Cathodoluminescence study of GaN-based film structures

GaN films grown on sapphire substrate with an emphasis on epitaxial lateral overgrown (ELOG) layers with an array of rhombic shaped mask area as well as InGaN/GaN MQW laser diode layer structures were investigated by cathodoluminescence (CL) spectroscopy and CL imaging at room and low temperatures. The microscopic imaging with a high-spatial resolution clearly reveals the distribution of threading dislocations and point defects in ELOG GaN films. The secondary electron and CL data measured on cleaved faces of laser diodes are analyzed in consideration with luminescence mechanisms in semiconductor heterostructures and around the p - n junction, providing important information on the defects and carrier dynamics in laser diode devices.

Interface as the origin of ferromagnetism in cobalt doped ZnO film grown on silicon substrate

We have investigated the magnetic properties of Co-doped zinc oxide (ZnO) film deposited on silicon substrate by magnetron sputtering. Co ions have a valence of 2+ and substitute for Zn sites in the lattice. By using a chemical etching method, an extrinsic ferromagnetism was demonstrated. The observed ferromagnetism is neither associated with magnetic precipitates nor with contamination, but originates from the silicon/silicon oxide interface. This interface ferromagnetism is characterized by being temperature independent and by having a parallel magnetic anisotropy. (C) 2008 American Institute of Physics. [DOI: 10.1063/1.2989128]

Preparation of self-supporting hierarchical nanostructured anatase/rutile composite TiO2 film

Via the combination of an electrospinning method with a hydrothermal reaction, a large-scale cedar-like hierarchical nanostructured TiO2 film with an anatase/rutile composite phase was fabricated.

Doped polycrystalline 3C-SiC films deposited by LPCVD for radio-frequency MEMS applications

Polycrystalline 3C-SiC films are deposited on SiO2 coated Si substrates by low pressure chemical vapour deposition (LPCVD) with C3H8 and SiH4 as precursors. Controlled nitrogen doping is performed by adding NH3 during SiC growth to obtain the low resistivity 3C-SiC films. X-ray diffraction (XRD) patterns indicate that the deposited films are highly textured (111) orientation. The surface morphology and roughness are determined by scanning electron microscopy (SEM) and atomic force microscopy (AFM). The surface features are spherulitic texture with average grain size of 100 nm, and the rms roughness is 20nm (AFM 5 x 5 mu m images). Polycrystalline 3C-SiC films with highly orientational texture and good surface morphology deposited on SiO2 coated Si substrates could be used to fabricate rf microelectromechanical systems (MEMS) devices such as SiC based filters.

Stress analysis of ZnO film with a GaN buffer layer on sapphire substrate

A 5.35-mu m-thick ZnO film is grown by chemical vapour deposition technique on a sapphire (0001) substrate with a GaN buffer layer. The surface of the ZnO film is smooth and shows many hexagonal features. The full width at half maximum of ZnO (0002) omega-rocking curve is 161 arcsec, corresponding to a high crystal quality of the ZnO film. From the result of x-ray diffraction theta - 2. scanning, the stress status in ZnO film is tensile, which is supported by Raman scattering measurement. The reason of the tensile stress in the ZnO film is analysed in detail. The lattice mismatch and thermal mismatch are excluded and the reason is attributed to the coalescence of grains or islands during the growth of the ZnO film.

Growth parameter dependence of magnetic property of CrAs thin film

This paper has systematically investigated the substrate temperature and thickness dependence of surface morphology and magnetic property of CrAs compound films grown on GaAs by molecular-beam epitaxy. It finds that the substrate temperature affects the surface morphology and magnetic property of CrAs thin film more potently than the thickness.

Using different carrier gases to control AlN film stress and the effect on morphology, structural properties and optical properties

On the metalorganic chemical vapour deposition growth of AlN, by adjusting H-2+N-2 mixture gas components, we can gradually control island dimension. During the Volmer - Weber growth, the 2-dimensional coalescence of the islands induces an intrinsic tensile stress. Then, this process can control the in-plane stress: with the N-2 content increasing from 0 to 3 slm, the in-plane stress gradually changes from 1.5 GPa tensile stress to - 1.2GPa compressive stress. Especially, with the 0.5 slm N-2 + 2.5 slm H-2 mixture gas, the in-plane stress is only 0.1 GPa, which is close to the complete relaxation state. Under this condition, this sample has good crystal and optical qualities.

Enhancement of field emission of the ZnO film by the reduced work function and the increased conductivity via hydrogen plasma treatment

The ZnO films deposited by magnetron sputtering were treated by H/O plasma. It is found that the field emission (FE) characteristics of the ZnO film are considerably improved after H-plasma treatment and slightly deteriorated after O-plasma treatment. The improvement of FE characteristics is attributed to the reduced work function and the increased conductivity of the ZnO H films. Conductive atomic force microscopy was employed to investigate the effect of the plasma treatment on the nanoscale conductivity of ZnO, these findings correlate well with the FE data and facilitate a clearer description of electron emission from the ZnO H films.

Synthesis and characterization of well-aligned Zn1-xMgxO nanorods and film by metal organic chemical vapor deposition

Well-aligned Zn1-xMgxO nanorods and film with Mg-content x from 0 to 0.051 have been successfully synthesized by metal organic chemical vapor deposition (MOCVD) without any catalysts. The characterization results showed that the diameters and lengths of the nanorods were in the range of 20-80 nm and 330-360 nm, which possessed wurtzite structure with a c-axis growth direction. As the increase of Mg precursor flows into the growth chamber, the morphology of Zn1-xMgxO evolves from nanorods to a film with scale-like surface and the height of the nanorods and the film was almost identical, it is suggested that the growth rate along the c-axis was hardly changed while the growth of six equivalent facets of the type {1 0 (1) over bar 0} of the Zn1-xMgxO has been improved. Photoluminescence and Raman spectra show that the products have a good crystal quality with few oxygen vacancies. With the Mg incorporation, multiple-phonon scattering become weak and broad, and the intensities of all observed vibrational modes decrease. And the ultraviolet near-band-edge emission shows a clear blueshift (x=0.051, as much as 90 meV) and slightly broadening compared with that of pure ZnO nanorods. (C) 2008 Elsevier B.V. All rights reserved.

An investigation of the mode characteristics of SOI submicron rib waveguides using the film mode matching method

The mode characteristics of SOI (silicon-on-insulator) submicron rib waveguides are very different from those of micrometer-sized ones. Using the full-vector film mode matching method, we propose a simple criterion to determine whether a waveguide mode is guided or not. The single-mode condition for deep-etched waveguides is obtained using this criterion. We also obtain the inherent TM mode leakage and sharp cancelation effects due to TE-TM mode coupling in shallow-etched rib waveguides from numerical simulations, which agree well with the analytical results based on total internal reflection and interference theories.

Strain status in ZnO film on sapphire substrate with a GaN buffer layer grown by metal-source vapor phase epitaxy

ZnO film of 8 mu m thickness was grown on a sapphire (0 0 1) substrate with a GaN buffer layer by a novel growth technique called metal-source vapor phase epitaxy (MVPE). The surface of ZnO film measured by scanning electron microscope (SEM) is smooth and shows many regular hexagonal features. The full width at half maximum (FWHM) of ZnO(0 0 2) and (1 0 2) omega-scan rocking curves are 119 and 202 arcsec, corresponding a high crystal quality. The status of the strain in ZnO thick film was particularly analyzed by X-ray diffraction (XRD) omega-20 scanning. The results show that the strain in ZnO film is compressive, which is also supported by Raman scattering spectroscopy. The compressive strain can solve the cracking problem in the quick growth of ZnO thick film. (c) 2008 Elsevier Ltd. All rights reserved.

Hillocks and hexagonal pits in a thick film grown by HVPE

A GaN film with a thickness of 250 mu m was grown on a GaN/sapphire template in a vertical hydride vapor phase epitaxy (HVPE) reactor. The full-width at half-maximum (FWHM) values of the film were 141 and 498 arcsec for the (0 0 2) and (1 0 2) reflections, respectively. A sharp band-edge emission with a FWHM of 20 meV at 50 K was observed, which corresponded to good crystalline quality of the film. Some almost circular-shaped hillocks located in the spiral growth center were found on the film surface with dimensions of 100 mu m, whose origin was related to screw dislocations and micropipes. Meanwhile, large hexagonal pits also appeared on the film surface, which had six triangular {1 0 (1) over bar 1} facets. The strong emission in the pits was dominated by an impurity-related emission at 377 nm, which could have been a high-concentration oxygen impurity. (c) 2008 Elsevier Ltd. All rights reserved.

Design of plasmonic back structures for efficiency enhancement of thin-film amorphous Si solar cells

Metallic back structures with one-dimensional periodic nanoridges attached to a thin-film amorphous Si (a-Si) solar cell are numerically studied. At the interfaces between a-Si and metal materials, the excitation of surface-plasmon polaritons leads to obvious absorption enhancements in a wide near-IR range for different ridge shapes and periods. The highest enhancement factor of the cell external quantum efficiency is estimated to be 3.32. The optimized structure can achieve an increase of 17.12% in the cell efficiency. (C) 2009 Optical Society of America

Growth of crack-free AlGaN film on thin AlN interlayer by MOCVD

We have studied the effect of low-temperature-deposited (LT) and high-temperature-deposited (FIT) AlN interlayer with various thickness on AlGaN film grown on GaN using c-plane sapphire as substrate. All the Al0.25Ga0.75N films thicker than 1 mum with LT-AlN interlayer or with HT-AlN interlayer were free of cracks, however, their surfaces were different: the Al0.25Ga0.75N films with LT-AlN interlayer showed smooth surface, while those with HT-AlN interlayer exhibit rough surface morphology. The results of X-ray double crystal diffraction and Rutherford backscattering showed that all of the AlGaN films were under compressive strain in the parallel direction. The compressive strain resulted from the effect of interlayer-induced stress relieving and the thermal mismatch for the samples with LT-AlN interlayer, and it was due to the thermal mismatch between AlGaN and the underlying layers for those with HT-AlN interlayer. (C) 2004 Elsevier B.V. All rights reserved.