Optical characterization of high-purity cubic GaN grown on GaAs (001) substrate by metalorganic chemical vapor deposition

The optical properties of cubic GaN films have been investigated in the temperature range of 10-300 K. Five peaks were observed at 10 K. From the dependence of photoluminescence emissions on the temperature and excitation intensity, we have assigned two of the five peaks (2.926 and 2.821 eV) to donor-acceptor pair (DAP) transitions. Furthermore, these two peaks were found to be related to a common shallow donor involved in the peak position previously reported at 3.150 eV. The intensities of DAP transitions were much weaker than that of excitonic emission even at low temperature, indicating a relatively high purity of our samples. (C) 2000 American Institute of Physics. [S0003-6951(00)00921-9].

The structural and photoluminescence properties of self-organized quantum dots in InAs/In0.53Ga0.47As multilayer on InP substrate

Self-organized InAs/In0.53Ga0.47As quantum dot (QD) multilayers were grown on InP substrate by molecular beam epitaxy. The structural and optical properties were characterized by using cross-sectional transmission electron microscopy (TEM) and photoluminescence (PL), respectively. Vertically aligned InAs quantum dots multilayer on InP substrate is demonstrated for the first time. Photoluminescence with a line width of similar to 26 meV was observed from the QDs multilayer. (C) 2000 Elsevier Science B.V. All rights reserved.

Infrared absorption efficiency in AlAs/AlxGa1-xAs type-II multiple-quantum-well structure grown on (211) GaAs substrate

We have made a normal incidence high infrared absorption efficiency AlAs/Al0.55Ga0.45As multiple-quantum-well structure grown on (211) GaAs substrates by molecular beam epitaxy (MBE). A strong infrared absorption signal at 11.6 mu m due to the transition of the ground state to the first excited state, and a small signal at 6.8 mu m due to the transition from the ground state to continuum. were observed. A 45 degrees tilted incidence measurement was also performed on the same sample for the comparison with a normal incidence measurement. Both measurements provide important information about the quantum well absorption efficiency. Efficiencies which evaluate the absorption of electric components perpendicular and parallel to the well plane are eta(perpendicular to) = 25% and eta(parallel to) = 88%, respectively. The total efficiency is then deduced to be eta = 91%. It is apparent that the efficiency eta(parallel to) dominates the total quantum efficiency eta Because an electron in the (211) AlAs well has a small effective mass (m(zx)* or m(zy)*), the normal incidence absorption coefficient is expected to be higher:than that grown on (511) and (311) substrates. Thus, in the present study, we use the (211) substrate to fabricate QWIP. The experimental results indicate the potential of these novel structures for use as normal incidence infrared photodetectors.

Arsenic clusters on the surface of vertically aligned InAs islands on GaAs substrate by annealing

The formation of arsenic clusters in a system of vertically aligned InAs quantum islands on GaAs during thermal annealing under As overpressure has been investigated by transmission electron microscopy (TEM) and Raman scattering. Semicoherent arsenic clusters, identified by TEM examination, have been formed on the surface of the GaAs capping layer. The existence of arsenic precipitates is also confirmed by Raman spectra, showing new peaks from the annealed specimen at 256 and 199 cm(-1). These peaks have been ascribed to A(1g) and E-g Raman active phonons of crystalline arsenic. The phenomenon can be understood by a model of strain-induced selected growth under As overpressure. (C) 1999 American Institute of Physics. [S0003-6951(99)02045-8].

Improvement of photoluminescence of strained SiGe/Si layers on patterned Si substrate

A strained SiGe/Si superlattice structure has been grown on a patterned Si substrate and its photoluminescence has been studied. The patterned substrate is composed of pyramid-like structures. It is found that there are Ge-rich SiGe quantum wires (QWR) at the crossings of adjacent planes that form the pyramid-like structure. Photoluminescence of strained the SiGe layer grown on a planar substrate and a patterned substrate was compared. The total intensity of photoluminescence from the patterned substrate was 5.2 times larger than that from the planar substrates. The result is discussed and it is believed that this increase in photoluminescence is related to the observed QWRs. (C) 1999 Elsevier Science Ltd. All rights reserved.

Structural and optical properties of self-assembled InAs quantum dots grown on GaAs (311) A substrate

We report the structural and optical characteristics of InAs quantum dots (QDs) grown on GaAs (311)A substrates. Atomic force microscopic result shows that QDs on (311)A surface exhibit a nonconventional, faceted, arrowhead-like shapes aligned in the [233] direction. The photoluminescence (PL) intensity, peak position and the full width at half maxinum (FWHM) are all closely related to the measurement temperature. The fast redshift of PL energy and monotonous decrease of linewidth with increasing temperature were observed and explained by carriers being thermally activated to the barrier produced by the wetting layer and then being retrapped and recombined in energetically lower-lying QDs states. This model explains our results well.

Raman scattering in hexagonal GaN epitaxial layer grown on MgAl2O4 substrate

The room temperature Raman spectra of the hexagonal GaN epilayer grown on [111]- oriented MgAl2O4 substrate were measured in various backscattering and right angle scattering geometries. All of the symmetry-allowed optical phonon modes were observed except the E-2 (low frequency) mode. The quasitransverse and quasilongitudinal modes were also observed in the x(zx)z and x(yy)z configurations, which are the mixed modes of pure transverse and longitudinal modes with A(1) and E-1 symmetry, respectively. (C) 1999 American Institute of Physics. [S0021-8979(99)01416-4].

Substrate surface atomic structure influence on the growth of InAlAs quantum dots

We have examined the influence of substrate surface orientation on self-assembled InAlAs/AlGaAs quantum dots grown on (0 0 1) and (n 1 1) A/B (n = 3, 5) GaAs substrates by molecular beam epitaxy (MBE). Preliminary characterizations have been performed using photoluminescence (PL) and transmission electron microscopy (TEM). The PL emission energies of quantum dots on high Miller index surface are found to be strongly dependent on the atomic-terminated surface (A or B surface) of the substrate. We observed that there were planar ordering larger islands on (3 1 1)B surface compared to (0 0 1) surface, in contrast, a rough interface and smaller "grains" on (3 1 1)A surface, this result is identical with PL emission energy from these islands. We propose that the rapid strain-induced surface "roughening" impedes the formation of 3D islands on A surface, and indicating that this is a promising approach of the realization of ordering distribution on (3 1 1)B plane for devices such as red-emitting semiconductor quantum dots lasers. (C) 1999 Elsevier Science B.V. All rights reserved.

A Raman scattering study of GaAs: As films lifted off GaAs substrate

We performed Raman scattering investigations on low-temperature-grown (LTG) films of GaAs that had been lifted off the GaAs substrate. The Raman measurements unambiguously show the effects of excess arsenic on phonon scattering from LTG films of GaAs. The larger downwards shift of the LO phonon frequency for unannealed free-standing films is explained by invoking the elimination of mismatch strain. The Raman signal due to precipitates of elemental arsenic in the annealed GaAs : As films is determined. It is confirmed that the arsenic clusters formed by rapid thermal annealing are mainly amorphous, giving rise a broad Raman peak in the range 180-260 cm(-1).

Interference effects in differential reflectance spectra of the GaAs epilayers grown on Si substrate

We report the observation of oscillating features in differential reflectance spectra from the GaAs epilayer grown on Si substrate in the energy range both below and above the fundamental band gap. It is demonstrated that the oscillating features are due to the difference in the interference between two neighboring areas of the sample. The interference arises from two light beams reflected from different interfaces of the sample. The calculated spectra in the nonabsorption region are in good agreement with measured data. It is shown that the interference effect can be used as a sensitive method to characterize the inhomogeneity of the semiconductor heterostructures. (C) 1998 American Institute of Physics. [S0021-8979(98)08723-4].

Microstructure evolution of GaN buffer layer on MgAl2O4 substrate

Microstructure of GaN buffer layer grown on (111)MgAl2O4 substrate by metalorganic vapor phase epitaxy (MOVPE) was studied by transmission electron microscopy (TEM). It has been observed that the early deposition of GaN buffer layer on the substrate at a relatively low temperature formed a continual island-sublayer (5 nm thick) with hexagonal crystallographic structure, and the subsequent GaN buffer deposition led to crystal columns which are composed of nano-crystal slices with mixed cubic and hexagonal phases. After high-temperature annealing, the crystallinity of nano-crystal slices and island-sublayer in the buffer layer have been improved. The formation of threading dislocations in the GaN him is attributed not only to the lattice mismatch of GaN/MgAl2O4 interface, but also to the stacking mismatches at the crystal column boundaries. (C) 1998 Published by Elsevier Science B.V. All rights reserved.

The growth and characterization of GaN grown on an Al2O3 coated (001)Si substrate by metalorganic vapor phase epitaxy

Single crystal GaN films have been grown on to an Al2O3 coated (001)Si substrate in a horizontal-type low-pressure MOVPE system. A thin Al2O3 layer is an intermediate layer for the growth of single crystal GaN on to Si although it is only an oriented polycrystal him as shown by reflection high electron diffraction. Moreover, the oxide was not yet converted to a fully single crystal film, even at the stage of high temperature for the GaN overlayer as studied by transmission electron microscopy. Double crystal X-ray diffraction showed that the linewidth of (0002) peak of the X-ray rocking curve of the 1.3 mu m sample was 54 arcmin and the films had heavy mosaic structures. A near band edge peaking at 3.4 eV at room temperature was observed by photoluminescence spectroscopy. (C) 1998 Elsevier Science B.V. All rights reserved.

The effect of buried AlxGa1-xN isolating layers on the transport properties of GaN deposited on sapphire substrate by molecular beam epitaxy using NH3

It is believed that the highly dislocated region near the GaN/sapphire interface is a degenerate layer. In this paper a direct evidence for such a proposal is presented. By inserting a buried AlxGa1-xN (x > 0.5) isolating layer to separate the interface region from the bulk region, the background electron concentration can be significantly reduced, while care must be taken to guarantee that there is no degrading of Hall mobility when choosing the thickness of the isolating layer. (C) 1998 Elsevier Science B.V. All rights reserved.

Triclinic deformation and anisotropic strain relaxation of an InAs film on a GaAs(001) substrate measured by a series of symmetric double crystal X-ray diffraction

We presented a series of symmetric double crystal X-ray diffraction (DCXD) measurements, (0 0 4), (2 2 0) and (2 - 2 0) diffraction, to investigate the strain relaxation in an InAs film grown on a GaAs(0 0 1) substrate. The strain tensor and rotation tensor were calculated according to the DCXD results. It is found that the misfit strain is relaxed nearly completely and the strain relaxation caused a triclinic deformation in the epilayer. The lattice parameter along the [1 1 0] direction is a little longer than that along the [1 - 1 0] direction. Furthermore, a significant tilt, 0.2 degrees, towards the [1 1 0] direction while a very slight one: 0.002 degrees, towards [1 - 1 0] direction were discussed. This anisotropic strain relaxation is attributed to the asymmetric distribution of misfit dislocations, which is also indicated by the variation of the full-width at half-maximum (FWHM) of (0 0 4) diffraction along four azimuth angles. (C) 1998 Elsevier Science B.V. All rights reserved.

Electronic and vibrational Raman scattering in resonance with yellow luminescence transitions in GaN on sapphire substrate

We analyze low-temperature Raman and photoluminescence spectra of MBE-grown GaN layers on sapphire. Strong and sharp Raman peaks are observed in the low frequency region. These peaks, which are enhanced by excitation in resonance with yellow luminescence transitions, are attributed to electronic transitions related to shallow donor levels in hexagonal GaN. It is proposed that a low frequency Raman peak at 11.7 meV is caused by a pseudo-local vibration mode related to defects involved in yellow luminescence transitions. The dependence of the photoluminescence spectra on temperature gives additional information about the residual impurities in these GaN layers.