966 resultados para hydrothermal
Resumo:
It was explored by density functional calculations that exchanged La or P species exert great influence on the local Al sites as well as on the adjacent exchanged species. In partially exchanged La- or P/H-ZSM-5 zeolite, some of the Al sites will fall off from the zeolite framework even more easily than in H-form ZSM-5, consistent with our XRF experiments. However, when exchanged by both La and P species, Al at either of the two exchanged sites shows better stability compared to H-from. zeolite. La and P species will interact strongly with each other, as evidenced by the charge donation process and the shortening of P-O-1 bond length. It was just the cooperation of La and P species that enabled RSCC catalysts worked normally under severe conditions. (C) 2004 Elsevier B.V. All rights reserved.
Resumo:
A high quality pure hydroxy-sodalite zeolite membrane was successfully synthesized on an alpha-Al2O3 support by a novel microwave-assisted hydrothermal synthesis (MARS) method. Influence of synthesis conditions, such as synthesis time, synthesis procedure, etc., on the formation of hydroxy-sodalite zeolite membrane by MAHS method was studied by X-ray diffraction (XRD), scanning electron microscopy (SEM) and gas permeation measurements. The synthesis of hydroxy-sodalite zeolite membrane by MAHS method only needed 45 min and synthesis was more than 8 times faster than by the conventional hydrothermal synthesis (CHS) method. A pure hydroxy-sodalite zeolite membrane was easily synthesized by MAHS method, while a zeolite membrane, which consisted of NaX zeolite, NaA zeolite and hydroxy-sodalite zeolite, was usually synthesized by CHS method. The effect of preparation procedures had a dramatic impact on the formation of hydroxy-sodalite zeolite membrane and a single-stage synthesis procedure produced a pure hydroxy-sodalite zeolite membrane. The pure hydroxy-sodalite zeolite membrane synthesized by MARS method was found to be well inter-grown and the thickness of the membrane was 6-7 mum. Gas permeation results showed that the hydrogen/n-butane permselectivity of the hydroxy-sodalite zeolite membrane was larger than 1000. (C) 2004 Elsevier Inc. All rights reserved.
Resumo:
Two organically templated trivalent metal-containing crystalline zirconium phosphate materials FeZrPO-8 and AlZrPO-8 have been prepared hydrothermally by using fluoride as a mineralizer, and 1,6-diaminohexane (DAH) as templates. The powder XRD patterns indicate that the as-synthesized products are new materials. Substitutions of Al3+ or Fe3+ into Zr4+ sites were confirmed by a combination of powder X-ray diffraction (XRD) and nuclear magnetic resonance (NMR) studies. The thermal behavior of the title compounds have been investigated using TG-DTA and X-ray thermodiffractometry, which indicated that the inorganic framework of the compounds are thermally stable up to similar to400 degreesC. (C) 2004 Elsevier B.V. All rights reserved.
Resumo:
Aluminum was incorporated into the mesoporous framework of ethane-silica by one-pot condensation of Al(OiPr)(3) with 1,2-bis(trimethoxysilyl)ethane using octadecyltrimethylammonium chloride as surfactant. Powder X-ray diffraction patterns, nitrogen sorption analysis, and TEM results reveal the formation of an ordered mesoporous material with uniform porosity. Al-27 MAS NMR confirms the incorporation of aluminum in the framework. The synthesized materials exhibit extremely high hydrothermal stability in boiling water (no obvious change of mesostructure and textural properties was observed even after refluxing in water for 100 h), which could be mainly contributed to the ethane-bridged mesoporous framework. The aluminum-containing mesoporous ethane-silicas are efficient catalysts for the alkylation of 2,4-di-tert-butylphenol by cinnamyl alcohol to yield a flavan.