Study of post-deposition contamination in low-temperature deposited polysilicon films

The presence of hydrogen in polysilicon films obtained at low temperatures by hot-wire CVD and the post-deposition oxidation by air-exposure of the films are studied in this paper. The experimental results from several characterization techniques (infrared spectroscopy, X-ray photoelectron spectroscopy, secondary ion mass spectrometry and wavelength dispersive spectroscopy) showed that hydrogen and oxygen are homogeneously distributed at grain boundaries throughout the depth of the films. Hydrogen is introduced during the growth process and its concentration is higher in samples deposited at lower temperatures. Oxygen diffuses along the grain boundaries and binds to silicon atoms, mainly in Si 2O groups.

Amorphous silicon thin film solar cells deposited entirely by Hot-Wire Chemical Vapour Deposition at low temperature (<150 ºC)

Amorphous silicon n-i-p solar cells have been fabricated entirely by Hot-Wire Chemical Vapour Deposition (HW-CVD) at low process temperature < 150 °C. A textured-Ag/ZnO back reflector deposited on Corning 1737F by rf magnetron sputtering was used as the substrate. Doped layers with very good conductivity and a very less defective intrinsic a-Si:H layer were used for the cell fabrication. A double n-layer (μc-Si:H/a-Si:H) and μc-Si:H p-layer were used for the cell. In this paper, we report the characterization of these layers and the integration of these layers in a solar cell fabricated at low temperature. An initial efficiency of 4.62% has been achieved for the n-i-p cell deposited at temperatures below 150 °C over glass/Ag/ZnO textured back reflector.

Electronic transport in low temperature nanocrystalline silicon thin-film transistors obtained by Hot-Wire CVD

Hydrogenated nanocrystalline silicon (nc-Si:H) obtained by hot-wire chemical vapour deposition (HWCVD) at low substrate temperature (150 °C) has been incorporated as the active layer in bottom-gate thin-film transistors (TFTs). These devices were electrically characterised by measuring in vacuum the output and transfer characteristics for different temperatures. The field-effect mobility showed a thermally activated behaviour which could be attributed to carrier trapping at the band tails, as in hydrogenated amorphous silicon (a-Si:H), and potential barriers for the electronic transport. Trapped charge at the interfaces of the columns, which are typical in nc-Si:H, would account for these barriers. By using the Levinson technique, the quality of the material at the column boundaries could be studied. Finally, these results were interpreted according to the particular microstructure of nc-Si:H.

Top-gate microcrystalline silicon TFTs processed at low temperature (<200ºC)

N-type as well P-type top-gate microcrystalline silicon thin film transistors (TFTs) are fabricated on glass substrates at a maximum temperature of 200 °C. The active layer is an undoped μc-Si film, 200 nm thick, deposited by Hot-Wire Chemical Vapor. The drain and source regions are highly phosphorus (N-type TFTs) or boron (P-type TFTs)-doped μc-films deposited by HW-CVD. The gate insulator is a silicon dioxide film deposited by RF sputtering. Al-SiO 2-N type c-Si structures using this insulator present low flat-band voltage,-0.2 V, and low density of states at the interface D it=6.4×10 10 eV -1 cm -2. High field effect mobility, 25 cm 2/V s for electrons and 1.1 cm 2/V s for holes, is obtained. These values are very high, particularly the hole mobility that was never reached previously.

In vitro culture at low temperature and ex vitro acclimatization of Vriesea inflata an ornamental bromeliad

(In vitro culture at low temperature and ex vitro acclimatization of Vriesea inflata an ornamental bromeliad). In vitro culture by seeds is a technique for preservation of threatened species because it may provide a large number of plants with genetic diversity. The bromeliad Vriesea inflata (Wawra) Wawra, an ornamental bromeliad, is extensively and illegally collected from the nature and must be preserved. It is possible to form plant threatened collections in vitro by reducing the temperature of culture, while occupying little space, with the consequent reduction of maintenance costs. This work evaluated the influence of temperature on in vitro growth and morphology of plants of V. inflata, with the aim of establishing a slow growth-rate and analyzing the ex vitro acclimatization. Seeds were germinated in vitro in Murashige and Skoog (MS) medium, with macronutrients reduced to 50% (MS/2). After three months the plants were transferred to flasks of new same medium and kept in two germination chambers with the temperature adjusted to 15 °C and to 28 °C. After 24 months the plants were subject to biometric, photosynthetic pigments content and anatomical analyses. Results showed that plants maintained at 15 °C were smaller than those at 28 °C. Nevertheless, there were no alterations in pigments content, anatomy. In both treatments there was a survival rate of 100%. This work showed that plants of this species can be kept in vitro at 15 °C with the aim of forming a slow-growth collection, thereby seeking its preservation, and can be transferred to growth at ex vitro condition to achieved 100% survival rate.

Effect of thinning on flower and fruit and of edible coatings on postharvest quality of jaboticaba fruit stored at low temperature

Jaboticaba is a Brazilian fruit, native to the Atlantic forest, which belongs to the Myrtaceae family. In this work we describe the effect of the thinning of "flower", "fruit" and "flower & fruit" compared to non-thinned fruit (control) and of edible coatings with respect on nutritional composition, overall acceptability and shelf-life of jaboticaba ‘Sabara’, grown in an irrigated commercial orchard. "Flower and fruit" thinning allows fruit with higher quality as diameter, volume and mass. Non-thinned fruit shows higher yield, however fruit have lower quality. As a result of the improving quality at harvest, the shelf life was twice (~8 days) for thinned fruit. The lack of change in concentration of soluble sugar and absence of formation of volatile compounds during storage indicate that there was no natural fermentation of the jaboticaba pulp after harvest. Treatments with wax and calcium did not improve the jaboticaba shelf life.

Kr-Ar laser Raman spectrometer for low temperature measurements /

A Czerny Mount double monochromator is used to measure Raman scattered radiation near 90" from a crystalline, Silicon sample. Incident light is provided by a mixed gas Kr-Ar laser, operating at 5145 A. The double monochromator is calibrated to true wavelength by comparison of Kr and Ar emission Une positions (A) to grating position (A) display [1]. The relationship was found to be hnear and can be described by, y = 1.219873a; - 1209.32, (1) where y is true wavelength (A) and xis grating position display (A). The Raman emission spectra are collected via C"*""*" encoded software, which displays a mV signal from a Photodetector and allows stepping control of the gratings via an A/D interface. [2] The software collection parameters, detector temperature and optics are optimised to yield the best quality spectra. The inclusion of a cryostat allows for temperatmre dependent capabihty ranging from 4 K to w 350 K. Silicon Stokes temperatm-e dependent Raman spectra, generally show agreement with Uterature results [3] in their frequency haxdening, FWHM reduction and intensity increase as temperature is reduced. Tests reveal that a re-alignment of the double monochromator is necessary before spectral resolution can approach literature standard. This has not yet been carried out due to time constraints.

Pigment orientation changes detected by low temperature linear dichroism spectroscopy: cold-hardening transition in phycobilisome-containing organisms

Low temperature (77K) linear dichroism spectroscopy was used to characterize pigment orientation changes accompanying the light state transition in the cyanobacterium, Synechococcus sp. pee 6301, and cold-hardening in winter rye (Secale cereale L. cv. Puma). Samples were oriented for spectroscopy using the gel squeezing method (Abdourakhmanov et aI., 1979) and brought to 77K in liquid nitrogen. The linear dichroism (LD) spectra of Synechococcus 6301 phycobilisome/thylakoid membrane fragments cross-linked in light state 1 and light state 2 with glutaraldehyde showed differences in both chlorophyll a and phycobilin orientation. A decrease in the relative amplitude of the 681nm chlorophyll a positive LD peak was observed in membrane fragments in state 2. Reorientation of the phycobilisome (PBS) during the transition to state 2 resulted in an increase in core allophycocyanin absorption parallel to the membrane, and a decrease in rod phycocyanin parallel absorption. This result supports the "spillover" and "PBS detachment" models of the light state transition in PBS-containing organisms, but not the "mobile PBS" model. A model was proposed for PBS reorientation upon transition to state 2, consisting of a tilt in the antenna complex with respect to the membrane plane. Linear dichroism spectra of PBS/thylakoid fragments from the red alga, Porphyridium cruentum, grown in green light (containing relatively more PSI) and red light (containing relatively more PSll) were compared to identify chlorophyll a absorption bands associated with each photosystem. Spectra from red light - grown samples had a larger positive LD signal on the short wavelength side of the 686nm chlorophyll a peak than those from green light - grown fragments. These results support the identification of the difference in linear dichroism seen at 681nm in Synechococcus spectra as a reorientation of PSll chromophores. Linear dichroism spectra were taken of thylakoid membranes isolated from winter rye grown at 20°C (non-hardened) and 5°C (cold-hardened). Differences were seen in the orientation of chlorophyll b relative to chlorophyll a. An increase in parallel absorption was identified at the long-wavelength chlorophyll a absorption peak, along with a decrease in parallel absorption from chlorophyll b chromophores. The same changes in relative pigment orientation were seen in the LD of isolated hardened and non-hardened light-harvesting antenna complexes (LHCII). It was concluded that orientational differences in LHCII pigments were responsible for thylakoid LD differences. Changes in pigment orientation, along with differences observed in long-wavelength absorption and in the overall magnitude of LD in hardened and non-hardened complexes, could be explained by the higher LHCII monomer:oligomer ratio in hardened rye (Huner et ai., 1987) if differences in this ratio affect differential light scattering properties, or fluctuation of chromophore orientation in the isolated LHCII sample.

A Novel Accelerator Combination for the Low Temperature Curing of Silica-Filled NBR Compounds

Zinc salts of ethyl, isopropyl, and butyl xanthates were prepared in the laboratory. The effect of these xanthates in combination with zinc diethyldithiocarbamate (ZDC) on the vulcanization of silica-filled NBR compounds has been studied at different temperatures. The cure times of these compounds were compared with that of NBR compounds containing tetramethylthiuram disulphide/dibenzthiazyl disulphide. The rubber compounds with the xanthates and ZDC were cured at various temperatures from 60 to 150°C. The sheets were molded and properties such as tensile strength, tear strength, crosslink density, elongation at break, compression set, abrasion resistance, flex resistance, heat buildup, etc. were evaluated. The properties showed that zinc salt of xanthate/ZDC combination has a positive synergistic effect on the cure rate and mechanical properties of NBR compounds.

Low Temperature Curing of NBR for Property Improvement

Zinc salts of ethyl, isopropyl, and butyl xanthates are prepared in the laboratory, and the effect of these xanthates with zinc diethyl dithiocarbamate (ZDC) on the vulcanization of HAF-filled nitrile butadiene rubber (NBR) compounds has been studied at different temperatures. The cure times of these compounds have been compared with that of NBR compounds containing TMTD/MBTS. The rubber compounds with the three xanthate accelerators and ZDC are cured at various temperatures from 60 to 150°C. The sheets are molded and properties such as tensile strength, tear strength, cross-link density, elongation at break, compression set, abrasion resistance, flex resistance, etc. have been evaluated. The properties show that zinc salt of the xanthate/ZDC accelerator system has a positive synergistic effect on the cure rate and mechanical properties of NBR compounds.

Development of Polybutadiene (BR)-Polyethylene (LDPE) Blend Based Microcellular Soles for Low-Temperature Applications

Microcellular (MC) soles based on polybutadiene (BR) and low-density polyethylene (LDPE) blends for low-temperature applications were developed. A part of BR in BR-LDPE blend was replaced by natural rubber (NR) for property improvement. The BR-NR-LDPE blend-based MC sole shows good technical properties. Sulphur curing and DCP curing were tried in BR-LDPE and NR-BR-LDPE blends. Study shows that sulphur-cured MC sheets possess better technical properties than DCPcured MC sheets. 90/10 BR-LDPE and 60/30/10 BR-NR-LDPE blend combinations are found to be suitable for low-temperature applications.

Xanthate Accelerators for Low Temperature Curing of Natural Rubber

ABSTRACT: Zinc salts of ethyl, isopropyl, and butyl xanthates were prepared in the laboratory. They were purified by reprecipitation and were characterized by IR, NMR, and thermogravimetric analysis techniques. The melting points were also determined. The rubber compounds with different xanthate accelerators were cured at temperatures from 30 to 150°C. The sheets were molded and properties such as tensile strength, tear strength, crosslink density, elongation at break, and modulus at 300% elongation were evaluated. The properties showed that all three xanthate accelerators are effective for room temperature curing.

Characterization of Hydrothermally Annealed Low Temperature Bioactive Thin Film Coatings of Hydroxyapatite on TiAl6V4 Implant material

This thesis summarizes the results on the growth and characterisation of thin films of HA grown on TiAl6V4 (Ti) implant material at a lower substrate temperature by a combination of Pulsed laser deposition and a hydrothermal treatment to get sufficiently strong crystalline films suitable for orthopaedic applications. The comparison of the properties of the coated substrate has been made with other surface modification techniques like anodization and chemical etching. The in-vitro study has been conducted on the surface modified implants to assess its cell viability. A molecular level study has been conducted to analyze the adhesion mechanism of protein adhesion molecules on to HA coated implants.