Nanocomposites of crosslinked starch phthalate and silane modified nanoclay: Study of mechanical, thermal, morphological, and biodegradable characteristics

Biodegradable composites comprising of modified starch and modified nanoclay have been prepared. Starch has been modified by esterification and subsequently crosslinked. The thermal, mechanical, and biodegradation characteristics of the composites have been investigated. The compressive properties of the composites with the addition of nanoclay were twice that of crosslinked starch phthalate without addition of nanoclay. Predictive theories were used to analyze the obtained experimental results. SEM studies on fracture morphology indicated quasi-brittle fracture. Flexural properties showed considerable improvement due to nanoclay addition. The water uptake increased up to 6% nanoclay, beyond which the uptake decreased. Biodegradation studies showed an initial time lag prior to the onset of degradation.

Fine scale characterization of surface/subsurface and nanosized debris particles on worn Cu-10 % Pb nanocomposites

The identification of the damage mechanisms involved in the wear process demands the finer scale characterization of the surface, as well as the subsurface region of the wear scar region, and to this end, this article discusses the results obtained with Cu-10 wt% Pb-based metallic nanocomposites using a host of characterization techniques, including transmission electron microscopy and ion milling microscopy. Apart from finer scale characterization to understand deformation and cracking during the wear process, X-ray photoelectron spectroscopy analysis of wear debris confirms the occurrence of oxidation of Pb phase to Pb3O4. In order to understand the role of oxides on friction and wear, sliding wear tests in argon were also carried out and such tests did not result in the formation of any tribo-oxides, as confirmed using electron probe microanalysis. Conclusively, oxidative wear is attributed as the dominant wear mechanism in ambient conditions for Cu-10 wt% Pb composite.

Microscopic and dielectric studies of ZnO nanoparticles loaded in ortho-chloropolyaniline nanocomposites

We have studied the preparation of zinc oxide nanoparticles loaded in various weight percentages in ortho-chloropolyaniline by in situ polymerization method. The length of the O-chloropolyaniline tube is found to be 200 nm and diameter is about 150 nm wherein the embedded ZnO nanoparticles is of 13 nm as confirmed from scanning electron microscopy as well as transmission electron microscopy characterizations. The presence of the vibration band of the metal oxide and other characteristic bands confirms that the polymer nanocomposites are characterized by their Fourier transmission infrared spectroscopy. The X-ray diffraction pattern of nanocomposites reveals their polycrystalline nature. Electrical property of nanocomposites is a function of the filler as well as the matrix. Cole-Cole plots reveal the presence of well-defined semicircular arcs at high frequencies which are attributed to the bulk resistance of the material. Among all nanocomposites, 30 wt% shows the low relaxation time of 151 s, and hence it has high conductivity.

Exchange-spring mechanism of soft and hard ferrite nanocomposites

The paper reports exchange-spring soft and hard ferrite nanocomposites synthesized by chemical co-precipitation with or without the application of ultrasonic vibration. The composites contained BaFe12O19 as the hard phase and CoFe2O4/MgFe2O4 as the soft phase. X-ray diffraction patterns of the samples in the optimum calcined condition indicated the presence of soft ferrites as face-centred cubic (fcc) and hard ferrites as hexagonal close packed (hcp) structure respectively. Temperature dependence of magnetization in the range of 20-700 degrees C demonstrated distinct presence of soft and hard ferrites as magnetic phases which are characterized by wide difference in magnetic anisotropy and coercivity. Exchange-spring mechanism led these nanocomposite systems to exchange-coupled, which ultimately produced convex hysteresis loops characteristic of a single-phase permanent magnet. Fairly high value of coercivity and maximum energy product were observed for the samples in the optimum calcined conditions with a maximum applied field of 1600 kA/m (2 T).

On the densification mechanisms and properties of Cu-Pb and Cu-Pb-TiB2 nanocomposites densified using spark plasma sintering

The present paper is aimed to understand the sub-processes triggered by rapid heating during spark plasma sintering as well as to assess the extent to which densification and properties of metallic materials can be enhanced using such superfast consolidation process. Using nanocrystalline Cu-Pb as a model system, the influence of Pb as well as TiB2 addition on the densification mechanisms and properties are discussed. Importantly, a high hardness of 2 GPa is achieved in Cu-based nanocomposites. (C) 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Liquefied Petroleum Gas Sensing of Polyaniline-Titanium Dioxide Nanocomposites

Polyaniline/titaniurn dioxide nanocomposites were prepared using alpha-dextrose as surfactant and ammonium persulphate as an oxidant. The PANI/TiO2 nanocomposite is characterized by FTIR, XRD and TEM. The FTIR spectra revel that the presence of characteristic peaks of benzenoid, qunoide rings and metal-oxygen stretching. The XRD studies show the monoclinic structure of the nanocomposites. The TEM study shows that the size of TiO2 is in the order of 9 nm where as the composite size is of the order of 13 nm and further it was observed that the TiO2 particles are intercalated to form a core shell of PANI. The maximum sensing response for LPG is found to be 90% for 30 wt.% of PANI/TiO2 nanocomposites at 400 ppm whereas for Benzene and Toluene it is negligibly small (<= 20%) and for the cyclohexane sensing response it is around 30% for different wt.%.

Characterization, charge transport and magnetic properties of multi-walled carbon nanotube-polyvinyl chloride nanocomposites

Multi-walled carbon nanotube (MWCNT)-polyvinyl chloride (PVC) nanocomposites, with MWCNT loading up to 44.4 weight percent (wt%), were prepared by the solvent mixing and casting method. Electron microscopy indicates high degree of dispersion of MWCNT in PVC matrix, achieved by ultrasonication without using any surfactants. Thermogravimetric analysis showed a significant monotonic enhancement in the thermal stability of nanocomposites by increasing the wt% of MWCNT. Electrical conductivity of nanocomposites followed the classical percolation theory and the conductivity prominently improved from 10(-7) to 9 S/cm as the MWCNT loading increased from 0.1 to 44.4 wt%. Low value of electrical percolation threshold similar to 0.2 wt% is achieved which is attributed to high aspect ratio and homogeneous dispersion of MWCNT in PVC. The analysis of the low temperature electrical resistivity data shows that sample of 1.9 wt% follows three dimensional variable range hopping model whereas higher wt% nanocomposite samples follow power law behavior. The magnetization versus applied field data for both bulk MWCNTs and nanocomposite of 44.4 wt% display ferromagnetic behavior with enhanced coercivities of 1.82 and 1.27 kOe at 10 K, respectively. The enhancement in coercivity is due to strong dipolar interaction and shape anisotropy of rod-shaped iron nanoparticles. (C) 2013 Elsevier B.V. All rights reserved.

Nonlinear optical second harmonic generation in ZnS quantum dots and observation on optical properties of ZnS/PMMA nanocomposites

ZnS quantum dots (QDs) of different sizes are synthesized by a simple chemical co-precipitation method at room temperature, by varying pH value of the reaction mixture. Samples are characterized by an X-ray diffractometer, transmission electron microscope, energy-dispersive X-ray analysis, etc. Linear optical properties, including UV-visible absorption and photoluminescence emission characteristics, of as-prepared QDs are measured. Size dependent nonlinear optical property, such as second harmonic generation (SHG) of 1064 nm Nd:YAG laser fundamental radiation in the synthesized ZnS QDs, is reported for the first time, to the best of our knowledge, by using the standard Kurtz-Perry powder method. In not to study the possibility of the synthesized ZnS QDs in different device applications ZnS/PMMA (polymethylmethacrylate) nanocomposites are also synthesized. The presence of weak chemical interaction between the polymer matrix and ZnS QDs is confirmed by Fourier transform infrared spectroscopy. Thermal properties of the nanocomposites are studied by differential scanning calorimetry and thermo-gravimetric analysis techniques, which show that the composites are stable up to similar to 300 degrees C temperature. (C) 2013 Elsevier B.V. All rights reserved.

Microstructure-Wear Resistance Correlation and Wear Mechanisms of Spark Plasma Sintered Cu-Pb Nanocomposites

The dispersion of a softer phase in a metallic matrix reduces the coefficient of friction (COF), often at the expense of an increased wear rate at the tribological contact. To address this issue, unlubricated fretting wear tests were performed on spark plasma sintered Cu-Pb nanocomposites against bearing steel. The sintering temperature and the Pb content as well as the fretting parameters were judiciously selected and varied to investigate the role of microstructure (grain size, second-phase content) on the wear resistance properties of Cu-Pb nanocomposites. A combination of the lowest wear rate (similar to 1.5 x 10(-6) mm(3)/Nm) and a modest COF (similar to 0.4) was achieved for Cu-15 wt pct Pb nanocomposites. The lower wear rate of Cu-Pb nanocomposites with respect to unreinforced Cu is attributed to high hardness (similar to 2 to 3.5 GPa) of the matrix, Cu2O/Fe2O3-rich oxide layer formation at tribological interface, and exuding of softer Pb particles. The wear properties are discussed in reference to the characteristics of transfer layer on worn surface as well as subsurface damage probed using focused ion beam microscopy. Interestingly, the flash temperature has been found to have insignificant effect on the observed oxidative wear, and alternative mechanisms are proposed. Importantly, the wear resistance properties of the nanocomposites reveal a weak Hall-Petch-like relationship with grain size of nanocrystalline Cu. (C) The Minerals, Metals & Materials Society and ASM International 2013

Synthesis and Characterization of CoFe2O4/Polyaniline Nanocomposites for Electromagnetic Interference Applications

The Cobalt ferrite (CoFe2O4) powders were synthesized by Co-precipitation method. The as prepared ferrite powders were incorporated into a polyaniline matrix at various volumetric ratios. The as prepared composites of ferrite and polyaniline powders were characterized using X-ray diffraction (XRD), transmission electron microscope (TEM). The particle size of CoFe2O4 is found to be 20 nm. The saturation magnetization (M-s) of all the composites was found to be decreasing with decrease of ferrite content, while coercivity (H-c) remained at the value corresponding to pure cobalt ferrite nanopowders. The complex permittivity (epsilon' and epsilon `') and permeability (mu' and mu `') of composite samples were measured in the range of 1 MHz to 1.1 GHz. The value of epsilon' and mu' found to be increased with ferrite volume concentration.

Exfoliated graphite/titanium dioxide nanocomposites for photodegradation of eosin yellow

An improved photocatalyst consisting of a nanocomposite of exfoliated graphite and titanium dioxide (EG-TiO2) was prepared. SEM and TEM micrographs showed that the spherical TiO2 nanoparticles were evenly distributed on the surface of the EG sheets. A four times photocatalytic enhancement was observed for this floating nanocomposite compared to TiO2 and EG alone for the degradation of eosin yellow. For all the materials, the reactions followed first order kinetics where for EG-TiO2, the rate constant was much higher than for EG and TiO2 under visible light irradiation. The enhanced photocatalytic activity of EG-TiO2 was ascribed to the capability of graphitic layers to accept and transport electrons from the excited TiO2, promoting charge separation. This indicates that carbon, a cheap and abundant material, can be a good candidate as an electron attracting reservoir for photocatalytic organic pollutant degradation. (C) 2014 Elsevier B.V. All rights reserved.

Effect of morphology on electrical treeing in low density polyethylene nanocomposites

Influence of polymer morphology on the inception and the growth of electrical trees in unfilled low density polyethylene (LDPE) as well as LDPE filled with 1, 3 and 5% by weight nanoalumina samples stressed with 50 Hz ac voltage has been studied. It is seen that there is a significant improvement in tree inception voltage with filler loading in LDPE filled with nanoparticles. Tree inception voltage increased with the filler loading up to 3% by weight nanoalumina loading and showed a reduction at 5% by weight loading. Change in tree growth patterns from branch to bush as well as a slower tree growth with increase in filler loading in LDPE alumina nanocomposites were observed. The degree of crystallinity and change in crystalline morphology induced by the presence of alumina nanoparticles in LDPE was studied using differential scanning calorimetry (DSC) and scanning electron microscopy (SEM). DSC results show a similar melting behaviour for both unfilled LDPE and LDPE nanocomposites. However, there is a reduction in the degree of crystallinity for LDPE filled with 5% by weight nanoalumina. An increase in lamellae packing with increase in filler loadings and a highly disordered spherulitic structure for LDPE filled with 5% by weight nanoalumina was observed from the SEM images. The slow propagation of tree growth as well as reduction in tree inception voltage with increase in filler loadings were attributed to the morphological changes observed in the LDPE nanocomposites.

Life Estimation of Electrothermally Stressed Epoxy Nanocomposites

Accelerated electrothermal aging tests were conducted at a constant temperature of 60 degrees C and at different stress levels of 6 kV/mm, 7 kV/mm and 8 kV/mm on unfilled epoxy and epoxy filled with 5 wt% of nano alumina. The leakage current through the samples were continuously monitored and the variation in tan delta values with aging duration was monitored to predict the impending failure and the time to failure of the samples. It is observed that the time to failure of epoxy alumina nanocomposite samples is significantly higher as compared to the unfilled epoxy. Data from the experiments has been analyzed graphically by plotting the Weibull probability and theoretically by the linear least square regression analysis. The characteristic life obtained from the least square regression analysis has been used to plot the inverse power law curve. From the inverse power law curve, the life of the epoxy insulation with and without nanofiller loading at a stress level of 3 kV/mm, i.e. within the midrange of the design stress level of rotating machine insulation, has been obtained by extrapolation. It is observed that the life of epoxy alumina nanocomposite of 5 wt% filler loading is nine times higher than that of the unfilled epoxy.

Surface Degradation of Silicone Rubber Nanocomposites Due to DC Corona Discharge

Corona discharge is recognized as one of the mechanisms that can influence the surface hydrophobicity of Silicone Rubber (SR) because of the chemical changes that occur on its surface. In this study SR samples were exposed to positive and negative DC corona for 25 and 50 hours using a needle-plane electrode system. Hydrophobicity changes were monitored using a sessile drop contact angle measurement facility. The physical changes on the surface were studied using Scanning Electron Microscopy (SEM) and surface roughness measurements. The effect of positive dc corona was found to be different from that of negative dc corona. Significant surface degradation and loss of hydrophobicity was found in the case of negative dc corona exposed samples. Significant improvement in the above mentioned properties were obtained by adding small quantities of nSIL into the SR matrix.

Functionality preservation with enhanced mechanical integrity in the nanocomposites of the metal-organic framework, ZIF-8, with BN nanosheets

Metal-organic frameworks (MOFs) and boron nitride both possess novel properties, the former associated with microporosity and the latter with good mechanical properties. We have synthesized composites of the imidazolate based MOF, ZIF-8, and few-layer BN in order to see whether we can incorporate the properties of both these materials in the composites. The composites so prepared between BN nanosheets and ZIF-8 have compositions ZIF-1BN, ZIF-2BN, ZIF-3BN and similar to ZIF-4BN. The composites have been characterized by PXRD, TGA, XPS, electron microscopy, IR, Raman and solid state NMR spectroscopy. The composites possess good surface areas, the actual value decreasing only slightly with the increase in the BN content. The CO2 uptake remains nearly the same in the composites as in the parent ZIF-8. More importantly, the addition of BN markedly improves the mechanical properties of ZIF-8, a feature that is much desired in MOFs. Observation of microporous features along with improved mechanical properties in a MOF is indeed noteworthy. Such manipulation of properties can be profitably exploited in practical applications.