Investigation of spontaneous microemulsion formation in supercritical carbon dioxide using high-pressure NMR

NMR spectroscopy and relaxometry were used to investigate microemulsion formation in supercritical CO2. The droplets were stabilised by the salt of a perfluorinated polyether. Spontaneous microemulsion formation was observed over a period of 5 h in the absence of applied sheer. Time-resolved relaxation times of the surfactant tail showed a stepwise increase in mobility of the tail over this period. Conversely, the translational mobility of water confined within the droplet decreased over the same interval. This data is consistent with the gradual decrease in droplet size as time progressed. Indeed, NMR self-diffusion coefficients were used to show that droplets with a radius of approximately 5 nm were formed at equilibrium.

NMR microscopy: A tool for measuring monomer diffusion in supercritical CO2

The diffusion of styrene into linear low density polyethylene in a solution of supercritical CO2 was investigated using NMR microimaging. For both pure styrene and styrene dissolved in supercritical CO2, the diffusion was found to follow Fickian kinetics. Supercritical CO2 was found to enhance the rate and extent of diffusion of styrene into the substrate by up to three times under the conditions of this investigation, compared to pure styrene. NMR imaging was used to measure the concentration profiles of the styrene penetrants in real time, and the results were fitted to a Fickian model for diffusion. At a CO2 pressure of 150 bar and temperature of 40 degrees C, the diffusion coefficient of a 30 wt-% solution of styrene into LLDPE was calculated to be 1 X 10(-11) m(2). s(-1). This is significantly faster than the diffusion coefficient measured for pure styrene diffusion at 40 degrees C (3 x 10(-12) m(2). s(-1)). The diffusion coefficients determined by gravimetric analysis were slightly higher than those determined by the imaging method. This was probably due to residual styrene and/or polystyrene adhering to the surface of the films in the gravimetric technique.

DOSY NMR studies of chemical exchange behavior of poly(2-hydroxyethyl methacrylate)

PFG-NMR was used to study the chemical exchange of linear PHEMA having a range of molecular weights with water in DMSO containing varying quantities of water. The aim was to investigate the use of PFG-NMR to study chemical exchange between a polymer with exchangeable protons and a small fast diffusing molecule to provide insight into the conformation adopted by a polymer in solution. The experimental data were simulated closely for the two-site exchange case using the Bloch equations modified for chemical exchange and diffusion. The exchange rate could be used to detect changes in polymer conformation resulting from changes in the solvent. PHEMA of MW 10 000 showed significant time-dependent changes in exchange rate, resulting from preferential solvation of the OH sites by water, and subsequent conformational changes which altered accessibility of the OH sites to water. This behavior was not observed for larger MW PHEMA, which adopted a stable conformation immediately. Large changes in the exchange rate were not reflected in changes to the hydrodynamic radius, suggesting that a minimal overall change in the chain dimensions occurred. DMSO was found to be a poor solvent for PHEMA, which adopts a compact conformation in DMSO. This work has demonstrated that PFG-NMR is a sensitive method for detecting subtle changes in polymer conformation in polymers with exchangeable protons.