Avaliação dos aspectos de processo no torneamento de madeiras tratadas termicamente

Pós-graduação em Engenharia Mecânica - FEG

Moisture content and its influence on the roughness and noise emission during wood machining

Numerous factors influencing the surface quality of wood after machining, among them we highlight the machining parameters and the properties of the wood. In the analysis of the influence of these factors on machining and in determining the quality measurement systems are used to obtain surface characteristics, these systems are divided into methods of contact and non-contact. The method for mechanical contact performed with the aid of the surface roughness tester is the most valued in the measurement of roughness of wood, however, aiming at a greater agility in these measurements, there is a need to seek alternatives for evaluation of surface quality, and one of these options is to use the forms of indirect measurements of this quality, as for example, the use of noise emission during the machining process. With this, the aim was to analyze the influence of the moisture content of the wood, at different levels, on surface quality of the species Pinus elliottii, determined by the method of mechanical probing move and relate this roughness with the sound emission issued for each class of humidity, during machining. The planning of experiments and statistical analyses were performed with the help of Taguchi method. The specimens were conditioned in greenhouses climatizadoras automatics for obtaining three classes of humidity. Machining tests of wooden pieces were performed on a machining center specific for this type of material. The roughness values were measured by a roughness verifier and the noise emission values were measured by for a measurer sound pressure level. Statistically significant differences were observed, the significance level of 10 %, on roughness and noise emission between the three levels of moisture. It was observed that with the increase in the moisture content occurred an increase of roughness and a reduction in noise emission. Monitoring of surface quality through noise level is an interesting alternative to the method of mechanical contact.

WOOD NATURAL RESISTANCE OF SEVEN FOREST SPECIES TO WHITE ROT CAUSED BY Pycnoporus sanguineus

This research evaluated the natural resistance of Platanus x acerifolia, Luehea divaricate, Carya illinoinensis, Peltophorum dubium, Araucaria angustifolia, Eucalyptus grandis and Hovenia dulcis, to accelerated decay of the white-rot fungus Pycnoporus sanguineus. The Specific Density at 12% was determinated. The accelerated decay test was conducted with glass bottles (capacity of 500 mL) filled with 100 g of moist soil, autoclaved, and kept at 25 degrees C. The initial establishment of fungal colonies on plates was supported by samples of Pinus elliottii sapwood. In this study, three samples of dimensions 9.0 x 25.0 x 25.0 mm were used for each species evaluated and, after 16 weeks of incubation, the percentage loss of mass was calculated. The degree of natural resistance was performed according to the percentages of mass loss. The results obtained from weight loss were compared by Tukey test at 5%. The natural resistance of woods was not influenced by specific gravity The wood of Carya illinoinensis, Eucalyptus grandis, Platanus x acerifolia, Luehea divaricata and Peltophorum dubium were classified as very resistant, Houvenia dulcis as resistant and Araucaria angustifolia as moderate resistant.

Developing Ecological Criteria for Prescribed Fire in South Florida Pine Rockland Ecosystems

The pine rocklands of South Florida, characterized by a rich herbaceous flora with many narrowly endemic taxa beneath an overstory of south Florida slash pine (Pinus elliottii var. densa), are found in three areas: the Miami Rock Ridge of southeastern peninsular Florida, the Lower Florida Keys, and slightly elevated portions of the southern Big Cypress National Preserve. Fire is an important element in these ecosystems, since in its absence the pine canopy is likely to be replaced by dense hardwoods, resulting in loss of the characteristic pineland herb flora. Prescribed fire has been used in Florida Keys pine forests since the creation of the National Key Deer Refuge (NKDR), with the primary aim of reducing fuels. Because fire can also be an effective tool in shaping ecological communities, we conducted a 4-year research study which explored a range of fire management options in NKDR. The intent of the study was to provide the Fish and Wildlife Service and other land managers with information regarding when and where to burn in order to perpetuate these unique forests.

Resampling of Permanent Pine Rockland Vegetation Plots on Big Pine Key

The pine rocklands of South Florida are characterized by an herbaceous flora with many narrowly endemic taxa, a diverse shrub layer containing several palms and numerous tropical hardwoods, and an overstory of south Florida slash pine (Pinus elliottii var. densa). Fire has been considered as an important environmental factor for these ecosystems, since in the absence of fire these pine forests are replaced by dense hardwood communities, resulting in loss of the characteristic pineland herb flora. Hence, in the Florida Keys pine forests, prescribed fire has been used since the creation of the National Key Deer Refuge. However, such prescribed burns were conducted in the Refuge mainly for fuel reduction, without much consideration of ecological factors. The USGS and Florida International University conducted a research study for four years, from 1998 to 2001, the objective of which was to document the response of pine rockland vegetation to a range of fire management options and to provide Fish and Wildlife Service and other land managers with information useful in deciding when and where to burn to perpetuate these unique pine forests. This study is described in detail in Snyder et al. (2005).

Genetic Variation in an International Provenance-Progeny Test of Pinus caribaea Mor. var. bahamensis Bar. et Gol., in São Paulo, Brazil

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Propriedades mecânicas de peças com dimensões estruturais de Pinus spp: correlação entre resistência à tração e classificação visual

A redução da disponibilidade de espécies de madeiras nativas e seus efeitos na economia, associada ao fortalecimento dos conceitos de preservação ambiental, criou a necessidade de desenvolvimento de alternativas viáveis para utilização racional de espécies de reflorestamento. E uma das opções é a realização de classificação visual das peças. Autores de trabalhos desenvolvidos nessa linha de pesquisa verificaram a adequação das regras de classificação visual do Southern Pine Inspection Bureau (SPIB) dos EUA à madeira de Pinus do Brasil e apresentaram proposta para normalizar o processo de classificação visual dessa madeira. Nessa classificação, os aspectos com maior influência são: presença de nós, desvio de grã em relação ao eixo da peça e densidade de anéis de crescimento. Assim, esta pesquisa apresenta um estudo experimental que consistiu na classificação visual e determinação da resistência à tração de 85 peças de Pinus spp e um estudo teórico, que propôs uma equação para determinar a resistência à tração média de peças estruturais em função da classificação visual. Com este trabalho, foi possível observar a influência dos nós e dos anéis de crescimento sobre a resistência à tração das peças analisadas.

Relevance of extractives and wood transformation products on the biodegradation of Pinus taeda by Ceriporiopsis subvermispora

Ceriporiopsis subvermispora is a promising white-rot fungus for biopulping. However, the underlying biochemistry involved in lignin removal and insignificant cellulose degradation by this species is not completely understood. This paper addresses this topic focusing on the involvement of ethanol-soluble extractives and wood transformation products in the biodegradation process. Cultures containing ethanol-extracted or in natura wood chips presented similar levels of extracellular enzymes and degradation of wood components. Fe3+-reducing compounds present in undecayed Pinus taeda were rapidly diminished by fungal degradation. Lignin-degradation products released during biodegradation restored part of the Fe3+-reducing activity. However, Fe3+ reduction was ineffective in presence of 0.5 mM oxalate at pH 4.5. Fungal consumption of Fe3+-reducing compounds and secretion of oxalic acid minimized the significance of Fenton`s reaction in the initial stages of wood biotreatment. This would explain limited polysaccharide degradation by the fungus that also lacks a complete set of hydrolytic enzymes. Scientific relevance of the paper: Ceriporiopsis subvermispora is a white-rot fungus suitable for biopulping processes because it degrades lignin selectively and causes significant structural changes on the wood components during the earlier decay stages. However, the intricate mechanism to explain lignin transformation and insignificant cellulose degradation by this species remains poorly understood. Some recent evidences pointed out for lipid peroxidation reactions as all initiating process explaining lignin degradation. On the other hand, alkylitaconic acids produced by the fungus via transformations of fatty acids occurring in wood showed to prevent polysaccharide degradation in Fenton reactions. In this context, one may conclude that the involvement of native wood substances or their transformation products in the overall wood biodegradation process induced by C subvermispora is still a matter of discussion. While free and esterified fatty acids present in wood extractives may be involved in the biosynthesis of alkylitaconic acids and in lipid peroxidation reactions, some extractives and lignin degradation products can reduce Fe3+, providing Fe2+ species needed to form OH radical via Fenton`s reaction. The present study focuses on this topic by evaluating the relevance of ethanol-soluble extractives and wood transformation products on the biodegradation of P. taeda by C subvermispora. For this, solid-state cultures containing ethanol-extracted and in natura wood chips were evaluated in details for up to 4 weeks. (C) 2007 Elsevier Ltd. All rights reserved.

Behavior of Ceriporiopsis subvermispora during Pinus taeda biotreatment in soybean-oil-amended cultures

Pinus taeda wood chips were treated with the biopulping fungus Ceriporiopsis subvermispora in soybean-oil-amended cultures The secretion of oxalic acid and the accumulation of thiobarbituric acid reactive substances were significantly increased in soybean-oil-amended cultures By contrast the secretion of hydrolytic and oxidative enzymes was not altered in the cultures Biotreated wood samples were characterized for weight and component losses as well as by in-situ thioacidolysis Residual lignins were also extracted from biotreated wood using a mild-non-razing extraction procedure The lignins were characterized by (31)P nuclear magnetic resonance ((31)P-NMR) spectroscopy Soybean oil amendment in the cultures was found to affect lignin degradation routes however it inhibited depolymerization reactions detectable in the residual lignin that was retained in the biotreated wood As a consequence chemithermomechanical pulping of the biotreated samples was not improved by soybean oil amendment in the cultures Crown Copyright (C) 2010 Published by Elsevier Ltd All rights reserved

Characterization of tree-rings of Pinus caribaea var. hondurensis Barr. et Golf. trees by X ray densitometry

This work aimed to determining the anatomical structure of wood, through methodology of histology and X-ray densitometry, of resin-tapped and not resin-tapped Pinus caribaea var. hondurensis trees samples, of three diameter classes. Pine trees, in forest plantation established in 1969, in the Ecological Experimental Station of Itirapina, from the Forestry Institute of Sao Paulo State, were measured and stratified into three classes of trunk diameter. The pine trees were resin-tapped since 2004, with the opening of two simultaneous and opposing panels. Sixty samples of pine wood trees were extracted from the tree trunk through a non-destructive method and in the laboratory. Tree rings were determined in the laboratory and wood apparent density by X-ray densitometry. The test results showed that: (i) false tree rings occur in the early wood and late wood of the tree rings due to climate change; (ii) the X-ray densitometry allowed the demarcation of the tree rings limits; (iii) the wood apparent density average was significantly different between the trees in high class diameter and in the medium-low class; (iv) the wood characteristics from the resin-tapped and non resin-tapped faces did not show significant differences.

Material properties and nondestructive evaluation of laminated veneer lumber (LVL) made from Pinus oocarpa and P. kesiya

This study aimed at evaluating the mechanical, physical and biological properties of laminated veneer lumber (LVL) made from Pinus oocarpa Schiede ex Schltdl (PO) and Pinus kesiya Royle ex Gordon (PK) and at providing a nondestructive characterization thereof. Four PO and four PK LVL boards from 22 randomly selected 2-mm thickness veneers were produced according to the following characteristics: phenol-formaldehyde (190 g/m(2)), hot-pressing at 150A degrees C for 45 min and 2.8 N/mm(2) of specific pressure. After board production, nondestructive evaluation was conducted, and stress wave velocity (v (0)) and dynamic modulus of elasticity (E (Md) ) were determined. The following mechanical and physical properties were then evaluated: static bending modulus of elasticity (E (M) ), modulus of rupture (f (M) ), compression strength parallel to grain (f (c,0)), shear strength parallel to glue-line (f (v,0)), shear strength perpendicular to glue-line (f (v,90)), thickness swelling (TS), water absorption (WA), and permanent thickness swelling (PTS) for 2, 24, and 96-hour of water immersion. Biological property was also evaluated by measuring the weight loss by Trametes versicolor (Linnaeus ex Fries) Pilat (white-rot) and Gloeophyllum trabeum (Persoon ex Fries.) Murrill (brown-rot). After hot-pressing, no bubbles, delamination nor warping were observed for both species. In general, PK boards presented higher mechanical properties: E (M) , E (Md) , f (M) , f (c,0) whereas PO boards were dimensionally more stable, with lower values of WA, TS and PTS in the 2, 24, and 96-hour immersion periods. Board density, f (v,0), f (v,90) and rot weight loss were statistically equal for PO and PK LVL. The prediction of flexural properties of consolidated LVL by the nondestructive method used was not very efficient, and the fitted models presented lower predictability.

Chemical composition changes in eucalyptus and pinus woods submitted to heat treatment

This study investigated the influence of heat treatment on the chemical composition of Eucalyptus saligna and Pinus caribaea var. hondurensis woods to understand its role in wood processing. E. saligna and P. caribaea var. hondurensis woods were treated in a laboratorial electric furnace at 120, 140, 160 and 180 degrees C to induce their heat treatment. The chemical composition of the resulting products and those from original wood were determined by gas chromatography. Eucalyptus and Pinus showed a significant reduction in arabinose, manose, galactose and xylose contents when submitted to increasing temperatures. No significant alteration in glucose content was observed. Lignin content, however, increased during the heat process. There was a significant reduction in extractive content for Eucalyptus. On the other hand, a slight increase in extractive content has been determined for the Pinus wood. and that only for the highest temperature. These different behaviors can be explained by differences in chemical constituents between softwoods and hardwoods. The results obtained in this study provide important information for future research and utilization of thermally modified wood. (c) 2008 Elsevier Ltd. All rights reserved.