Tetrahedral amorphous carbon-silicon heterojunction band energy offsets

Non-hydrogenated tetrahedral amorphous carbon (ta-C) has shown superior field emission characteristics. The understanding of the emission mechanism has been hindered by the lack of any directly measured data on the band offsets between ta-C and Si. In this paper results from direct in situ X-ray photoemission spectroscopy (XPS) measurements of the band-offset between ta-C and Si are reported. The measurements were carried out using a filtered cathodic vacuum arc (FCVA) deposition system attached directly to an ultra-high vacuum (UHV) XPS chamber via a load lock chamber. Repeated XPS measurements were carried out after monolayer depositions on in situ cleaned Si substrates. The total film thickness for each set of measurements was approximately 5 nm. Analysis of the data from undoped ta-C on n and p Si show the unexpected result that the conduction band barrier between Si and ta-C remains around 1.0 eV, but that the valence band barrier changes from 0.7 to 0.0 eV. The band line up derived from these barriers suggests that the Fermi level in the ta-C lies 0.3 eV above the valence band on both p and n+Si. The heterojunction barriers when ta-C is doped with nitrogen are also presented. The implications of the heterojunction energy barrier heights for field emission from ta-C are discussed.

SOI diode temperature sensor operated at ultra high temperatures-a critical analysis

This paper investigates the performance of diode temperature sensors when operated at ultra high temperatures (above 250°C). A low leakage Silicon On Insulator (SOI) diode was designed and fabricated in a 1 μm CMOS process and suspended within a dielectric membrane for efficient thermal insulation. The diode can be used for accurate temperature monitoring in a variety of sensors such as microcalorimeters, IR detectors, or thermal flow sensors. A CMOS compatible micro-heater was integrated with the diode for local heating. It was found that the diode forward voltage exhibited a linear dependence on temperature as long as the reverse saturation current remained below the forward driving current. We have proven experimentally that the maximum temperature can be as high as 550°C. Long term continuous operation at high temperatures (400°C) showed good stability of the voltage drop. Furthermore, we carried out a detailed theoretical analysis to determine the maximum operating temperature and exlain the presence of nonlinearity factors at ultra high temperatures. © 2008 IEEE.