Preparation of poly(4-vinylpyridine)/silica hybrids supported cyclopentadienyltitanium trichloride (CpTiCl3) catalyst and styrene polymerization

Poly(4 - vinylpyridine)/silica( PVP/SiO2) organic - inorganic nanoscale hybrid was prepared using sol - gel method, in which PVP was used as an organic component and TEOS as a SiO2 precusor, This hybrid was used as CpTiCl3 support. The XPS and IR measurements showed that two kinds of catalytic active site were formed through analyzing the interaction mode between support and CpTiCl3. The results of styrene polymerization showed that syndiotactic was the highest at 50 degreesC. The catalytic activity was 1.09 x 10(6) g PS/ (mol Ti . h) at 70 degreesC when n(Al)/n(Ti) = 1500. GPC results showed a bimodal molecular weight distribution.

Studies on the structure and properties of thermotropic liquid crystalline poly(aryl ether ketone)s

Series of thermotropic liquid crystalline poly (aryl ether ketone) s were synthesized by mucleophilic substitution reactions of 4,4'-biphenol and substituted hydroquinone with different difluoromonomers, The relationship between structure and properties of the novel copolymers was investigated. For the copolymers with liquid crystalline properties, their melting transition temperatures show no great change with increase the content of the crystal-disrupting unit. The reason is that the crystal phase is directly transformed from the ordered liquid crystal phase. Side-groups have important effect on mesophase stability, The temperature range of mesophase stability for the chloro-polymers is smaller than those of other series of copolymers (P-phenyl, t-butyl, methoxy, 3-trifluoromethylbenzene). This behavior indicates that the effect of geometric repulsive factor on the thermodynamic stability of the mesophase is much larger than that of the polarizability attractive factor. Different ordered liquid crystal phases are observed in the polymers with different molecular weights. At low molecular weight, highly ordered smectic liquid crystal phases form. With increasing the molecular weight, the ordered degree of the liquid crystals decreases, and only the nematic liquid crystal phase is observed in the polymer with higher molecular weight.

The effects of different alkyl substitution on the structures and properties of poly(3-alkylthiophenes)

In order to investigate the influence of different alkyl side chain substitution on the structures and properties of P3ATs, X-ray diffraction, differential scanning calorimetry (DSC), thermal gravity analysis (TGA), Fourier transform infrared spectra (FTIR) and ultraviolet-visible spectra (W-VIS) were applied to characterizing the samples of ploy(3-octylthiophene) (P3OT), poly(3-dodecylthiophene) (P3DDT) and poly(3-octadecylthiophene) (P3ODT). It is found that the different length of alkyl group substitution leads to great difference in molecular chain packings, according to the room temperature X-ray diffraction results. The temperature dependence of X-ray diffraction experiments were also performed to study the melting processes of P3ATs. With the increase in the number of carbon atoms in alkyl side chains, the melting point decreases, and the thermal stability decreases too. The results of both FTIR and W-VIS spectra indicate that the conjugation length of P3DDT is the longest. among the three P3ATs. (C) 2001 Elsevier Science B.V. All rights reserved.

Novel sodium sulfonate-functionalized poly(ether ether ketone)s derived from 4,4 '-thiodiphenol

Novel sodium sulfonate-functionalized poly(ether ether ketone)s derived from 4,4'-thiodiphenol with degree of sulfonation up to 2.0 were synthesized by nucleophilic polycondensation of various amount of 5,5 '-carbonylbis(2-fluorobenzenesulfonate) (1) and 4,4'-difluorobenzophenone (2) with 4,4'-thiodipheno (3). Component and structure of the polymers were confirmed by TR, NMR and elemental analysis. Wide angle X-ray diffraction patterns indicated an amorphous structure of the polymers. All the polymers showed excellent thermal stability and poor solubility in water. (C) 2001 Elsevier Science Ltd. All rights reserved.

Syntheses and properties of thermotropic copolyesters of p-hydroxybenzoic acid

Two series of thermotropic copolyesters of p-hydroxybenzoic acid (HBA) were synthesized by direct thermal polycondensation. One comprised aromatic copolyesters from HBA, terephthalic acid, bis(4-hydroxyphenyl) ketone (BHP) and resorcinol. The other comprised semi-aromatic copolyesters from HBA, terephthalic acid, BHP and alpha,-diols with carbon atom number of 4, 6, 8, 10. The properties of the two series were characterized by polarized light microscopy, differential scanning calorimetry and wide angle X-ray diffraction. Most of the resulting copolyesters could form a nematic phase over a wide temperature range above their melting points. The effects of Variation in composition and monomer structure on the properties of copolyesters were discussed. (C) 2001 Elsevier Science Ltd. All rights reserved.

Phase structure and transitions in a poly(methyloctadecylsilane) oligomer

A poly(methyloctadecylsilane) oligomer was synthesized by a typical Wurtz coupling reaction. Upon cooling, three transitions were observed at temperatures of 39.9, 37.5 and 33.9 degreesC at a rate of 2.5 degreesC/min in differential scanning calorimetry (DSC). The first transition, with enthalpy change of 0.47 kT/mol and supercooling of 0.2 degreesC, was characteristic of the conformational change in the Si-Si backbone into an all-trans conformation, which was detected by temperature-dependent Fourier transform infrared (FT-FR) spectroscopy. The second and the third transitions with large supercooling were identified as the formation of two-dimensional hexagonal crystal packing and three-dimensional two-chain orthorhombic crystal packing, respectively. The crystal structure was determined by the combination of WAXD and transmission electron microscopy (TEM) experiments. (C) 2000 Elsevier Science Ltd. All rights reserved.

Non-isothermal crystallization kinetics of the poly(3-alkylthiophenes)

According to the data obtained from Differential Scanning Calorimetry (DSC),the method of Jeziorny, BOPOXOBCKHH and a new approach proposed by our laboratry are applied to study the nonisothermal crystallization behavior of poly( 3-dodecylthiophene) (P3DDT) and poly(3-octadecylthiophene) (P3ODT),and Kissinger method is used to get the value of the crystallization activation energy. The effect of the different alkyl substitution on crystallization is also investigated. In comparison to the methods of Jeziorny and BOPOXOBCKHH in which it can be found that the deviation from the line occurs in the later stage of crystallization, the new approach appears applicable due to the better linear relation. The values of the crystallization activation energy of P3DDT and P3ODT are estimated as 184.78kJ/mol and 246.93kJ/mol, respectivley, which implies that it is easiser to crystallize P3DDT than P3ODT.

Synthesis and characterization of optically active aromatic polyimides derived from 2,2 '-bis(2-trifluoro-4-aminophenoxy)-1,1 '-binaphthyl and aromatic tetracarboxylic dianhydrides

Optically active 2,2'-bis(2-trifluoro-4-aminophenoxy)-1,1'-binaphthyl and its corresponding racemate were prepared by a nucleophilic substitution reaction of 1,1'-bi-2-naphthol with 2-chloro-5-nitrotrifluorotoluene and subsequently by the reduction of the resulting dinitro compounds. a series of optically active and optically inactive aromatic polyimides also were prepared therefrom, These polymers readily were soluble in common organic solvents such as pyridine, N,N'-dimethylacetamide, and m-cresol and had glass-transition temperatures of 256 similar to 278 degrees C. The specific rotations of the chiral polymers ranged from 167 similar to 258 degrees, and their chiroptical properties also were studied. (C) 1999 John Wiley & Sons Inc.

Effect of physical aging on the microstructure and the crystallization of amorphous poly(aryl ether ether ketone ketone) (PEEKK)

Physical aging of poly(aryl ether ether ketone ketone) (PEEKK) has been investigated. Heat flow responses were measured after annealing the amorphous samples obtained by quenching the melt into an ice-water bath close to, but below, the glass transition temperature. The extent of aging is related to the supercooling from the glass transition temperature and to the aging time. The activation energy of the aging process, which was estimated by a Williams-Watt expression, is similar in magnitude to that obtained for the cold crystallization for the aged samples. The quenched glass is a metastable glass. The conformation of molecular chains rearranges with physical aging which results in the formation of a denser packing in the amorphous phase. The dense amorphous phase may form an initial nucleus for crystallization. Isothermal cold crystallization of the aged samples was carried out. The Avrami equation was used to determine the kinetic parameters, and the Avrami constant n is about 2. An Arrhenius expression was used to evaluate the activation energy of relaxation upon physical aging and the activation energy of transportation upon isothermal crystallization. The activation energy of relaxation is similar in magnitude to that of crystallization for aged samples. Results obtained are interpreted as kinetic effects associated with the glass formation process.

Synthesis of a new kind of polyamide and polyester including aromatic spirodilactone

A new kind of monomers including aromatic spirodilactone-5, 5'-carboxy-7,7'-dioxo-2,2'-spirobi(benzo-[c]tetrahydrofuran) is synthesized from m-xylene and paraformaldehyde. It is converted to a series of polyamides and polyesters by means of low-temperature solution polycondensation and interfacial polycondensation. NMR and IR spectra, solubility, mechanical and thermal properties of all these polymers are investigated. The polymers have high glass transition temperatures and good thermal oxidative properties. All polyamides have high viscosity and good solubility in strong polar organic solvents such as DMSO, DMAc, DMF and NMP. All polyamides can be cast into transparent, flexible and tough films possessing good tensile properties.

End-column electrochemical detection for aromatic amines with high performance capillary electrophoresis

Electrochemical detection of five species of aromatic amines at a carbon fiber microdisk electrode after separation by capillary electrophoresis is described. Under the optimum conditions, the detection limit for 3,4-dihydroxybenzylamine, N,N-dimethylaniline, p-phenylenediamine, p-aminophenol and aniline sulfate was 0.9, 0.03, 0.075, 1.2 and 0.15 mu M (S/N = 3), respectively. The linear response range was 5-1000, 0.1-500, 0.5-500, 5-500 and 1-200 mu M, respectively The effect of the electrode position and buffer pH on the detection was also studied. This method is very simple, sensitive and stable for the detection of these compounds.

Ring-banded spherulite surface structure of poly(epsilon-caprolactone) in its miscible mixtures with poly(styrene-co-acrylonitrile)

The surface structure of the ring-banded spherulites in polymer blends PCL/SAN (90/10) was studied by optical microscopy, SEM, and TEM, respectively. It is interesting to find that the surface structure of the ring-banded spherulites in polymer blends PCL/SAN (90/10) is made up of the convex bands. The landscape of the convex bands on the surface has been little emphasized before. Radial fibrils are arranged on the bands. Details of the radial fibrils on the bands can be observed by TEM. The landscape of the convex bands on the surface and twisting of lamellae in the convex bands for PCL/SAN blends may be useful to explain the formation mechanism of the ring banded spherulites in polymer blends or even in homopolymers. (C) 1999 John Wiley & Sons, Inc.

Miscibility and crystallization behavior of poly(beta-hydroxybutyrate)/poly(ethylene oxide) blends

The miscibility and crystallization behavior of poly(beta-hydroxybutyrate) (PHB)/poly(ethylene oxide) (PEO) blends were studied by differential scanning calorimetry(DSC) and polarizing microscopy (POM). It is found that the miscibility is related to the composition of the blends. When the PEO content is over 20 percent, the miscible blends turn into partially miscible and the phase separation can be observed with POM. The addition of the PEO influences not only the morphology of PHB crystals and the radial growth rate of spherulites, but also the cold crystallization temperature.

Crystallization behevior of poly(3-dodecylthiophene)

The crystallization behavior of poly (3-dodecylthiophene) (P3DDT) is studied bq differential scanning calorimetry (DSC) under different cooling rates. When the methods of Jeziorny., Ozawa and a new one proposed by our laboratory are applied to describe its nonisothermal crystallization behavior, the new one is confirmed to be the best and convenient. By determining kinetic parameters, the analysis of the nonisothermal crystallization behavior is performed. According to Kissinger method, the crystallization activation energy of P3DDT is also evaluated.

Synthesis of poly(phenylenesulfidephenylenamine) by self-polycondensation of methyl-(4-anilinophenyl) sulfide with antimony pentachloride

Poly(phenylenesulfidephenylenamine)(PPSA) an alternating copolymer and the hybrid structure of poly(phenylene sulfide)(PPS) and polyaniline(PAn), was synthesized by self-polycondensation of methyl-(4-anilino-phenyl) sulfide with antimony pentachloride and by the acid-induced self-polycondensation of methyl-(4-anilino-phenyl) sulfoxide.