Elastic Constants And Structural Parameters Of Selected Polycrystalline Ceramics By Ultrasonic Technique

The present work is an attempt to probe the elastic properties in some dielectric ceramics, by using ultrasonic pulse echo overlap technique. The base Ba6-xSm8+2xTi18O54 and Ca5Nb2TiO12 are very important dielectrics ceramics used for microwave communication as well as for substrate materials. Ultrasonic is one of the most widely used and powerful techniques to measure elastic properties of solids. The ultrasonic technique is nondestructive in nature and the measurements are relatively straightforward to perform. One unique advantantage of the ultrasonic technique is that both static and dynamic properties can be measured simultaneously. The velocity and attenuation coefficients of the ultrasonic waves propagating through a medium are related to the microscopic structure of the material and they provide valuable information about the structural changes in the system. Among the various ultrasonic techniques, the pulse echo overlap method is the most accurate and precise one. In the present case the decreased elastic properties of Cas-XMg,Nb2TiO12 and Cas-,ZnNb2TiO12 ceramics can be attributed to their mixture phases beyond x = 1. Moreover, the abrupt change in elastic properties observed for x >1 can also be correlated to the structural transformation of the materials from their phase pure form to mixture phases for higher extent of substitution of the concerned material . Ca4(ANb2Ti)012 (A = Mg, Zn) is the strongest compound with the maximum values for elastic properties . This could be due to the possible substitution of Mg/Zn ions with lesser radius [25] than Ca2+ in perovskite B-site of Ca(Cali4Nb2i4Tili4) O3 material to contribute more ordering and symmetry to the system [20]. All other compositions (x > 1) contain mixed-phases and for such mixed-phase samples, the mechanical properties are difficult to explain.

Investigations on Ultrasonic Transducer Array Systems for NDE of Underwater Pipelines

The main objective of carrying out this investigation is to develop suitable transducer array systems so that underwater pipeline inspection could be carried out in a much better way, a focused beam and electronic steering can reduce inspection time as well. Better results are obtained by optimizing the array parameters. The spacing between the elements is assumed to be half the wavelength so that the interelement interaction is minimum. For NDT applications these arrays are operated at MHz range. The wavelengths become very small in these frequency ranges. Then the size of the array elements becomes very small, requiring hybrid construction techniques for their fabrication. Transducer elements have been fabricated using PVDF as the active, mild steel as the backing and conducting silver preparation as the bonding materials. The transducer is operated in the (3,3) mode. The construction of a high frequency array is comparatively complicated. The interelement spacing between the transducer elements becomes considerably small when high frequencies are considered. It becomes very difficult to construct the transducer manually. The electrode connections to the elements can produce significant loading effect. The array has to be fabricated using hybrid construction techniques. The active materials has to be deposited on a proper substrate and etching techniques are required to fabricate the array. The annular ring, annular cylindrical or other similar structural forms of arrays may also find applications in the near future in treatments were curved contours of the human body are affected.

Ultrasonic measurement of the elastic constants of selected nonlinear optical /semiorganic crystals with orthorhombic symmetry

Ultrasonic is a good tool to investigate the elastic properties of crystals. It enables one to determine all the elastic constants, Poisson’s ratios, volume compressibility and bulk modulus of crystals from velocity measurements. It also enables one to demonstrate the anisotropy of elastic properties by plotting sections of the surfaces of phase velocity, slowness, group velocity, Young’s modulus and linear compressibility along the a-b, b-c and a-c planes. They also help one to understand more about phonon amplification and help to interpret various phenomena associated with ultrasonic wave propagation, thermal conductivity, phonon transport etc. Study of nonlinear optical crystals is very important from an application point of view. Hundreds of new NLO materials are synthesized to meet the requirements for various applications. Inorganic, organic and organometallic or semiorganic classes of compounds have been studied for several reasons. Semiorganic compounds have some advantages over their inorganic and inorganic counterparts with regard to their mechanical properties. High damage resistance, high melting point, good transparency and non-hygroscopy are some of the basic requirements for a material to be suitable for device fabrication. New NLO materials are being synthesized and investigation of the mechanical and elastic properties of these crystals is very important to test the suitability of these materials for technological applications

Analysis and Testing of a Novel Oadm Based on FBG and Machzehnder Interferometer

A novel optical add-drop multiplexer (OADM) based on the Mach-Zelauler interferometer (MZI) and the fiber Bragg grating (FBG) is proposed for the first tittle to the authors ' knowledge. In the structure, the Mach-Zehnder interferometer acts as an optical switch. The principle of the OADM is analyzed in this paper. The OADM can add/drop one of the multi-input channels or pass the channel directly by adjusting the difference of the two arms of the interferometer. The channel isolation is more than 20 dB

Phase transitions in lithium ammonium sulfate below room temperature: An ultrasonic study

A detailed ultrasonic study of the elastic properties of lithium ammonium sulfate ~LiNH4SO4! or LAS has been carried out below room temperature. The elastic constants of LAS at room temperature are reported. The discrepancy present in earlier elastic constant data associated with the different choice of axes for this orthorhombic system are clarified. The results of the temperature variation study down to 220 K confirm the ferroelastic phase transition at 285 K and establish a thermal hysteresis of about 2.5 K between the cooling and heating cycles. Results of the investigation on the suspected weak phase transition at 256 K suggest that this transition occurs at 242 K on cooling and at 256 K on heating, thus having a thermal hysteresis of about 14 K. However, since the observed elastic anomaly for this transition is very small, the nature of this transition still remains unclear

Anisotropy in elastic properties of lithium sodium sulphate hexahydrate single crystal—An ultrasonic study

The double sulfate family (ABSO4), where A and B are alkali metal cations, is the object of great interest owing to the complexity and richness of its sequence of phase transition induced by temperature variation. A new sulfate salt characterized by the presence of water molecule in the unit cell with the chemical formula, Li2Na3(SO4)2⋅6H2O (LSSW), was obtained. The ultrasonic velocity measurement was done with pulse echo overlap technique [PEO]. All the six second order elastic stiffness constants, C11 = C22, C33, C44 = C55, C12, C14 and C13 = C23 are reported for the first time. The anisotropy in the elastic properties of the crystal are well explained by the pictorial representation of the polar plots of phase velocity, slowness, Young’s modulus and linear compressibility in a–b and a–c planes.

Ultrasonic measurement of the elastic properties of benzoyl glycine single crystals

Certain organic crystals are found to possess high non- linear optical coefficients,often one to two orders of magnitude higher than those of the well known inorganic non-linear optical materials.Benzoyl glycine is one such crystal whose optical second-harmonic generation efficiency is much higher than that of potassium dihydrogen phosphate. Single crystals of benzoyl glycine are grown by solvent evaporation technique using N,N-dimethyl formamide as the solvent.All the nine second-order elastic stiffness constants of this orthorhombic crystal are determined from ultrasonic wave velocity measurements employing the pulse echo overlap technique.The anisotropy of elastic wave propagation in this crystal is demonstrated by plotting the phase velocity, slowness,Young's modulus and linear compressibility surfaces along symmetry planes.The volume compressibility, bulk modulus and relevant Poisson's ratios are also determined. Variation of the diagonal elastic stiffness constants with temperature over a limited range are measured and reported.

Non-destruct|ve testing of non-metallic materials using microwaves

The motivatitni for" the present work is from .a project sanctioned by TSRO. The work involved the development of a quick and reliable test procedure using microwaves, for tflue inspection of cured propellant samples and a method to monitor the curing conditions of propellant mix undergoing the curing process.Normal testing CHE the propellant samples involvecuttimg a piece from each carton and testing it for their tensile strength. The values are then compared with standard ones and based on this result the sample isaccepted or rejected. The tensile strength is a measure ofdegree of cure of the propellant mix. But this measurementis a destructive procedure as it involves cutting of the sample. Moreover, it does not guarantee against nonuniform curing due to power failure, hot air-line failure,operator error etc. This necessitated the need for the development of a quick and reliable non-destructive test procedure.

Testing Isotropy and a related Random Walk problem

One comes across directions as the observations in a number of situations. The first inferential question that one should answer when dealing with such data is, “Are they isotropic or uniformly distributed?” The answer to this question goes back in history which we shall retrace a bit and provide an exact and approximate solution to this so-called “Pearson’s Random Walk” problem.

Simulation on the process of fatigue crack initiation in a martensitic stainless steel

Die vorliegende Arbeit beschäftigt sich mit der Computersimulation des Rissinitiierungsprozesses für einen martensitischen Stahl, der der niederzyklischen Ermüdung unterworfen wurde. Wie auf der Probenoberfläche beobachtet wurde, sind die Initiierung und das frühe Wachstum dieser Mikrorisse in hohem Grade von der Mikrostruktur abhängig. Diese Tatsache wurde in mesoskopischen Schädigungsmodellen beschrieben, wobei die Körner als einzelne Kristalle mit anisotropem Materialverhalten modelliert wurden. Das repräsentative Volumenelement (RVE), das durch einen Voronoi-Zerlegung erzeugt wurde, wurde benutzt, um die Mikrostruktur des polykristallinen Materials zu simulieren. Spannungsverteilungen wurden mit Hilfe der Finiten-Elemente-Methode mit elastischen und elastoplastischen Materialeigenschaften analysiert. Dazu wurde die Simulation zunächst an zweidimensionalen Modellen durchgeführt. Ferner wurde ein vereinfachtes dreidimensionales RVE hinsichtlich des sowohl dreidimensionalen Gleitsystems als auch Spannungszustandes verwendet. Die kontinuierliche Rissinitiierung wurde simuliert, indem der Risspfad innerhalb jedes Kornes definiert wurde. Die Zyklenanzahl bis zur Rissinitiierung wurde auf Grundlage der Tanaka-Mura- und Chan-Gleichungen ermittelt. Die Simulation lässt auf die Flächendichten der einsegmentige Risse in Relation zur Zyklenanzahl schließen. Die Resultate wurden mit experimentellen Daten verglichen. Für alle Belastungsdehnungen sind die Simulationsergebnisse mit denen der experimentellen Daten vergleichbar.