Mg-Zr-Sr alloys as biodegradable implant materials

Novel Mg–Zr–Sr alloys have recently been developed for use as biodegradable implant materials. The Mg–Zr–Sr alloys were prepared by diluting Mg–Zr and Mg–Sr master alloys with pure Mg. The impact of Zr and Sr on the mechanical and biological properties has been thoroughly examined. The microstructures and mechanical properties of the alloys were characterized using optical microscopy, X-ray diffraction and compressive tests. The corrosion resistance was evaluated by electrochemical analysis and hydrogen evolution measurement. The in vitro biocompatibility was assessed using osteoblast-like SaOS2 cells and MTS and haemolysis tests. In vivo bone formation and biodegradability were studied in a rabbit model. The results indicated that both Zr and Sr are excellent candidates for Mg alloying elements in manufacturing biodegradable Mg alloy implants. Zr addition refined the grain size, improved the ductility, smoothed the grain boundaries and enhanced the corrosion resistance of Mg alloys. Sr addition led to an increase in compressive strength, better in vitro biocompatibility, and significantly higher bone formation in vivo. This study demonstrated that Mg–xZr–ySr alloys with x and y ⩽5 wt.% would make excellent biodegradable implant materials for load-bearing applications.

Dynamic strain-induced ferrite transformation during hot compression of low carbon Si-Mn steels

The dynamic strain-induced transformation (DSIT) of austenite to ferrite was investigated under different undercooling conditions using three low carbon Si-Mn steels. The undercooling of austenite (ΔT) was controlled by varying the cooling rate between austenitization and deformation temperatures. Uniform DSIT ferrite grains (∼2.3 μm) were produced at a relatively high deformation temperature above 840°C using a low carbon high Si steel (0.077C-0.97Mn-1.35Si, mass%) in connection with a larger ΔT. The critical conditions for DSIT were determined based on the flow stress-strain curves measured during hot compression tests. Influence of deformation temperature on DSIT of low carbon Si-added steel was also discussed.

Microstructures, mechanical properties and in vitro corrosion behaviour of biodegradable Mg-Zr-Ca alloys

The microstructures, mechanical properties, corrosion behaviour and biocompatibility of the Mg-Zr-Ca alloys have been investigated for potential use in orthopaedic applications. The microstructures of the alloys were examined using X-ray diffraction analysis, optical microscopy and scanning electron microscopy. The mechanical properties of Mg-Zr-Ca alloys were determined from compressive tests. The corrosion behaviour has been investigated using an immersion test and electrochemical measurement. The biocompatibility was evaluated by cell growth factor using osteoblast-like SaOS2 cell. The experimental results indicate that the hot-rolled Mg-Zr-Ca alloys exhibit much finer microstructures than the as-cast Mg-Zr-Ca alloys which show coarse microstructures. The compressive strength of the hot-rolled alloys is much higher than that of the as-cast alloys and the human bone, which would offer appropriate mechanical properties for orthopaedic applications. The corrosion resistance of the alloys can be enhanced significantly by hot-rolling process. Hot-rolled Mg-0.5Zr-1Ca alloy (wt %) exhibits the lowest corrosion rate among all alloys studied in this paper. The hot-rolled Mg-0.5Zr-1Ca and Mg-1Zr-1Ca alloys exhibit better biocompatibility than other studied alloys and possess advanced mechanical properties, corrosion resistance and biocompatibility, suggesting that they have a great potential to be good candidates for orthopaedic applications. © 2012 Springer Science+Business Media New York.

Multiscale modelling of stress and strain partitioning in high strength dual phase steels

Multiscale modelling of stress and strain partitioning in DP steel was carried out using both realistic microstructure-based RVE models as well as stochastic microstructures generated by Monte Carlo method. The stochastic microstructure models were shown to resemble that of realistic microstructures, enabling research on the specific aspects of the microstructure that could be difficult to control and study during experimental work. One such feature of the realistic microstructures studied in this work was the grain size and microstructure morphology. The microstructures were generated with varying average grain sizes while all other parameters, such as boundary conditions, material properties and volume fractions of martensite and ferrite were kept constant. It is found that the effect of grain size is much more pronounced during the initial localisation of the plastic deformation at and around the interface of the phases. In addition, the decrease in ductility and increase in strength of the DP steels are directly related to the refinement of grain sizes of each phase and the stress-strain partitioning in between them.

Compositional effects on the restoration behaviour in Mg-Zn-Re alloys

Additions of rare earth elements to magnesium alloys are qualitatively reported in the literature to retard recrystallisation. However, their effect in the presence of other (non-rare earth) alloy additions has not been systematically shown nor has the effect been quantified. The microstructural restoration following the hot deformation of Mg-xZn-yRE (x = 2.5 and 5 wt.%, y = 0 and 1 wt.%, and RE = Gd and Y) alloys has been studied using double hit compression testing and microscopy. It was found that, in the absence of rare earth additions, increases in zinc level had a negligible influence on the kinetics of restoration and the microstructure developed both during extrusion and throughout double hit testing. Adding rare earth elements to Mg-Zn alloys was found to retard restoration of the microstructure and maintain finer recrystallised grains. However, in the Mg-Zn-RE alloys, increasing the zinc concentration from 2.5 wt.% to 5 wt.% accelerated the restoration process, most likely due to a depletion of rare earth elements from solid solution and modification of the particles present in the matrix.

Recrystallization kinetic behavior of copper-bearing strip cast steel

In the present study, copper-bearing low carbon steels were produced by direct strip casting (DSC) method on a pilot scale. The effects of copper on mechanical, microstructural, and recrystallization behavior were investigated. As-cast microstructure mainly consists of polygonal ferrite and Widmanstatten ferrite. The increase in Cu increases the amount of Widmanstatten ferrite and induces the formation of bainite in the as-cast condition. It was found that copper increases strength and hardness by solid solution strengthening, grain refinement, and precipitation hardening and the increment is significant above 1% Cu in as-cast condition. Six different compositions were selected for recrystallization study. All the samples were cold rolled to 70% reduction and annealed at three different temperatures, 600, 650, and 700°C for various times. Recrystallization responses were strongly dependent on initial microstructure and Cu content and the effect is dramatic between 1 and 2% Cu. Recrystallization time and temperature were found to be increased with increase in copper content.

Deformation behaviour of a commercial pure titanium alloy during hot compression testing

The flow curve behaviour and microstructure evolution of commercially pure titanium (CP-Ti) through uniaxial hot compression was investigated at 850 °C and a strain rate of 0.1/s. Electron back scattered diffraction (EBSD) was employed to characterize the microstructure and crystallographic texture development for different thermomechanical conditions. The stress-strain curves of CP-Ti alloy under hot compression displayed a typical flow behaviour of metals undergoing dynamic recrystallization (DRX), which resulted in grain refinement. The critical strain for the onset of DRX was 0.13 using the double differentiation analysis technique. It was also revealed that the texture was markably altered during hot deformation. © (2014) Trans Tech Publications, Switzerland.

Collagen type-I leads to in vivo matrix mineralization and secondary stabilization of Mg-Zr-Ca alloy implants

Biodegradable magnesium-zirconia-calcium (Mg-Zr-Ca) alloy implants were coated with Collagen type-I (Coll-I) and assessed for their rate and efficacy of bone mineralization and implant stabilization. The phases, microstructure and mechanical properties of these alloys were analyzed using X-ray diffraction (XRD), optical microscopy and compression test, respectively, and the corrosion behavior was established by their hydrogen production rate in simulated body fluid (SBF). Coll-I extracted from rat tail, and characterized using fourier transform infrared (FT-IR) spectroscopy, was used for dip-coating the Mg-based alloys. The coated alloys were implanted into the femur bones of male New Zealand white rabbits. In vivo bone formation around the implants was quantified by measuring the bone mineral content/density (BMC/BMD) using dual-energy X-ray absorptiometry (DXA). Osseointegration of the implant and new bone mineralization was visualized by histological and immunohistochemical analysis. Upon surface coating with Coll-I, these alloys demonstrated high surface energy showing enhanced performance as an implant material that is suitable for rapid and efficient new bone tissue induction with optimal mineral content and cellular properties. The results demonstrate that Coll-I coated Mg-Zr-Ca alloys have a tendency to form superior trabecular bone structure with better osteoinduction around the implants and higher implant secondary stabilization, through the phenomenon of contact osteogenesis, compared to the control and uncoated ones in shorter periods of implantation. Hence, Coll-I surface coating of Mg-Zr-Ca alloys is a promising method for expediting new bone formation in vivo and enhancing osseointegration in load bearing implant applications.

The effect of treatment temperature on corrosion resistance and hydrophilicity of an ionic liquid coating for mg-based stents

Mg alloys are attractive candidate materials for biodegradable stents. However, there are few commercially available Mg-based stents in clinical use because Mg alloys generally undergo rapid localized corrosion in the body. In this study, we report a new surface coating for Mg alloy AZ31 based on a low-toxicity ionic liquid (IL), tributyl(methyl)phosphonium diphenyl phosphate (P1,4,4,4 dpp), to control its corrosion rate. Emphasis is placed on the effect of treatment temperature. We showed that enhancing the treatment temperature provided remarkable improvements in the performances of both corrosion resistance and biocompatibility. Increasing treatment temperature resulted in a thicker (although still nanometer scale) and more homogeneous IL film on the surface. Scanning electron microscopy and optical profilometry observations showed that there were many large, deep pits formed on the surface of bare AZ31 after 2 h of immersion in simulated body fluid (SBF). The IL coating (particularly when formed at 100 °C for 1 h) significantly suppressed the formation of these pits on the surface, making corrosion occur more uniformly. The P1,4,4,4 dpp IL film formed at 100 °C was more hydrophilic than the bare AZ31 surface, which was believed to be beneficial for avoiding the deposition of the proteins and cells on the surface and therefore improving the biocompatibility of AZ31 in blood. The interaction mechanism between this IL and AZ31 was also investigated using ATR-FTIR, which showed that both anion and cation of this IL were present in the film, and there was a chemical interaction between dpp(-) anion and the surface of AZ31 during the film formation.

The development of ultrafine-grained hot rolling products using advanced thermomechanical processing

The aim of the work is development of industry guidance concerning production of ultrafine-grained (UFG) High Strength Low Alloy (HSLA) steels using strain-induced dynamic phase transformations during advanced thermomechanical processing. In the first part of the work, the effect of processing parameters on the grain refinement was studied. Based on the obtained results, a multiscale computer model was developed in the second part of the work that was subsequently used to predict the mechanical response of studied structures. As an overall outcome, a process window was established for the production of UFG steels that can be adopted in existing hot rolling mills. © 2014 Elsevier B.V.

Finite element analysis of residual stresses in metallic coatings through a compound casting

Al and Mg alloys are widely used in industry as main lightweight alloys. They have excellent properties, such as low density, high ductility, and high specific strength, and so on. Generally speaking, Mg alloys are better than Al alloys. However the corrosion of Mg alloys is much more difficult to control compared Al alloys. Therefore to combine these two lightweight alloys, a composite-like structure is an ideal solution since Al alloys can be used as protective coatings for Mg alloys. Compound casting is a realistic technique to get this coating system. In the current study, we numerically study the compound casting using finite element method (FEM) to make these two alloys, a composite-like structure, satisfy requirements to resist corrosion required from industry, in which the aluminum layer is acting as a protective coating for the magnesium substrate. Several finite element models have been developed by using the birth and death element technique and we focus on compound casting-induced residual stresses in the compounded structure. The numerical results obtained from the proposed finite element models show the distribution profiles of thermal residual stresses. We found the major factors influencing the residual stresses are the temperature to pre-heating the Al substrate and the thickness of Mg deposits. © (2014) Trans Tech Publications, Switzerland.