Evolution of microstructure and changes of mechanical properties of CLAM steel after long-term aging

The China Low Activation Martensitic (CLAM) steel has been developed as a candidate structural material for future fusion reactors. It is essential to investigate the evolution of microstructure and changes of mechanical properties of CLAM steel during thermal exposure. In this study, the long-term thermal aging of the CLAM steel has been carried out in air at 600 °C and 650 °C for 1100 h, 3000 h and 5000 h. The microstructural evolution with aging time was studied, including characteristics of the growth of M23C6 carbides and the formation of Laves-phase precipitates as well as the evolved subgrains. The microstructural evolution leads to the changes of mechanical properties of the CLAM steel. The Ductile–Brittle Transition Temperature (DBTT) increases significantly during the thermal aging, which is related to the formation of Laves-phase in the steel matrix. The possible mechanism of stabilizing microstructure during the thermal exposure has been analyzed based on the interaction between M23C6 carbides and subgrain boundaries.

Microstructure and high cycle fatigue fracture surface of a Ti-5Al-5Mo-5V-1Cr-1Fe titanium alloy

Because of the requirements for the damage tolerance and fatigue life of commercial aircraft components, the high cycle fatigue (HCF) properties of Ti–5Al–5Mo–5V–1Cr–1Fe titanium alloy forgings are important. The effects of microstructure types of the α+β titanium alloy on fatigue properties need to be understood. In this paper, by analysing the fracture surfaces of the titanium alloy having four types of microstructure, the effects of microstructure are investigated. The differences of initiation areas and crack propagation among different microstructures were studied. It was found that the area of the initiation region decreases in the order of coarse basketweave, fine basketweave, Widmanstätten, and bimodal microstructure.