Grain refinement efficiency and mechanism of aluminium carbide in Mg-Al alloys

Detailed microscopic examination using optical and electron microscopes suggests that Al4C3, often observed in the central regions of magnesium grains on polished sections, is a potent substrate for primary Mg. Calculations of the crystallographic relationships between magnesium and Al4C3 further support the experimental observations. (c) 2005 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Eutectic grain size and strontium concentration in hypoeutectic aluminium-silicon alloys

Recently it has been shown that modification with strontium causes an increase in the size of eutectic grains. The eutectic grain size increases because there are fewer nucleation events, possibly due to the poisoning of phosphorus-based nuclei that are active in the unmodified alloy. The current paper investigates the effect of strontium concentration on the eutectic grain size. In the aluminium-10 wt.% silicon alloy used in this research, for fixed casting conditions, the eutectic grain size increases as the strontium concentration increases up to approximately 150ppm, beyond which the grain size is relatively stable. This critical strontium concentration is likely to differ depending on the composition of the base alloy, including the concentration of minor elements and impurities. It is concluded that processing and in-service properties of strontium modified aluminium-silicon castings are likely to be more stable if a minimum critical strontium concentration is exceeded. If operating below this critical strontium concentration exceptional control over composition and casting conditions is required. (c) 2005 Elsevier B.V. All rights reserved.

Fatigue crack propagation in a sintered 2xxx series aluminium alloy

Many potential applications for sintered aluminium are limited by the poor fatigue properties of the material. In order to increase understanding of the fatigue mechanisms in sintered aluminium, fatigue tests were carried out on a sintered 2xxx series aluminium alloy, AMB-2712. The alloy has a fatigue endurance strength of approximately 145 MPa (R = 0.1). Three regions were identified on the fatigue fracture surfaces. Region I contains the initiation site and transgranular crack propagation. When the size of the cyclic plastic zone ahead of the crack becomes comparable to the grain size, microstructural damage at the crack tip results in a transition to intergranular propagation. Region 2 mainly contains intergranularly fractured material, whilst the final fracture area makes up Region 3, in the form of dimple coalescence and intergranular failure. Transgranular fractographic features observed on fatigued specimens include fissure-type striations, cross-hatched grains, furrowed grains and grains containing step-like features. (c) 2006 Elsevier B.V. All rights reserved.

On the role of tin in the nitridation of aluminium powder

The role of tin in the mechanism by which aluminium nitride grows on aluminium powder is explored. In the absence of tin, the aluminium powder nitrides rapidly, with growth occurring both into and out from the surface of the particles. In contrast, nitridation occurs more slowly in the presence of tin, which is incorporated in the growing nitride. When the tin is depleted, rapid nitridation occurs. The initial tin concentration determines the point at which the growth rate changes. (c) 2006 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

GFAP analysis in aluminium chloride-treated rat brain regions

The neurotoxicity of aluminium chloride was assessed in maleWistar albino rats. Rats were treated with aluminium chloride dissolved in distilled water at a dose of 300 mg/kg body weight daily by oral gavage (1 ml) for 45 days. Controls were treated with distilled water only. Animals were sacrificed and different brain regions were dissected. GFAP analysis was carried out by Western blotting using mouse anti-GFAP monoclonal antibody (Pharmingen: 60311D) at 1:1000. Blots were developed with HRP-linked goat anti-mouse secondary antibody and quantified by densitometry.

Microanalysis of quenched and self-extinguished aluminium rods burned in oxygen

Promoted ignition tests and quench tests have been conducted and analysed for 3.2 mm aluminum rods in 99.995% oxygen. Tests have been conducted in oxygen pressures varying from 538 kPa to 773 kPa. Samples that self-extinguished or were quenched were selected for further analysis. The microstructure of the selected samples were analysed by electron microscopy, using energy dispersive spectrometry and electron back-scatter techniques, to identify and visualize, respectively, the species present. The grain structures of these samples were etched, viewed and photographed under polarized light by an optical microscope. From the micrographs produced by the post-test analysis, clearly defined boundaries between the oxide and the melted and resolidified metal have been observed. In both the melted and resolidified metal and the oxide layer, significant numbers of gas bubbles, solid inclusions and several diffuse oxide bubbles have been captured during the cooling process. It is concluded that convective movement is occurring within the molten drop and that analysis of quenched samples provides more useful information on the state of the burning droplet than samples allowed to cool slowly to room temperature. Recommendations are made regarding future investigations into aluminum burning, focusing on the transport of reactants through the liquid oxide layer.