Helical conformations of three crystalline pentapeptide fragments of suzukacillin, a membrane channel forming polypeptide

The crystal structures of three pentapeptide fragments of suzukacillin-A have been determined. Boc-Aib-Pro-Val-Aib-Val-OMe (peptide 1–5) adopts a distorted helical conformation, stabilized by three intramolecular hydrogen bonds (two 5→1, one 4→1). Boc-Ala-Aib-Ala-Aib-Aib-OMe (peptide 6–10) and Boc-Leu-Aib-Pro-Val-Aib-OMe (peptide 16–20) adopt 310 helical structures stabilized by three and two 4→1 intramolecular hydrogen bonds, respectively. These structures provide substantial support for a largely helical conformation for the suzukacillin membrane channel.

Two- and three-dimensional lead-1H-imidazole-4,5-dicarboxylates

Reaction of lead nitrate and 1H-imidazole-4,5-dicarboxylic acid under hydrothermal conditions carried out at different temperatures and pH yields a hybrid Compound Pb-2(1H-imidazole-4,5-dicarboxylate)2, 1, and a three-dimensional coordination polymer Pb(1H-imidazole-4,5-dicarboxylate), It. The two-dimensional double-layered compound, 1, with two-dimensional inorganic connectivities and one-dimensional organic connectivity is novel since hybrid compounds formed by 1H-imidazole-4,5-dicarboxylic acid are uncommon. The lead atoms in I have holodirectional geometry, while those in II show hemidirectionality. In both I and II, 1H-imidazole-4,5-dicarboxylic acid acts as a multi-dentate ligand with both the carboxylic groups and the amine group taking part in coordination. (C) 2009 Elsevier B.V. All rights reserved.

Anomeric effect in sulfur-containing systems: An Ab-initio study

The anomeric effect in S---C---S and O---C---S systems was studied by using closed-shell Hartree-Fock theory. A comparison of the STO-3G level with the 4–31G and 6–31G* levels was performed for the O---C---O system, and the STO-3G level found adequate for study of the anomeric effect. Optimization of bond lengths and angles was conducted at the STO-3G level and limited studies were made at the 4–31G level. The nature of the torsional potential curves is compared for the O---C---O, O---C---S, and S---C---S systems. The possible reasons for the decreased anomeric effect in sulfur systems are discussed.

X-ray photoelectron spectroscopic studies of surface oxidation of metallic glasses

Surface oxidation of the metallic glass Fe40Ni38Mo4B18 has been studied by X-ray photoelectron spectroscopy. The oxidation behaviour of the metallic glass has been compared with a crystallized sample of the same composition. A similar study has been carried out on the metallic glass Ni76Si12B12,which shows the importance of chemical composition in determining the surface oxidation behaviour of these alloys.

DNase I Site Mapping and Micrococcal Nuclease Digestion of Pachytene Chromatin Reveal Novel Structural Features

A comparison of the DNase I digestion products of the 32P-5’-end-labeled pachytene nucleosome core particles (containing histones H2A, TH2A, X2, H2B, THPB, H3a, nd H4) and liver nucleosome core particles (containing somatic histones H2A, H2B, H3, and H4) revealed that the cleavage sites that are 30, 40, and 110 nucleotidesa way from the 5’-enda re significantly more accessiblei n the pachytene core particles than in the liver core particles. These cleavage sites correspond to the region wherein H2B interacts with the nucleosome core DNA. These results, therefore, suggest that the histone-DNA interactiona t these sites in the pachytene core particles is weaker, possibly because of the presence of the histone variant THBB interacting at similar topological positions in the nucleosome core as that of its somatic counterpart H2B. Such a loosened structumrea y also be maintainede ven in the native pachytene chromatin since micrococcal nuclease digestion of pachytene nuclei resulted in a higher ratio of subnucleosomes (SN4 + SN?) to mononucleosomes than that observed liinv er chromatin

EXAFS studies of arsenic chalcogenide glasses

An EXAFS study at the AsK edge of the ternary glasses As2(S, Se)3 and As2(Se, Te)3 and the binary As2S3, As2Se3 and As2Te3 glasses has been carried out. Radial structure functions show that the environment of As in glasses of intermediate compositions is quite different from that in the binary glasses. In the As2(S, Se)3 system, this might arise from chemical disorder in the network while in the As2(Se, Te)3 system increased ionicity could be the cause of this behaviour. Glasses where the constituent atoms are of similar size seem to exhibit fewer peaks in the radial structure function.

An experimental study of oxidation of zinc sulphide pellets

Oxidation of zinc sulphide pellets is carried out in the ranges of 600-826°C temperature, 0.3-0.5 porosity and 15-50 minutes of reaction time. An experimental technique is employed to simultaneously determine the rate of weight loss of the solid and conversions of the solid reactant at various levels in the pellet for different reaction times. A structural model is used to explain the experimental results. It is found that the model predicts both the experimental results obtained under various conditions reasonably well.

High-temperature superconductivity in the 100 K region in perovskite-related oxides of the Ln-Ba-Cu-O (Ln=Y or La) system

Oxides of the Y-Ba-Cu-O system are found to show onset of superconductivity in the 100–120 K region.

Pulsatile blood flow in a stenosed arteryâ a theoretical model

Abstract is not available.

A combined XPS-UPS-EELS study of nitrogen adsorbed on clean and barium-promoted iron surfaces: The nature of the precursor to dissociation

For N2 on a clean Fe surface, the adsorbed precursor in a parallel orientation becomes predominant around 110 K, while at lower temperatures it coexists with a weakly adsorbed species. On a Ba-promoted Fe surface, however, N2 is present exclusively in the precursor state in the temperature range 80–150 K following moderate exposure. Besides exhibiting a low N-N stretching frequency of 1530 cm−1, the precursor shows a clear separation between the 5σ and 1π levels in the UPS; the precursor dissociates to give a nitridic species around 160 K.

Load Transfer from a Smooth Elastic Pin to a Large Sheet

The plane problem of load transfer from an elastic interference or clearance fit pin to a large elastic sheet with a perfectly smooth interface is solved. As the load on the pin is monotonically increased, the pin-hole interface is in partial contact above certain critical load in interference fit and throughout the loading range in clearance fit.Such situations result in mixed boundary-value problems with moving boundaries and the arc of contact varies nonlinearly with applied load. These problems are analyzed by an inverse technique in which the arcs of contact/separation are prescribed and the causative loads are evaluated. A direct method of analysis is adopted using biharmonic polar trigonometric stress functions and a simple collocation method for satisfying the boundary conditions. A unified analytical formulation is achieved for interference and clearance fits. The solutions for the linear problem of push fits are inherent in the unified analysis. Numerical results highlighting the effects of pin and sheet elasticity parameters are presented.

Performance of graphic aluminium particulate composite materials

Friction characteristics of journal bearings made from cast graphic aluminum particulate composite alloy were determined under mixed lubrication and compared with those of the base alloy (without graphite) and leaded phosphor bronze. All three materials ran without seizure while the performance of the particulate composite and leaded phosphor bronze improved with running. Temperature rise in the journal bearing under mixed/boundary lubrication was also measured. It was found that with 0.3D/1000 to 1.5D/1000 clearance and a low lubrication rate (typical value for a bearing of diameter 35 mm × length 35 mm is 80 mm3/min) and at a PV value of 73 × 106 Nm m−2 min−1 graphitic aluminium alloy journal bearings operate satisfactorily without seizure and excessive temperature rise. In comparison, the bronze bearings, with all the other parameters remaining the same, could not run without excessive temperature rise at clearances below D/1000 at lubrication rates lower than 200 mm3/min

Glass Formation in the Ternary Sulphate System, K2S04-Na2S04-ZnS04

Glasses have been prepared by conventional quenching techniques in the ternary sulphate system KzSO4-Na2SO4-ZnSO4, in the range 30-80 % ZnS04. The proportions of alkali sulphates in the glass have been varied widely. The glass formation region has been delineated and densities, refractive indices and microhardnesses have been measured. The heat capacities of the glasses have been measured over a wide range of temperature by differential scanning calorimetry. The effect of composition on molar volume, molar polarization and glass transition have been explained on the basis of a random close-packing model.

Small nickel metal particles in Ni---Al2O3 metal-ceramic composites

Magnetic measurements have been used in combination with transmission electron microscopy to investigate small nickel metal particles in metal-ceramic composites. Estimates of the average number of atoms in the particles are given for nonmagnetic samples with low Ni content.

Concerning hypophyllanthin

The structure (1) for hypophyllanthin was confirmed by X-ray crystallography.