Effect of Process Conditions on Microstructure and Corrosion Resistance of Cold-Sprayed Ti Coatings

Ti and Ti alloys can be applied to steels as a protective coating in view of its excellent resistance to corrosive environment. Cold spraying, as a new coating technique, has potential advantages in fabrication of Ti coating in comparison with conventional thermal spraying techniques. In this study, Ti coatings were prepared on carbon steel substrates by cold spraying via controlling the process conditions. The microstructure of coatings was observed by SEM. The porosity of coatings was estimated by image analysis and the bond strength was tested for comparison of the process conditions. Potentiodynamic polarization and open-circuit potential (OCP) measurements were performed to understand the corrosion behavior of the coatings. The SEM examination shows that the coatings become more compact with the increases of pressure and temperature of driving gas. The potentiodynamic polarization curves indicate that the coating which has lower porosity has lower corrosion current. The polarization and OCP measurement reveal that cold-sprayed Ti coating can provide favorable protection to carbon steel substrate. The polishing treatment of coating surface polishes the rough outer layer including the small pores as well as decreases the actual surface area of the coating, leading to the considerable improvement of corrosion resistance.

Hydrogen permeation and corrosion behaviour of high strength steel 35CrMo under cyclic wet-dry conditions

Hydrogen permeation behaviours of high strength steel 35CrMo under different cyclic wet-dry conditions have been investigated by using Devanathan-Stachurski's technique. Four electrolytes were used: distilled water, seawater, seawater containing 1500 ppm H2S and seawater containing 0.03 mol L-1 SO2. The corrosion weight loss of 35CrMo in the wet-dry cycles was measured simultaneously. The experimental results show that hydrogen can be detected at the surface opposite to the corroding side of the specimen during wet-dry cycles and the permeation current density during a wet-dry cycle showed a maximum during the drying process. The hydrogen permeation was obviously promoted by Cl- ions, H2S and SO2. The hydrogen permeation in the real marine atmosphere has also been investigated. There is a clear correlation between the amount of hydrogen permeated and the corrosion weight losses. Results show the importance of hydrogen permeation that merits further investigation.

Three phases of dark-recovery course from photoinhibition resolved by the chlorophyll fluorescence analysis in soybean leaves under field conditions

The chlorophyll fluorescence in soybean leaves was observed by a portable fluorometer CF-1000 under field conditions. On clear days, F-0 increased while F, and F-v/F-m decreased gradually in the morning. At midday F-O reached its maximum while F-v and F-v/F-m reached their minimum. The reverse changes occurred in the afternoon. At dusk these parameters could return to levels near those at dawn. Following exposure to a strong sunlight for more than 3 h, the dark-recovery process displayed three phases: (1) slow increases in F-0, F-v and F-v/F-m within the first hour; (2) a faster decrease in F-0 and faster increases in F-v and F-v/F-m within subsequent two hours; (3) a slow decrease in F-0 and slow increases in F-v and F-v/F-m within the fourth hour. In comparison with darkness, weak irradiance had no stimulating effect on the recovery from photoinhibition. Hence the photoinhibition in soybean leaves is mainly the reflection of reversible inactivation of some photosystem 2 reaction centres, but not the result of D1 protein loss.