Effect of a post-polymerization treatments on the flexural strength and vickers hardness of reline and acrylic denture base resins

This study evaluated the effect of water-bath and microwave post-polymerization treatments on the flexural strength and Vickers hardness of four autopolymerizing reline resins (Duraliner II-D, Kooliner-K, Tokuso Rebase Fast-TR and Ufi Gel Hard C-UGH) and one heat-polymerized acrylic resin (Lucitone 550-L), processed using two polymerization cycles (short cycle - 90 minutes at 73°C and 100°C for 30 minutes; and long cycle - 9 hours at 71°C). For each material, thirty specimens (64 x 10 x 3.3 mm) were made and divided into 3 groups (n=10). Specimens were tested after: processing (control group); water-bath at 55°C for 10 minutes (reline materials) or 60 minutes (L); and microwave irradiation. Flexural strength tests were performed at a crosshead speed of 5 mm/min using a three-point bending device with a span of 50 mm. The flexural strengths values were calculated in MPa. One fragment of each specimen was submitted to Vickers hardness test. Data were analyzed by 2-way ANOVA followed by Tukey's HSD test (α=0.05). L microwaved specimens (short cycle) exhibited significantly higher flexural strength means than its respective control group (p<0.05). Water-bath promoted a significant increase (p<0.05) in flexural strength of K and L (long cycle). The hardness of the tested materials was not influenced by the post-polymerization treatments. Post-polymerization treatments could be used to improve the flexural strength of some materials tested.

Microhardness and fluoride release of restorative materials in different storage media

This study evaluated the surface microhardness and fluoride release of 5 restorative materials - Ketac-Fil Plus, Vitremer, Fuji II LC, Freedom and Fluorofil - in two storage media: distilled/deionized water and a pH-cycling (pH 4.6). Twelve specimens of each material, were fabricated and the initial surface microhardness (ISM) was determined in a Shimadzu HMV-2000 microhardness tester (static load Knoop). The specimens were submitted to 6- or 18-h cycles in the tested media. The solutions were refreshed at the end of each cycle. All solutions were stored for further analysis. After 15-day storage, the final surface microhardness (FSM) and fluoride release were measured. Fluoride dose was measured with a fluoride-specific electrode (Orion 9609-BN) and digital ion analyzer (Orion 720 A). The variables ISM, FSM and fluoride release were analyzed statistically by analysis of variance and Tukey's test (p<0.05). There was significant difference in FSM between the storage media for Vitremer (pH 4.6 = 40.2 ± 1.5; water = 42.6 ± 1.4), Ketac-Fil Plus (pH 4.6 = 73.4 ± 2.7; water = 58.2 ± 1.3) and Fluorofil (pH 4.6 = 44.3 ± 1.8; water = 38.4 ± 1.0). Ketac-Fil Plus (9.9 ± 18.0) and Fluorofil (4.4 ± 1.3) presented higher fluoride release in water, whereas Vitremer (7.4 ± 7.1), Fuji II LC (5.7 ± 4.7) and Freedom (2.1 ± 1.7) had higher fluoride release at pH 4.6. Microhardness and fluoride release of the tested restorative materials varied according to the storage medium.