Dielectric characterization of conducting textiles using free space transmission measurements: accuracy and methods for improvement

The dielectric behaviour of in-situ polymerized thin polypyrrole (PPy) films on synthetic textile substrates were obtained in the 1–18 GHz region using free space transmission and reflection methods. The PPy/para-toluene-2-sulphonic acid (pTSA) coated fabrics exhibited an absorption dominated total shielding effectiveness (SE) of up to −7.34 dB, which corresponds to more than 80% of incident radiation. The permittivity response is significantly influenced by the changes in ambient conditions, sample size and diffraction around the sample. Mathematical diffraction removal, time-gating tools and high gain horns were utilized to improve the permittivity response. A narrow time-gate of 0.15 ns produced accurate response for frequencies above 6.7 GHz and the high gain horns further improved the response in the 7.5–18 GHz range. Errors between calculated and measured values of reflection were most commonly within 2%, indicating good accuracy of the method.

Conducting polymer coated fabrics for potential applications in microwave frequencies : a study of electromagnetic properties

The microwave reflection, transmission and complex permittivity of paratoluene-2-sulfonic acid doped conducting polypyrrole (PPy/pTSA) coated Nylon-Lycra textiles in the 1-18 GHz frequency were investigated. The real part of permittivity increased with polymerization time and dopant concentration, reaching a plateau at certain dopant concentration and polymerization time. The imaginary part of permittivity showed a frequency dependent change throughout the tested range. All the samples had higher values of absorption than reflection. The total electromagnetic shielding effectiveness exceeded 80% for the highly pTSA doped samples coated for 3 hours.

A calibration for surface analysis on aluminium alloys by RF-Glow-Discharge Optical Emission Spectrometry

Glow-Discharge Optical Emission Spectrometry (GD-OES) is a powerful technique for the rapid analysis of elements in a solid surface as a function of depth. DC-GD-OES allows depth profiling on electrically conductive surfaces only, and has proven to be difficult for the analysis of insulating layers, such as oxides. However, the technique of radio-frequency (RF) GD-OES has the advantage of being able to depth profile through multiple layers, both conducting and insulating. In this work, a LECO GDS- 850A spectrometer was calibrated for aluminium, oxygen, and other elements, with the RF source installed. A quantitative depth profile for a sample of tempered aluminium alloy 7475 is presented and compared with earlier work[1,2].

Characterization of conducting polymer coated fabrics at microwave frequencies

Purpose – The purpose of this paper is to investigate microwave reflection, transmission, and complex permittivity of p-toluene-2-sulfonic acid doped conducting polypyrrole coated nylon-lycra textiles in the 1-18?GHz frequency with a view to potential applications in the interaction of electromagnetic radiation with such coated fabrics.

Design/methodology/approach – The chemical polymerization of pyrrole is achieved by an oxidant, ferric chloride and doped with p-toluene sulfonic acid (pTSA) to enhance the conductivity and improve stability. Permittivity of the conducting textile substrates is performed using a free space transmission method accompanied by a mathematical diffraction reduction method.

Findings – The real part of permittivity increases with polymerization time and dopant concentration, reaching a plateau at certain dopant concentration and polymerization time. The imaginary part of permittivity shows a frequency dependent change throughout the test range. All the samples have higher values of absorption than reflection. The total electromagnetic shielding effectiveness exceeds 80 percent for the highly pTSA doped samples coated for 3?h.

Originality/value – A non-contact, non-destructive free space method thin flexible specimens to be tested with high accuracy across large frequency range. The non-destructive nature of the experiments enables investigation of the stability of the microwave transmission, reflection, absorption and complex permittivity values. Moreover, mathematical removal of the diffraction enables higher accuracy.

The influence of polymerization time and dopant concentration on the absorption of microwave radiation in conducting polypyrrole coated textiles

Temperature changes in conducting polypyrrole/para-toluene-2-sulphonic acid (PPy/pTSA) coated nylon textiles due to microwave absorption in the 8–9 GHz and 15–16 GHz frequency ranges were obtained by a thermography station during simultaneous irradiation of the samples. The temperature values are compared and related to the amounts of reflection, transmission and absorption obtained with a non-contact free space transmission technique, indicating a relationship between microwave absorption and temperature increase. Non-conductive samples showed no temperature increase upon irradiation irrespective of frequency range. The maximum temperature difference of around 4 °C in the conducting fabrics relative to ambient temperature was observed in samples having 48% absorption and 26.5 ± 4% reflection. Samples polymerized for 60 or 120 min with a dopant concentration of 0.018 mol/l or polymerized for 180 min with a dopant concentration of 0.009 mol/l yielded optimum absorption levels. As the surface resistivity decreased and the reflection levels increased, the temperature increase upon irradiation reduced.

Conducting nylon, cotton and wool yarns by continuous vapor polymerization of pyrrole

Conductive textile yarns were prepared by a continuous vapor polymerization method; the application of polypyrrole by the continuous vapor polymerization method used is designed for the easy adaptation into industrial procedures. The resultant conductive yarns were examined by longitudinal and cross-sectional views, clearly showing the varying levels of penetration of the polymer into the yarn structure. It was found that for wool the optimum specific resistance was achieved by using the 400 TPM yarn with a FeCl3 solution concentration of 80 g/L FeCl3 to produce 1.69 Ω g/cm2. For cotton yarn, the optimum specific resistance of 1.53 Ω g/cm2 was obtained with 80 g/L of a FeCl3 solution.