PtRuO/Ti anodes with a varying Pt:Ru ratio for direct methanol fuel cells

PtRuO/Ti anodes with a varying Pt:Ru ratio were prepared by thermal deposition of a PtRuO catalyst layer onto a Ti mesh for the direct methanol fuel cell (DMFC). The morphology and structure of the catalyst layers were analyzed by SEM, EDX, and XRD. The catalyst coating layers became porous with increase of the Ru content, and showed oxide and alloy characteristics. The relative activities of the PtRuO/Ti electrodes were assessed and compared using half-cell tests and single DMFC experiments. The results showed that these electrodes were very active for the methanol oxidation and that the optimum Ru surface coverage was ca. 38% for a DMFC operating at 20-60 °C. © 2006 Elsevier B.V. All rights reserved.

Preparation and characterization of new anodes based on Ti mesh for direct methanol fuel cells

A novel anode structure based on Ti mesh for the direct methanol fuel cell (DMFC) has been prepared by thermal deposition of ~5 µm PtRuO2 catalyst layer on ~50 µm Ti mesh. The preparation procedures and the main characteristics of the anode were studied by half-cell testing, scanning electron microscopy analysis, energy-dispersive X-ray measurement, and single-cell testing. The optimum calcination temperature is 450°C, calcination time is 90- 120 min, PtRuO2 catalyst loading is 5.0 mg cm-2, Pt precursor concentration range of solution is 0.14- 0.4 M, and solution aging time is 1 day. The performances of the anodes prepared using the solution kept within 20 days showed no significant difference. When it was used in DMFC feed with low-concentration methanol solution at 90°C, this new anode shows better performance than that of the conventional anode, because its thin hydrophilic structure is a benefit to the transport of methanol and carbon dioxide. However, due to its opening structure, when higher concentration methanol was employed, the performance of the cell with new anode became worse. © 2006 The Electrochemical Society. All rights reserved.

Development of a PtSn bimetallic catalyst for direct fuel cells using bio-butanol fuel

Pt and PtSn catalysts were studied for n-butanol electro-oxidation at various temperatures. PtSn showed a higher activity towards butanol electro-oxidation compared to Pt in acidic media. The onset potential for n-butanol oxidation on PtSn is ~520 mV lower than that found on Pt, and significantly lower activation energy was found for PtSn compared with that for Pt.