The aims of the present study were to evaluate the morphometry of corpus luteum (CL) and progesterone (P-4) plasma concentration of 86 buffaloes (33 pregnant and 53 non-pregnant) and 95 cows (36 pregnant and 59 non-pregnant) at the moment of slaughter. Seventy CLs of buffaloes and 110 CL of cattle were analyzed. The CL classified as II and III were more common in both species (35.7 and 41.4% for buffaloes and 43.6 and 35.5% for cows). The 29 non-pregnant buffaloes had a total of 36 CL, being 19.4% CLI; 33.3% CL II; 27.8% CL III and 19.4% CL IV. The 51 nonpregnant cows had a total of 71 CL, being 26.8% CL I; 47.9% CL II; 21.1% CL III and 4.2% CL IV. The average diameters of bubaline and bovine CL were 5.2 +/- 0.9 and 6.4 +/- 1.8 mm (CL I); 17.6 +/- 2.6 and 19.8 +/- 3.2 mm (CL II); 17.2 +/- 2.1 and 20.0 +/- 3.2 mm (CL III); 7.8 +/- 1.8 and 8.7 +/- 2.7 mm (CL IV), respectively. The mean plasma concentrations of P4 were 5.6 (CL I); 5.4 (CL II); 4.7 (CL III) and 0.5 (CL IV) ng/mL for buffaloes and 0.02 (CL I); 6.3 (CL II) and 6.4 (CL III) ng/mL for cows. In both species, P4 concentration was similar between stages II and III. The results indicated that the characterization of the CL provides important information about the status of estrous cycle.

A Quality Assessment of Titanium Castings Produced in an Experimental Short-Heating-Cycle Investment

The aim of this study was to evaluate the quality of casting produced in an experimental short-term heating-cycle investment. Thus, reaction layer and castability of titanium casting using an experimental spinel-based investment (VR) with short heating cycle were compared with the commercial short-heating-cycle spinel-based investment Trinell (TR), the silica-phosphate-based investment Rematitan Plus ( RP), and the conventional spinel-based investment Rematitan Ultra (RU). VR has polymeric fibers added to inorganic particles. Reaction layer assessments were carried out using Vickers hardness and elemental analysis using dispersive X-ray microanalysis (EDX). Mesh patterns were used for castability test, and powder characterization was made by scanning electron microscopy (SEM). Hardness evaluation showed no difference among the investments between 100 and 200 mu m. The most important contaminant element for VR, TR, and RU was oxygen. Higher levels of mold filling were found for TR, VR, and RU compared with that obtained with RP. The quality of castings, characterized by means of the assessments of reaction layer and castability, made from the VR was similar to the commercial investments TR and RU but superior to the RP.