Síntese, caracterização e estudo das propriedades magnéticas de ortoferritas de lantânio dopadas com manganês

Orthoferrites AFeO3 (A = rare earth) are an important class of perovskite oxides that exhibit weak ferromagnetism. These materials find numerous applications as chemical sensors, cathodes for fuel cells and catalysis, which make them interesting from the standpoint of science and technology. Their structural, electrical and magnetic properties are dependent on many factors such as the preparation method, heat treatment conditions, chemical composition and replacement of cations in sites A and/or B. In this paper, LaFe1-xMnxO3 (0 ≤ x ≤ 1) orthoferrites-type was prepared by Pechini method and Microwave-assisted combustion reaction in order to evaluate the influence of synthesis route on the formation of oxide, as well as the effect of parcial replacement of iron by manganese and heat treatment on the magnetic properties. The precursor powders were calcined at 700°C, 900°C, 1100°C and 1300°C for 4 hours and they were characterized by the techniques: Thermogravimetric analysis (TGA), X ray diffraction (XRD), Refinement by Rietveld method, Scanning electron microscopy (SEM), Reduction temperature programmed (RTP) and Magnetic hysteresis measurements performed at room temperature. According to the XRD patterns, the formation of perovskite phase with orthorhombic structure was observed for the systems where 0 ≤ x ≤ 0.5 and rhombohedral for x = 1. The results also showed a decrease of lattice parameters with the parcial replacement of iron by manganese and consequently a reduction in cell volume. The hysteresis curves exhibited weak ferromagnetism for the systems prepared by both synthesis methods. However, a dependence of magnetization as a function of dopant content was observed for samples produced by Pechini method. As for the systems prepared by combustion reaction, it was found that the secondary phases exert a strong influence on the magnetic behavior

Síntese pelo método pechini e caracterização da zircônia dopada com cério e neodímio

In this study five compositions were synthesized zirconia doped with cerium and neodymium ions in the system Ce10-xNdx Zr90O2 with 0,5 ≤ x ≤ 4,0 using the Pechini method. The powders were characterized by thermogravimetric analysis, differential thermal analysis, infrared spectroscopy and X-ray diffraction, with application of Rietveld refinement of the calcination temperatures of 350ºC/3h and 30 minutes at 900ºC/3h. All compositions stabilized with a mixture of cubic and tetragonal phase zirconia. The samples were pressed into bars and sintered at 1500°C/3h and 1500°C/6h, being characterized by Xray diffraction, with application of the Rietveld refinement, density and porosity using Archimedes method, scanning electron microscopy and resistance the three point bending. It has been observed the increase in strength with increasing sintering temperature for the compositions x = 2,0 and x = 4,0. For x = 2,0 the main phase was the cubic with 92,56% with crystallite size of 0,56 μm, density and porosity of 96,82% from 1,36%. For x = 4,0 was a mixture of cubic and tetragonal phase with 21% and 37,98%, respectively. The crystallite size was 54,21 nm and 49,64 nm with a density porosity of 97,45% and 1,32% respectively. In the analysis of the fracture surface was observed a greater amount of grain fracture intragranular type, which contribute to increase the mechanical strength of the ceramic. Increased addition of the neodymium ion in the crystal lattice of the zirconium showed a nearly linear behavior with increasing mechanical strength of the zirconia ceramic. Was obtained a bending resistance of 537 ± 38 MPa for the composition x = 2,0 predominantly attributed to cubic phase with 92,56%

Síntese e caracterização de ferritas de níquel dopadas com cobalto e efeito da substituição nas suas propriedades magnéticas

The ferrite composition Ni1 - xCoxFe2O4 (0 ≤ x ≤ 0.75) were obtained by the method of microwave assisted synthesis and had their structural and magnetic properties evaluated due to the effect of the substitution of Ni by Co. The compounds were prepared: according to the concept of chemical propellants and heated in the microwave oven with power 7000kw. The synthesized material was characterized by absorption spectroscopy in the infrared (FTIR), Xray diffraction (XRD) using the Rietveld refinement, specific surface area (BET) , scanning electron microscopy (SEM) with aid of energy dispersive analysis (EDS) and magnetic measurements (MAV). The results obtained from these techniques confirmed the feasibility of the method of synthesis employed to obtain the desired spinel structure, the ferrite, nickel ferrite as for nickel doped with cobalt. The results from XRD refinement ally showed the formation of secondary phases concerning stages α - Fe2O3, FeO, (FeCo)O e Ni0. On the other hand, there is an increase in crystallite size with the increase of cobalt in systems, resulting in an increased crystallinity. The results showed that the BET systems showed a reduction in specific surface area with the increase of cobalt and from the SEM, the formation of irregular porous blocks and that the concentration of cobalt decreased the agglomerative state of the system. The magnetic ferrites studied showed different characteristics according to the amount of dopant used, ranging from a very soft magnetic material (easy magnetization and demagnetization ) - for the system without cobalt - a magnetic material with a little stiffer behavior - for systems containing cobalt. The values of the coercive field increased with the increasing growth of cobalt, and the values of saturation magnetization and remanence increased up to x = 0,25 and then reduced. The different magnetic characteristics presented by the systems according to the amount of dopant used, allows the use of these materials as intermediates magnetic

Avaliação de variante somaclonal de porte baixo de bananeira 'Nanicão Jangada' (Musa sp) em duas densidades

Avaliou-se, sob duas densidades de plantio, um variante somaclonal de porte baixo de bananeira, comparando-o com a variedade Nanicão Jangada que lhe deu origem. Os materiais genéticos 'Nanicão Jangada'(controle) e o variante somaclonal representado pelas seleções 224 e 225 de um ensaio anterior, foram avaliados nos espaçamentos 2,0m X 2,0m (densidade 2500 plantas ha-1) e 3,0m X 2,0m (1666plantas ha-1), na Fazenda de Ensino e Pesquisa da Faculdade de Engenharia - UNESP, Campus de Ilha Solteira-SP. O ensaio foi conduzido em blocos ao acaso com cinco repetições, com utilização de mudas micropropagadas, sob irrigação por gotejamento, no período de dezembro de 1998 a março de 2001, com avaliação dos dois primeiros ciclos de produção. Constatou-se efeito da densidade e do ciclo sobre a produção estimada de frutos sendo que no cultivo mais denso, a média foi de 81,25 t.ha-1 no primeiro ciclo de produção e 67,93 t.ha-1 no segundo ciclo. No cultivo de menor densidade a produção estimada no primeiro ciclo foi de 51,35 t.ha-1 e 44,08 t.ha-1 no segundo. As seleções do variante de porte baixo apresentaram menor altura da planta e mostraram-se relativamente mais precoces e com produção semelhante a cv. Nanicão Jangada no primeiro ciclo. No segundo ciclo houve uma queda na produção do bananal, com maior intensidade para a seleção 225 do variante.

Debris, Roughness and Friction of Stainless Steel Archwires Following Clinical Use

Objective: To investigate the degree of debris, roughness, and friction of stainless steel orthodontic archwires before and after clinical use.Materials and Methods: For eight individuals, two sets of three brackets (n = 16) each were bonded from the first molar to the first premolar. A passive segment of 0.019- x 0.025-inch stainless steel archwire was inserted into the brackets and tied by elastomeric ligature. Debris level (via scanning electron microscopy), roughness, and frictional force were evaluated as-received and after 8 weeks of intraoral exposure. Mann-Whitney, Wilcoxon signed-rank, and Spearman correlation tests were used for statistical analysis at the .05 level of significance.Results: There were significant increases in the level of debris (P = .0004), roughness of orthodontic wires (P = .002), and friction (P = .0001) after intraoral exposure. Significant positive correlations (P < .05) were observed between these three variables.Conclusion: Stainless steel rectangular wires, when exposed to the intraoral environment for 8 weeks, showed a significant increase in the degree of debris and surface roughness, causing an increase in friction between the wire and bracket during the mechanics of sliding. (Angle Orthod. 2010;80:521-527.)

Intrapleural analgesia after endoscopic thoracic sympathectomy

OBJETIVO: Comparar a analgesia tradicionalmente utilizada para simpatectomia videotoracoscópica à injeção intrapleural de ropivacaína em duas doses diferentes. MÉTODOS: Vinte e quatro pacientes foram distribuídos em três grupos semelhantes, e todos eles receberam dipirona endovenosa. O grupo A recebeu tramadol endovenoso e injeção intrapleural de solução salina. O grupo B recebeu injeção intrapleural de ropivacaína a 0,33%, e Grupo C ropivacaína a 0,5%. Os aspectos analisados foram: capacidade inspiratória, freqüência respiratória e dor. A dor foi avaliada no período pós-operatório por meio da escala visual analógica e durante o período de uma semana. RESULTADOS: Nos grupos A e B, a redução da capacidade inspiratória foi observada no período pós-operatório. Nas primeiras 12 horas de pós-operatório, apenas 12,5% dos pacientes nos grupos B e C apresentaram dor intensa em comparação a 25% no Grupo A. Na semana seguinte, apenas um paciente do grupo A apresentou dor leve, enquanto o restante relatou dor intensa. No Grupo B, metade dos pacientes apresentou dor intensa, e no Grupo C, apenas um apresentou intensa dor. CONCLUSÃO: A analgesia intrapleural com ropivacaína resultou em menos dor no pós-operatório tardio com os melhores resultados analgésicos nas doses mais altas, proporcionando um melhor padrão ventilatório.

Tobacco smoke-induced left ventricular remodelling is not associated with metalloproteinase-2 or -9 activation

Aim: To investigate the role of MMP-2 and MMP-9 in cardiac remodelling induced by tobacco smoke exposure in rats.Methods: Rats were allocated into two groups: C (n = 9): control animals; ETS (n = 9): exposed to tobacco smoke. After 4months, the animals underwent echocardiography, morphometric study and determination of MMP-2 and MMP-9 activity.Results: ETS rats had larger diastolic (C= 15.6 +/- 1.2 mm/kg, ETS = 18.0 +/- 0.9 mm/kg; p < 0.001) and systolic (C= 7.3 +/- 1.2 mm/kg, ETS = 9.2 0.9 mm/kg; p = 0.001) ventricular diameters adjusted for body weight. Fractional shortening (C= 53 +/- 4.8%, ETS = 48 +/- 3.3%; p = 0.031) and ejection fraction (C= 0. 89 +/- 0.03 5 ETS = 0. 86 +/- 0.02; p = 0.03 0) were smaller in the ETS group. Myocyte cross-sectional area (C= 245 8 mu m(2), ETS=253 8 mu m(2); p = 0.028) was higher in ETS rats. There were no differences in MNtP-2 (C=50 +/- 14%; ETS 43 +/- 11%, p 0.22 +/- 8) or MMP-9 (C=0.36 +/- 0.3%; ETS=0.62 +/- 0.3%, p=0.630) activity between the groups.Conclusion: MMP-2 and MMP-9 did not participate in the remodelling process induced by tobacco smoke exposure. (c) 2007 European Society of Cardiology. Published by Elsevier B.V. All rights reserved.

A exposição crônica à fumaça do cigarro resulta em remodelação cardíaca e prejuízo da função ventricular em ratos

OBJETIVO: Determinar as alterações cardíacas estruturais e funcionais causadas pela exposição à fumaça do cigarro em ratos. MÉTODOS: Os animais foram aleatoriamente distribuídos em dois grupos: fumante (F), composto por 10 animais, expostos à fumaça do cigarro, na taxa de 40 cigarros/dia e controle (C), constituído por 10 animais não submetidos à exposição. Após 4 meses, os animais foram submetidos a estudo morfológico e funcional por meio do ecocardiograma. As variáveis estudadas foram analisadas pelo teste t ou pelo teste de Mann-Whitney. RESULTADOS: Os ratos fumantes apresentaram maior átrio esquerdo (F=4,2± 0,7mm; C=3,5±0,6mm; p<0,05), maiores diâmetros diastólicos (F=7,9±0,7mm; C=7,2±0,5mm; p<0,05) e sistólicos (F=4,1 ±0,5; C=3,4±0,5; p<0,05) do ventrículo esquerdo (VE). O índice de massa do VE foi maior nos animais fumantes (F=1,5 mg/kg± 0,2; C=1,3 mg/kg±0,2; p<0,05), e a fração de ejeção (F=0,85±0,03; C=0,89±0,03; p<0,05) e a fração de encurtamento (F=47,8 %±3,7; C=52,7%±4,6; p<0,05) maiores no grupo controle. Não foram identificadas diferenças nas variáveis de fluxo diastólico (onda E, na onda A e na relação E/A) transmitral. CONCLUSÃO: A exposição crônica à fumaça do cigarro resulta em remodelação cardíaca, com diminuição da capacidade funcional ventricular.

A exposição à fumaça de cigarro intensifica a remodelação ventricular após o infarto agudo do miocárdio

OBJETIVO: Analisar os efeitos da exposição à fumaça de cigarro (EFC) na remodelação ventricular após o infarto agudo do miocárdio (IAM). MÉTODOS: Ratos foram infartados e distribuídos em dois grupos: C (controle, n = 31) e F (EFC: 40 cigarros/dia, n = 22). Após seis meses, foi realizado ecocardiograma, estudo funcional com coração isolado e morfometria. Para comparação, foi utilizado o teste t (com média ± desvio padrão) ou teste de Mann-Whitney (com mediana e percentis 25 e 75). RESULTADOS: Os animais EFC apresentaram tendência a maiores áreas ventriculares diastólicas (C = 1,5 ± 0,4 mm², F = 1,9 ± 0,4 mm²; p = 0,08) e sistólicas (C = 1,05 ± 0,3 mm², F = 1,32 ± 0,4 mm²; p = 0,08) do VE. A função sistólica do VE, avaliada pela fração de variação de área, tendeu a ser menor nos animais EFC (C = 31,9 ± 9,3 %, F = 25,5 ± 7,6 %; p = 0,08). Os valores da - dp/dt dos animais EFC foram estatisticamente inferiores (C = 1474 ± 397 mmHg, F = 916 ± 261 mmHg; p = 0,02) aos animais-controle. Os animais EFC apresentaram maior peso do VD, ajustado ao peso corporal (C = 0,8 ± 0,3 mg/g, F = 1,3 ± 0,4 mg/g; p = 0,01), maior teor de água nos pulmões (C = 4,8 (4,3-4,8)%, F = 5,4 (5,1-5,5); p = 0,03) e maior área seccional do miócito do VE (C = 239,8 ± 5,8 µm², F = 253,9 ± 7,9 µm²; p = 0,01). CONCLUSÃO: A exposição à fumaça de cigarro intensifica a remodelação ventricular após IAM.

THE ROLE of OXIDATIVE STRESS and LIPID PEROXIDATION IN VENTRICULAR REMODELING INDUCED BY TOBACCO SMOKE EXPOSURE AFTER MYOCARDIAL INFARCTION

OBJECTIVE: To evaluate the roles of oxidative stress and lipid peroxidation in the ventricular remodeling that is induced by tobacco smoke exposure after myocardial infarction.METHODS: After induced myocardial infarction, rats were allocated into two groups: C (control, n=25) and ETS (exposed to tobacco smoke, n=24). After 6 months, survivors were submitted to echocardiogram and biochemical analyses.RESULTS: Rats in the ETS group showed higher diastolic (C = 1.52 +/- 0.4 mm(2), ETS = 1.95 +/- 0.4 mm(2); p=0.032) and systolic (C = 1.03 +/- 0.3, ETS = 1.36 +/- 0.4 mm(2)/g; p=0.049) ventricular areas, adjusted for body weight. The fractional area change was smaller in the ETS group (C = 30.3 +/- 10.1 %, ETS = 19.2 +/- 11.1 %; p=0.024) and E/A ratios were higher in ETS animals (C = 2.3 +/- 2.2, ETS = 5.1 +/- 2.5; p=0.037). ETS was also associated with a higher water percentage in the lung (C = 4.8 (4.3-4.8), ETS = 5.5 (5.3-5.6); p=0.013) as well as higher cardiac levels of reduced glutathione (C = 20.7 +/- 7.6 nmol/mg of protein, ETS = 40.7 +/- 12.7 nmol/mg of protein; p=0.037) and oxidized glutathione (C = 0.3 +/- 0.1 nmol/g of protein, ETS = 0.9 +/- 0.3 nmol/g of protein; p=0.008). No differences were observed in lipid hydroperoxide levels (C = 0.4 +/- 0.2 nmol/mg of tissue, ETS = 0.1 +/- 0.1 nmol/mg of tissue; p=0.08).CONCLUSION: In animals exposed to tobacco smoke, oxidative stress is associated with the intensification of ventricular re-remodeling after myocardial infarction.

Papel da lipoperoxidação na intensificação da remodelação causada pelo betacaroteno após o infarto

FUNDAMENTO: Os mecanismos envolvidos na maior remodelação causada pelo betacaroteno após o infarto são desconhecidos. OBJETIVO: Analisar o papel da lipoperoxidação na remodelação ventricular após o infarto do miocárdio, em ratos suplementados com betacaroteno. MÉTODOS: Ratos foram infartados e distribuídos em dois grupos: C (controle) e BC (500mg/kg/dieta). Após seis meses, foram realizados ecocardiograma e avaliação bioquímica. Utilizamos o teste t, com significância de 5%. RESULTADOS: Os animais do grupo BC apresentaram maiores médias das áreas diastólicas (C = 1,57 ± 0,4 mm²/g, BC = 2,09 ± 0,3 mm²/g; p < 0,001) e sistólicas (C = 1,05 ± 0,3 mm²/g, BC = 1,61 ± 0,3 mm²/g; p < 0,001) do VE, ajustadas ao peso corporal do rato. A função sistólica do VE, avaliada pela fração de variação de área, foi menor nos animais suplementados com betacaroteno (C = 31,9 ± 9,3 %, BC = 23,6 ± 5,1 %; p = 0,006). Os animais suplementados com betacaroteno apresentaram valores maiores da relação E/A (C = 2,7 ± 2,5, BC = 5,1 ± 2,8; p = 0,036). Não foram encontradas diferenças entre os grupos em relação aos níveis cardíacos de GSH (C = 21 ± 8 nmol/mg de proteína, BC = 37 ±15 nmol/mg de proteína; p = 0,086), GSSG (C = 0,4 (0,3-0,5) nmol/g de proteína, BC = 0,8 (0,4-1,0; p = 0,19) de proteína; p = 0,246) e lipoperóxidos (C = 0,4 ± 0,2 nmol/mg de tecido, BC = 0,2 ± 0,1 nmol/mg de tecido; p = 0,086). CONCLUSÃO: A maior remodelação em animais infartados e suplementados com betacaroteno não depende da lipoperoxidação.

Hematologic, serum biochemistry and urinary values for captive Crab-eating Fox (Cerdocyon thous) in São Paulo state, Brazil

A importância do estudo dos valores hematológicos, de bioquímica sérica e urinários de Cachorro-do-mato (Cerdocyon thous) baseia-se na necessidade de cuidados e manutenção da sanidade destas populações. Este estudo visou investigar os parâmetros fisiológicos hematológicos, de bioquímica sérica e urinários dos Cachorros-do-mato de cativeiro, comparando as possíveis diferenças sexuais e de faixa etária. Foram colhidas amostras de sangue de 52 animais, pertencentes a diversos Zoológicos do Estado de São Paulo, Brasil. Foram colhidos cerca de 7mL de sangue, que foram utilizados para se obter os valores hematológicos e o perfil de bioquímica sérica. Também foram colhidos 5mL de urina para realização da urinálise. Não se encontraram diferenças entre os valores obtidos para machos e fêmeas tanto na hematologia, quanto na bioquímica sérica. Alguns parâmetros hematológicos e de bioquímica sérica foram afetados pela idade, mostrando diferenças significativas. Os resultados da urinálise foram demonstrados apenas em forma descritiva. Os principais valores encontrados foram, hemácias 4,35+0,73 x 106 células /µL, leucócitos totais 7,72+3,66 x 103 células /µL (predomínio de neutrófilos segmentados), plaquetas 227,06+111,58 x 103 células /µL, ureia 43,06+14,28mg/dL e creatinina 1,03+0,24mg/dL. Os valores hematológicos, de bioquímica sérica e urinários obtidos neste estudo podem ser utilizados como valores fisiológicos de Cachorros-do-mato de cativeiro. Pode-se concluir que as espécies silvestres necessitam de seus próprios valores de referência com necessidade de se diferenciar animais em cativeiro de animais de vida livre.

Teoria da Ruína em um Modelo de Markov com dois Estados

In this work, we present a risk theory application in the following scenario: In each period of time we have a change in the capital of the ensurance company and the outcome of a two-state Markov chain stabilishs if the company pays a benece it heat to one of its policyholders or it receives a Hightimes c > 0 paid by someone buying a new policy. At the end we will determine once again by the recursive equation for expectation the time ruin for this company

Determination and padronization of normal values of bone mineral density (BMD) of the acessory carpus bone in young Thoroughbred horse using optical densitometry in radiographic image

Em 12 fêmeas e 12 machos da raça Puro Sangue Inglês com idade média de 12 meses, avaliou-se os valores normais da densidade mineral óssea do carpo acessório em milímetros de alumínio (mmAl) até o momento do fechamento completo da epífise distal do rádio, por meio do método de densitometria óptica em imagens radiográficas. A avaliação foi realizada por meio de um programa computacional (software) especialmente desenvolvido para medida de densidade óptica em filmes de raios-X, o qual contém a imagem radiográfica do osso carpo acessório, região de partes moles adjacente ao carpo acessório e os degraus de uma escala de alumínio (phatom), que permitiu a medida de densidade mineral óssea, sendo esta a média aritmética da região de interesse determinada no osso carpo acessório correspondente ao valor em milímetros da escala. Os valores da densidade mineral óssea em mmAl do acessório do carpo em função da idade não apresentaram diferenças entre os sexos (p=0,86) permitindo que uma equação de reta fosse ajustada para ambos os sexos (densidade mineral óssea (DMO) mmAl = 3.109 + 0,056 x idade em meses), na faixa etária estudada.

Clinical evaluation and induced corneal vascularization study by native and anionic collagen membranes in rabbits corneas

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)