Direct preparation and characterization of copper pentacyanonitrosylferrate nanoparticles

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Rietveld refinement, cluster modelling, growth mechanism and photoluminescence properties of CaWO4: Eu3+ microcrystals

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

A joint experimental and theoretical study on the electronic structure and photoluminescence properties of Al-2(WO4)(3) powders

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Structural and optical properties of ZnS/MgNb2O6 heterostructures

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Structure, Morphology, and Optical Properties of (Cal(1-3x)Eu(2x)) WO4 Microcrystals

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

The modification of structural and optical properties of nano- and submicron ZnO powders by variation of solvothermal syntheses conditions

Nano- (30-60 nm) and submicron (100-350 nm) ZnO particles were synthesized using solvothermal method at 200 degrees C from an ethanolic solution of zinc acetate dihydrate, applying different reaction conditions, i.e., pH value of precursor and time of the reaction. The X-ray diffraction (XRD), field emission scanning electron microscopy (FE-SEM), transmission electron microscopy (TEM), UV-vis diffuse reflectance (DR), Raman spectroscopy, and photoluminescence (PL) spectroscopy have been employed for characterization of synthesized ZnO powders. It was shown that the structural, morphological, and optical properties are largely determined by reaction conditions during solvothermal synthesis. The particle crystallinity improves with the decrease of pH value and/or the increase of time of the reaction. The Raman and PL spectra analyses indicate that the oxygen interstitials are dominant intrinsic defects in solvothermally synthesized ZnO powders. It was observed that concentration of defects in wurtzite ZnO crystal lattices slightly changes with the variation of pH value of the precursor and time of the solvothermal reaction. The correlation between structural ordering and defect structure of particles and corresponding growth processes was discussed.

Synthesis and optical property of MgMoO4 crystals

In this work, we report on the synthesis of MgMoO4 crystals by oxide mixed method. The powder was calcined at 1100 degrees C for 4h and analyzed by X-ray diffraction (XRD), Fourier transform infrared (FT-IR), Field emission gun scanning electron microscopy (FEG-SEM), Ultraviolet-visible (UV-vis) absorption spectroscopy and Photoluminescence (PL) measurement. XRD analyses revealed that the MgMoO4 powders crystallize in a monoclinic structure and are free secondary phases. UV-vis technique was employed to determine the optical band gap of this material. MgMoO4 crystals exhibit an intense PL emission at room temperature with maximum peak at 579 nm (yellow region) when excited by 350 nm wavelength at room temperature.

Morphological and electrical evolution of ZnO:Al thin films deposited by rf magnetron sputtering onto glass substrates

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

alpha-SiAlON-SiC composites obtained by gas-pressure sintering and hot-pressing

The objective of this work was the obtaining in situ of alpha-SiAlON-SiC composite, using an alternative rare-earth oxide mixture, RE2O3, as sintering additive, by two different sintering processes. As sintering additive, 20 vol.% of AlN-RE2O3 in a molar ratio of 90: 10 was mixed to the alpha-Si3N4 powder. In the Si3N4-AlN-RE2O3 powder mixture, 0, 10, 15 and 20wt.% of SiC were added. The powder batches were milled, dried and compacted by cold isostatic pressing. Two different sintering processes were used: gas-pressure sintering at 1950 degrees C for 1 h under 1.5 MPa of N-2 atmosphere, or uniaxial hot-pressing at 1750 degrees C, for 30 min under pressure of 20 MPa. The sintered samples were characterized by X-ray diffraction, scanning electron microscopy and mechanical properties. XRD patterns indicate only alpha-SiAlON (alpha') and beta-SiC as crystalline phases. It was observed that the SiC addition did not influence the alpha-SiAlON formation, although the growth of elongated alpha'-grains is substantially decreased. The hot-pressed composites presented better mechanical properties, exhibiting fracture toughness of 5 MPa m(1/2) and hardness around 21.5 GPa. (c) 2007 Elsevier B.V. All rights reserved.

Structural, optical, and magnetic properties of NiMoO4 nanorods prepared by microwave sintering

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Thermal and crystalographic studies of mixture La2O3-SrO prepared via reaction in the solid state

The compound obtained via state solid reaction of the La2O3 and SrO oxides and expose the room atmosphere shows the crystallographic data of the compound reported as La2SrOx. However, thermogravimetric, differential thermal analysis and XRD with controlled temperature indicated that the stoichiometry of the compound is 2La(OH)(3)-SrCO3, which structural parameters were determined by using the Rietveld method. It was verified that when the compound exposed at room atmosphere, the mixture oxide absorbs H2O and CO2 producing hydroxide and carbonate of lanthanum and strontium, respectively, which thermal decomposition occurs by the same steps, producing the La2O3-SrO.

The preparation and thermal decomposition of some metal compounds of 4-dimethylaminobenzylidenepyruvate in the solid state

Solid M-DMBP compounds, where M represents Mg(II), Ca(II), Sr(II), Ba(II), Ni(II), Cu(II), Zn(II), Fe(III), La(III), Th(IV), and DMBP is 4-dimethylaminobenzylidenepyruvate, have been prepared. Thermogravimetry-derivative thermogravimetry (TG-DTG), differential scanning calorimetry (DSC) and other methods of analysis have been used to characterize and to study the thermal stability and thermal decomposition of these compounds. © 1995.

Bio-hydrogen production based on catalytic reforming of volatiles generated by cellulose pyrolysis: an integrated process for ZnO reduction and zinc nanostructures fabrication

The paper presents a process of cellulose thermal degradation with bio-hydrogen generation and zinc nanostructures synthesis. Production of zinc nanowires and zinc nanoflowers was performed by a novel processes based on cellulose pyrolysis, volatiles reforming and direct reduction of ZnO. The bio-hydrogen generated in situ promoted the ZnO reduction with Zn nanostructures formation by vapor–solid (VS) route. The cellulose and cellulose/ZnO samples were characterized by thermal analyses (TG/DTG/DTA) and the gases evolved were analyzed by FTIR spectroscopy (TG/FTIR). The hydrogen was detected by TPR (Temperature Programmed Reaction) tests. The results showed that in the presence of ZnO the cellulose thermal degradation produced larger amounts of H2 when compared to pure cellulose. The process was also carried out in a tubular furnace with N2 atmosphere, at temperatures up to 900 °C, and different heating rates. The nanostructures growth was catalyst-free, without pressure reduction, at temperatures lower than those required in the carbothermal reduction of ZnO with fossil carbon. The nanostructures were investigated by X-ray diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and transmission electron microscopy (TEM). The optical properties were investigated by photoluminescence (PL). One mechanism was presented in an attempt to explain the synthesis of zinc nanostructures that are crystalline, were obtained without significant re-oxidation and whose morphologies are dependent on the heating rates of the process. This route presents a potential use as an industrial process taking into account the simple operational conditions, the low costs of cellulose and the importance of bio-hydrogen and nanostructured zinc.

Morphology and properties of (Ba, Sr, Ca) titanates synthesized by microwave-assisted hydrothermal method

Ba1-xCaxTiO3, Ba1-xSrxTiO3 and Sr1-xCaxTiO3 (x = 0, 0.25, 0.50, 0.75 and 1) nanoparticles were synthesized using the microwave-assisted hydrothermal method. Samples were prepared for 40 minutes at 140°C under a pressure of 3 MPa using an adapted domestic microwave oven. The samples were characterized by X-Ray diffraction (XRD), scanning electron microscopy (FE-SEM), and Raman, photoluminescence (PL) and ultraviolet-visible (UV-Vis) spectroscopies. XRD data show that ceramic powders have crystalline phases associated with a short-range structural disorder. This structural disorder is confirmed by Raman spectral bands indicating multi-phonon processes and the presence of defects or impurities. Such defects account for a broad band in the photoluminescence spectrum in the green light (460 nm) region for all samples. Gap energy variation, obtained from UV-Vis spectra, suggest a non-uniform band structure of these titanates in accordance with the PL results. The morphology of each sample is changed with doping and varies from a spherical to cubic appearance for energy minimization.

Effect of Zn Sputtering Rate on the Morphological and Optical Properties of ZnO Films

Zinc oxide (ZnO) and aluminum-doped zinc oxide (ZnO:Al) thin films were deposited onto glass and silicon substrates by RF magnetron sputtering using a zinc-aluminum target. Both films were deposited at a growth rate of 12.5 nm/min to a thickness of around 750 nm. In the visible region, the films exhibit optical transmittances which are greater than 80%. The optical energy gap of ZnO films increased from 3.28 eV to 3.36 eV upon doping with Al. This increase is related to the increase in carrier density from 5.9 × 1018 cm-3 to 2.6 × 1019 cm-3. The RMS surface roughness of ZnO films grown on glass increased from 14 to 28 nm even with only 0.9% at Al content. XRD analysis revealed that the ZnO films are polycrystalline with preferential growth parallel to the (002) plane, which corresponds to the wurtzite structure of ZnO.