Analysis on turning Ti-6Al-4V with different cooling methods

The aim of this paper is to optimize the machining of Ti-6Al-4V alloy, by studying the chip formation, roughness and tool wear for different cooling conditions. The results were compared between cooling methods, minimal quantity of fluid (MQF) and flooding, and also without fluid for the tool H13A. The turning of Ti-6Al-4V has shown good results on roughness (0, 8μm) and tool life, which was 11% lower with MQF than with the flooding method. The tool wear causes variation of the shear angle, which promotes strength hardening of the chip. As a result, the machined surface could be damaged. The use of the cutting fluid helps to save the cutting edge and could reduce the strength hardening. Nevertheless, it could also facilitate the formation of built-up edge. The nucleation of alpha lamellar colonies can occur due to a combination of deformation rates and temperature, mainly when the flooding is used, but it's not conclusive. The lamellar colonies were also found with the MQF in some regions, however, this structure did not show hardness variation compared to equiaxial. For all this reasons, the machining parameters might be carefully chosen.

Obtenção de fosfatos de cálcio pelo método biomimético sobre a superfície da liga Ti-6Al-4V modificada pelo laser Nd:YAG

In this work, surface modification of the Ti-6Al-4V alloy by irradiation with a Nd:YAG laser beam was studied. The matrix spacing was varied and the other parameters were kept constant. After theirradiation, the samples were immersed into SBF solution (Simulated Body Fluid) for 7 days at 37 ° C for nucleation and formation of calcium phosphates. After this period, the samples were subjected to a heat treatment at 600 °C. X-ray diffraction results indicated the formation of a mixture of phases containing hydroxyapatite and tricalcium phosphate. Infrared analysis demonstrated the presence of bands related to hydroxyapatite. SEM micrographs showed that different matrix spacing used leads to the formation of different morphologies.The 0.01 cm spacing induced the formation of microspheres, characteristic of the hydroxyapatite phase, while for 0.02 cm spacing, only a non-homogeneous coating was obtained. Therefore, the use of laser in the production of active surfaces for deposition of bioceramics proved to be viable, and the final coating has potential for applications in the field of dental implants.

Estudo in vitro das alterações na superfície do titânio comercialmente puro e da liga de titânio Ti -6Al-4V submetida a diferentes tratamentos

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito de tratamentos térmicos na resistência à tração e na dureza Vickers do Ti c.p. e da liga Ti-6Al-4V obtidos por fundição odontológica

Pós-graduação em Reabilitação Oral - FOAR

Efeitos de diferentes concentrações de dextrose e lipopolissacarídeo no comportamento corrosivo da liga Ti-6Al-4V com superfície usinada e tratada com duplo ataque ácido

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Ensaio de citotoxicidade osteoblástica em amostras porosas das ligas Ti-6Al-4V, Ti-13Nb-13Zr, Ti-35Nb, Ti-35Nb-7Zr-5Ta e TiCP

Pós-graduação em Biopatologia Bucal - ICT

Processamento, caracterização microestrutural e propriedades elásticas de metais celulares do sistema Ti-6Al-4V para fins de regeneração óssea

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Effects of Dextrose and Lipopolysaccharide on the Corrosion Behavior of a Ti-6Al-4V Alloy with a Smooth Surface or Treated with Double-Acid-Etching

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Corrosion kinetics and topography analysis of Ti-6Al-4V alloy subjected to different mouthwash solutions

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Corrosion-fatigue life of commercially pure titanium and Ti-6Al-4V alloys in different storage environments

Statement of problem. Removable partial dentures are affected by fatigue because of the cyclic mechanism of the masticatory system ansi frequent insertion and removal. Titanium and its alloys have been used in the manufacture of denture frameworks; however, preventive agents with fluorides are thought to attack titanium alloy surfaces.Purpose. This study evaluated, compared, analyzed the corrosion-fatigue life of commercially pure titanium and Ti-6Al-4V alloy in different storage environments.Material and methods. For each metal, 33 dumbbell rods, 2.3 mm in diameter at the central segment, were cast in the Rematitan system. Corrosion-fatigue strength test was carried out through a universal testing machine with a load 30% lon er than the 0.2% offset yield strength and a combined influence of different: environments: in air at room temperature, with synthetic saliva, and with fluoride synthetic saliva. After failure, the number of cycles were recorded, and fracture surfaces were examined with on SEM.Results. ANOVA and Tukey's multiple comparison rest indicated that Ti-6Al-4V alloy achieved 21,269 cycles (SD = 8,355) against 19,157 cycles (SD = 3,624) for the commercially purr Ti. There were no significant differences between either metal in the corrosion-fatigue life for dry specimens, but when the solutions were present, the fatigue life was significantly reduced, probably because of the product-ion of corrosion pits caused by superficial reactions.

Modificação da superfície do titânio e de sua liga Ti-6Al-4V por recobrimento com TiO2 e hidroxiapatita

In this work, the influence of modifications of the cp-Ti and Ti 6Al 4V alloy, by treating the surface with NaOH and depositing titanium oxide and hydroxyapatite by sol-gel method, on their biocompatibility was studied. The coatings were characterized by scanning electron microscopy and X-ray diffraction which showed that the coatings on Ti 6Al 4V are better than on cp-Ti. Adhesion tests showed that adhesion strength of the coatings on cp-Ti substrate is less than on Ti 6Al 4V as well as cytotoxicity for L929 fibroblast cells is higher

The effect of thermal cycling on the shear bond strength of porcelain/Ti-6Al-4V interfaces

The aim of the study was to evaluate the effect of thermal cycling on the shear bond strength of the porcelain/Ti-6Al-4V interfaces prepared by two different processing routes and metallic surface conditions. Polished and SiO2 particle abraded Ti-6Al-4V alloy and Triceram bonder porcelain were used to produce the interfaces. Porcelain-to-metal specimens were processed by conventional furnace firing and hot pressing. Thermal cycling was performed in Fusayama's artificial saliva for 5000 cycles between 5 +/- 1 and 60 +/- 2 degrees C. After thermal cycling, shear bond tests were carried out by using a custom-made stainless steel apparatus. The results were analyzed using t-Student test and non-parametric Kruskal-Wallis test (p<0.01). Most of the polished-fired specimens were fractured during thermal cycling; thus, it was not possible to obtain the shear bond strength results for this group. Sandblasted-fired, polished-hot pressed, and sandblasted-hot pressed specimens presented the shear bond strength values of 76.2 +/- 15.9, 52.2 +/- 23.6, and 59.9 +/- 22.0 MPa, respectively. Statistical analysis indicated that thermal cycling affected the polished specimens processed by firing, whereas a significant difference was not observed on the other groups. (C) 2015 Elsevier Ltd. All rights reserved.

Estudo da aplicação de mínima quantidade de fluido no fresamento de acabamento da liga Ti-6Al-4V

Pós-graduação em Engenharia Mecânica - FEG

Influência dos tratamentos térmicos na microestrutura e nos micromecanismos de fratura da liga ti-6al-4v produzida por sinterização direta de metal por laser (DMLS)

Pós-graduação em Engenharia Mecânica - FEIS

L’influenza del trattamento superficiale di pallinatura sulle prestazioni a fatica della lega Ti-6Al-4V

In questa tesi sono stati studiati i dati presenti in letteratura sugli gli effetti benefici sulla vita a fatica della lega Ti6Al4V del processo di pallinatura,con particolare interesse agli effetti sul processo della dimensione dei pallini e della durata del processo. Inoltre si sono analizzati i dati di letteratura riguardanti l'incremento di vita a fatica della lega Ti6Al4V ottenuto tramite il processo di ripallinatura e la relazione tra pallinatura,ripallinatura e fretting fatigue. Infine sono stati esaminati i dati sul comportamento a fatica della lega Ti6Al4V grado ELI per uso biomedico sottoposta a carico oligociclico ed ad alto numero di cicli.