The influence of residual stress and crystallite size on the magnetic properties of electrodepo sited nanocrystalline Pd-Co alloys

Nanocrystalline Pd-Co alloys were obtained by electrodeposition from an ammoniacal chloride bath. The influence of the crystallite size and the residual stress on the magnetic properties of the alloys was investigated. The residual stress increased as the applied current density was increased. It was associated to the high nucleation rate during electrodeposition and correlated to the lattice strain, estimated from the XRD patterns. Also from the XRD patterns the average crystallite size and the lattice constant were determined by Scherrer's and Rietveld's methods, respectively. Both parameters were directly influenced by the applied current density. Magnetic properties such as coercivity, remanence, saturation magnetization and squareness showed strong dependence on the residual stress and crystallite size. Coercivity higher than 1 kOe was achieved when a high current density was applied. High coercivity was attributed to the presence of residual stress and to the small crystallite size of deposits. (C) 2007 Elsevier B.V. All rights reserved.

Barium titanate screen-printed thick films

Barium titanate (BT) thick films were prepared from mechanically activated powders based on BaCO(3) and TiO(2). After homogenization and milling in a high-energy vibro mill, the powders were calcined at 700 degreesC for 2 h by slow heating and cooling rates. A thick film paste was prepared by mixing BT fine powders with small amount of low temperature sintering aid and organic binder. The thick films were screen-printed on alumina substrates electroded with Ag-Pd. The BT films were sintered at 850 degreesC for 1 h. The thickness was 25-75 mum depending of number of layers. The microstructure of thick films and the compatibility between BT layers and substrate were investigated by SEM Results of dielectric property measurements are also reported. (C) 2002 Elsevier B.V. Ltd and Techna S.r.l. All rights reserved.

Thermal behavior of alpha-(Cu-Al-Ag) alloys

Thermal behavior of alpha-(Cu-Al-Ag) alloys, i.e. alloys with composition less than about 8.5 mass% Al, was studied using differential scanning calorimetry (DSC), differential thermal analysis (DTA), scanning electron microscopy (SEM), energy dispersive X-ray analysis (EDX) and X-ray diffractometry (XRD). The results indicated that the presence of silver introduces new thermal events ascribed to the formation of a silver-rich phase and, after addition higher amounts than 8 mass% Ag to the Cu-8 mass% Al alloy it is possible to observe the formation of the gamma(1) phase (Al4Cu9), which is only observed in alloys containing minimum of 9 mass% Al. These results may be attributed to some Ag characteristics and its interaction with Cu and Al.

Experimental and theoretical study of the compound [Pd(dmba)(NCO)(imz)]

The compound [Pd(dmba)(NCO)(imz)] (dmba = N,N-dimethylbenzilamine; NCO = cyanate; imz = imidazole) was studied through experimental and theoretical methods. The complex was synthesized and characterized by IR and NMR spectroscopy. To an appropriate representation of the molecular environment, Gaussian basis sets for the constituent atoms of the compound were built and, after adequate supplementation with polarization and diffuse functions, they were used to study the molecule. Calculations of electronic and vibrational structure of two possible isomers were carried out, showing that the compound, which contains the NCO GROUP trans to the Pd-C bond, is 4.29 kcal/mol more stable than the analogous one, where the imz ligand is trans to the Pd-C bond. The calculated molecular parameters, bond distances, and bond angles showed that the geometry around the metallic center is square-planar with the cyanate being linear. The theoretical infrared spectrum of C(1) symmetry (electronic state (1)A) is in accordance with the experimental one. It also verified the contribution of Pd (4d(xz) + 4d(yz)) and Pd (4d(xy)) in the HOMO and LUMO orbitals, respectively. (c) 2006 Elsevier B.V. All rights reserved.

Low-weight coordination polymers derived from the self-assembly reactions of Pd(II) pyrazolyl compounds and azide ion

The low-weight Pd(II) coordination polymers [(N(3))(HL)Pd {Pd(3)(mu-N(3))(mu-L)(5)}10(mu-L)(2)Pd(L)(HL)]{L = Pz(-) (1); mPz(-) (2), IPz(-)(3)} and [(N(3))(HPz)Pd{Pd(6)(mu-N(3))(2)(mu-PZ)(5)(mu-L)(5)}(10)(mu-L)(2)Pd(Pz)(HPz)] {L = mPz(-) (4), dmPz(-) (5); IPz(-) (6)} {L = pyrazolate (Pz(-)), 4-methylpyrazolate(mPz(-)), 4-iodopyrazo late (IPz(-)), 3,5-dimethylpyrazolate (dmPz(-))} have been prepared in this work. IR spectra clearly indicated the exobidentate nature of pyrazolato ligands as well the end-on coordination mode of the azido group. The molecular weight determinations by osmometry indicated that the species have a low degree of polymerization (n = 10). NMR experiments showed two pyrazolate environments in a 2:1 ratio, being assigned to the six-membered ring Pd(mu-L)(2)Pd and the Pd(mu-N(3))(mu-L)Pd metallocycle, respectively. UV-visible spectroscopy gave further evidences for the oligomeric structures of 1-6. Some alternative structures for the isostructural polymers have been suggested. (c) 2005 Elsevier Ltd. All rights reserved.

Efficient plasmonic coupling between Er3+:(Ag/Au) in tellurite glasses

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Er3+-doped germanate glasses for active waveguides prepared by Ag+/K+ <-> Na+ ion-exchange

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Effect of Ag concentration on the thermal behavior of the Cu-10 mass% Al and Cu-11 mass% Al alloys

In this work the effect of Ag concentration on the thermal behavior of the Cu-10 mass% Al and Cu-11 mass% Al alloys with additions of 4, 6, 8 and 10 mass% Ag was studied using differential scanning calorimetry (DSC), in situ X-ray diffractometry (XRD) and scanning electron microscopy (SEM). The results showed that for the Cu-10 mass% Al alloy Ag addition induce the beta'(1) phase formation and for the Cu-11 mass% Al alloy these additions increase the amount of martensite formed on quenching and decrease the stability range of this phase on heating.

Crystal structure of di-mu(N,S)-thiocyanato-bis[(N-benzylideneaniline-C-2,N)palladium(II)], [Pd(C6H4CH=NC6H5)(mu-SCN)](2)

C28H20N4Pd2S2, monoclinic, P12(1)/c1 (No. 14), a = 11.325(1) Angstrom, b = 13.530(1) Angstrom, c = 17.925(1) Angstrom, beta = 106.23(1)degrees, V = 2637.1 Angstrom(3), Z = 4, R-gt(F) = 0.052, wR(ref)(F-2) = 0.129, T = 293 K.

Thermal behavior of the Cu-22.55 at.%Al alloy with small Ag additions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Completeness of beta-phase decomposition reaction in Cu-Al-Ag alloys

The completeness of beta-phase decomposition reaction in the Cu-11wt%Al-xwt%Ag alloys (x = 0, 1, 2, and 3) was studied using differential scanning calorimetry (DSC), X-ray diffractometry (XRD), and optical microscopy (OM). The results indicated that beta-phase transformations are highly dependent on cooling rate and on the presence of Ag. on slow cooling, the silver presence prevents the beta- and beta(1)-phase decomposition; thus, inducing the martensitic phase formation. After rapid cooling, a new thermal event is observed and the reverse martensitic transformation is shifted to lower temperatures.

Thermal study of mononuclear Pd(II) complexes of the type [Pd(X)(2)(Rtu)(PPh3)] (X = Cl, SCN; Rtu = N-methylthiourea, N-phenylthiourea)

The synthesis, spectroscopic characterization, and thermal analysis of the compounds [Pd(X)(2)(mtu)(PPh3)] (X = Cl- (1), SCN- (2); mtu = N-methylthiourea; PPh3 = triphenylphosphine) and [Pd(X)(2)(phtu)(PPh3)] (X = Cl- (3), SCN- (4); phtu = N-phenylthiourea) are described. The thermal decomposition of the compounds occurs in two, three, or four stages and the final decomposition products were identified as Pd-0 by X-ray powder diffraction. The thermal stability order of the complexes is 4 > 3 > 2 > 1.

Pt(II) and Ag(I) complexes with acesulfame: Crystal structure and a study of their antitumoral, antimicrobial and antiviral activities

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)