Effect of Cold Rolling Ratio and Heating Rate of Batch Annealing on Textures of Micro-Carbon Steel Sheet

在四辊冷轧试验机和Gleeble-1500试验机上进行了热轧微碳钢板的冷轧和退火试验。用D/max-RC衍射仪测量了试样的,/”层织构,并用Roe软件进行了ODF分析。研究表明,所研究的热轧微碳深冲板压下率约为75%,退火升温速度为20-40℃/h时,试样为{111}织构特征；压下率较大(80%)时,退火织构为较弱的{111}组分。无论{111}织构还是非{111}织构都是在形核阶段开始形成,在晶粒长大优先长大,受到定向形核和选择生长双重机制的作用。

Analysis of asymmetrical cold rolling with varying coefficients of friction

In this research, asymmetrical cold rolling was produced by the difference in the coefficient of friction between rolls and sheets rather than the difference of roll radius or rotation speeds. The influence of friction coefficient ratio on the cross shear deformation, rolling pressure and torque was investigated using slab analysis. The results showed that the shear deformation zone length increased with the increase of the friction coefficient ratio. The rolling force decreased only under the condition that the friction coefficient ratio increased while the sum of the friction coefficients was held constant. As the reduction per pass was increased, the shear deformation zone length increased and the rolling force also increased. An increase of the front tension resulted in a decrease of the shear deformation zone length. An increase of back tension, however, led to an increase of the shear deformation zone length. The reduction of rolling torque for the work roll with higher surface roughness was greater than that for the work roll with lower surface roughness. (C) 2002 Elsevier Science B.V. All rights reserved.

The Cryo-EM Structure of a Complete 30S Translation Initiation Complex from Escherichia coli

11 p.