Effect of grain size on the performance of extruded magnesium alloy tubes in three-point bending

The performance of extruded AZ31, AZ61 and AM-EX1 tubes was examined in three-point bending. Different extrusion temperatures were used to investigate the effect of grain size on the load-carrying capacity, energy absorption and fracture propensity of the tubes. Results showed that while the peak load increased with a smaller average recrystallised grain size, the retention of large elongated un-recrystallised grains in the microstructure reduced the load. The presence of the large elongated grains also appeared detrimental to the ability of the tube to deform before fracture.

An investigation of a phosphinate-based ionic liquid for corrosion protection of magnesium alloy AZ31

This work reports a preliminary exploration of the potential of the ionic liquid trihexyl(tetradecyl)phosphonium bis(2,4,4-trimethylpentyl)phosphinate (P_6,6,6,14M₃PPh) for use as a conversion coating agent for corrosion protection of magnesium alloy AZ31. Results obtained for the as received IL did not indicate any measureable improvement in protection. However, when the IL was allowed to reach equilibrium/saturation with moisture from the atmosphere, treatment with this ‘wet’ solution resulted in a substantial improvement in corrosion resistance. Preliminary electrochemical, optical, and spectroscopic characterization of the film will be presented along with a possible mechanism for film formation.

Corrosion of magnesium alloy ZE41 – The role of microstructural features

Magnesium alloy ZE41, used extensively in the aerospace industry, possesses excellent mechanical properties albeit poor corrosion resistance. This paper investigates the mechanism of corrosion and the interaction between the grain boundary intermetallic phases, the Zr-rich regions within the grains and the bulk Mg-rich matrix. The results of optical and scanning electron microscopy (SEM) together with energy-dispersive X-ray (EDX) and atomic force microscopy (AFM) potential map measurements have shown the importance of the microstructure in the initiation and propagation of corrosion in an aqueous environment, indicating that the Zr-rich regions play a distinct role in the early stages of corrosion in this alloy.

Synthesis and physical property characterisation of phosphonium ionic liquids based on P(O)2(OR)2− and P(O)2(R)2− anions with potential application for corrosion mitigation of magnesium alloys

Phosphonium cation based ionic liquids (ILs) have become of interest due to their unique chemical and electrochemical stability as well as their promising tribological properties. At the same time, interest has also grown in the use of phosphate and phosphinate based ionic liquids for corrosion protection of reactive metals. In this work we describe the synthesis and characterization of six novel ionic liquids based on the tetraalkylphosponium cation coupled with organophosphate and organophosphinate anions and their sulfur analogues. The conductivity and viscosity of these ILs has been measured and discussed in terms of the nature of the interactions, effect of anion basicity and the extent of ionic character. The reaction of the IL with a ZE41 magnesium aerospace alloy surface is also demonstrated.

Control of magnesium interfacial reactions in aqueous electrolytes towards a biocompatible battery

A stable magnesium battery has been developed based on a magnesium anode, a poly(dioxyethane thiophene) (PEDOT) cathode and a near-saturated aqueous solution of LiCl, MgCl₂, or mixture of these salts at pH of 11. This combination leads to a low water activity in the electrolyte, which thus suppresses the hydrogen evolution reaction on Mg, as well as producing a stable oxy-hydroxide film which protects the metal surface from freely corroding. The conducting polymer cathode is reduced somewhat during the discharge process, however, appears to be readily re-oxidised (as determined from the resistance) by the oxygen present in the cell. The cell is therefore primarily a Mg/O₂ battery, however, the PEDOT appears to enhance the performance, in particular the discharge voltage.

Atomic scale simulation of deformation in magnesium single crystals

The deformation behaviour of magnesium single crystals under plane strain conditions has been examined using molecular dynamics modelling. The simulations were based on an existing atomic potential for magnesium taken from the literature. A strain of 10% was applied at rates of 3x10⁹s^-1 and 3x10⁷s^-1. The simulations predicted the formation of mechanical twins that accommodated extension in the c-axis direction of the hexagonal unit cell. However, the predicted twin is not of the same kind found in magnesium, but is that commonly observed in titanium. It is believed that further analysis of the physical properties predicted by this interatomic potential will shed more light on the atomic processes controlling twinning in Magnesium alloys. It also highlights the need for improvements to the interatomic potential such that more accurate deformation behaviour can be attained.

Potentiostatic control of ionic liquid surface film formation on ZE41 magnesium alloy

The generation of potentially corrosion-resistant films on light metal alloys of magnesium have been investigated. Magnesium alloy, ZE41 [Mg−Zn−Rare Earth (RE)-Zr, nominal composition 4 wt % Zn, 1.7 wt % RE (Ce), 0.6 wt % Zr, remaining balance, Mg], was exposed under potentiostatic control to the ionic liquid trihexyl(tetradecyl)phosphonium diphenylphosphate, denoted [P_6,6,6,14][DPP]. During exposure to this IL, a bias potential, shifted from open circuit, was applied to the ZE41 surface. Electrochemical impedance spectroscopy (EIS) and chronoamperometry (CA) were used to monitor the evolution of film formation on the metal surface during exposure. The EIS data indicate that, of the four bias potentials examined, applying a potential of −200 mV versus OCP during the exposure period resulted in surface films of greatest resistance. Both EIS measurements and scanning electron microscopy (SEM) imaging indicate that these surfaces are substantially different to those formed without potential bias. Time of flight-secondary ion mass spectrometry (ToF-SIMS) elemental mapping of the films was utilized to ascertain the distribution of the ionic liquid cationic and anionic species relative to the microstructural surface features of ZE41 and indicated a more uniform distribution compared with the surface following exposure in the absence of a bias potential. Immersion of the treated ZE41 specimens in a chloride contaminated salt solution clearly indicated that the ionic liquid generated surface films offered significant protection against pitting corrosion, although the intermetallics were still insufficiently protected by the IL and hence favored intergranular corrosion processes.

Visualisation of chemical processes during corrosion of zinc using magnetic resonance imaging

Compositional and structural changes within an electrolyte solution above an electrochemically active metal surface have been visualised using magnetic resonance imaging (MRI) for the first time. In these proof-of-concept experiments, zinc metal was galvanically corroded in a saturated lithium chloride solution. Magnetic resonance relaxation maps were taken during the corrosion process and spatial variations in both T₁ and T₂ relaxation times were observed to change with time. These changes were attributed to changes in the speciation of zinc ions in the electrolyte.

Association between magnesium intake and depression and anxiety in community-dwelling adults : The Hordaland Health Study

Objective: Systemic inflammation is associated with both the dietary intake of magnesium, and depression. Limited experimental and clinical data suggest an association between magnesium and depression. Thus, there are reasons to consider dietary magnesium as a variable of interest in depressive disorders. The aim of the present study was to examine the association between magnesium intake and depression and anxiety in a large sample of community-dwelling men and women. This sample consisted of 5708 individuals aged 46–49 or 70–74 years who participated in the Hordaland Health Study in Western Norway.

Methods: Symptoms of depression and anxiety were self-reported using the Hospital Anxiety and Depression Scale, and magnesium intake was assessed using a comprehensive food frequency questionnaire.

Results: There was an inverse association between standardized energy-adjusted magnesium intake and standardized depression scores that was not confounded by age, gender, body habitus or blood pressure (β=−0.16, 95% confidence interval (CI)=−0.22 to −0.11). The association was attenuated after adjustment for socioeconomic and lifestyle variables, but remained statistically significant (β=−0.11, 95%CI=−0.16 to −0.05). Standardized magnesium intake was also related to case-level depression (odds ratio (OR)=0.70, 95%CI=0.56–0.88), although the association was attenuated when adjusted for socioeconomic and lifestyle factors (OR=0.86, 95%CI=0.69–1.08). The inverse relationship between magnesium intake and score and case-level anxiety was weaker and not statistically significant in the fully adjusted models.

Conclusion: The hypothesis that magnesium intake is related to depression in the community is supported by the present findings. These findings may have public health and treatment implications.