Preparação e caracterização de filmes óxidos contendo componentes opticamente ativos

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Direct Synthesis of Ag Nanoparticles Incorporated on a Mesoporous Hybrid Material as a Sensitive Sensor for the Simultaneous Determination of Dihydroxybenzenes Isomers

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis and characterization of alpha-nickel (II) hydroxide particles on organic-inorganic matrix and its application in a sensitive electrochemical sensor for vitamin D determination

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Simultaneous determination of epinephrine and dopamine by electrochemical reduction on the hybrid material SiO2/graphene oxide decorated with Ag nanoparticles

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Electrical properties of highly conducting Sno2:Sb nanocrystals synthesized using a nonaqueous sol gel method

This work describes the synthesis of highly conducting antimony-doped tin oxide (ATO) nanocrystals prepared via a nonaqueous sol–gel route in the size range of 4–6 nm and provides insights into its electrical properties. The antimony composition was varied from 1 to 18 mol% and the lowest resistivity (4.0 × 10−4Ω·cm) was observed at room temperature in the SnO2:8.8 mol% Sb composition. The samples were evaluated by X-ray diffraction, high-resolution transmission electron microscopy, energy-dispersive X-ray spectroscopy, and scanning electron microscope, and resistivity measurements were taken in the four-probe mode in the temperature range of 13–300 K. The results show highly crystalline nanoparticles in a monodisperse colloidal system, dependence on the shape of ATO nanoparticles as a function of Sb distribution, low resistivity, and semiconductor–metal transition.

Structural and optical properties of Er3+ doped SiO2-Al2O3-GeO2 compounds prepared by a simple route

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Fingerprints of short-range and long-range structure in BaZr1-xHfxO3 solid solutions: an experimental and theoretical study

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Synthesis, structure and magnetic properties of Y3Fe5-xAlxO12 garnets prepared by the soft chemical method

Conselho Nacional de Desenvolvimento Científico e Tecnológico (CNPq)

Estudo da relação de ordem-desordem estrutural em nanopartículas de TiO2

Pós-graduação em Química - IQ

Membranas de biocelulose como substrato para o crescimento de nanofios de ZnO: síntese e aplicação

Pós-graduação em Química - IQ

Membranas de biocelulose como substrato para o crescimento de nanofios de ZnO: síntese e aplicação

Pós-graduação em Química - IQ

Relationship between Crystal Shape, Photoluminescence, and Local Structure in SrTiO3 Synthesized by Microwave-Assisted Hydrothermal Method

This paper describes the effect of using different titanium precursors on the synthesis and physical properties of SrTiO3 powders obtained by microwave-assisted hydrothermal method. X-ray diffraction measurements, X-ray absorption near-edge structure (XANES) spectroscopy, field emission scanning electron microscopy (FE-SEM), and high-resolution transmission electron microscopy (HRTEM) were carried out to investigate the structural and optical properties of the SrTiO3 spherical and cubelike-shaped particles. The appropriate choice of the titanium precursor allowed the control of morphological and photoluminescence (PL) properties of SrTiO3 compound. The PL emission was more intense in SrTiO3 samples composed of spherelike particles. This behavior was attributed to the existence of a lower amount of defects due to the uniformity of the spherical particles.

Nanosized precipitates in H13 tool steel low temperature plasma nitriding

A comprehensive study of pulsed nitriding in AISI H13 tool steel at low temperature (400 degrees C) is reported for several durations. X-ray diffraction results reveal that a nitrogen enriched compound (epsilon-Fe2-3N, iron nitride) builds up on the surface within the first process hour despite the low process temperature. Beneath the surface, X-ray Wavelength Dispersive Spectroscopy (WDS) in a Scanning Electron Microscope (SEM) indicates relatively higher nitrogen concentrations (up to 12 at.%) within the diffusion layer while microscopic nitrides are not formed and existing carbides are not dissolved. Moreover, in the diffusion layer, nitrogen is found to be dispersed in the matrix and forming nanosized precipitates. The small coherent precipitates are observed by High-Resolution Transmission Electron Microscopy (HR-TEM) while the presence of nitrogen is confirmed by electron energy loss spectroscopy (EELS). Hardness tests show that the material hardness increases linearly with the nitrogen concentration, reaching up to 14.5 GPa in the surface while the Young Modulus remains essentially unaffected. Indeed, the original steel microstructure is well preserved even in the nitrogen diffusion layer. Nitrogen profiles show a case depth of about similar to 43 mu m after nine hours of nitriding process. These results indicate that pulsed plasma nitriding is highly efficient even at such low temperatures and that at this process temperature it is possible to form thick and hard nitrided layers with satisfactory mechanical properties. This process can be particularly interesting to enhance the surface hardness of tool steels without exposing the workpiece to high temperatures and altering its bulk microstructure. (c) 2012 Elsevier B.V. All rights reserved.

Development of Ternary and Quaternary Catalysts for the Electrooxidation of Glycerol

This work consisted in the preparation of platinum-based catalysts supported on carbon (Vulcan XC-72) and investigation of their physicochemical and electrochemical properties. Catalysts of the C/Pt-Ni-Sn-Me (Me = Ru or Ir) type were prepared by the Pechini method at temperature of 350 degrees C. Four different compositions were homemade: C/Pt60Sn10Ni30, C/Pt60Sn10Ni20Ru10, C/Pt60Sn10Ni10Ru20, and C/Pt60Sn10Ni10Ir20. These catalysts were electrochemically and physically characterized by cyclic voltammetry (CV), chronoamperometry (CA) in the presence of glycerol 1.0 mol dm(-3), X-ray diffraction (XRD), and high-resolution transmission electron microscopy (HRTEM). XRD results showed the main peaks of face-centered cubic Pt. The particle sizes obtained from XRD and HRTEM experiments were close to values ranging from 3 to 8.5 nm. The CV results indicate behavior typical of Pt-based catalysts in acid medium. The CV and CA data reveal that quaternary catalysts present the highest current density for the electrooxidation of glycerol.

Effect of partial preferential orientation and distortions in octahedral clusters on the photoluminescence properties of FeWO4 nanocrystals

This communication is a report of our initial research to obtain iron tungstate (FeWO4) nanocrystals by the microwave-hydrothermal method at 170 degrees C for 45 min. X-ray diffraction patterns showed that the FeWO4 nanocrystals prepared with polyethylene glycol-200 have a partial preferential orientation in the (011) plane in relation to other nanocrystals prepared with sodium bis(2-ethylhexyl) sulfosuccinate and water. Rietveld refinement data indicates that all nanocrystals are monophasic with wolframite-type monoclinic structures and exhibit different distortions on octahedral [FeO6]/[WO6] clusters. High resolution transmission electron microcopy revealed an oriented attachment mechanism for the growth of aggregated FeWO4 nanocrystals. Finally, we observed that the photoluminescence properties of these nanocrystals are affected by partial preferential orientation in the (011) plane and distortions on [FeO6]/[WO6] clusters.