Synthesis, mechanical and electrical properties of carbon microcoils and nanocoils

The results on the synthesis, mechanical and electrical properties of carbon microcoils and nanocoils (CMCs, CNCs) synthesized using catalytic CVD and Ni-P and Co-P catalyst alloys, respectively, are reported. SEM analysis reveals that the CMCs and CNCs have unique helical morphologies, and diameters of 5.0-9.0 μm and 450-550 nm, respectively. Moreover, CMCs with flat cross-section can be stretched to 3 times their original coil lengths. Current-voltage characteristics of a single microcoil have also been obtained. It is found that the CMCs have the electrical conductivity between 100 and 160 S/cm, whereas the electrical resistance increases by about 20% during the coil extension. Besides, the microcoils can produce light in vacuum when the test voltage reaches 10 V. The emission intensity increases as the voltage increases. The mechanical and electrical properties of CMCs and CNC make them potentially useful in many applications in micromagnetic sensors, mechanical microsprings and optoelectronics.

Tailoring microplasma nanofabrication : from nanostructures to nanoarchitectures

An innovative approach to fabricate tailored Mo-oxide nanostructures and composite nanoarchitectures using atmospheric microplasmas sustained in a gap between a Mo wire and a Si substrate is reported. It is shown that at smaller gap distances spherical nanoparticles are produced whereas sheet-like structures emerge when the gap is increased. When the wire is consumed continuously, it is possible to synthesize complex nanoarchitectures made of nanoparticles decorated with nanosheets. These processes can be applied for other metal and metal oxide materials and suggest a way to improve control and predictability, common problems in high-yield nanofabrication.

Unconventional Ni–P alloy-catalyzed CVD of carbon coil-like micro- and nano-structures

Conventional catalyzed thermal CVD of carbon microcoils commonly suffers from poor control of the coil shape and morphology and rarely reaches the nanoscale size range. This article reports on an unconventional Ni-P alloy-catalyzed, high-throughput, highly reproducible CVD of ultra-long carbon coil-like micro- and nano-structures using acetylene precursor at relatively low process temperatures. Helical carbon microcoils with consistently uniform, circular cross-sections and a high degree of crystallinity have been synthesized at 750 °C. A further reduction of the temperature to 650 °C led to the growth of ultra-long (up to several mm) wave-like carbon nanofibers made of two nanowires with the diameters in the 100-200 nm range. The results of the XRD and Raman analysis reveal that the nanofibers feature only a slightly more disordered structure compared to the microcoils. Our results suggest that morphology and structure of the carbon coil-like micro- and nano-structures can be tailored by the appropriate alloying of the catalyst and the choice of the CVD process parameters.

Numerical modelling and analysis of the blast performance of laminated glass panels and the influence of material parameters

This paper presents a comprehensive numerical procedure to treat the blast response of laminated glass (LG) panels and studies the influence of important material parameters. Post-crack behaviour of the LG panel and the contribution of the interlayer towards blast resistance are treated. Modelling techniques are validated by comparing with existing experimental results. Findings indicate that the tensile strength of glass considerably influences the blast response of LG panels while the interlayer material properties have a major impact on the response under higher blast loads. Initially, glass panes absorb most of the blast energy, but after the glass breaks, interlayer deforms further and absorbs most of the blast energy. LG panels should be designed to fail by tearing of the interlayer rather than failure at the supports to achieve a desired level of protection. From this aspect, material properties of glass, interlayer and sealant joints play important roles, but unfortunately they are not accounted for in the current design standards. The new information generated in this paper will enhance the capabilities of engineers to better design LG panels under blast loads and use better materials to improve the blast response of LG panels.

Structure, bonding state and in-vitro study of Ca–P–Ti film deposited on Ti6Al4V by RF magnetron sputtering

Experimental investigation of functionally graded calcium phosphate-based bio-active films on Ti-6A1-4V orthopaedic alloy prepared in an RF magnetron sputtering plasma reactor is reported. The technique involves concurrent sputtering of Hydroxyapatite (HA) and Ti targets, which results in remarkably enhanced adhesion of the film to the substrate and stability of the interface. The films have been characterized using X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS). The XPS data show that the films are composed of O, Ca, P and Ti, and reveal the formation of O=P groups and hybridization of O-Ca-P. The XRD pattern shows that the Ca-P thin films are of crystalline calcium oxide phosphate (4CaO·P2O5) with preferred orientation varying with processing parameters. High-resolution optical emission spectra show that the emission of CaO is dominant. The CaO, PO and CaPO species are strongly influenced by deposition conditions. The introduction of Ti element during deposition provides a stable interface between bio-inert substrates Ti-6A1-4V and bioactive HA coating. In-vitro cell culturing tests suggest excellent biocompatibility of the Ca-P-Ti films.