Long-term quantification of the release of monomers from dental resin composites and a resin-modified glass ionomer cement

This study quantified the release of monomers from polymerized specimens of four commercially available resin composites and one glass ionomer cement immersed in water:ethanol solutions. Individual standard curves were prepared from five monomers: (1) triethylene glycol dimethacrylate (TEGDMA), (2) 2-hydroxy-ethyl methacrylate (HEMA), (3) urethane dimethacrylate (UDMA), (4) bisphenol A glycidyl dimethacrylate (BISGMA), and (5) bisphenol A. The concentration of the monomers was determined at Days 1, 7, 30, and 90 with the use of electrospray ionization/mass spectrometry. Data were expressed in mean mumol per mm(2) surface area of specimen and analyzed with Scheffe's test (P < 0.05). The following monomers were found in water: monomers (1) and (2) from Delton sealant, monomer (5) from ScotchBond Multipurpose Adhesive and Delton sealant, monomer (3) from Definite and monomer (4) from Fuji II LC, ScotchBond Multipurpose Adhesive, Synergy and Definite. All these monomers increased in concentration over time, with the exception of monomer (1) from Delton sealant. Monomers (3) and (5) were found in extracts of materials despite their absence from the manufacturer's published composition. All monomers were released in significantly higher concentrations in water:ethanol solutions than in water. The greatest release of monomers occurred in the first day. The effect of the measured concentrations of monomers (1-5) on human genes, cells, or tissues needs to be considered with the use of a biological model. (C) 2002 Wiley Periodicals, Inc.

Fracture resistance of Class II glass-ionomer cement restorations

Purpose: To investigate in vitro the effect of retentive grooves, GIC type and insertion method on the fracture resistance of Class II glass-ionomer cement (GIC) restorations. Methods: Premolars were divided into 12 groups (n=10) according to three variables: retentive grooves [presence (PR) or absence AR)], GICs type [Ketac-Molar (KM), Fuji VIII (F8) and RelyX Luting (RX)], and insertion method [syringe injector (SI) or spoon excavator (SE)]. The specimens were subjected to fracture resistance test. Data were submitted to three-way ANOVA and multiple comparisons were performed using a Tukey test (P < 0.05). Results: Mean fracture resistance values (Kgf) +/- standard deviations (SD) were: KM (PR+SI) 65.66 +/- 2.5; KM (PR+SE) = 62.58 +/- 2.1; KM (AR+SI) = 57.11 +/- 1.9; KM (AR+SE) = 51.94 +/- 2.3; F8 (PR+SI) = 63.05 +/- 2.1; F8 (PR+SE) = 60.12 +/- 2.3; F8 (AR+SI) = 55.11 +/- 1.9; F8(AR+SE)=49.20 +/- 1.6; RX (PR+SI)=50.99 +/- 2.4; RX (PR+SE)=48.81 +/- 2.5; RX (AR+SI)=45.53 +/- 2.6; RX (AR+SE)=41.88 +/- 3.0. Statistically significant differences were observed among all the groups tested (P=0.001). There was significant difference when pooled means for GIC type were compared with retentive grooves (P=0.01) and when pooled means for retentive grooves were compared with insertion method (P=0.01).

Six-year evaluation of the atraumatic restorative treatment approach in permanent-tooth Class III restorations

Purpose: The aim of this study was to assess the 6-year performance of the ART (atraumatic restorative treatment) approach in Class III restorations in permanent teeth. Materials and Methods: A total of 127 ART Class III restorations, using Ketac-Molar (3M ESPE) ionomer cement, was performed in 58 adult patients by one experienced operator in 1998. After a 6 years, 34 patients and 65 restorations were evaluated according to ART criteria. Two calibrated examiners carried out the evaluation. Data were analyzed by exact 95% Confidence Interval and Survival Analysis using the Jackknife method for standard error determination. Results: Among assessed restorations, 73.8% (95% CI = 61.5% to 86.2%) were in good condition and classified as successful, with a 67.6% (95% CI = 54.4% to 80.7%) cumulative survival rate. Failed restorations included 13.9% completely or partially missing restorations, 9.2% restorations that had been replaced by other treatment, 1.5% restorations with a large defect at the margin, and 1.5% restorations that presented high wear on the surface. No caries was observed even in those teeth in which restorations were absent. Conclusion: The 6-year success rate of the ART approach in anterior permanent teeth (Class III) was considered high.

Cytotoxicity of resin-based light-cured liners

Purpose: To evaluate the cytotoxic effects of resin-based light-cured liners on culture of pulp cells. Methods: Discs measuring 4 mill in diameter and 2 mm thick were fabricated from TheraCal (TCMTA), Vitrebond (VIT), and Ultrablend Plus (UBP). These specimens were immersed in serum-free culture medium (DMEM) for 24 hours or 7 days to produce the extracts. After incubating the pulp cells for 72 hours, the extracts were applied on the cells and the cytotoxic effects were determined based on the cell metabolism (MTT), total protein expression and cell morphology (SEM). In the control group, fresh DMEM was used. Data from MTT analysis and protein expression were submitted to Kruskal-Wallis and Mann-Whitney tests at the preset level of significance of 5%. Results: When in contact with the 24-hour extract, TCMTA, VIT, and UBP decreased the cell metabolism by 31.5%, 73.5% and 71.0%, respectively. The total protein expressed by the cells in contact with VIT and UBP was lower than TCMTA and DMEM (Mann-Whitney, P< 0.05). When in contact with the 7-day extract, TCMTA, VIT, and UBP decreased the metabolic activity by 45.9%, 77.1% and 64.4%, respectively. All the liners expressed statistically lower amounts of proteins when compared to the control. A reduction in the number of cells was observed for all liners. The remaining cells from TCMTA group resembled those from the control group while for VIT and UBP the cells presented significant morphological alterations. (Ani J Dent 2009;22:137-142).

Effect of pH variations in a cycling model on the properties of restorative materials

This study evaluated the effect of cycling various pH demineralizing solutions on the surface hardness, fluoride release and surface properties of restorative materials (Ketac-Fil Plus, Vitremer, Fuji II LC, Freedom and Fluorofil). Thirty specimens of each material were made and the surface hardness measured. The specimens were randomized into five groups according to the pH (4.3; 4.6; 5.0; 5.5 and 6.2) of the demineralizing solution. The specimens were submitted to pH-cycling for 15 days. The specimens remained in the demineralizing solution for six hours and in the remineralizing solution for 18 hours. Then, the surface hardness (SH) was remeasured and the surface properties were assessed. Fluoride release was determined daily. Data from SH and the percentage of alteration in surface hardness were analyzed by analysis of variance (p < 0.05); the Kruskal-Wallis test was performed for the fluoride release results. When hardness was compared, the variation in pH led to a positive correlation for glass ionomer cements and a negative correlation for fluoride release. For polyacid-modified resin composites, a negative correlation was found with regards to fluoride release; no significant correlation was observed for hardness. Surface properties were influenced: an acidic pH led to a greater alteration, except for polyacid-modified resin composites. The pH of the demineralizing solution influenced fluoride release from the tested materials. The pH variation altered hardness and surface properties of glass ionomer cements but did not influence polyacid-modified resin composites.

Short-term evaluation of the pulpo-dentin complex response to a resin-modified glass-ionomer cement and a bonding agent applied in deep cavities

Objectives. To evaluate the response of the pulpo-dentin complex following application of a resin-modified glass-ionomer cement or an adhesive system in deep cavities performed in human teeth.Methods. Deep class V cavities were prepared on the buccal surface of 26 premolars. In Group I the cavity walls (dentin) and enamel were conditioned with 32% phosphoric acid and the dentin adhesive system One Step (Bisco, Inc., Itasca, IL, USA) was applied. In Groups 2 and 3, before total etching and application of bonding agent, the cavity floor was lined with the resin-modified glass-ionomer cement-Vitrebond (3M ESPE Dental Products Division, St. Paul, MN, USA) or the calcium hydroxide cement-Dycal (control group, Dentsply, Mildford, DE, USA), respectively. The cavities were restored using light-cured Z-100 composite resin (3M ESPE). The teeth were extracted between 5 and 30 days and prepared for microscopic assessment. Serial sections were stained with H/E, Masson's trichrome, and Brown and Brenn techniques.Results. In Group 1, the inflammatory response was more evident than in Groups 2 and 3. Diffusion of dental material components across dentinal tubules was observed only in Group 1, in which the intensity of the pulp response increased as the remaining dentin thickness decreased. Bacteria were evidenced in the lateral walls of two samples (Group 2) which exhibited no inflammatory response or tissue disorganization.Conclusions. Based on the experimental conditions, it was concluded total acid etching followed by application of One Step bonding agent cannot be recommended as adequate procedures. In this clinical condition the cavity walls should be lined with a biocompatible dental material, such as Vitrebond or Dycal. 2003 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

Mechanical and biological characterization of resin-modified glass-ionomer cement containing doxycycline hyclate

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Evaluation of the radiopacity of calcium hydroxide- and glass-ionomer-based root canal sealers

Aim To evaluate the radiopacity of calcium hydroxide-based root canal sealers (Acroseal, Sealapex and Sealer 26), a glass-ionomer-based sealer (Activ GP Sealer) and a zinc oxide and eugenol-based sealer (Intrafill).Methodology Five disc-shaped specimens (10 x 1 mm) were fabricated from each material, according to the International Organization for Standardization (ISO) 6876/2001 standard. After setting of the materials, radiographs were taken using occlusal films and a graduated aluminum step-wedge varying from 2 to 16 mm in thickness. The dental X-ray unit (GE1000) was set at 50 Kvp, 10 mA, 18 pulses s(-1) and distance of 33.5 cm. The radiographs were digitized and the radiopacity compared with that of the aluminum step-wedge, using WIXWIN-2000 software (Gendex). Data (mm Al) were submitted to ANOVA and Tukey test.Results Intrafill was the most radiopaque material (7.67 mm Al) followed by Sealer 26 (6.33 mm Al), Sealapex (6.05 mm Al) and Acroseal (4.03 mm Al). Activ GP was the least radiopaque material (1.95 mm Al, P < 0.05).Conclusions The sealers evaluated in this study had different radiopacities. However, except for the glass-ionomer-based sealer, all materials had radiopacity values above the minimum recommended by the ISO standard.

Biocompatibility of a resin-modified glass-ionomer cement applied as pulp capping in human teeth

Purpose: to evaluate the human pulp response following pulp capping with calcium hydroxide (CI-I, Group 1), and the resin-modified glass-ionomer Vitrebond (VIT, Group 2). Materials and Methods: Intact teeth with no cavity preparation were used as control Group (ICG, Group 3). Buccal Class V cavities were prepared in 34 sound human premolars. After exposing the pulps, the pulp capping materials were applied and the cavities were Filled using Clearfil Liner Bond 2 bonding agent and Z100 resin-based composite. The teeth were extracted after 5, 30, and from 120 to 300 days, fixed in 10% buffered formalin solution, and prepared according to routine histological techniques. 6-mu m sections were stained with hematoxylin and eosin, Masson's trichrome, or Brown gr Brenn technique for bacterial observation. Results: At 5 days, CH caused a large zone of coagulation necrosis, the mononuclear inflammatory reaction underneath the necrotic zone was slight to moderate. VIT caused a moderate to intense inflammatory pulp response with a large necrotic zone. A number of congested venules associated with plasma extravasation and neutrophilic infiltration was observed. Over time, only CH allowed pulp repair and complete dentin bridging around the pulp exposure site. VIT components displaced into the pulp tissue triggered a persistent inflammatory reaction which appeared to be associated with a lack of dentin bridge formation. After 30 days a few histological sections showed a number of bacteria on the lateral dentin walls. In these samples the pulp response was similar to those samples with no microleakage. VIT was more irritating to pulp tissue than CH, which allowed pulp repair associated with dentin bridge formation. These results suggested that VIT is not an appropriate dental material to be used in direct pulp capping for mechanically exposed human pulps.

Determination of the properties of an experimental glass polyalkenoate cement prepared from niobium silicate powder containing fluoride

Objectives. The purpose of this paper is to modify the conventional calcium fluoro-aluminosilicate glass, which is used in the formation of glass ionomer cements (CIGs) by the niobium addition and to study the properties of GICs obtained.Materials and methods. Sol-gel process was used to prepare the powder at lower temperature than fusion method. Glass-ceramic powder obtained in this way was used to prepare the GICs. The properties such as working and setting times, microhardness and diametral tensile strength were evaluated for the experimental GICs and a commercial luting cement.Results. The ideal powder:liquid (P:L) ratio determined to prepare the experimental GICs was equal to 1:1. The cements prepared using this ratio showed working and setting times similar to the commercial GICs. in mechanical tests it was observed that microhardness and diametral tensile strength of the experimental GICs decreased significantly with the reduction of P:L ratio. on the other hand, the results obtained in microhardness tests indicated that the presence of niobium was a positive factor.Significance. The chemical process allows the development of glass-ceramic powder at 600 degrees C which is the goal of the present paper. It was concluded that GICs containing niobium might be used in dental applications and these results encourage further researches on other compositions. (c) 2007 Academy of Dental Materials. Published by Elsevier Ltd. All rights reserved.

A retrospective look at esthetic resin composite and glass-ionomer Class III restorations: A 2-year clinical evaluation

Objective: A restorative material for Class III cavities must, besides being functional, be esthetically satisfactory, providing good working conditions and several shade and color options. A clinical evaluation was initiated to compare the suitability of resin composite and glass-ionomer cement materials for such restorations.Method and materials: Forty-two Class III conservative cavities, esthetically important because of facial extensions, were selected. Resin composite restorations were placed in 21 cavities, and the remaining 21 were restored with glass-ionomer cement. The following characteristics were studied: color or-esthetics, anatomic shape, surface texture, staining, marginal infiltration, dental plaque retention, and occurrence of fracture. After 24 months, the restorations were evaluated.Results: the only statistically significant difference between the resin composite and glass-ionomer cement restorations in the experimental period involved color or esthetics.Conclusion: Resin composites and glass-ionomer materials provide excellent functional and esthetic results in Class III cavities when properly indicated.

Rugosidade e pigmentação superficial de materiais ionoméricos

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)