Temperature Distribution in Resin Impregnated Paper Insulation for Transformer Bushings

The overall reliability of a power transformer depends to a great extent on the sound operation of the bushings thereof. Oil impregnated paper (OIP) insulated bushings have been in use for a long time now. In many situations, it becomes necessary to avoid OIP insulation in bushings. In the recent past, a new technological breakthrough has been achieved whereby the OIP is replaced by epoxy resin impregnated crepe paper (RIP) insulation. This new system has several advantages over OIP and has now become the insulation of choice. However, its long time thermal and electrical performance need to be carefully assessed. This paper reports the results of a study of temperature distribution in the body of insulation, based on the ac conductivity of RIP insulation. A method of computing the maximum thermal voltage of this system is also given.

Cascaded Cross Flow DBD-Adsorbent Technique for NOX Abatement in Diesel Engine Exhaust

In this paper, a different type of cross flow dielectric barrier discharge (DBD) reactor was designed and tested. Here the gas flow is perpendicular to the barrier discharge electrode. Discharge plasma was utilized to oxidize NO contained in the exhaust gas to NO2 and subsequent NO2 removal can be improved using an adsorbent system. A detailed study of DeNO(X) in a stationary diesel engine exhaust was carried out using pulsed electrical discharges/adsorbent processes. Activated alumina (Al2O3) and MS-13x were used as adsorbents at room temperature. The main emphasis is laid on the removal of NOX from the filtered diesel engine exhaust. In filtered exhaust environment, the cross flow reactor along with adsorbent exhibits a superior performance with regard to NOX removal when compared to that with axial flow of gas. In this paper we bring out a relative comparison of discharge plasma and plasma-adsorbent process at various gas flow rates, ranging from 2 l/min to 25 l/min. The discharge plasma-adsorbent assisted barrier discharge reactor has shown promising results in NOX removal at high flow rates.

Complex Permittivity Characteristics of Epoxy Nanocomposites at Low Frequencies

The complex permittivity characteristics of epoxy nanocomposite systems were examined and an attempt has been made to understand the underlying physics governing some of the unique macroscopic dielectric behaviors. The experimental investigations were performed using two different nanocomposite systems with low filler concentrations over the frequency range of 10(-2)-400 Hz, but for some cases, the data has been reported upto 10(6) Hz for a better understanding of the behaviors. Results demonstrate that nanocomposites do possess unique permittivity behaviors as compared to those already known for unfilled polymer and microcomposite systems. The nanocomposite real permittivity and tan delta values are found to be lower than that of unfilled epoxy. In addition, results show that interfacial polarization and charge carrier mobilities are suppressed in epoxy nanocomposite systems. The complex permittivity spectra coupled with the ac conductivity characteristics with respect to frequency was found to be sufficient to identify several of the nanocomposite characteristics like the reduction in permittivity values, reduction in the interfacial polarization mechanisms and the electrical conduction behaviors. Analysis of the results are also performed using electric modulus formalisms and it has been seen that the nanocomposite dielectric behaviors at low frequencies can also be explained clearly using this formalism.

Electrical Relaxation and Transport in 0.5Cs(2)O-0.5Li(2)O-3B(2)O(3) Glasses

The frequency and temperature dependence of the dielectric constant and the electrical conductivity of the transparent glasses in the composition 0.5Cs(2)O-0.5Li(2)O-3B(2)O(3) (CLBO) were investigated in the 100 Hz - 10 MHz frequency range. The dielectric constant for the as-quenched glass increased with increasing temperature, exhibiting anomalies in the vicinity of the glass transition and crystallization temperatures. The temperature coefficient of dielectric constant was estimated (35 +/- 2 ppm. K-1) using Havinga's formula. The dielectric loss at 313 K is 0.005 +/- 0.0005 at all the frequencies understudy. The activation energy associated with the electrical relaxation determined from the electric modulus spectra was found to be 1.73 +/- 0.05 eV, close to that of the activation energy obtained for DC conductivity (1.6 +/- 0.06 eV). The frequency dependent electrical conductivity was analyzed using Jonscher's power law. The combination of these dielectric characteristics suggests that these are good candidates for electrical energy storage device applications.

Partial Discharge Resistant Characteristics of Epoxy Nanocomposites

Epoxy nanocomposite samples with a good dispersion of alumina nanoparticles in epoxy matrix were prepared and experiments were performed to measure their partial discharge resistant characteristics. Epoxy alumina nanocomposites with 0.1, 1, 5, 10 and 15 wt% nanofillers were prepared in the laboratory and partial discharge (PD) experiments were conducted at a voltage of 10 kV for different durations using IEC (b) type electrodes. The degradation of the sample surfaces were analyzed using SEM techniques, surface profile studies, FTIR spectroscopy as well as PD studies. An attempt was made to understand the interaction dynamics between the nanoparticle and the epoxy chain by measuring the glass transition temperature of the nanocomposites. The partial discharge resistance obtained for the nanocomposites are compared with those of unfilled epoxy and epoxy microcomposites. It was observed that even with 0.1 wt% of nanofiller added to the epoxy matrix, the partial discharge resistance to degradation gets improved considerably. It was also observed that the inter particle distance has a significant effect on the discharge resistance to degradation. The improvement in the degradation resistance is attributed to the interactions between the nanoparticle and the epoxy chain. A possible mechanism for the surface degradation of nanocomposites has been proposed.

Variation of surface flashover voltage in SF6 with pressure

Surface flashover characteristics of solid spacers in a rod-plane configuration have been investigated in SF6, at pressures to 400 kPa, for switching impulse voltages to determine the effect of spacer, spacer materials and polarity of applied impulses. The effect of spacer material on the flashover voltage is not significant. For negative polarity impulses, the influence of the spacer is also insignificant. But for positive polarity impulses, at pressures < 200 kPa, the spacer efficiency becomes > 1.0. On the other hand, at pressures > 200 kPa, the presence of spacer drastically reduces the flashover voltage of the system. At about atmospheric pressure also, the spacer efficiency in air has been found to be > 1.0, with the same electrode geometry.

Long-term Accelerated Weathering of Outdoor Silicone Rubber Insulators

Multistress aging/weathering of outdoor composite polymeric insulators has been a topic of interest for power transmission research community in the last few decades. This paper deals with the long-term accelerated weathering of full-scale distribution class silicone rubber composite insulators. To evaluate the long-term synergistic effect of electric stress, temperature and UV radiation on insulators, they were subjected to accelerated weathering in a specially designed multistress-aging chamber for 30,000 h. All the insulators were subjected to the same level of electrical and thermal stresses but different UV radiation levels. Chemical, physical and electrical changes due to degradation have been assessed using various techniques. It was found that there was a monotonous reduction of the content of low molecular weight (LMW) molecules with the duration of the weathering. Further, due to oxidation and weathering there is an appreciable increase in surface roughness and atomic percentage of oxygen. There is no change in the leakage current of new and aged insulators under both wet and dry conditions at the end of the aging. The results also indicate that there is no influence of UV radiation on the silicone rubber for the durations and conditions under which the studies were made.

Rapid thermal processed thin films of niobium pentoxide (Nb2 O5) deposited by reactive magnetron sputtering

Niobium pentoxide thin films have been deposited on silicon and platinum-coated silicon substrates by reactive magnetron sputtering. The as-deposited films were amorphous and showed good electrical properties in terms of a dielectric permittivity of about 30, and leakage current density of 10(-6) A cm(-2) al a field of 120 kV cm(-1). A rapid thermal annealing process at 800 degrees C further increased the dielectric constant to 90 and increased the leakage current density to 5 x 10(-6) A cm(-2). The current-voltage characteristics observed at low and high fields suggested a combination of phenomena at different regimes of applied electric field. The capacitance-voltage characteristics performed in the metal-insulator-semiconductor configuration indicated good electronic interfaces with a nominal trap density of 4.5 x 10(12) cm(-2) eV(-1), which is consistent with the behavior observed with conventional dielectrics such as SiO2 on silicon surfaces.

Effect of Post-Metallization Hydrogen Annealing on C-V Characteristic of Zirconia Grown Using Atomic Layer Deposition

Substantial amount of fixed charge present in most of the alternative gate dielectrics gives rise to large shifts in the flat-band voltage (VFB) and charge trapping and de-trapping causes hysterectic changes on voltage cycling. Both phenomena affect stable and reliable transistor operation. In this paper we have studied for the first time the effect of post-metallization hydrogen annealing on the C-V curve of MOS capacitors employing zirconia, one of the most promising gate dielectric. Samples were annealed in hydrogen ambient for up to 30 minutes at different temperatures ranging from room temperature to 400°C. C-V measurements were done after annealing at each temperature and the hysteresis width was calculated from the C-V curves. A minimum hysteresis width of ∼35 mV was observed on annealing the sample at 200°C confirming the excellent suitability of this dielectric

AC Breakdown Characteristics of Epoxy Nanocomposites

Experiments were conducted to measure the ac breakdown strength of epoxy alumina nanocomposites with different filler loadings of 0.1, 1 and 5 wt%. The experiments were performed as per the ASTM D 149 standard on samples of thickness 0.5 mm, 1 mm and 3 mm in order to study the effect of thickness on the ac breakdown strength of epoxy nanocomposites. In the case of epoxy alumina nanocomposites it was observed that the ac breakdown strength was marginally lower for 0.1 wt% and 1 wt% filler loadings and then increased at 5 wt% filler loading as compared to the unfilled epoxy. The Weibull shape parameter (beta) increased with the addition of nanoparticles to epoxy as well as with the increasing sample thickness for all the filler loadings considered. DSC analysis was done to study the material properties at the filler resin interface in order to understand the effect of the filler loading and thereby the influence of the interface on the ac breakdown strength of epoxy nanocomposites. It was also observed that the decrease in ac electric breakdown strength with an increase in sample thickness follows an inverse power-law dependence. In addition, the ac breakdown strength of epoxy silica nanocomposites have also been studied in order to understand the influence of the filler type on the breakdown strength.

A comparative study of erbium oxide and gadolinium oxide high-k dielectric thin films grown by low-pressure metalorganic chemical vapour deposition (MOCVD) using beta-Diketonates as precursors

In this paper, a comparative study of thin films of Er2O3 and Gd2O3 grown on n-type Si(100) by low-pressure metalorganic chemical vapour deposition (MOCVD) under the identical conditions has been presented. beta-Diketonate complex of rate earth metals was used as precursor. Description on the evolution of the morphology, structure, optical, and electrical characteristics of films with respect to growth parameters and post-deposition annealing process has been presented. As-gown Gd2O3 films grow with <111> texture, whereas the texture of Er2O3 films strongly depends on the growth temperature (either <100> or <111>). Compositional analysis reveals that the Gd2O3 films grown at or above 500degreesC are carbon free whereas Er2O3 films at upto 525degreesC show the presence of heteroatoms and Er2O3 films grown above 525degreesC are carbon five. The effective dielectric constant is in the range of 7-24, while the fixed charge density is in the range - 10(11) to 10(10) CM-2 as extracted from the C-V characteristics. DC I-V study was carried out to examine the leakage behaviour of films. It reveals that the as-grown Gd2O3 film was very leakey in nature. Annealing of the films in oxidizing ambient for a period of 20 min results in a drastic improvement in the leakage behaviour. The presence of heteroatoms (such as carbon) and their effect on the properties of films are discussed.

Tracking and Erosion of Silicone Rubber Nanocomposites under DC Voltages of both Polarities

In order to improve the tracking and erosion performance of outdoor polymeric silicone rubber (SR) insulators used in HV power transmission lines, micron sized inorganic fillers are usually added to the base SR matrix. In addition, insulators used in high voltage dc transmission lines are designed to have increased creepage distance to mitigate the tracking and erosion problems. ASTM D2303 standard gives a procedure for finding the tracking and erosion resistance of outdoor polymeric insulator weathershed material samples under laboratory conditions for ac voltages. In this paper, inclined plane (IP) tracking and erosion tests similar to ASTM D2303 were conducted under both positive and negative dc voltages for silicone rubber samples filled with micron and nano sized particles to understand the phenomena occurring during such tests. Micron sized Alumina Trihydrate (ATH) and nano sized alumina fillers were added to silicone rubber matrix to improve the resistance to tracking and erosion. The leakage current during the tests and the eroded mass at the end of the tests were monitored. Scanning Electron Microscopy (SEM) and Energy dispersive Xray (EDX) studies were conducted to understand the filler dispersion and the changes in surface morphology in both nanocomposite and microcomposite samples. The results suggest that nanocomposites performed better than microcomposites even for a small filler loading (4%) for both positive and negative dc stresses. It was also seen that the tracking and erosion performance of silicone rubber is better under negative dc as compared to positive dc voltage. EDX studies showed migration of different ions onto the surface of the sample during the IP test under positive dc which has led to an inferior performance as compared to the performance under negative dc.

Portable HVAC and Pulsed Plasma Sources for Control of NOX in Diesel Engine Exhaust

In this paper studies were carried out on two compact electric discharge plasma sources for controlling nitrogen oxides (NOX) emission in diesel engine exhaust. The plasma sources consist of an old television flyback transformer to generate high frequency high voltage ac (HVAC) and an automobile ignition coil to generate the high voltage pulses (HV Pulse). The compact plasma sources are aimed at retrofitting the existing catalytic converters with electric discharge assisted cleaning technique. To enhance NOX removal efficiency cascaded plasma-adsorbent technique has been used. Studies were reported at different flow rates and load conditions of the diesel engine.

Dielectric Barrier Discharge Cascaded with Red Mud Waste to Enhance NOX Removal from Diesel Engine Exhaust

Red mud is a waste by-product generated during the processing of bauxite, the most common ore of aluminium. With the presence of ferric oxide, high surface area, resistance to poisoning and low cost, red mud made itself a good alternative to the existing commercial automobile catalyst. The cascading of dielectric barrier discharge plasma with red mud improved the NOX removal from diesel engine exhaust significantly. The DeNO(X) efficiency with discharge plasma was 74% and that with red mud was 31%. The efficiency increased to 92% when plasma was cascaded with red mud catalyst operating at a temperature of 400 degrees C. The NOX removal was dominated by NO2 removal. The studies were conducted at different temperatures and the results were discussed.

Electrical Treeing and the Associated PD Characteristics in LDPE Nanocomposites

Treeing in low density polyethylene (LDPE) filled with alumina nanocomposite as well as unfilled LDPE samples stressed with 50 Hz ac voltage has been studied. The tree inception voltage was monitored for various samples with different nano-filler loadings and it is seen that there is an increase in tree inception voltage with filler loading in LDPE. Treeing pattern and tree growth duration for unfilled and nano-filled LDPE samples have also been studied. Different tree growth patterns as well as a slower tree growth with increase in filler loading in LDPE nanocomposites were observed. The observed slow propagation of tree growth with filler loading is attributed to the changes in the polymer crystalline morphology induced by the presence of nano-particles and the greater ability of the nanoparticles to resist discharge growth. SEM studies carried out to determine the morphology of unfilled and nano-filled LDPE showed an increase in lamellae packing in LDPE nanocomposites and this increased lamellar density leads to a reduction in the tree propagation rate. Partial discharge activities were also monitored during the electrical tree growth in both the unfilled and the nano-filled LDPE samples and were found to be significantly different. PD magnitude and the number of PD pulses per cycle were found to be lower with electrical tree growth duration in LDPE nanocomposites as compared to unfilled LDPE. The same trend was seen with increased filler loading also.