Microstructure and photoluminescence of a-SiOx : H

Two strong photoluminescence (PL) bands in the spectral range of 550-900 nm have been observed at room temperature from a series of a-SiOx:H films fabricated by plasma-enhanced chemical vapor deposition (PECVD) technique. One is composed of a main band in the red-light region and a shoulder; the other is located at about 850 nm, only found after 1170 degrees C annealing in N-2 atmosphere. In conjunction with infrared (IR) and micro-Raman spectra, it is thought that the two PL bands are associated with a-Si clusters in the SiOx network and nanocrystalline silicon in SiO2, respectively.

Study of microstructure of high stability hydrogenated amorphous silicon films by Raman scattering and infrared absorption spectroscopy

The microstructure, hydrogen bonding configurations and hydrogen content of high quality and stable hydrogenated amorphous silicon (a-Si:H) films prepared by a simple ''uninterrupted growth/annealing" plasma enhanced chemical vapor deposition technique have been investigated by Raman scattering and infrared absorption spectroscopy. The high stability a-Si:H films contain small amounts of a microcrystalline phase and not less hydrogen (10-16 at. %), particularly, the clustered phase hydrogen, Besides, the hydrogen distribution is very inhomogeneous. Some of these results are substantially distinct from those of conventional device-quality n-Si:H film or stable cr-Si:H films prepared by the other techniques examined to date. The stability of n-Si:H films appears to have no direct correlation with the hydrogen content or the clustered phase hydrogen concentration. The ideal n-Si:H network with high stability and low defect density is perhaps not homogeneous. (C) 1998 American Institute of Physics.

Silicon thin films prepared in the transition region and their use in solar cells

Diphasic silicon films (nc-Si/a-Si:H) have been prepared by a new regime of plasma enhanced chemical vapour deposition in the region adjacent of phase transition from amorphous to microcrystalline state. Comparing to the conventional amorphous silicon (a-Si:H), the nc-Si/a-Si:H has higher photoconductivity (sigma(ph)), better stability, and a broader light spectral response range in the longer wavelength range. It can be found from Raman spectra that there is a notable improvement in the medium range order. The blue shift for the stretching mode and red shift for the wagging mode in the IR spectra also show the variation of the microstructure. By using this kind of film as intrinsic layer, a p-i-n junction solar cell was prepared with the initial efficiency of 8.51 % and a stabilized efficiency of 8.01% (AM 1.5, 100 mw/cm(2)) at room temperature. (c) 2006 Published by Elsevier B.V.

STUDY OF MICROSTRUCTURE AND DEFECTS IN HYDROGENATED MICROCRYSTALLINE SILICON FILMS

Microcrystalline silicon films were deposited by very high frequency (VHF) plasma-enhanced chemical vapor deposition (PECVD) with different hydrogen dilution. The microstructure of these films was investigated using Raman spectroscopy and infrared absorption (IR) spectra. The crystalline, amorphous, and grain boundary volume fractions X-c, X-a and X-gb were estimated from Raman measurements. An interface structure factor (R-if) is proposed to characterize the grain boundary volume fractions in IR spectroscopy. The density of states (DOS) of the microcrystalline crystalline silicon films were studied by phase-shift analysis of modulated photocurrent (MPC) and photoconductivity spectroscopy. It was observed that DOS increases with increasing grain boundary volume fractions, while the values of electron mobility-lifetime product mu T-e(e) disease.

Variation of Optical Quenching of Photoconductivity with Resistivity in Unintentional Doped GaN

The optical quenching of photoconductivity under dual illumination in GaN samples with different resistivity is investigated to reveal the variation of deep levels. The samples are grown by metal organic chemical vapour deposition without intentional doping. Quenching bands centered at 1.35 eV, 1.55 eV, 1.98 eV, and 2.60 eV are observed. It is found that the 1.98 eV quenching band is dominated in all the samples and the 2.60 eV band is observed only in the high-resistivity samples. The possible defect levels responsible for the quenching bands and the origin of different quenching behaviour at 2.60 eV are discussed. It is suggested that the defect level responsible for quenching at 2.60 eV plays an important role for the enhancement of resistivity.

Electroluminescence behavior of ZnO/Si heterojunctions: Energy band alignment and interfacial microstructure

n-ZnO/p-Si heterojunction light-emitting diodes (LEDs) show weak defect-related electroluminescence (EL). In order to analyze the origin of the weak EL, the energy band alignment and interfacial microstructure of ZnO/Si heterojunction are investigated by x-ray photoelectron spectroscopy. The valence band offset (VBO) is determined to be 3.15 +/- 0.15 eV and conduction band offset is -0.90 +/- 0.15 eV, showing a type-II band alignment. The higher VBO means a high potential barrier for holes injected from Si into ZnO, and hence, charge carrier recombination takes place mainly on the Si side rather than the ZnO layer. It is also found that a 2.1 nm thick SiOx interfacial layer is formed at the ZnO/Si interface. The unavoidable SiOx interfacial layer provides to a large number of nonradiative centers at the ZnO/Si interface and gives rise to poor crystallinity in the ZnO films. The weak EL from the n-ZnO/p-Si LEDs can be ascribed to the high ZnO/Si VBO and existence of the SiOx interfacial layer.