Gelatin-based protonic electrolyte for electrochromic windows

Proton-conducting gel polymer electrolytes based on gelatin plasticized with glycerol and containing acetic acid were investigated, characterized, and applied to electrochromic window. For glycerol contents varying from 7% to 48%, the conductivity of the uniform and predominantly amorphous gel electrolyte was found to follow a Vogel-Tamman-Fulcher behavior with the temperature. Typically, for the electrolyte chosen to make 7 x 2 cm(2) electrochromic smart window with the configuration: glass/fluor-doped tin oxide (FTO)/WO(3)/gelatin electrolyte/CeO(2)-TiO(2)/FTO/glass and containing 28% of glycerol, the conductivities were found to be of the order of 5 x 10(-5) S/cm at room temperature and 3.6 x 10(-4) S/cm at 80 A degrees C. The device was characterized by spectroelectrochemical techniques and was tested up to 10,000 cycles showing a fast coloring/bleaching behavior, where the coloring process was achieved in 10 s and the bleaching in 2 s. The transmission variation at the wavelength of 550 nm was about 15%. The cyclic voltammograms showed a very good reversibility of the cathodic/anodic processes, and the charge density was about 3.5 mC/cm(2). The memory tests showed that the transmittance in the colored state increased by 8% in 90 min after removing the potential.

Agar-based films for application as polymer electrolytes

New types of polymer electrolytes based on agar have been prepared and characterized by impedance spectroscopy, X-ray diffraction measurements, UV-vis spectroscopy and scanning electronic microscopy (SEMI). The best ionic conductivity has been obtained for the samples containing a concentration of 50 wt.% of acetic acid. As a function of the temperature the ionic conductivity exhibits an Arrhenius behavior increasing from 1.1 x 10(-4) S/cm at room temperature to 9.6 x 10(-4) S/cm at 80 degrees C. All the samples showed more than 70% of transparency in the visible region of the electromagnetic spectrum, a very homogeneous surface and a predominantly amorphous structure. All these characteristics imply that these polymer electrolytes can be applied in electrochromic devices. (C) 2009 Elsevier Ltd. All rights reserved.