Ionic conductivity of solid polymer electrolytes based on modified alternating maleic anhydride copolymer with oligo(oxyethylene) side chains

Comb-like polymers (CP) based on modified alternating methyl vinyl ether/maleic anhydride copolymer with oligo-oxyethylene side chains of the type -O(CH2CH2O)(n)CH3 have been synthesized and characterized, and complexed with lithium salts to form amorphous polymer electrolytes. CP/salt complexes showed conductivity up to 10(-5)Scm(-1) at room temperature. The temperature dependence of ionic conductivity suggests that the ion transport is controlled by segmental motion of the polymer, shown by linear curves obtained in Vogel-Tammann-Fulcher plots. The ionic conductivity maximum moves to a higher salt concentration as the temperature increases. IR results indicate that the ester in CP might decompose at 140 degrees C and reproduce the maleic anhydride ring.

Study of the blends containing core-shell latex polymer

Polycarbonate (PC) and a core-shell latex polymer composed of poly(butyl acrylate) and poly(methyl methacrylate) (PBA-cs-PMMA) as core and shell, respectively, were mixed using a Brabender-like apparatus under different conditions. The mechanical properties, the morphology and the processability of the blends were investigated. Because of the good compatibility of PC and PMMA, even dispersion of PBA-cs-PMMA in PC matrix and good adhesion between the components have been achieved. PBA-cs-PMMA is thus a very good impact modifier for PC. The toughening mechanism is both cavitation and shear yielding, as indicated by SEM observation. (C) 1997 Elsevier Science Ltd.

Morphology, thermal behavior, and mechanical properties of PA1010/PP and PA1010/PP-g-GMA blends

The modification of polypropylene (PP) was accomplished by melt grafting glycidyl methacrylate (GMA) on its molecular chains. The resulting PP-g-GMA was used to prepare binary blends of polyamide 1010 (PA1010) and PP-g-GMA. Different blend morphologies were observed by scanning electron microscopy (SEM) according to the nature and content of PA1010 used. Comparing the PA1010/PP-g-GMA and PA1010/PP binary blends, the size of the domains of PP-g-GMA were much smaller than that of PP at the same compositions. It was found that mechanical properties of PA1010/PP-g-GMA blends were obviously better than that of PA1010/PP blends, and the mechanical properties were significantly influenced by wetting conditions for uncompatibilized and compatibilized blends. A different dependence of the flexural modulus on water was found for PA1010/PP and PA1010/PP-g-GMA. These behaviors could be attributed to the chemical interactions between the two components and good dispersion in PA1010/PP-g-GMA blends. Thermal and rheological analyses were performed to confirm the possible chemical reactions taking place during the blending process. (C) 1997 John Wiley & Sons, Inc.

Study of the miscibility and thermodynamics of cellulose diacetate-poly(vinyl pyrrolidone) blends

The miscibility of blends of cellulose diacetate (CDA) and poly(vinyl pyrrolidone) (PVP) was extensively studied by means of differential thermal analysis and dynamic mechanical thermal analysis, tensile test, measuring viscosity of diluted and concentrated solutions of blends in acetone-ethanol mixture and morphological observations. A single glass transition temperature is observed, which is intermediate between the glass transition temperatures associated with each component and depends on composition. A synergism in mechanical properties of blends was found. The absolute viscosity and the intrinsic viscosity of solutions of blends are much higher than the weight average values of solutions of CDA and PVP. Optically clear and thermodynamically stable films were formed in the composition range of CDA/PVP = 100/0 to 50/50w/w. Fourier transform infrared was used to investigate the nature of CDA-PVP interaction. Hydrogen bonds were formed between hydroxyl groups of CDA and carbonyl groups of PVP. Heats of solutions of CDA/PVP blends and their mechanical mixtures were measured by using a calorimeter. Mixing enthalpy obtained with Hess's law approach was used to quantify interaction parameters of this blending system. It was found that mixing enthalpies and interaction parameters were negative and composition dependent. (C) 1997 Elsevier Science Ltd.

Study on the two class glass transition and ion transport of a comb polymer electrolyte

The thermal behaviour and ion-transport properties of a comb polymer electrolyte CP350/LiSCN based on methyl vinyl ether/maleic anhydride copolymer with oligo-oxyethylene side chains were studied by means of DSC and ac impedance method. The two glass transition temperatures which can be attributed to side chains and main chains respectively were found to increase with increasing salt concentration. Conductivities which displayed non-Arrhenius behaviour were analyzed by using Vogel-Tammann-Fulcher equation and interpreted on the basis of the configurational entropy model derived by Gibbs and coworkers. The optimum ionic conductivity at 25 degrees C achieved was 2.19x10(-5)S/cm.

Synthesis and ionic conductivity studies of solid polymer electrolytes based on modified alternating maleic anhydride copolymer with oligo(oxyethylene) side chains

Comb-like polymers (CP) based on modified alternating methyl vinyl ether/maleic anhydride copolymer with oligo-oxyethylene side chains of the type-O(CH2CH2O)(n)CH3 have been synthesized and characterized, and complexed with LiNO3 to form an amorphous polymer electrolyte. CP/salt complexes showed conductivity up to 10(-5) S/cm at room temperature. The temperature dependence of ionic conductivity suggests that the ion transport is controlled by segmental motion of the polymer, shown by linear curves obtained in Vogel-Tammann-Fulcher plots. The ionic conductivity maximum moves to a higher salt concentration as the temperature increases. IR results also indicate that the ester in CP might decompose at 140 degrees C and reproduce the maleic anhydride ring.

Dynamic mechanical properties of interpenetrating polymer networks based on polyacrylates and epoxy

Interpenetrating polymer networks (IPNs) based on polyacrylate (poly(polyethylene glycol diacrylate), PEGDA) and epoxy(diglycidyl ether of bisphenol A, DGEBA) were prepared simultaneously Dynamic mechanical properties of the SINs (simultaneous interpenetrating networks) with various compositions were studied. Enhanced mechanical properties were found in this case. From the point of view of pre-swollen networks, all of the PEGDA/DGEBA IPNs were composed of the individual pre-swollen networks. A micro-phase segregation system was produced in the SIN. Glass transition temperatures shifted inward, which was attributed to molecular packing effects or mutual-entanglements of molecular segments among the individual pre-swollen networks. In accordance with the additivity of properties, namely the parallel model, the entanglement density between the two polymer networks reached its maximum at 50/50 PEGDA/DGEBA IPN.

A new solid-state electrolyte: Rubbery 'polymer-in-salt' containing LiN(CF3SO2)(2)

A new class of rubbery 'polymer-in-salt' electrolytes for application in solid-state lithium batteries has been explored by differential scanning calorimetry and a.c. impedance analysis. Simple phase diagrams of LiN(CF3SO2)(2)+LiClO4 and LiC(CF3SO2)(3)+LiN(CF3SO2)(2) have been drawn, which are very important to determine polymer-in-salt electrolyte materials. The conductivities obtained by a.c. impedance measurement are smaller for the electrolyte that contains acetate LiOAc salt than for the electrolyte without this salt.

Studies on the two class glass transition and the typical VTF behaviour of an amorphous comb polymer electrolyte

A comb polymer (CP350) with oligo-oxyethylene side chains of the type -(CH2CH2O)(7)CH3 was prepared from methyl vinyl ether/maleic anhydride copolymer and poly(ethylene glycol) methyl ether. The polymer can dissolve LiNO3 salt to form homogeneous amorphous polymer electrolyte. This electrolyte system was first found to have two class glass transitions, and the two T(g)s were observed to increase with increasing salt content. The ionic conduction was measured by using the complex impedance method, and conductivities were investigated as functions of temperature and salt concentration. At 25 degrees C, the ionic conductivity maximum of this system can get to 3.72 X 10(-5) S/cm at the [Li]/ [EO] ratio of 0.057. The appearance of the conductivity maximum has been interpreted as being due to the effect of T-g and the so called physical crosslinks. The temperature dependence of the ionic conductivity displaying non-Arrhenius behaviour can be analyzed using the Vogel-Tammann-Fulcher equation and interpreted on the basis of the configurational entropy model.

Comblike polymer electrolyte with main chain glass transition near room temperature

A new amorphous comblike polymer (CBP) based on methylvinyl ether/maleic anhydride altering copolymer backbone and on oligooxyethylene side chain was synthesized. The dynamic mechanical properties of CBP and its Li salt complexes were investigated by means of DDV-11-EA type viscoelastic spectrometry. Results showed that there were two glass transitions (alpha-transition and beta-transition) in the temperature range from -100 to 100 degrees C. The beta-transition was assigned to oligo-PEO side chains and the temperature of beta-transition increases with increasing Li salt content. The alpha-transition was assigned to the main chain of CBP. The temperature of the alpha-transition (T-alpha) is also dependent upon the Li-salt content, but not monotonic. The value of T-alpha lies between 30-45 degrees C in the Li salt concentration range studied, near room temperature. It was found that the CBP-Li salt complexes showed an unusual dependence of ionic conductivity on Li salt content. There are two peaks in the plot of the ionic conductivity vs. Li salt concentration, which has been ascribed to the movability of the CBP main chain at ambient temperature. The temperature dependence bf the ionic conductivity indicated that the Arrhenius relationship was not obeyed, and the plot of log sigma against 1/(T - T-0) showed the unusual dual VTF behavior when using side chain glass transition temperature (T-beta) as T-0.

Study of ion solvation and ion association in polymer gel electrolyte with polyethylene oxide-co-polypropylene oxide as a plasticizer

Using a molal conductance method, ion solvation and ion association in polytriethylene glycol dimethacrylate (PTREGD)-LiClO4 gel electrolytes with amorphous ethylene oxide-co-propylene oxide (EO-co-PO, <(M)over bar (n)>, = 1750) as the plasticizer were investigated. It was found that the fraction of solute existing as single ions (alpha(i)) and ion pairs (alpha(p)) decreases, while that of triple ions (alpha(t)) increases linearly with increasing salt concentration. The dependence of these fractions on molecular weight of plasticizer was also examined. It was shown that alpha(i) and alpha(t) increase and alpha(p) decreases with increasing molecular weight. The result of temperature dependence of these fractions was very interesting: when the temperature is lower than 55 degrees C, alpha(i) increases while alpha(p) and alpha(t) decrease with increasing temperature; however, when the temperature is higher than 55 degrees C, the reverse is true.

Comb polymer electrolytes - Ionic conductivity and cation-polymer interaction

Three comb polymers(CP) with oligo-oxyethylene side chains of the type -O(CH2CH2O)(n)CH3 were prepared from methyl vinyl ether/maleic anhydride alternating copolymer. Homogeneous amorphous polymer electrolytes were made from CP and LiCF3SO3 or LiClO4 by solvent-casting method, and their conductivities were measured as a function of temperature and salt concentration. The conductivity which displayed non-Arrhenius behaviour was analyzed using the Vogel-Tammann-Fulcher equation. The conductivity maximum appears at lower salt concentration when CP has longer side chains. XPS was used to study the cation-polymer interaction.

Lithium ion conducting polymer electrolytes based on alternating maleic anhydride copolymer with oligo-oxyethylene side chains

A comb polymer with oligo-oxyethylene side chains of the type -(CH2CB2O)(12)CH3 was prepared from methyl vinyl ether/maleic anhydride copolymer and poly (ethylene glycol) methyl ether. The polymer can dissolve LiClO4 salt to form homogeneous amorphous polymer electrolyte. The ac ion conduction was measured using the complex impedance method, and conductivities were investigated as functions of temperatures and salt concentration. The complexes were first found to have two classes of glass transition which increase with increasing salt content, The optimum conductivity attained at 25 degrees C is in the order of 5.50 x 10(-6)Scm(-1). IR spectroscopy was used to study the cation-polymer interaction.

A study of the dependence of ferrocene diffusion on chain length in polymer electrolytes

The diffusion rates of ferrocene have been estimated in five kinds of poly(ethylene glycol) solution, containing the electrolyte LiClO4, by using non-steady-state chronoamperometry. The D-app of ferrocene increases with increasing temperature, and the dependency of D-app on temperature obeys the Williams-Landel-Ferry equation. The D-app of ferrocene decreases with increasing polymer chain length. Both the chain length and temperature dependence conform to a simple free volume model. A relation between current and polymer chain length is suggested at room and high temperatures.

Properties of ethylene-propylene copolymer/PA-1010 blends using ethylene-propylene copolymer-graft-acrylic acid as a compatibilizing agent

The modification of ethylene-propylene copolymer (EP) has been accomplished by radical EP-graft-acrylic acid (EP-g-AA) has been used to obtain ternary PA/EP/EP-g-AA blends by melt mixing. Different blend morphologies were observed by scanning electron microscopy; the domain size of the EP-dispersed phase in the polyamide 1010 matrix of compatibilized blends decreased compared with that of uncompatibilized blends. It is found that EP-g-AA used as the third component has a profound effect on the mechanical properties of the resulting blends. This behavior has been attributed to serious chemical interactions taking place between the two components. Thermal analysis shows that some thermal properties of PA in compatibilized PA/EP/EP-g-AA changed because of chemical reactions taken place during the blending process. Wide angle x-ray diffraction measurements also confirmed this result. (C) 1996 John Wiley & Sons, Inc.