Effect of the addition of ZnO seeds on the electrical proprieties of ZnO-based varistors

ZnO has the characteristic of presenting an intermediate value for the effective 3 eV barrier at room temperature. ZnO ceramics are applied in high-voltage systems or circuits. Attempts were made to reduce the number of effective barriers in the system by adding large particles of ZnO to the varistor composition. This procedure reduced the breakdown field of the varistors by values up to 90% lower than those initially obtained, and produced nonlinear coefficients as low as 20. (C) 2003 Elsevier B.V. B.V. All rights reserved.

Titanium and zirconium complexes containing sterically hindered hydrotris(pyrazolyl)borate ligands: synthesis, structural characterization, and ethylene polymerization studies

The synthesis, characterization and ethylene polymerization behavior of a set of Tp'MCl3 complexes (4, M = Ti, Tp' HB(3-neopentyl-pyrazolyl)(3)(-) (Tp(NP)); 5, M = Ti, Tp'= HB(3-tert-butyl-pyrazolyl)(3)(-) (Tp(tBu)); 6, M = Ti, Tp' = HB(3-phenyl-pyrazolyl)(3)(-) (Tp(Ph)); 7, M = Zr, Tp' = HB(3-phenyl-pyrazolyl)(3)(-) (Tp(ph)); 8, M = Zr, Tp' = HB(3-tert-butyl-pyrazolyl)(3)(-) (Tp(tBu))) is described. Treatment of these tris(pyrazolyl)borate Group IV compounds with methylalumoxane (MAO) generates active catalysts for ethylene polymerization. For the polymerization reactions performed in toluene at 60 degreesC and 3 atm of ethylene pressure, the activities varied between 1.3 and 5.1 X 10(3) g of PE/mol[M](.)h. The highest activity is reached using more sterically open catalyst precursor 4. The viscosity-average molecular weights ((M-v) over bar) of the PE's produced with these catalyst precursors varying from 3.57 to 20.23 x 10(5) gmol(-1) with melting temperatures in the range of 127-134 degreesC. Further polymerization studies employing 7 varying Al/Zr molar ratio and temperature of polymerization showed that the activity as well as the polymer properties are dependent on these parameters. In that case, higher activity was attained at 60 degreesC. The viscosity-average molecular weights of the polyethylene's decreases with increasing AI/Zr molar ratio. (C) 2003 Elsevier B.V. All rights reserved.

AN ACTINOMETRIC STUDY OF C2H2 PLASMA POLYMERIZATION AND FILM PROPERTIES

Thin polymer films were grown in radio frequency discharges containing C2H2. Actinometry revealed the trend in the plasma concentration of the CH species as a function of the operating pressure. The C-H bond density in the films, revealed by infrared analysis, was found to increase with the pressure of C2H2 in a similar way to that of the concentration of the CH species in the discharge. From transmission ultraviolet-visible spectroscopy data, optical parameters of the polymers, namely, the refractive index and the optical gap, were calculated. For the range of pressure studied, the refractive index decreased from 1.73 to 1.63 and the optical gap increased from 2.4 to 3.3 eV. Finally, measurements of the residual stress of the polymer films were carried out by the bending beam method, using a He-Ne laser, yielding values from 0.05 to 0.3 GPa. (C) 1995 American Vacuum Society.

Sensitivity of SnO2 non-ohmic behavior to the sintering process and to the addition of La2O3

The work reported here consisted of a study of the sensitivity of the nonlinear electrical properties of dense SnO2. CoO ceramic systems to low concentrations of La2O3, sintering temperature and cooling rates. The nonlinear electrical properties of these systems were found to increase with decreasing cooling rates, a behavior attributed to the CoO solid state reactions at temperatures below 1000 degreesC. Post-annealing treatment in N-2-rich atmospheres strongly decreases the non-ohmic behavior of SnO2. CoO ceramic systems. However, this behavior may be restored through thermal treatment in an O-2-rich atmosphere. (C) 2001 Elsevier B.V. Ltd. All rights reserved.

Photoluminescent BaMoO4 nanopowders prepared by complex polymerization method (CPM)

The BaMoO4 nanopowders were prepared by the Complex Polymerization Method (CPM). The structure properties of the BaMoO4 powders were characterized by FTIR transmittance spectra, X-ray diffraction (XRD), Raman spectra, photoluminescence spectra (PL) and high-resolution scanning electron microscopy (HR-SEM). The XRD, FTIR and Raman data showed that BaMoO4 at 300 degrees C was disordered. At 400 degrees C and higher temperature, BaMoO4 crystalline scheelite-type phases could be identified, without the presence of additional phases, according to the XRD, FTIR and Raman data. The calculated average crystallite sizes, calculated by XRD, around 40 nm, showed the tendency to increase with the temperature. The crystallite sizes, obtained by HR-SEM, were around of 40-50 nm. The sample that presented the highest intensity of the red emission band was the one heat treated at 400 degrees C for 2 h, and the sample that displayed the 'highest intensity of the green emission band was the one heat treated at 700 degrees C for 2 h. The CPM was shown to be a low cost route for the production of BaMoO4 nanopowders, with the advantages of lower temperature, smaller time and reduced cost. The optical properties observed for BaMoO4 nanopowders suggested that this material is a highly promising candidate for photoluminescent applications. (C) 2005 Elsevier B.V. All rights reserved.

Linear low density polyethylene (LLDPE) from ethylene using Tp(Ms)NiCl (Tp(Ms) = hydridotris(3-mesitylpyrazol-1-yl)) and CP2ZrCl2 as a tandem catalyst system

Linear low density polyethylene (LLDPE) with different branching contents were prepared from ethylene, without the addition of alpha-olefin comonomer, using a combination of catalyst precursors {Tp(Ms)}NiCl (1) (Tp(Ms) = hydridotris(3-mesitylpyrazol-1-yl)) and Cp2ZrCl2 (2) activated with MAO/TMA (1:1) in toluene at 0degreesC and by varying the nickel loading mole fraction (x(Ni)). The polymerization results showed that the turnover frequencies are strongly dependent on the x(Ni) varying from 6.6 x 10(3) to 32.1 x 10(3) mol[C2H4]/mol[Zr] h. The C-13 NMR spectra of the copolymers showed that the branch contents of the polymers increase as the x(Ni) increase in the medium promoting the production of polymers with a wide range of melting point (T-m) (C) 2004 Elsevier B.V. All rights reserved.

Polymerization of ethylene by the tris(pyrazolyl)borate titanium(IV) compound immobilized on MAO-modified silicas

The immobilization of soluble catalyst {Tp(Ms)}TiCl3 (Tp(Ms*)HB(3-mesityl-pyrazolyl)(2)(5-mesityl-pyrazolyl)(-)) on silica and MAO-modified silicas containing 4.0, 8.0 and 23.0 wt.% Al/SiO2 yields active supported catalysts for ethylene polymerization. Among the supported catalysts studied by XRF spectroscopy, higher titanium content was obtained using MAO-modified silica containing 8.0 wt.% Al/SiO2 as support. For the ethylene polymerization reactions carried out in hexane at 60degreesC using a combination of triisobutylaluminum (TiBA) and methylaluminoxane (MAO) (1:1), the activities varied between 24.4 and 113.5 kg of PE/mol [Ti] h. The highest activity is reached using MAO-modified silica containing 4.0 wt.% Al/SiO2 as support. The viscosity-average molecular weights ((M) over bar (v)) of the PE's produced with the supported catalysts varying from 1.44 to 9.94 x 10(5) g/mol with melting temperatures in the range of 125-140degreesC. The use of other Lewis acid cocatalysts, including TiBA, diethylaluminium chloride (DEAC), and trimethylaluminum (TMA) resulted also in the formation of active catalysts for ethylene polymerization. However, the activities are lower than that one using a combination of TiBA and MAO. The viscosity-average molecular weights (R,) of PE's are influenced by varying the cocatalysts as well as the Al/Ti molar ratio. The supported catalyst generated in situ under ethylene atmosphere is roughly four times more active than supported one containing 4.0 wt.% Al/SiO2. (C) 2003 Elsevier B.V. All rights reserved.

Influence of simultaneous addition of MnO2 and CoO on properties of SnO2-based ceramics

This paper reports on a study of the: effect of replacing CoO by MnO2 on the sintering and electrical propel-ties of the 98.95% SnO2 + (1 - x)% CoO + x% MnO2 + 0.05% Ta2O5 system. All the samples were compacted into pellets and sintered at 1300 degrees C for 1 h, when they reached densities of about 98% of the theoretical density. An X-ray diffraction (XRD) analysis showed no other detectable phases other than SnO2. Current-voltage characterization indicated varistor behavior in the systems. The non-linear coefficient (alpha) and breakdown electric field (Eb) increased as the amount of MnO2 was increased. The results are explained in terms of an electric barrier modification, due to the presence of adsorbed negative oxygen species at the grain boundary inter face. (C) 2000 Elsevier B.V. B.V. All rights reserved.

Effect of La2O3 addition and O-2 atmosphere on the electric properties of SnO2TiO2

The electric properties of (Sn, Ti)O-2 doped with 1.00 mol% CoO, 0.05 mol% Nb2O5 and xmol% La2O3 (0.25 less than or equal to x less than or equal to 1.00) have been studied. Sn0.25Ti0.75Co0.01Nb0.005 doped with 0.50 mol% La2O3 has a nonlinearity coefficient of 6. An increase in the concentration of La2O3 raised its resistivity, thereby altering the electric properties of the material. A thermal treatment in oxygen atmosphere increased the nonlinearity coefficient to a value of 9. (C) 2003 Elsevier B.V. All rights reserved.