UVC emitting phosphors obtained by spray pyrolysis

The broadband inter-configurational (4f(1)5d(1)-->4f(2)) emission of Pr(3+) doped in lanthanum orthophosphate (LaPO(4)) and in calcium pyrophosphate (Ca(2)P(2)O(7)) has been investigated under plasma excitation. The synthesis by spray pyrolysis at moderate temperature followed by a controlled annealing proves to be a very efficient way to produce good quality UVC emitting phosphor Ca(1.92)Pr(0.04)Na(0.04)P(2)O(7) (alpha phase). The emission of this phosphor in the wavelength range 200-350 nm has been measured with a prototype device, which can be employed for anti-microbial testing. (C) 2010 Elsevier B.V. All rights reserved.

Microstructural characterization of layers produced by plasma nitriding on austenitic and superaustenitic stainless steel grades

High chromium content is responsible for the formation of a protective passive surface layer on austenitic stainless steels (ASS). Due to their larger amounts of chromium, superaustenitic stainless steels (SASS) can be chosen for applications with higher corrosion resistance requirements. However, both of them present low hardness and wear resistance that has limited their use for mechanical parts fabrication. Plasma nitriding is a very effective surface treatment for producing harder and wear resistant surface layers on these steel grades, without harming their corrosion resistance if low processing temperatures are employed. In this work UNS S31600 and UNS S31254 SASS samples were plasma nitrided in temperatures from 400 °C to 500 °C for 5 h with 80% H 2-20% N2 atmosphere at 600Pa. Nitrided layers were analyzed by optical (OM) and transmission electron microscopy (TEM), x-ray diffraction (XRD), and Vickers microhardness testing. Observations made by optical microscopy showed that N-rich layers were uniform but their thicknesses increased with higher nitriding temperatures. XRD analyses showed that lower temperature layers are mainly composed by expanded austenite, a metastable nitrogen supersaturated phase with excellent corrosion and tribological properties. Samples nitrided at 400 °C produced a 5 μm thick expanded austenite layer. The nitrided layer reached 25 lm in specimens treated at 500 °C. There are indications that other phases are formed during higher temperature nitriding but XRD analysis was not able to determine that phases are iron and/or chromium nitrides, which are responsible for increasing hardness from 850 up to 1100 HV. In fact, observations made by TEM have indicated that formation of fine nitrides, virtually not identified by XRD technique, can begin at lower temperatures and their growth is affected by both thermodynamical and kinetics reasons. Copyright © 2012 by ASTM International.

Osseointegration assessment of chairside argon-based nonthermal plasma-treated Ca-P coated dental implants

This study investigated the effect of an Argon-based nonthermal plasma (NTP) surface treatment-operated chairside at atmospheric pressure conditions applied immediately prior to dental implant placement in a canine model. Surfaces investigated comprised: Calcium-Phosphate (CaP) and CaP + NTP (CaP-Plasma). Surface energy was characterized by the Owens-Wendt-Rabel-Kaelble method and chemistry by X-ray photoelectron spectroscopy (XPS). Six adult beagles dogs received 2 plateau-root form implants (n = 1 each surface) in each radii, providing implants that remained 1 and 3 weeks in vivo. Histometric parameters assessed were bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO). Statistical analysis was performed by Kruskall-Wallis (95% level of significance) and Dunn's post-hoc test. The XPS analysis showed peaks of Ca, C, O, and P for the CaP and CaP-Plasma surfaces. Both surfaces presented carbon primarily as hydro-carbon (CAC, CAH) with lower levels of oxidized carbon forms. The CaP surface presented atomic percent values of 38, 42, 11, and 7 for C, O, Ca, and P, respectively, and the CaPPlasma presented increases in O, Ca, and P atomic percent levels at 53, 12, and 13, respectively, in addition to a decrease in C content at 18 atomic percent. At 1 week no difference was found in histometric parameters between groups. At 3 weeks significantly higher BIC and BAFO were observed for CaPPlasma treated surfaces. Surface elemental chemistry was modified by the Ar-based NTP. Ar-based NTP improved bone formation around plateau-root form implants at 3 weeks compared with CaP treatment alone. © 2012 Wiley Periodicals, Inc.

Spray Nozzles, Pressures, Additives and Stirring Time on Viability and Pathogenicity of Entomopathogenic Nematodes (Nematoda: Rhabditida) for Greenhouses

The objective of this study was to evaluate different strategies for the application of entomopathogenic nematodes (EPN). Three different models of spray nozzles with air induction (AI 11003, TTI 11003 and AD-IA 11004), three spray pressures (207, 413 and 720 kPa), four different additives for tank mixtures (cane molasses, mineral oil, vegetable oil and glycerin) and the influence of tank mixture stirring time were all evaluated for their effect on EPN (Steinernema feltiae) viability and pathogenicity. The different nozzles, at pressures of up to 620 kPa, were found to be compatible with S. feltiae. Vegetable oil, mineral oil and molasses were found to be compatible adjuvants for S. feltiae, and stirring in a motorized backpack sprayer for 30 minutes did not impact the viability or pathogenicity of this nematode. Appropriate techniques for the application of nematodes with backpack sprayers are discussed. © 2013 Moreira et al.

A meta-analytical study about the relation of blood plasma addition in diets for piglets in the post-weaning and productive performance variables

The meta-analysis was used to evaluate the performance of piglets in post-weaning period, without imposition of sanitary challenge and fed diets containing blood plasma, obtained by spray-dried process (SDBP). Piglets are faced with normal challenges in post-weaning period such as environmental stress and the substitution of the liquid diet to a solid one. References regarding sanitary challenges were disregarded in this study. Only data regarding normal and expected challenges were considered. Data were obtained from indexed journals with information extracted from the material, methods and results sections of pre-selected scientific articles. First, the database was analyzed graphically to observe the distribution of data and presence of outliers. Afterwards correlation analysis and variance-covariance analyses were carried out. The database contained a total of 23 articles. The average initial weight of the piglets was 8.02. kg (4.00-9.28. kg) and the average initial age was 27 days (14-32 days). The average duration of feeding diets containing spray-dried blood plasma (SDBP) was 9 days (6-28 days). SDBP increased the feed conversion by 20.2% (P<0.05) during the initial period. Feed conversion during the total period was 10.2% higher (P<0.05) for animals fed with SDBP. Average daily weight gain and daily feed intake were not affected (P>0.05) during the entire period, but average daily gain was higher (P<0.05) for animals fed with SDBP during the initial period. The initial age of supplementation influenced the average daily weight gain and average daily feed intake of animals fed with SDBP. Better results were obtained than those obtained for animals up to 35 days of age fed diets without added SDBP supplementation. In early post-weaning period for piglets weaned up to 35 days of age, the SDBP supplementation positively influenced the average daily weight gain and feed conversion. © 2013 Elsevier B.V.

Esterilização de materiais termossensíveis através de aplicação de plasma gerado por descarga com barreira dielétrica (DBD)

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Estudo das propriedades de barreira de filmes depositados a plasma sobre a liga de alumínio 2024

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Alteração das propriedades superficiais do alumínio via eletrólise e plasma

Pós-graduação em Ciência e Tecnologia de Materiais - FC

Estudo de polímeros comerciais tratados a plasma em pressão atmosférica

Fundação de Amparo à Pesquisa do Estado de São Paulo (FAPESP)

Tratamento de polímeros com jato de plasma em pressão atmosférica

Pós-graduação em Física - FEG

Propriedades mecânicas e tribológicas de filmes sintetizados mediante técnica de deposição e implantação iônica por imersão em plasma

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Caracterização mecânica e microestrutural de um aço 4340 com estrutura multifásicas e tratamento de nitrocarbonetação a plasma

Coordenação de Aperfeiçoamento de Pessoal de Nível Superior (CAPES)

Treatment of polycarbonate by dielectric barrier discharge (DBD) at atmospheric pressure

Generally most plastic materials are intrinsically hydrophobic, low surface energy materials, and thus do not adhere well to other substances. Surface treatment of polymers by discharge plasmas is of great and increasing industrial application because it can uniformly modify the surface of sample without changing the material bulk properties and is environmentally friendly. The plasma processes that can be conducted under ambient pressure and temperature conditions have attracted special attention because of their easy implementation in industrial processing. Present work deals with surface modification of polycarbonate (PC) by a dielectric barrier discharge (DBD) at atmospheric pressure. The treatment was performed in a parallel plate reactor driven by a 60Hz power supply. The DBD plasmas at atmospheric pressure were generated in air and nitrogen. Material characterization was carried out by contact angle measurements, and X-ray photoelectron spectroscopy (XPS). The surface energy of the polymer surface was calculated from contact angle data by Owens-Wendt method using distilled water and diiodomethane as test liquids. The plasma-induced chemical modifications are associated with incorporation of polar oxygen and nitrogen containing groups on the polymer surface. Due to these surface modifications the DBD-treated polymers become more hydrophilic. Aging behavior of the treated samples revealed that the polymer surfaces were prone to hydrophobic recovery although they did not completely recover their original wetting properties.

Aging of plasma-activated copper and gold surfaces and its hydrophilic recovery after water immersion

A significant increase of surface hydrophilicity of copper and gold surfaces was obtained after atmospheric pressure plasma treatment using the surface dielectric barrier discharge with specific electrode geometry, the so-called diffuse coplanar surface barrier discharge. Surface wettability was estimated using the sessile drop method with further calculation of the surface free energy. After the plasma treatments, it was observed that the treated surfaces exhibited hydrophobic recovery (or aging effect). The aging effect was studied in different storage environments, such as air, low and high vacuum. The role of plasma and the reasons of the following aging effect are discussed with respect to the observed hydrophilic recovery after immersing the aged surfaces into deionized water. The changes in the surface morphology, composition and bond structure are presented and discussed as well. (C) 2013 Elsevier B. V. All rights reserved.

Fadiga axial do aço inoxidável 15-5 PH tratado pela implantação iônica por imersão em plasma

When materials for application in aircraft structural components are studied, it must be considered that they will be submitted to cyclic loading, and this is an important parameter to design the study in fatigue life of the materials. Whereas, for example, a landing gear operation, the study of fatigue life and corrosion in the materials used in it is essential, especially when you want to use new techniques for surface treatments. The objective is to study the influence of surface treatment of immersion ion implantation nitrogen plasma, in axial fatigue of Stainless steel 15-5 PH in 39-42 HRC condition. Stainless steel 15-5 PH was tested in axial fatigue and corrosion in salt spray. It was also performed microindentation tests, optical microscopy for microstructural analysis and scanning electron microscopy for fractographic analysis. It was observed that the 3IP had no effect on the thickness of the material and not the hardness of it, and still provided a significant increase in fatigue life of the material