 for LFpen, and 1.0 ± 0.0, 1.0 ± 0.1 and 1.0 ± 0.1 for FC. SMH and ΔKHN showed significant differences between demineralization and remineralization phases. There was a negative and significant correlation between SMH and LF and LFpen in the remineralization phase. In conclusion, LF and LFpen devices were effective in detecting demineralization and remineralization on smooth surfaces provoked in situ.

Genetic association study of QT interval highlights role for calcium signaling pathways in myocardial repolarization

The QT interval, an electrocardiographic measure reflecting myocardial repolarization, is a heritable trait. QT prolongation is a risk factor for ventricular arrhythmias and sudden cardiac death (SCD) and could indicate the presence of the potentially lethal mendelian long-QT syndrome (LQTS). Using a genome-wide association and replication study in up to 100,000 individuals, we identified 35 common variant loci associated with QT interval that collectively explain ∼8-10% of QT-interval variation and highlight the importance of calcium regulation in myocardial repolarization. Rare variant analysis of 6 new QT interval-associated loci in 298 unrelated probands with LQTS identified coding variants not found in controls but of uncertain causality and therefore requiring validation. Several newly identified loci encode proteins that physically interact with other recognized repolarization proteins. Our integration of common variant association, expression and orthogonal protein-protein interaction screens provides new insights into cardiac electrophysiology and identifies new candidate genes for ventricular arrhythmias, LQTS and SCD.

Susceptibility of enamel to initial erosion in relation to tooth type, tooth surface and enamel depth

This study aimed at assessing the susceptibility of different tooth types (molar/premolar), surfaces (buccal/lingual) and enamel depths (100, 200, 400 and 600 μm) to initial erosion measured by surface microhardness loss (ΔSMH) and calcium (Ca) release. Twenty molars and 20 premolars were divided into experimental and control groups, cut into lingual/ buccal halves, and ground/polished, removing 100 μm of enamel. The initial surface microhardness (SMH 0 ) was measured on all halves. The experimental group was subjected to 3 consecutive erosive challenges (30 ml/tooth of 1% citric acid, pH 3.6, 25 ° C, 1 min). After each challenge, ΔSMH and Ca release were measured. The same teeth were consecutively ground to 200, 400 and 600 μm depths, and the experimental group underwent 3 erosive challenges at each depth. No difference was found in SMH 0 between experimental and control groups. Multivariate nonparametric ANOVA showed no significant differences between lingual and buccal surfaces in ΔSMH (p = 0.801) or Ca release (p = 0.370). ΔSMH was significantly greater in premolars than in molars (p < 0.05), but not different with respect to enamel depth. Ca release decreased significantly with increasing depth. Regression between Ca release and ΔSMH at 100 μm depth showed lower slope and r 2 value, associated with greater Ca release values. At 200-600 μm depths, moderately large r 2 values were observed (0.651-0.830). In conclusion, different teeth and enamel depths have different susceptibility to erosion, so when Ca release is used to measure erosion, the depth of the test facet in enamel should be standardized, whereas this is less important if ΔSMH is used.

Fluoride varnishes containing calcium glycerophosphate: fluoride uptake and the effect on in vitro enamel erosion

OBJECTIVES Calcium glycerophosphate (CaGP) was added to fluoride varnishes to analyze their preventive effect on initial enamel erosion and fluoride uptake: potassium hydroxide (KOH)-soluble and KOH-insoluble fluoride bound to enamel. MATERIALS AND METHODS This study was carried out in two parts. Part 1: 108 enamel samples were randomly distributed into six varnish groups: base varnish (no active ingredients); Duraphat® (2.26 %NaF); Duofluorid® (5.63 %NaF/CaF2); experimental varnish 1 (1 %CaGP/5.63 %NaF/CaF2); experimental varnish 2 (5 %CaGP/5.63 %NaF/CaF2); and no varnish. Cyclic demineralization (90 s; citric acid, pH = 3.6) and remineralization (4 h) was made once a day, for 3 days. Change in surface microhardness (SMH) was measured. Part 2: 60 enamel samples were cut in half and received no varnish (control) or a layer of varnish: Duraphat®, Duofluorid®, experimental varnishes 1 and 2. Then, KOH-soluble and KOH-insoluble fluoride were analyzed using an electrode. RESULTS After cyclic demineralization, SMH decreased in all samples, but Duraphat® caused less hardness loss. No difference was observed between varnishes containing CaGP and the other varnishes. Similar amounts of KOH-soluble and insoluble fluoride was found in experimental varnish 1 and Duofluorid®, while lower values were found for experimental varnish 2 and Duraphat®. CONCLUSION The addition of CaGP to fluoride varnishes did not increase fluoride bound to enamel and did not enhance their protection against initial enamel erosion. CLINICAL RELEVANCE We observe that the fluoride varnishes containing CaGP do not promote greater amounts of fluoride bound to enamel and that fluoride bound to enamel may not be closely related to erosion prevention.

Vapnikite Ca3UO6 – a new double-perovskite mineral from pyrometamorphic larnite rocks of the Jabel Harmun, Palestinian Autonomy, Israel

The new mineral species vapnikite, Ca3UO6, was found in larnite pyrometamorphic rocks of the Hatrurim Formation at Jabel Harmun in the Judean desert, Palestinian Autonomy, Israel. Vapnikite is an analogue of the synthetic ordered double-perovskite β-Ca3UO6 and is isostructural with the natural fluorperovskite – cryolite Na3AlF6. Vapnikite Ca3UO6 (P21/n,Z = 2, a = 5.739(1), b = 5.951(1), c = 8.312(1) Å, β = 90.4(1)°, V = 283.9(1) Å3) forms yellow-brown xenomorphic grains with a strong vitreous lustre. Small grains up to 20 – 30 m m in size are wedged between larnite, brownmillerite and ye'elimite. Vapnikite has irregular fracture, cleavage and parting were not observed. The calculated density is 5.322 g cm–3, the microhardness is VHN25 = 534 kg mm–2 (mean of seven measurements) corresponding to the hardness of ~5 on the Mohs scale. The crystal structure of vapnikite Ca3UO6 differs from that of its synthetic analogue β-Ca3UO6 by having a larger degree of Ca, U disorder. Vapnikite formed at the high-temperature retrograde stage of pyrometamorphism when larnite rocks were altered by fluids/melts of high alkalinity.

The effect of enamel proteins on erosion.

Enamel proteins form a scaffold for growing hydroxyapatite crystals during enamel formation. They are then almost completely degraded during enamel maturation, resulting in a protein content of only 1% (w/v) in mature enamel. Nevertheless, this small amount of remaining proteins has important effects on the mechanical and structural properties of enamel and on the electrostatic properties of its surface. To analyze how enamel proteins affect tooth erosion, human enamel specimens were deproteinated. Surface microhardness (SMH), surface reflection intensity (SRI) and calcium release of both deproteinated and control specimens were monitored while continuously eroding them. The deproteination itself already reduced the initial SMH and SRI of the enamel significantly (p < 0.001 and p < 0.01). During the course of erosion, the progression of all three evaluated parameters differed significantly between the two groups (p < 0.001 for each). The deproteinated enamel lost its SMH and SRI faster, and released more calcium than the control group, but these differences were only significant at later stages of erosion, where not only surface softening but surface loss can be observed. We conclude that enamel proteins have a significant effect on erosion, protecting the enamel and slowing down the progression of erosion when irreversible surface loss starts to occur.

Effectiveness of Fluorescence-based Methods in Monitoring Progression of Noncavitated Caries-like Lesions on Smooth Surfaces

Although there has been a significant decrease in caries prevalence in developed countries, the slower progression of dental caries requires methods capable of detecting and quantifying lesions at an early stage. The aim of this study was to evaluate the effectiveness of fluorescence-based methods (DIAGNOdent 2095 laser fluorescence device [LF], DIAGNOdent 2190 pen [LFpen], and VistaProof fluorescence camera [FC]) in monitoring the progression of noncavitated caries-like lesions on smooth surfaces. Caries-like lesions were developed in 60 blocks of bovine enamel using a bacterial model of Streptococcus mutans and Lactobacillus acidophilus . Enamel blocks were evaluated by two independent examiners at baseline (phase I), after the first cariogenic challenge (eight days) (phase II), and after the second cariogenic challenge (a further eight days) (phase III) by two independent examiners using the LF, LFpen, and FC. Blocks were submitted to surface microhardness (SMH) and cross-sectional microhardness analyses. The intraclass correlation coefficient for intra- and interexaminer reproducibility ranged from 0.49 (FC) to 0.94 (LF/LFpen). SMH values decreased and fluorescence values increased significantly among the three phases. Higher values for sensitivity, specificity, and area under the receiver operating characteristic curve were observed for FC (phase II) and LFpen (phase III). A significant correlation was found between fluorescence values and SMH in all phases and integrated loss of surface hardness (ΔKHN) in phase III. In conclusion, fluorescence-based methods were effective in monitoring noncavitated caries-like lesions on smooth surfaces, with moderate correlation with SMH, allowing differentiation between sound and demineralized enamel.

EXPOSURE OF PHARMACY PERSONNEL TO ANTINEOPLASTIC DRUGS

This dissertation consists of two parts: (1) Exposure of pharmacy personnel to antineoplastic drugs. The Salmonella reversion test was used to measure the mutagenic activities of urine concentrates from individuals preparing antineoplastic drugs for intravenous administration. Longitudinal studies were performed in which the total urine produced in 24-hour periods was collected, starting on a Sunday at 7 P.M. after a duty-free weekend and extending over an eight-day period. There was no detectable increase in mutagenic activity in the urine concentrates of three pharmacy administrators who had no contact with these drugs. All six individuals admixing drugs in open-faced, horizontal laminar flow hoods displayed a two-fold increase in mutagenesis by the fourth day with peak values of 2.7 to 24-fold occurring on days five and six, reduced values by day seven with a return to the spontaneous level by day eight. When four of the six positive individuals in the preceding experiment admixed comparable amounts of antineoplastic drugs in a closed-faced, vertical laminar flow hood, no increase in mutagenic activity was detected in their urine concentrates over the eight-day period. (2) Estimate of potential carcinogenic risks of antineoplastic drugs. Excision repair is the major repair system that is involved with the elimination of chemically induced DNA (deoxyribonucleic acid) lesions. This DNA excision repair capability increases in mammalian species with longer life span such as humans. In this study, the effect of functional DNA excision repair on the mutagenesis invoked by 17 antineoplastic drugs was determined by using a Salmonella/Microsome assay which was expanded to include some uvr('+) counterparts of the excisionless (uvrB) tester strains routinely employed. Although extrapolation cannot be made from bacteria to humans, one should be able to make a qualitative comparison as to which antineoplastic drugs are more potentially carcinogenic to humans based on the effects of excision repair on their mutagenesis in bacteria. The tested antineoplastic drugs were divided into three classes: those requiring excision repair for mutagenesis; those producing nonrepairable genetic damage; and those producing mostly repairable premutational DNA lesions. ^