Different methods of finishing and polishing enamel

Statement of problem. Highly polished enamel surfaces arc recommended for axial tooth surfaces that will serve as guiding planes and be contacted by component parts of a removable partial denture. There is little evidence to support the assumption that this tooth modification will provide accurate adaptation of the framework and prevent build-up of plaque.Purpose. The aim of this investigation was to evaluate the surface roughness of the tooth enamel, prepared to serve as guiding planes, with different polishing systems.Material and methods. Four different methods (designated A, B, C, and D) for finishing and polishing the prepared enamel surfaces of 20 freshly extracted third molar teeth were studied. Each method involved 3, 4, or 5 different steps. The roughness of each specimen was measured at the start of each method before recontouring, after recontouring, and after each step of the 4 finishing and polishing procedures. The 4 experimental finishing methods were applied after recontouring the axial surfaces (buccal, lingual, and proxinial) of each tooth. Thus the 20 teeth (60 surfaces) were finished and polished by use of 1 of the experimental methods. Surface roughness was measured with a profilometer (mum); the readings of the unpolished enamel Surfaces were recorded as control measurements. Results were statistically analyzed with one-way analysis of variance followed by Tukey's test at the 95% level of confidence.Results. The highest roughness mean values (14.41 mum to 16.44 mum) were found when the diamond bur was used at a high speed for tooth preparation. A significant decrease in roughness values was observed with the diamond bur at a low speed (P<.05). Analysis of the roughness values revealed that all polishing methods produced surface roughness similar to that of the corresponding control teeth.Conclusion. Within the limitations of this study, all finishing procedures tested effectively promoted an enamel surface similar to the original unpolished enamel.

Influence of age on the behavior of dental pulp of dog teeth after capping with an adhesive system or calcium hydroxide

This study evaluated histomorphologically the influence of chronological age of the dog on the dental pulp-healing process after capping with the All Bond 2 system or with calcium hydroxide paste. The animals were divided according to age into young and adult groups. Class 5-type cavities were prepared, and the pulp was submitted to an exposure of a diameter of 0.5 mm. The pulp of the teeth was then protected with the adhesive system or with a calcium hydroxide paste. Sixty days after treatment, the results obtained with the adhesive system in the young group were significantly better than those in the adult group. With calcium hydroxide, the results were similar for both groups. The pulp treated with calcium hydroxide exhibited a complete hard tissue bridge and a pulp without inflammatory reaction, a fact not observed when the adhesive system was used. In conclusion, the chronological age of the pulp influenced the comparative results only for the adhesive system (P = 0.1), and the total results were better with calcium hydroxide than with the All Bond 2 system (P = 0.01).

Pulpal temperature increases with Er : YAG laser and high-speed handpieces

Statement of problem. During tooth preparation, both high-speed handpieces and lasers generate heat, which, if not controlled, can cause pulpal necrosis.Purpose. The aim of this study was to compare temperature increases produced by a high-speed dental handpiece with those produced by a relatively new instrument, the Er:YAG (erbium: yttrium-aluminum-garnet) laser.Material and methods. Thirty bovine mandibular incisors were reduced to an enamel/dentin thickness of 2.5 mm. Class V preparations were completed to a depth of 2.0 mm, measured with a caliper or by a mark oil the burs. A thermocouple was placed inside the pulp chamber to determine temperature increases (degreesC). Analysis was performed on the following groups (n = 10): Group 1, high-speed handpiece without water cooling, Group 11, high-speed handpiece with water cooling (30 mL/min), and Group III, the noncontact Er:YAG laser (2.94 mum at 350 mJ/10 Hz) with water cooling (4.5 mL/min). The temperature increases were recorded by a computer linked to the thermocouples. The data were analyzed using the Kruskal-Wallis test. The Dunn multiple comparison test was used as post hoc test (alpha = .05).Results. The average temperature rises were: 11.64degreesC (+/-4.35) for Group 1, 0.96degreesC (+/-0.71) for Group 11, and 2.69degreesC (+/-1.12) for Group III. There were no statistical differences between Groups 11 and III, both 11 and III differed from Group I significantly (P = .000 and P = .002, respectively).Conclusion. The preparations made with the high-speed and the laser instrument generated similar heat increases under water cooling. Water cooling was essential to avoid destructive temperature increases when using both the high-speed handpiece and laser.

Sealing evaluation of the cervical base in intracoronal bleaching

Discoloration of non-vital teeth is an esthetic deficiency frequently requiring bleaching treatment. The purpose of this study was to evaluate in vitro the cervical base efficacy in order to prevent or to minimize the leakage along the root canal filling and into the dentinal tubules. Thirty-eight extracted single-root human teeth were used, which were biomechanically prepared, filled, and divided into three experimental groups: G1, a cervical base was applied (3 mm of thickness) below the cemento-enamel junction, with resin-modified glass-ionomer cement (Vitremer); G2, the base was done with glass-ionomer cement (Vidrion R); and G3 (Control), did not receive any material as base. A mixture of sodium perborate and hydrogen peroxide 30% was placed inside the pulp chamber for 3 days, and the access opening was sealed with Cimpat. This procedure was repeated thrice. Soon after this, a paste of calcium hydroxide was inserted into the pulp chamber for 14 days. All teeth were covered with two layers of sticky wax, except the access opening, and immersed in blue India Ink for 5 days. The results did not show statistically significant differences between the three groups concerning the leakage inside the dentinal tubules. Regarding the apical direction, a statistical difference (ANOVA P < 0.05) was observed among the experimental group G1 and control group G3. No statistically significant difference was observed between G2 and G3 groups. Therefore, the placement of a cervical base before internal bleaching procedures is still recommended.

Study of microleakage at class V cavities prepared by Er : YAG laser using rewetting surface treatment

Objective: This study was conducted to analyze microleakage in Class V cavity preparation, using rewetting (or not) just after burr or Er:YAG laser preparation of enamel and dentin walls in permanent teeth. Background Data: Several studies reported microleakage around composite restorations when cavity preparation was done or treated by Er:YAG laser. As the hybridized laser is removed when this laser is used to cut dental hard tissue, there is a need for new materials or techniques to minimize gaps and microleakage. Results: Primer solution showed significant effect in enamel and dentin, at the level of 5%, when Er:YAG laser was used as a cutting tool. Using primer solution after phosphoric acid in preparations with the laser, microleakage was similar in degree to when cavities were prepared with the burr. Conclusion: Re-wetting surface just after Er:YAG irradiation and chemical treatment with phosphoric acid using HEMA aqueous solution seems to improve the quality of bioattachment between the adhesive system and enamel/dentin, showing similarities between restoration behaviors independently of the cutting tool, whether burr or laser.