Adhesion between fiber post and root dentin: evaluation of post surface conditioning for bond strength improvement.

The aim of this paper was to evaluate two surface conditioning methods associated with the application of adhesive on the post surface for improving the bond to resin cement. Sixty single-rooted bovine teeth were sectioned at 16 mm in length, prepared (9 mm depth), embedded in a PVC cylinder using acrylic resin, and allocated into 3 groups (N.=20) according to post surface treatment: cleaning with ethanol (control group); etching with hydrogen peroxide; etching with hydrofluoric acid. Ten posts for each group were silanized and other 10 posts were silanized and received an adhesive agent. The posts were cemented with self-adhesive resin cement (RelyX U100 resin cement). All teeth were sectioned perpendicularly to the long axis (2 mm thickness per slice), submitted to push out bond strength testing and the type of failure was recorded. The obtained data were submitted to two-way ANOVA and Turkey's test, with the level of significance set at 5%. Neither the hydrofluoric acid or hydrogen peroxide post surface treatment, nor the adhesive application, had an influence on bond strength values. The main type of failure was adhesive between cement and dentin. Etching and the application of an adhesive on the post surface did not presented a significant influence on the bond strength results for the fiber post resin cement-root dentin assembly. The cement appears to adhere very well to the fiber post surface rather than the dentin surface.

Influence of buccal cusp reduction when using porcelain laminate veneers in premolars. A comparative study using 3-D finite element analysis

Objectives: Based on a maxillary premolar restored with laminate veneer and using the 3-D finite element analysis (FEA) and mCT data, the aim of this study was to evaluate the influence of different types of buccal cusp reduction on the stress distribution in the porcelain laminate veneer and in the resin luting cement layer. Methods: Two 3-D FEA models (M) of a maxillary premolar were built from mCT data. The buccal cusp reduction followed two configurations: Mt-buccal cusp completely covered by porcelain laminate veneer; and Mp-buccal cusp partially covered by porcelain laminate veneer. The loading (150 N in 458) was performed on the top of the buccal cusp. The finite element software (Ansys Workbench 10.0) was used to obtain the maximum shear stress (σmax) and maximum principal stress (σmax). Results: The Mp showed reduced the stress (σmax) in porcelain laminate veneer (from-2.3 to 24.5 MPa) in comparison with Mt (from-5.3 to 27.4 MPa). The difference between the peak and lower stress values of σmax in Mp (-6.8 to 26.7 MPa) and Mt (-5.3 to 27.4 MPa) was similar for the resin luting cement layer. The structures not exceeded the ultimate tensile strength or the shear bond strength. Conclusions: Cusp reduction did not affect significant increase in σmax and τmax. The Mt showed better stress distribution (τmax) than Mp. © 2011 Published by Elsevier Ireland on behalf of Japan Prosthodontic Society.

Shear bond strength of resin cement bonded to alumina ceramic after treatment by aluminum oxide sandblasting or silica coating

Purpose: To evaluate the shear bond strength and bond durability between a dual-cured resin cement (RC) and a high alumina ceramic (In-Ceram Alumina), subjected to two surface treatments. Materials and Methods: Forty disc-shaped specimens (sp) (4-mm diameter, 5-mm thick) were fabricated from In-Ceram Alumina and divided into two groups (n = 20) in accordance with surface treatment: (1) sandblasting by aluminum oxide particles (50 μm Al 2O 3) (SB) and (2) silica coating (30 μm SiO x) using the CoJet system (SC). After the 40 sp were bonded to the dual-cured RC, they were stored in distilled water at 37°C for 24 hours. After this period, the sp from each group were divided into two conditions of storage (n = 10): (a) 24 h-shear bond test 24 hours after cementation; (b) Aging-thermocycling (TC) (12,000 times, 5 to 55°C) and water storage (150 days). The shear test was performed in a universal test machine (1 mm/min). Results: ANOVA and Tukey (5%) tests noted no statistically significant difference in the bond strength values between the two surface treatments (p= 0.7897). The bond strengths (MPa) for both surface treatments reduced significantly after aging (SB-24: 8.2 ± 4.6; SB-Aging: 3.7 ± 2.5; SC-24: 8.6 ± 2.2; SC-Aging: 3.5 ± 3.1). Conclusion: Surface conditioning using airborne particle abrasion with either 50 μm alumina or 30 μm silica particles exhibited similar bond strength values and decreased after long-term TC and water storage for both methods. © 2011 by The American College of Prosthodontists.

Nd:YAG Laser Irradiation effect on apical intracanal dentin-a microleakage and SEM evaluation

The purpose of this in vitro study was to evaluate the effect of neodymium:yttrium-aluminum-garnet (Nd:YAG) laser irradiation on intracanal dentin surface by SEM analysis and its interference in the apical seal of filled canals. After endodontic treatment procedures, 34 maxillary human incisors were randomly assigned to 2 groups. In the negative control group (n=17), no additional treatment was performed and teeth were filled with vertically condensed gutta-percha; in the laser-treated group (n=17), the root canals were irradiated with Nd:YAG laser (1.5 W, 100 mJ, 15 Hz) before filling as described for the control group. Two specimens of each group were prepared for SEM analysis to evaluate the presence and extent of morphological changes and removal of debris; the other specimens were immersed in 0.5% methylene blue dye (pH 7.2) for 24 h for evaluation of the linear dye leakage at the apical third. SEM analysis of the laser-treated group showed dentin fusion and resolidification without smear layer or debris. The Student's t-test showed that the laser-treated group had significantly less leakage in apical third than the control group. Within the limitations of this study, it may be concluded that the morphological changes on the apical intraradicular dentin surface caused by Nd:YAG laser resulted in less linear dye apical leakage.

Analysis of hybrid layer thickness, resin tag length and their correlation with microtensile bond strength using a total etch adhesive to intact dentin.

The objective of this study was to evaluate the use of a two-step total etch and rinse adhesive, the correlation between the hyybrid layer thickness (HL) and bond strength (BS), and between resin tag length (RT) and bond strength in the same teeth, and also to evaluate the fracture patterns of the tested specimens. Ten human molars were used for the restorative procedure and then sectioned in two halves (mesio-distally). The materials used were Adper Single Bond 2, 3M ESPE, Ultra etch gel, Ultradent and Filtek Z250, 3M ESPE. One half were utilized to measure the HL thickness and RT length through light microscopy analysis (400x), and the other half was subject to a microtensile test to measure the BS. The fractured surfaces were analyzed by scanning electron microscopy and fracture patterns classified. The Pearson correlation test was applied (p = 0.05). The results of the analyses of each specimen then were correlated: mean HL thickness = 4.39 (0.48) microm, mean length of RT = 9.94 (1.69) microm, mean BS = 23.98 (10.24) MPa. A statistically significant correlation between HL thickness and bond strength was found (r = 0.93). The two step etch and rinse adhesive system, showed a strong correlation between HL thickness and bond strength. The most common fractures were adhesive, followed by cohesive in resin.

Influence of the hybrid layer thickness and resin tag length on microtensile bond strength.

The purpose of this study was to evaluate the correlation between the hybrid layer thickness/resin tag length and the microtensile bond strength of conventional two-step adhesive system, when applied to healthy dentinal tissue. After performing the restorative adhesive procedures and tooth extractions, ten specimens were sectioned in the mesiodistal direction. One section was used for microscopic analysis of the resin tag lengths and the hybrid layer thickness, while the other was used for the microtensile bond strength test (0.5 mm/min). The fractured surface was classified according to the fracture pattern, under a stereoscopic microscope at 40x magnification. Data obtained were submitted to analysis using one-way ANOVA and Pearson's Correlation test (alpha=0.05). The means corresponding to the hybrid layer thickness, resin tag lengths and the microtensile test were 2.68 microm, 6.43 microm and 16.23 MPa, respectively. There was no correlation between the means of the values obtained for the microtensile test, and those presented by the hybrid layer (r2=0.40, p>0.05) and resin tags (r2=0.21, p>0.05). The microtensile bond strength of the conventional two-step adhesive system Adper Single Bond 2 did not depend on the thickness of the hybrid layer and length of resin tags.

Influence of acid-etching and ceramic primers on the repair of a glass ceramic

The objective of this study was to evaluate the influence of different primers on the microtensile bond strength (μT BS) between a feldspathic ceramic and two composites. Forty blocks (6.0 × 6.0 × 5.0 mm 3) were prepared from Vita Mark II . After polishing, they were randomly divided into 10 groups according to the surface treatment: Group 1, hydrofluoric acid 10% (HF) + silane; Group 2, CoJet + silane; Group 3, HF + Metal/Zirconia Primer; Group 4, HF + Clearfil Primer; Group 5, HF + Alloy Primer; Group 6, HF + V-Primer; Group 7, Metal/Zirconia Primer; Group 8, Clearfil Primer; Group 9, Alloy Primer; Group 10, V-Primer. After each surface treatment, an adhesive was applied and one of two composite resins was incrementally built up. The sticks obtained from each block (bonded area: 1.0 mm2 ± 0.2 mm) were stored in distilled water at 37°C for 30 days and submitted to thermocycling (7,000 cycles; 5°C/55°C ± 1°C). The μT BS test was carried out using a universal testing machine (1.0 mm/min). Data were analyzed using ANOVA and a Tukey test (α = 0.05). The surface treatments significantly affected the results (P < 0.05); no difference was observed between the composites (P > 0.05). The bond strength means (MPa) were as follows: Group 1a = 29.6; Group 1b = 33.7; Group 2a = 28.9; Group 2b = 27.1; Group 3a = 13.8; Group 3b = 14.9; Group 4a = 18.6; Group 4b = 19.4; Group 5a = 15.3; Group 5b = 16.5; Group 6a = 11; Group 6b = 18; Groups 7a to 10b = 0. While the use of primers alone was not sufficient for adequate bond strengths to feldspathic ceramic, HF etching followed by any silane delivered higher bond strength.

Using the self-etch adhesives in anterior restoration

With the arrival of self-etch adhesives systems, there has been a rise in interest among clinicians, making it imperative for health professionals to have knowledge of the properties, characteristics, the association as well as the dental structures of these materials, in order to select them and use them correctly. The self-etch adhesive systems show good values of bond strength, microleakage and performance, and have therefore become an option in direct adhesive restorations. In the regard, this case study aims to describe the technique involving the use of selfetch adhesives system for direct restoration of anterior teeth.

Correlation between hybrid layer thickness, resin tag length and microtensile bond strength of a self-etching adhesive system

The purpose of this study was to evaluate the correlation between the hybrid layer thickness, resin tag length and resin bond strength of a self-etching adhesive system to sound dentin tissue in vivo. After performing restorative procedures and tooth extractions, ten specimens were sectioned in a mesiodistal direction. One dental section was used for light microscope analysis, in which both the resin tag length and hybrid layer thickness were measured, while the other section was analyzed using a microtensile test (0.5 mm/min). The fractured surface of the latter section was characterized using a stereoscopic magnifying glass (40x magnifcation). The results were subject to statistical analysis using the Pearson Correlation Test (a = 0.05). The hybrid layer thickness, resin tag length and resin bond strength mean values were 2.19 microm (0.34), 4.34 microm (0.28) and 9.73 MPa (5,55), respectively. In addition, correlation tests between the resin tag length and the resin bond strength (r=0.014) and also between the hybrid layer thickness and bond strength (r=0.43), showed no statistically significant correlation. The microtensile bond strength of Adper Prompt L Pop self-etching adhesive system does not depend on hybrid layer thickness or resin tag length.

Bond strength of adhesive systems with different solvents to dry and wet dentin

Aim: This study evaluates bond strength between dentin and composite using adhesives with different solvents to dry and wet dentin. Materials and methods: Ninety bovine incisors were used; the vestibular surfaces were worn by the exposure of an area with a diameter of 4 mm of dentin. The specimens were divided into 6 groups, according to the type of adhesive used and hydratation stals: Group SB-wet: Single Bond 2 in wet dentin, Group SBdry: Single Bond 2 in dry dentin, Group SL-wet: Solobond M in wet dentin, Group SL-dry: Solobond M in dentin dry. Group XPwet: XP Bond in wet dentin, Group XP-dry: XP Bond in dentin dry. They were cut to obtain specimens in the shape of stick with 1 × 1 mm and subjected to microtensile test in universal testing machine with a cross speed of 1mm/min. The data were analyzed with ANOVA and Tukey's tests (5%). Results: ANOVA showed significant differences for surface treatment and interaction, but no difference was found for adhesive factor. The Tukey's test showed that the samples with wet dentin shown higher values of bond strength. Conclusion: The adhesive did not influence in the bond strength. The groups with wet dentin showed higher values of bond strength than groups with dry dentin.

Degree of conversion of polymer-matrix composite assessed by FTIR analysis

Aims and objectives: The behavior of polymer-matrix composite is dependent on the degree of conversion. The aim of this study was to evaluate the degree of conversion of two resin cements following storage at 37°C immediately, 24 and 48 hours, and 7 days after light-curing by FTIR analysis. Materials and methods: The specimens were made in a metallic mold and cured with blue LED with power density of 500 mW/cm2 for 30 seconds. The specimens were pulverized, pressed with KBr and analyzed with FTIR following storage times. Statistical analysis used: ANOVA (two-way) and Tukey's post hoc. Results: To the polymer-matrix composites between 24 and 48 hours does not show a significant increase (p > 0.05), however, the highest values were found after 7 days. Conclusion: The polymer-matrix composites used in this study showed similarity on the degree of conversion and increased of according to the time of storage.

Effects of cement-curing mode and light-curing unit on the bond durability of ceramic cemented to dentin

The aim of this study was to evaluate the effects of different light-curing units and resin cement curing types on the bond durability of a feldspathic ceramic bonded to dentin. The crowns of 40 human molars were sectioned, exposing the dentin. Forty ceramic blocks of VITA VM7 were produced according to the manufacturer's recommendations. The ceramic surface was etched with 10% hydrofluoric acid/60s and silanized. The dentin was treated with37% phosphoric acid/15s, and the adhesive was applied. The ceramic blocks were divided and cemented to dentin according to resin cement/RC curing type(dual-and photocured), light-curing unit (halogen light/QTH and LED), and storage conditions (dry and storage/150 days + 12,000 cycles/thermocycling). All blocks were stored in distilled water (37°C/24h) and sectioned (n = 10): G1-QTH + RC Photo, G2-QTH + RC Dual, G3-LED + RC Photo, G4-LED + RC Dual. Groups G5, G6, G7, and G8 were obtained exactly as G1 through G4, respectively, and then stored and thermocycled. Microtensile bond strength tests were performed (EMIC), and data were statistically analyzed by ANOVA and Tukey's test (5%). The bond strength values (MPa) were: G1-12.95 (6.40)ab; G2-12.02 (4.59)ab; G3-13.09 (5.62)ab; G4-15.96 (6.32)a; G5-6.22 (5.90)c; G6-9.48 (5.99)bc; G7-12.78 (11.30)ab; and G8-8.34 (5.98)bc. The same superscript letters indicate no significant differences. Different light-curing units affected the bond strength betweenceramic cemented to dentin when the photocured cement was used, and only after aging (LED>QTH). There was no difference between the effects of dual-and photo-cured resin-luting agents on the microtensile bond strength of the cement used in this study.

Avaliação da reação periodontal na técnica de colagem extra-alveolar de fraturas radiculares verticais simuladas: estudo histológico

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Efeito da ciclagem mecânica sobre a resistência de união de pinos intra-radiculares de fibra cimentados com resina à dentina

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Comparison of shear bond strength of orthodontics brackets on composite resin restorations with different surface treatments

INTRODUÇÃO: frequentemente, os pacientes ortodônticos apresentam restaurações de resina composta; no entanto, existem poucos estudos que avaliam a melhor forma de colagem ortodôntica nessa situação. OBJETIVO: o objetivo do presente trabalho foi avaliar a força adesiva de braquetes ortodônticos em restaurações resinosas com tratamento de superfície. MÉTODOS: foram utilizados 51 incisivos inferiores bovinos divididos aleatoriamente em três grupos. No grupo controle (GC), os braquetes foram colados em esmalte dentário; nos grupos experimentais com tratamento (GCT) e sem tratamento (GST), os braquetes foram colados em restauração de resina previamente realizada, diferenciando-se pelo tratamento de superfície com broca diamantada. Os dentes foram incluídos em tubos de PVC com resina acrílica autopolimerizável. O ensaio de cisalhamento foi executado em máquina universal de ensaios Emic. Os grupos foram submetidos à ANOVA com pós-teste de Tukey para verificação da diferença estatística entre os grupos (α = 0,05). RESULTADOS: GC (6,62MPa) e GCT (6,82MPa) apresentaram resultados semelhantes, enquanto o GST (5,07MPa) obteve resultados estatisticamente menores (p < 0,05). CONCLUSÃO: conclui-se que a melhor técnica de colagem de braquetes ortodônticos em restaurações de resina composta é a de realização de desgaste sobre a superfície.