含纳米晶颗粒的Yb^3＋/Er^3＋共掺透明碲酸盐玻璃陶瓷的光谱性质研究

在组成为15Li2O-15Nb2O5-70TeO2-0.1Er2O3-0.4Yb2O3（%, 摩尔分数）的碲酸盐玻璃基础上, 采用两步热处理法制备了透明的含纳米晶颗粒碲酸盐玻璃陶瓷. 通过X射线衍射（XRD）测试表明, 玻璃陶瓷中的晶体颗粒组成为Yb6Te5O19.2或Er6Te5O19.2, 晶粒尺寸约为55 nm. 根据Judd-Ofelt理论计算了Er^3＋离子在基质玻璃和玻璃陶瓷中的光谱参数Ωt（t＝2, 4, 6）以及Er^3＋：4I15/2→4I13/2跃迁自发辐射几率, 根据McCumber

Yb^3＋掺杂锌锗碲酸盐玻璃的热分析、光谱和激光性质

设计了组成为0．70TeO2-(0．20-x)ZnO-xGeO2—0．05La2O3-0．025K2O-0．025Na2O-0．01Yb2O3(摩尔分数x=0,0．05，0．10，0．15和0．20)的碲酸盐激光玻璃，测试了热学性质、吸收光谱、荧光光谱和荧光寿命。计算了Yb^3+离子的吸收截面、受激发射截面、荧光有效线宽等参数。结果表明，组成为0．70TeO2-0．20GeO2-0．05La2O3-0．025K2O-0．025Na2O的玻璃具有优于著名的碲锌钠(TZN)玻璃的热稳定性，高的受激发射截面(1

Effect of Fe impurity on the optical loss of Nd-doped phosphate laser glass

The optical loss coefficient at 1053-nm wavelength, influenced by Fe ions in N31-type Nd-doped phosphate laser glass, was determined precisely and analyzed in detail. It is found that the optical loss coefficient per unit of Fe concentration (cm^(-1)/ppmw) increases with Fe concentration in the range of 0---300 ppmw, but it approaches a constant as the Fe concentration is larger than 300 ppmw. Such a concentration effect is due to a shift in the redox equilibrium between Fe3+ and Fe2+ ions in the glass. The effect of oxygen pressure, temperature, and variable valence states of other metal ions in glass samples on the optical loss is also discussed.

Effect of network modifiers on spectroscopic properties of erbium-doped phosphate glasses

The integrated absorption cross section Sigma(abs), I peak emission cross section sigma(cmi), Judd-Ofeld intensity parameters Omega(iota) ( t = 2,4,6), and spontaneous emission probability A(R) of Er3+ ions were determined for Erbium doped alkali and alkaline earth phosphate glasses. It is found the compositional dependence of sigma(emi) 5 almost similar to that of Sigma(abs), which is determined by the sum, of Omega(1) (3 Omega(2) + 10 Omega(4) + 21 Omega(6)). In addition, the compositional dependence of Omega(1) was studied in these glass systems. As a result, compared with. Omega(4) and Omega(6) the Omega(2) has a stronger compositional dependence on the ionic radius and content of modifers. The covalency of Er-O bonds in phosphate glass is weaker than that in silicate glass, germanate glass, aluminate glass, and tellurate glass, since Omega(6) of phosphate glass is relatively large. A(R) is affected by the covalency of the Er3+ ion sites and corresponds to the Omega(6) value.

Infrared-to-visible upconversion emissions in Er3+ doped TeO2-based oxyhalide glasses

The fluorescence and up-conversion spectral properties of Er3+-doped TeO2-ZnO and TeO2-ZnO-PbCl2 glasses suitable for developing optical fiber amplifier and laser have been fabricate and characterized. Strong green (around 527-550 nm) and red (around 661 nm) up-conversion emissions under 977 nm laser diode excitation were investigated, corresponding to H-2(11/2), S-4(3/2), --> I-4(15/2) and F-4(9/2) --> I-4(15/2) transitions of Er3+ ions respectively, have been observed and the involved mechanisms have been explained. The dependence of up-converted fluorescence intensity versus laser power confirm that two-photons contribute to up-conversion of the green-red emissions. The novelty of this kind of optical material has been its ability in resisting devitrification, and its promising optical properties strongly encourage for their further development as the rare-earth doped optical fiber amplifiers and upconversion fiber laser systems.

Thermal stability and spectroscopic properties of Er3+-doped niobium tellurite glasses for broadband amplifiers

Three Er3+-doped tellurite glasses with compositions of 70TeO(2)-30ZnO, 70TeO(2)-20ZnO-10Nb(2)O(5) and 70TeO(2)-20ZnO-5BaO-5Nb(2)O(5) have been investigated for developing fiber and planar broadband amplifiers and lasers. The optical spectroscopic properties and thermal stability of Er3+-doped tellurite glasses have been discussed. The results show that the incorporation of Nb2O5 increases the thermal stability of Er3+-doped tellurite glasses significantly, Er3+-doped niobium tellurite glasses 70TeO(2)-20ZnO-10Nb(2)O(5) and 70TeO(2)-20ZnO-5BaO-5Nb(2)O(5) exhibit the good thermal stability (DeltaT > 150degreesC), the large emission cross-section (>10 x 10(-21) cm(2)) and broad full width at half maximum (similar to65 nm), will be preferable for broadband Er3+-doped fiber amplifiers. (C) 2004 Elsevier B.V. All rights reserved.

LD泵浦的镱铒共掺磷酸盐玻璃的光谱性质和激光性质

制备了Er^3＋/Yb^3＋共掺磷酸盐玻璃. 通过分析其吸收光谱, 根据McCumber理论计算得到了Er^3＋离子在波长1533 nm处的峰值发射截面为0.84×10^-20 cm^2, ^4I13/2能级的荧光寿命为8.5 ms. 利用激光二极管作为泵浦源, 成功地实现了Er^3＋/Yb^3＋共掺磷酸盐玻璃激光器的连续运转. 在室温下, 获得最大激光输出功率为80 mW, 斜率效率为16.5%.

铬镱铒共掺磷酸盐玻璃光谱和激光性质研究

测定了Cr14—05铬镱铒共掺磷酸盐玻璃的主要热光参数，并测试了吸收、荧光光谱和激光性能等。结果表明该玻璃具有较好的光谱和热光性质，其激光输出性能可满足人眼安全激光测距光源应用的要求。

Effect of lithium-potassium mixed alkali on spectroscopic properties of Er3+-doped aluminophosphate glasses

Er3+-doped lithium-potassium mixed alkali aluminophosphate glasses belonging to the oxide system xK(2)O-(15x)Li2O-4B(2)O(3)-11Al(2)O(3)-5BaO-65P(2)O(5) are obtained in a semi-continuous melting quenching process. Spectroscopic properties of Er3+-doped glass matrix have been analysed by fitting the experimental data with the standard Judd-Ofelt theory. It is observed that Judd-Ofelt intensity parameters-Omega(t)(t=2, 4 and 6) of Er3+ change when the second alkali is introduced into glass matrix. The variation of line strength S-ed[I-4(13/2),I-4(15/2)] follows the same trend as that of the Omega(6) parameter. The effect of mixed alkali on the spectroscopic properties of the aluminophosphate glasses, such as absorption cross-section, stimulated emission cross-section, spontaneous emission probability, branching ratio and the radiative lifetime, has also been investigated in this paper.

Ultrabroadband infrared luminescence and optical amplification in bismuth-doped germanosilicate glass

This letter reports the ultrabroadband infrared luminescence from 1000- to 1700-nm wavelength range and demonstrate optical amplification at the second optical communication window in a novel bismuth-doped germanosilicate glass. The full-width at half-maximum of the luminescence is about 300 mn and the optical gain is larger than 1.37 within the wavelength region from 1272 to 1348 nm with pump power 0.97 W. This material could be useful to fabricate ultrabroadband optical fiber amplifiers.

Judd-Ofelt intensity parameters of Er3+ doped mixed alkali aluminophosphate glasses

Lithium sodium mixed alkali aluminophosphate glasses of the composition xNa(2)O-(15-x)Li2O-4B(2)O(3)-11Al(2)O(3)-5BaO-65P(2)O(5) (where x=0, 3.75, 7.5, 11.25 and 15 mol%) containing 0.5 mol% Er2O3 were prepared by melt quenching. The absorption spectra of Er3+ were studied from the experimental oscillator strengths and the Judd-Ofelt intensity parameters were obtained. The variations of Judd-Ofelt intensity parameters (Omega(2), Omega(4) and Omega(6)), experimental oscillator strengths of certain excited states of Er3+ and hypersensitive band positions with different mixed alkali content have been discussed in detail. It was found that there were similar effects of mixed alkali on both Judd-Ofelt intensity parameter 02 and the experimental oscillator strength of the hypersensitive transition, I-4(15/2) -> H-2(11/2). No shifts in the peak wavelength of the studied transitions were found in different glasses. (c) 2006 Elsevier B.V. All rights reserved.

Effects of melting temperature on the broadband infrared luminescence of bi-doped and Bi/Dy co-doped chalcohalide glasses

Bismuth (Bi)-doped and Bi/Dy co-doped chalcohalide glasses are investigated as promising materials for amplifiers in optical communication. The samples synthesized at lower melting temperatures (MTs) are characterized by more intensified infrared emissions. With respect to the redox process of a liquid mixture at different MTs, we attribute an emission at 1230 nm to low-valent Bi ions. The lower MT favors the formation of LVB ions, i.e. Bi+ or Bi2+, while the higher MT promotes the production of higher-valent Bi ions Bi3+. An enhanced broadband infrared luminescence with the full-width at half-maximum over 200 nm is achieved from the present Bi/Dy co-doped chalcohalide glasses.

Spectroscopic properties and Judd-Ofelt theory analysis of Dy3+ doped oxyfluoride silicate glass

Dy3+ doped oxyfluoride silicate glass was prepared and its optical absorption, 1.3 mu m emission, and upconversion luminescence properties were studied. Furthermore, the Judd-Ofelt [Phys. Rev. 127, 750 (1962); J. Chem. Phys. 37, 511 (1962)] intensity parameters, oscillator strengths, spontaneous transition probability, fluorescence branching ratio and radiative lifetime were calculated by Judd-Ofelt theory, while stimulated emission cross section of H-6(9/2)+F-6(11/2)-> H-6(15/2) transition was calculated by McCumber theory [Phys. Rev. A. 134, 299 (1964)]. According to the obtained Judd-Ofelt intensity parameters Omega(2)=2.69x10(-20) cm(2), Omega(4)=1.64x10(-20) cm(2), and Omega(6)=1.64x10(-20) cm(2), the radiative lifetime was calculated to be 810 mu s for 1.3 mu m emission, whose full width at half maximum and sigma(e) were 115 nm and 2.21x10(-20)cm(2), respectively. In addition, near infrared to visible upconversion luminescence was observed and evaluated. The results suggest that Dy3+ doped oxyfluoride silicate glass can be used as potential host material for developing broadband optical amplifiers and laser applications.

Low-loss planar and stripe waveguides in Nd3+-doped silicate glass produced by oxygen-ion implantation

We report on the fabrication and characterization of low-loss planar and stripe waveguides in a Nd3+-doped glass by 6 MeV oxygen-ion implantation at a dose of 1x10(15) ions/cm(2). The dark mode spectroscopy of the planar waveguide was measured using a prism coupling arrangement. The refractive index profile of the planar waveguide was reconstructed from a code based on the reflectivity calculation method. The results indicate that a refractive index enhanced region as well as an optical barrier have been created after the ion beam processing. The near-field mode profiles of the stripe waveguide were obtained by an end-fire coupling arrangement, by which three quasitransverse electric modes were observed. After annealing, the propagation losses of the planar and stripe waveguides were reduced to be similar to 0.5 and similar to 1.8 dB/cm, respectively. (c) 2007 American Institute of Physics.

Broadband near-infrared emission from transparent Ni2+-doped silicate glass ceramics

Transparent Ni2+-doped MgO-Al2O3-TiO2-SiO2 glass ceramics were prepared, and the optical properties of Ni2+-doped glass ceramics were investigated. Broadband emission centered at 1320 nm was observed by 980 nm excitation. The longer wavelength luminescence compared with Ni2+-doped Li2O-Ga2O3-SiO2 glass ceramics is ascribed to the low crystal field hold by Ni2+ in MgO-Al2O3-TiO2-SiO2 glass ceramics. The change in optical signals at the telecommunication bands with or without 980 nm excitation was also measured when the seed beam passes through the bulk gain host.(C) 2007 American Institute of Physics.