Interference of the assessment method in pH values of an epoxy-based cement

Introduction: Alkalinization potential is a fundamental property of endodontic epoxy-based cements containing calcium hydroxide. Studies have shown discrepant pH results for same materials at different evaluation periods. A possible reason accounting for these differences may be the assessment procedures. Objective: To evaluate the pH value of an epoxy-based cement (Sealer 26) in different periods of analysis, using two assessment methods. Material and methods: Sealer 26 was manipulated and immediately placed into polyethylene tubes (n=10, each group) and immersed in distilled water. In G1, the tubes were kept in the same water during all experiment; and in G2, the tubes were removed and placed into another flask with an equal amount of water after the pH evaluation. The pH of these solutions was measured at 24 hours, 7, 14 and 28 days. Analysis were made within the same group according to the experimental periods and between groups in each experimental period. Data were submitted to ANOVA (α = 5%) and t test, respectively. Results: For G1 and G2, all periods showed different pH values (p < 0.05), except between 14 and 28 days (p > 0.05) and between 7 and 14 days (p > 0.05), respectively. In each period, no significant differences were observed between the groups. Conclusion: The method to obtain the pH values in different experimental periods no interfered in the final results. However, difference was observed when the results were analyzed at same group.

Evaluation of the physicochemical properties and push-out bond strength of mta-based root canal cement

Aim: This study investigated the flowability, setting time, pH, calcium release and bond strength of a MTA-based cement (MTA Fillapex®) compared to AH Plus and Sealapex. Materials and methods: For the flowability test, the ISO 6876:2001 specification was utilized and for the setting time test, the ASTM C266-03 specification was utilized. For the pH and calcium release measurements, 10 samples were prepared for each group and analyzed for several different periods. For the push-out test, dentin disks were distributed into three groups, according to the cement utilized and into three subgroups, according to the root third (n = 10). After obturation, the specimens underwent push-out testing. The data were compared statistically using a significance level of 5%. Results: The flowability of all materials was found to be similar (p > 0.05). The setting times were different among the groups tested (MTA Fillapex < Sealapex < AH Plus) (p < 0.05). At days 7 and 28, the MTA Fillapex presented the higher pH values (p < 0.05). At 24 hours and at 14 days, the calcium release of the MTA Fillapex was similar to that of Sealapex (p > 0.05). AH Plus presented the lowest pH and calcium release values (p < 0.05). In all root thirds, the adhesion to the dentin of the MTA Fillapex and Sealapex were significantly lower than that of AH Plus (p < 0.05). Conclusion: MTA Fillapex and Sealapex presented several similar properties and both were found to be different than AH Plus. Clinical significance: This study evaluated the physicochemical and mechanical properties of new MTA-based root canal cement, in order to use this scaler in root canal fillings. MTA Fillapex showed satisfactory properties for clinical use.

Indirect resin onlay cemented with self-adhesive resin cement: a comprehensive clinical overview

Advances in adhesive technology and esthetic dental materials have permitted clinicians to perform conservative preparation of the dentition for onlay restorations. Indirect resin onlays are a great alternative to dental crowns for reestablishment the function and esthetic in teeth with great destruction.

The association of chlorhexidine digluconate and calcium chloride to use as vehicle of a silicate calcium-based cement

Objective: The purpose of this study was to evaluate the influence of the addition of 2% chlorhexidine digluconate (CHX) associated with 5% calcium chloride (CaCl2 ) on antimicrobial activity, setting time, pH and calcium release of gray mineral trioxide aggregate (GMTA). Materials and Methods: GMTA powder was mixed with water, 2% CHX alone or 2% CHX combined with 5% CaCl2 . Antimicrobial activity was determined against Enterococcus faecalis (ATCC 29212) strains by agar diffusion test. Data obtained were submitted to kruskal wallis tests. Analysis of the setting time was evaluated by American society for testing and materials C266-03 requirements. The pH and calcium release analysis were evaluated, in 24 h, 7, 14 and 28 days using pH meter equipment and atomic absorption spectrophotometer, respectively. Data obtained were analyzed by ANOVA, in 5% significance level. Results: Significant differences were seen (P < 0.01) among the zones of bacterial growth inhibition produced by 5% CaCl2 + 2% CHX combination against E. faecalis when compared with water (P < 0.05). Regarding the setting time, that combination had the shortest setting time (P < 0.05). All associations were alkaline and released calcium. No statistical difference was observed between the experimental groups at the different periods of analysis (P > 0.05). Conclusion: Combination of 5% CaCl2 + 2% CHX reduced the setting time and enhanced the antimicrobial activity of GMTA without changing the pH and calcium release.

Effect of chlorhexidine gluconate on porosity and compressive strength of a glass ionomer cement

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Influence of the addition of chlorhexidine diacetate on bond strength of a high-viscosity glass ionomer cement to sound and artificial caries-affected dentin

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Addition of Chlorhexidine Gluconate to a Glass Ionomer Cement: A Study on Mechanical, Physical and Antibacterial Properties

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Double-setting alpha-tricalcium phosphate cement provided with interconection channels in rabbits after enucleation: a potential implant for the anophthalmic socket

The purpose of this study was to evaluate the macroscopy and microstructure of a double setting alpha-tricalcium phosphate bone cement sphere provided with interconnection channels (alpha-TCP-i), as well as the integration of the implant with the rabbits' orbital tissue, through macroscopic analysis and histopathology. The external and internal surfaces of the alpha-TCP-i were evaluated macroscopically and by electron microscopy. Twelve New Zealand rabbits received 12mm implants of alpha-TCP-i following enucleation of the left eye. The clinical assessment was undertaken daily during the first 15 days, followed by fortnightly assessment until the end of the study period. For the morphological analysis, exenteration was performed in 3 animals per experimental period (15, 45, 90 and 180 days). The external and internal surfaces of the implant appeared solid, smooth and compact, with six channels which interconnected centrally. The micro-architecture was characterized by the formation of columns of hexagonal crystals. No signs of infection, exposure, dehiscence of sutures or extrusion of the implant were noted in any of the animals during the entire period of the study. The morphological evaluation demonstrated the presence of a thin capsule around the implant, from whence appeared fibro-vascular projections, which penetrated it through the interconnecting channels. In the first days after the insertion of the implant, an intense inflammatory reaction was noted. At 180 days, however, there were no signs of inflammation. The alpha-tricalcium phosphate cement implant was well tolerated in this rabbit model and appeared to be relatively inert with some fibrovascular ingrowth through the large channels.

Can Application of Universal Primers Alone Be a Substitute for Airborne-Particle Abrasion to Improve Adhesion of Resin Cement to Zirconia?

Purpose: To determine whether universal primers alone can deliver similar levels of adhesion of resin cement to zirconia ceramic when compared to their application in conjunction with airborne-particle abrasion.Materials and Methods: Sintered zirconia blocks (N = 160) (Lava, 3M ESPE), (5.25 x 5.25 x 3 mm(3)) were embedded in acrylic resin, polished, and randomly distributed into 16 groups (n = 10 per group), according to the factors "universal primer" (8 levels) and "air-particle abrasion" (2 levels): 1. ctr: control, without application of a universal primer; 2. AP: Alloy Primer; 3. MP: Monobond Plus; 4. MZP: Metal Zirconia Primer; 5. MZ: MZ Primer; 6. Sg: Signum Zirconia Bond; 7. SbU: Singlebond Universal; 8. ZP: Z Prime Plus. The universal primers were also used after air abrasion (A) of zirconia to form the following 8 groups: Ctr-A, AP-A, MP-A, MZP-A, MZ-A, Sg-A, SbU-A, and ZP-A. After ultrasonic cleaning, air abrasion was performed using Al2O3 particles (110 mu m, 2.5 bar, 20 s at 10 mm) in a chairside air-abrasion device. After ultrasonic cleaning again, universal primers were applied according to each manufacturer's recommendation. The resin cement (RelyX ARC, 3M ESPE) was built up incrementally and photo-polymerized on the zirconia surface using a silicone mold (empty set = 3.5, height = 3 mm). All specimens were stored in distilled water (60 days at 37 degrees C) and then subjected to shear bond strength testing (SBS) in a universal testing machine (1 mm/min). On a separate set of zirconia specimens, contact angle measurements were made using the sessile drop technique with a goniometer after the application of universal primers on control and air-abraded zirconia surfaces. Data (MPa) were analyzed using one-way ANOVA, Tukey's test, and Student's t-test (alpha = 0.05).Results: When universal primers were used alone, SbU presented significantly higher mean SBS (19.5 +/- 5.8) that did the other primers (0 to 9.9 +/- 6.6) (p = 0.001). When air abraded, the groups AP-A (14.1 +/- 6.1), MP-A (15.9 +/- 5.4), ZP-A (16.9 +/- 7.3), SG-A (19.1 +/- 2.1), SbU-A (12 +/- 1.5) showed significant differences (p = 0.03). Adhesive performance of all universal primers was enhanced after air abrasion, with the exception of the SbU and MZ primers. After air abrasion, contact angle measurements were lower for the each primer (without air abrasion: 28.9 to 83.9; with air abrasion: 27.1 to 63.0), except for MZP.Conclusion: Air abrasion with 110 mu m Al2O3 followed by universal primer application increased the bond strength of tested resin cement to zirconia, with the exception of SbU and MZ.

Non-conventional cement-based composites reinforced with vegetable fibers: a review of strategies to improve durability

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Supercritical carbonation treatment on extruded fibre-cement reinforced with vegetable fibres

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Influence of Insertion Techniques for Resin Cement and Mechanical Cycling on the Bond Strength Between Fiber Posts and Root Dentin

Purpose: To evaluate the effect of the insertion technique for resin cement and mechanical cycling on the bond strength between fiber posts and root dentin.Materials and Methods: Sixty-four single-rooted bovine teeth were endodontically prepared to receive glass-fiber posts. The insertion of cement into the root canal was performed using one of the following techniques: POS, insertion with the post; LEN, the use of a lentulo-type drill; EXP, insertion with a straight-tip explorer; or CEN, the use of a Centrix syringe. Half of the specimens were mechanically cycled. All specimens were sectioned into slices of 1.8 mm for the push-out test and 0.5 mm for analysis of the cement layer quality.Results: The insertion technique affected the interaction between factors (bond strength and mechanical cycling; p < 0.0001). Insertion of the Centrix syringe after mechanical cycling showed the highest bond values (13.6 +/- 3.2 MPa). Group-to-group comparisons for baseline and cycled conditions indicated that mechanical cycling significantly influenced the bond strength (p < 0.0001) of the POS and CEN groups. The quality of the cement layer did not differ between the techniques when evaluated in the middle (p = 0.0612) and cervical (p = 0.1119) regions, but did differ in the apical region (p = 0.0097), where the CEN group had better layer quality for the two conditions tested (baseline and cycled).Conclusion: The use of the Centrix syringe improved the homogeneity of the cement layer, reducing the defects in the layer and increasing adhesive strength values to dentin, even after mechanical cycling.

Influence of thicknesses of smear layer on the transdentinal cytotoxicity and bond strength of a resin-modified glass-ionomer cement

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Study of thermocycling effect on the bond strength between an aluminous ceramic and a resin cement

This study evaluated the effect of thermocycling on the bond strength between Procera AllCeram (Nobel-Biocare) and a resin cement (Panavia F, Kuraray CO). Nine ceramic blocks with dimensions of 5x6x6mm were conditioned at one face with Rocatec System (Espe). After, they were luted with Panavia F to composite resin blocks (Clearfil AP-X, Kuraray CO). The nine groups formed by ceramic, cement and composite resin were split up obtaining 75 samples with dimensions of 12x1x1mm and adhesive surface presenting 1mm2±0.1mm2 of area. The samples were divided into 3 groups (n=25): G1 - 14 days in distilled water at 37ºC; G2 – 6,000 cycles in water (5ºC - 55ºC – 30s); G3 – 12,000 cycles in water (5ºC - 55ºC – 30s). The samples were tested in a universal testing machine (EMIC) at a crosshead speed of 1mm/min. Data were analyzed by ANOVA and Tukey tests. The results indicated that mean values of rupture tension (MPa) of G1 (10.71 ± 3.54) did not differ statistically (p <5%) from G2 (9.01 ± 3.90), however there was statistical difference between G1 and G3 (7.28 ± 3.00). It was concluded that thermocycling significantly reduced the bond strength values when samples were submitted to 12,000 cycles.

Influence of Nd:YAG or Er:YAG laser surface treatment on microtensile bond strength of indirect resin composites to resin cement. Lasers surface treatment of indirect resin composites

This study evaluated the influence of the surface pretreatment of indirect resin composite (Signum, Admira Lab and Sinfony) on the microtensile bond strength of a resin cement. Sixty samples made of each brand were divided into 6 groups, according to surface treatment: (1) control; (2) controlled-air abrasion with Al2O3; (3) Er:YAG Laser 200 mJ, 10 Hz, for 10s; (4) Er: YAG Laser 300 mJ, 10 Hz, for 10 s; (5) Nd:YAG 80 mJ, S15Hz for 1 min; (6) Nd:YAG 120mJ, 15 Hz for 1 min. After treatments, all the groups received an application of 37% phosphoric acid and adhesive. The pair of blocks of the same brand were cemented to each other with dual resin cement. The blocks were sectioned to obtain resin-resin sticks (1 x1 mm) and analyzed by microtensile bond testing. The bond strength values were statistically different, irrespective of the surface treatment performed, with highest values for Sinfony (43.81 MPa) and lowest values for Signum (32.33 MPA). The groups treated with the Nd:YAG laser showed the lowest bond strength values and power did not interfere in the results, both for Nd:YAG laser and Er:YAG. Controlled-air abrasion with Al203 is an efficient surface treatment method and the use of the Nd:YAG and Er:YAG lasers reduced bond strength, irrespective of the intensity of energy used.