Influence of viscosity and ionic concentration on morphology of PLZT thin films

PLZT thin films were prepared by a dip-coating process using Pechini's method. The PLZT solution was obtained from the mixture of the cation solutions. The viscosity of the solution was adjusted in the range of 20-40 cP, while the ionic concentration was adjusted in the range of 0.1 and 0.2 M. PLZT solutions were deposited on Si (1 0 0) substrate with withdrawal speed at 5 mm/min. The coated substrates were thermally treated with heating rate of 1 degreesC/min up to 300 and 5 degreesC/ min up to 650 degreesC in order to obtain homogeneous and crack free films. The influence of viscosity and ionic concentration on crystallization and morphology of PLZT (9/65/35) thin film will be discussed. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Multi-functional properties of CaCu3Ti4O12 thin films

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Structural study of thin films prepared from tungstate glass matrix by Raman and X-ray absorption spectroscopy

Thin films were prepared using glass precursors obtained in the ternary system NaPO(3)-BaF(2)-WO(3) and the binary system NaPO(3)-WO(3) with high concentrations of WO(3) (above 40% molar). Vitreous samples have been used as a target to prepare thin films. Such films were deposited using the electron beam evaporation method onto soda-lime glass substrates. Several structural characterizations were performed by Raman spectroscopy and X-ray Absorption Near Edge Spectroscopy (XANES) at the tungsten L(I) and L(III) absorption edges. XANES investigations showed that tungsten atoms are only sixfold coordinated (octahedral WO(6)) and that these films are free of tungstate tetrahedral units (WO(4)). In addition, Raman spectroscopy allowed identifying a break in the linear phosphate chains as the amount of WO(3) increases and the formation of P-O-W bonds in the films network indicating the intermediary behavior of WO(6) octahedra in the film network. Based on XANES data, we suggested a new attribution of several Raman absorption bands which allowed identifying the presence of W-O and W=O terminal bonds and a progressive apparition of W-O-W bridging bonds for the most WO(3) concentrated samples (above 40% molar) attributed to the formation of WO(6) clusters. (C) 2008 Elsevier B.V. All rights reserved.

Visible emission from Er-doped SnO2 thin films deposited by sol-gel

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Study of the dielectric and ferroelectric properties of chemically processed BaxSr1-xTiO3 thin films

Polycrystalline BaxSr1-xTiO3 (x = 0.4 and 0.8) thin films with a perovskite structure were prepared by the polymeric precursor method on a platinum-coated silicon substrate. High-quality thin films with uniform composition and thickness were successfully produced by dip-coating and spin-coating techniques. The resulting thin films prepared by dip and spin-coating showed a well-developed dense polycrystalline structure with uniform grain size distribution. The metal-BST-metal structure of the thin films displays good dielectric and ferroelectric properties. The ferroelectric nature to BaxSr1-xTiO3 (x = 0.8) thin film, indicated by butterfly-shaped C-V curves and confirmed by the hysteresis curve, showed 2P(r) = 5.0 muC/cm(2) and E-c = 20 kV/cm. The capacitance-frequency curve reveals that the dielectric constant may reach a value of up to 794 at 1 kHz. on the other hand, the BaxSr1-xTiO3 (x = 0.4) thin films had paraelectric nature and dielectric constant and the dissipation factor at a frequency of 100 kHz were 680 and 0.01, respectively, for film annealed at 700 degreesC. In addition, an examination of the film's I-V curve at room temperature revealed the presence of two conduction regions in the BaxSr1-xTiO3 (x = 0.4 and 0.8) thin films, showing ohmic-like behavior at low voltage and a Schottky-emission or Poole-Frenkel mechanism at high voltage. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Study on the orientation degree of Pb1-xLaxTiO3 thin films by the rocking curve technique and its morphological aspects

Thin films of perovskite-type materials such as PbTiO3, BaTiO3, (Pb,La)TiO3, (Pb, La)(ZrTi)O-3, KNbO3, and Pb(Mg,Nb)03 have been attracting great interest for applications like non-volatile memories, ultrasonic sensors and optical devices. Thin film should be epitaxially grown or at least highly textured since the properties of this anisotropic material depend on the crystallographic orientation. For optical devices, in particular, an epitaxial thin film without defects are essential to reduce optical propagation losses. Pb1-xLaxTiO3 (PLT) where x=0, 13 and 27% thin films were prepared by a chemical method (polymeric precursors method), and deposited by the spin coating technique onto substrates of SrTiO3 (STO) and LaAlO3 (LAO). The films were then beat treated at 500 degrees C in a controlled atmosphere of 0,. The orientation degree of the thin films was obtained from rocking curve technique, by means of X-ray difftaction analysis. A microstructural study revealed that the films were crack-free, homogeneous and have low roughness. (c) 2006 Elsevier B.V. All rights reserved.

Microstructural, dielectric and ferroelectric properties of calcium-modified lead titanate thin films derived by chemical processes

Ferroelectric Pb1-xCaxTiO3 (x = 0.24) thin films were formed on a Pt/Ti/SiO2/Si substrate by the polymeric precursor method using the dip-coating technique for their deposition. Characterization of the films bq X-ray diffraction showed a perovskite single phase with a tetragonal structure after annealing at 700 degreesC. Atomic force microscopy (AFM) analyses showed that the film had a smooth and crack-free surface with low surface roughness. In addition, the PCT thin film had a granular structure with an 80 nm grain size. The thickness of the films observed by the scanning electron microscopy (SEM) is 550 nm and there is a good adhesion between the film and substrate. For the electrical measurements metal-ferroelectric-metal of the type capacitors were obtained, where the thin films showed good dielectric and ferroelectric properties. The dielectric constant and dissipation factor at 1 kHz and measured at room temperature were found to be 457 and 0.03. respectively. The remanent polarization and coercive field for the: deposited films were P-r = 17 muC/cm(2) and E-c = 75 kV/cm, respectively. Moreover. The 550-nm-thick film showed a current density in the order of 10(-8) A/cm(2) at the applied voltage of 2 V. The high values of the thin film's dielectric properties are attributed to its excellent microstructural quality and the chemical homogeneity obtained by the polymeric precursor method. (C) 2001 Elsevier science Ltd. All rights reserved.

Improvement of the dielectric and ferroelectric properties in superlattice structure of Pb(Zr,Ti)O-3 thin films grown by a chemical solution route

Making heterolayered perovskite materials constitutes an approach for the creation of better dielectric and ferroelectric properties. In the experiment reported here, heterolayered PZT40/PZT60 films were grown on Pt/Ti/SiO2/Si (100) by a chemical solution deposition. The dielectric constant of the heterolayered thin film was significantly enhanced compared with that of pure PZT40 and PZT60 thin films. A dielectric constant of 701 at 100 kHz was observed for a stacking periodicity of six layers having a total thickness of 150 nm. The heterolayered film exhibited greater remanent polarization than PZT60 and PZT40 films. The values of remanent polarization were 7.9, 18.5, and 31 muC/cm(2), respectively, for pure PZT60, PZT40, and heterolayered thin films, suggesting that the superior dielectric and ferroelectric properties of the heterolayered thin film resulted from a cooperative interaction between the ferroelectric phases made from alternating tetragonal and rhombohedral phases of PZT, simulating the morphotropic phase boundary of this system. (C) 2004 American Institute of Physics.

Investigation of phase transition in ferroelectric Pb0.70Sr0.30TiO3 thin films

We have carried out dielectric and Raman spectroscopy studies at the 298-623 K temperature range in polycrystalline Pb0.70Sr0.30TiO3 thin films grown by a soft chemical method. The diffuse phase-transition behavior of the thin films was observed by means of the dielectric constant versus temperature curves, which show a broad peak. Such behavior was confirmed later by Raman spectroscopy measurements up to 823 K, indicating that a diffuselike phase transition takes place at around 548-573 K. The damping factor of the E(1TO) soft mode was calculated using the damped simple harmonic oscillator model. on the other hand, Raman modes persist above the tetragonal to cubic phase transition temperature although all optical modes should be Raman inactive. The origin of these modes was interpreted in terms of a breakdown of the microscopic local cubic symmetry by chemical disorder. The lack of a well-defined transition temperature and the presence of broad bands at some temperature interval above the ferroelectric-paraelectric phase-transition temperature suggested a diffuse nature of the phase transition. This result corroborates the dielectric constant versus temperature data, which showed a broad ferroelectric phase transition in this thin film. (C) 2004 American Institute of Physics.

Ultraviolet excitation of photoconductivity in thin films of sol-gel SnO2

Tin dioxide (SnO2) thin film photoconductivity spectra were measured for a large temperature range using a deuterium source, the intensity of photocurrent spectra in the range 200-400 nm is temperature dependent, and the photocurrent increases in the ultraviolet even for illumination with photon energies much higher than the bandgap transition. This behavior is related to recombination of photogenerated electron-hole pairs with oxygen adsorbed at grain boundaries, which is consistent with nanoscopic crystallite size of sol-gel deposited films. (c) 2005 Elsevier Ltd. All rights reserved.

Grazing incidence X-ray diffraction and atomic force microscopy analysis of BaBi2Ta2O9 thin films

Thin films of BaBi2Ta2O9 (BBT) composition were prepared through the metal organic decomposition method. The crystallinity, phase formation, crystallite size and morphology of the thin films were measured as a function of the type of substrate, stoichiometry of solution and process variables such as thickness and temperature. The thin films were investigated by grazing incidence X-ray diffractometry and atomic force microscopy (AFM) techniques. For the sample without excess of bismuth, diffraction peaks other than that of the BBT phase were observed. A well crystallized BBT single phase was observed for films prepared from a solution with 10% excess of bismuth, deposited on Si/Pt substrate, with a thickness up to 150 nm and sintered at temperatures of 700 degreesC. The thin BBT phase films heat-treated at 600 degreesC presented a diffraction pattern characteristic of samples with lower degree of crystallinity whereas for the thin films heat-treated at 800 degreesC, we observed the presence of other phases than the BBT. For the thin film deposited on the Sin+ substrate, we observe that the peaks corresponding to the BBT phase are broader than that observed on the samples deposited on the Pt and Si/Pt substrates. No variation of average crystallite size was observed as the excess of Bi increased from 10 to 20%. AFM images for the samples showed that the increasing the amount of bismuth promotes grain growth. The average surface roughness measured was in the range of 16-22 nm showing that the bismuth amount had no or little effect on the roughness of films. (C) 2002 Elsevier B.V. B.V. All rights reserved.

Correlation between the surface morphology and structure and the photoluminescence of amorphous PbTiO3 thin films obtained by the chemical route

A polymeric precursor method was used to synthesis PbTiO3 amorphous thin film processed at low temperature. The luminescence spectra of PbTiO3 amorphous thin films at room temperature revealed an intense single-emission band in the visible region, the visible emission band was found to be dependent on the thermal treatment history, Photoluminescence properties Versus different annealing temperatures were investigated. The experimental results (XRD, AFM, FL) indicate that the nature of photoluminescence (PL) must be related to the disordered structure of PbTiO3 amorphous thin films, Copyright (C) 2000 John Wiley & Sons, Ltd.

Microstructural and ferroelectric properties of PbZr1-xTi(x)O(3) thin films prepared by the polymeric precursor method

The polymeric precursor method was employed in the preparation of PZT thin films on Pt(111)Ti/SiO2/Si(100) substrates. X-ray diffraction patterns revealed the polycrystalline nature of the PZT (53:47) thin films, which had a granular structure and a grain size of approximately 70 nm. A 350-nm thick film was obtained by running three cycles of the dip-coating/heating process. Atomic force microscopy (AFM) analyses showed the surface of these thin films to be smooth, dense and crack-free with low surface roughness (= 2.0 nm). The PZT (53:47) thin films annealed at 700 degreesC showed a well-saturated hysteresis loop. The C-V curves of perovskite thin film displayed normal ferroelectric behavior, while the remanent polarization (2P(r)) and coercive field (E-e) of the film deposited and measured at room temperature were 40 muC/cm(2) and 110 kV/cm, respectively. (C) 2001 Elsevier B.V. B.V. All rights reserved.

Durango apatite fission-track dating using length-based age corrections and neutron fluence measurements by natural thorium thin films and natural U-doped glasses calibrated through natural uranium thin films

In this work, we present an approach for neutron fluence measurements based on natural thorium thin films and natural uranium-doped glasses calibrated through natural uranium thin films to be used for dating with the Fission-Track Method (FTM). This neutron dosimetry approach allows the employment of FTM even when dating is carried out using low neutron themalization facilities. Besides, it makes possible the determination of the Th/U ratio of the mineral to be dated. Durango apatite which is often employed in FTM as an age standard was analyzed. This apatite presented a fairly high Th/U ratio, 29.9 +/- 1.7. Th fissions were 18%, 12% and 10% of the total for irradiations where thermal to fast neutron flux ratios were 2.4, 4.4 and 5,2, respectively. These results show that Th fission must be considered for this apatite, when not well-thermalized irradiation facilities are used. The ratio between spontaneous and induced track length, L(S)/L(1), close to 0.89, indicates a certain amount of rejuvenation of the age of Durango apatite. Therefore, its apparent age should be corrected, the application of a technique based on track-length measurements produced a corrected age of 29.7 +/- 1.1 Ma, consistent with the independent reference age of this apatite (31.4 +/- 0.5 Ma). This result represents a support for viability of the neutron dosimetry approach studied in this work for FTM.(C) 2002 Elsevier B.V. B.V. All rights reserved.

Ferroelectric and dielectric properties of lanthanum-modified bismuth titanate thin films obtained by the polymeric precursor method

Lanthanum-modified bismuth titanate, Bi4-xLaxTi3O12 (BLT), thin films with a La concentration of 0.75 was grown on Pt/Ti/SiO2/Si substrates by using the polymeric precursor solution and spin-coating method. The scanning electron microscopy (SEM) showed rounded grains, which is not typical for these system. The BLT films showed well-saturated polarization-electric field curve which 2P(r) = 41.4 muC/cm(2) and V-c = 0.99 V. The capacitance dependence on the voltage is strongly nonlinear, confirming the ferroelectric properties of the film resulting from the domains switching. These properties make BLT a promising material for FERAM applications.