Microwave Dielectric Properties of RETiTaO6 (RE = La, Ce,Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Er, Yb, Al, and In) Ceramics

Microwave dielectric ceramics based on RETiTaO6 (RE = La, Cc, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Er, Yb, Al, and In) were prepared using a conventional solid-state ceramic route. The structure and microstructure of the samples were analyzed using x-ray diffraction and scanning electron microscopy techniques. The sintered samples were characterized in the microwave frequency region. The ceramics based on Ce, Pr, Nd, Sm, Eu, Gd, Tb, and Dy, which crystallize in orthorhombic aeschynite structure, had a relatively high dielectric constant and positive T f while those based on Ho, Er, and Yb, with orthorhombic euxenite structure, had a low dielectric constant and negative Tf. The RETiTaO6 ceramics had a high-quality factor. The dielectric constant and unit cell volume of the ceramics increased with an increase in ionic radius of the rare-earth ions, but density decreased with it. The value of Tf increased with an increase in RE ionic radii, and a change in the sign of Tf occurred when the ionic radius was between 0.90 and 0.92 A. The results indicated that the boundary of the aeschynite to euxenite morphotropic phase change lay between DyTiTaO6 and HoTiTaO6. Low-loss ceramics like ErTiTaO6 (Er = 20.6, Qxf = 85,500), EuTiTaO6 (Er = 41.3, Qxf = 59,500), and YTiTaO6 (Er = 22.1, Q„xf = 51,400) are potential candidates for dielectric resonator applications

Microwave dielectric properties of (1-x)CaTi03-xSm(Mg1 /2Ti1/2)03 [0. 1 _ceramics

The microwave dielectric properties of (I -x)CaTiO3-xSm(Mg1/2Tit,2)O3(0.1 <-x< 1.0) have been investigated. The system forms a solid solution throughout the entire compositional range. The dielectric constant decreases from 86 to 25 as x varies from 0.1 to 1.0. The Qxf varies non-linearly and increases for composition with x> 0.6. The nonmonotonic variation with composition x is more pronounced in Tt than in er. The microwave dielectric properties indicate the possibility of a phase transformation for x between 0.4 and 0.5

Tailoring the Microwave Dielectric Properties of GdTiNb 1 _-xTa,O6 and Sm 1 _X Y,TiTa06 Ceramics

Microwave dielectric ceramics based on GdTiNb,-,.Ta,O6 and Sml _.,Y,TiTa06 have been prepared by conventional solid state method . The GdTiTaO6 and SmTiTaO6 have aeschenite structure with positive rr and GdTiNbO6 and YTiTaO6 have euxenite structure with negative rr. The rr of the ceramics has been tuned by preparing solid solution phases between the aeschynites and euxenites for a possible zero rr material . It is observed that GdTiNbt_YTa.,O6 undergoes a phase transition from aeschynite to euxenite when x=0.75 and in Sml-,YxTiTa06 for x= 0.73. The microwave dielectric properties change abruptly near the transition region . The rr value approaches zero near the phase transition region while the samples have poor sinterability and poor quality factor . The unloaded quality factor, dielectric constant and the sign of rr of the solid solution phases are found to depend on the average ionic radius of the rare earth ion in RE ,-5RE',TiTaO6. The boundary of the euxenite-aeschynite phase transition occurs at an average ( RE) ionic radius of 0.915 A in Sm,_, Y,.TiTaO6 solid solution phases

Microwave Dielectric Properties of Ba(Mg1/3Ta(2-2x)/3Wx/3Tix/3) 03 Ceramics

microwave dielectric properties of ceramics based on Ba(Mgv3Ta(2-2x)t3W,t3Tixt3)O3 is investigated as a function of x. The 15 densification as well as dielectric properties deteriorate with increase in the substitution levels of (Ti 1,3W113)333 + at (Ta213)3.33+ site 16 in Ba(Mg113Ta213)03. The rt is approaching zero between x = 0.1 and 0.15 in Ba(Mg it3Ta(2-2,,.)t3W,it3Ti,Tt3)O3 where quality factor is 17 reasonably good (Qu x f = 80,000-90,000 GHz). The Ba(Mg1,3Ta(2_,013W,13Ti,,13)03 with x = 1.0 has e, = 15.4, rf= -25.1 ppm/ 18 "C, Q„ x f = 35,400 GHz

The effect of dopants on the microwave dielectric properties of Ba( Mgo.33Ta0.67)03 ceramics

The effect of dopants with different valencies and ionic radii on the densification, structural ordering, and microwave dielectric properties of Ba(Mg1t3Tazt3)O3 (BMT) is investigated. It is found that dopants such as Sb,05, MnO, ZrO,, WO1, and ZnO improve the microwave dielectric properties of BMT. Addition of trivalent dopants is detrimental to the cation ordering and dielectric properties of BMT. A correlation between the microwave dielectric properties of BMT and ionic radii of the dopant has been established. The variation of the dielectric properties of pure and doped BMT at cryogenic temperatures is also discussed

Microwave Dielectric Properties of BaO -2CeO2-nTiO2 Ceramics

The BaO-2CeO2-nTiO2 ceramics with n = 3, 4 and 5 have been prepared with CeO2 as starting material . The ceramics have been characterized using scanning electron microscopy , X-ray diffraction , Raman and X-ray photoelectron spectroscopy techniques. The microwave dielectric properties have been measured using standard dielectric resonator techniques . BaO-2CeO2-3TiO2 (123), BaO-2CeO2-4TiO2 ( 124) and BaO-2CeO2-5TiO2 ( 125) ceramics showed dielectric constants of 38, 27 and 32, respectively . All the ceramics showed fairly good unloaded Q - factors . 124 and 125 compounds exhibited low tf values, while 123 showed a high rf value

Preparation, Characterization and Microwave Dielectric Properties of Ba (B1/2Nb1/2)03 [B' = La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Yb and In] Ceramics

Microwave dielectric resonators (DRs) based on Ba(B1,2Nbi/2)03 [B' = La, Pr, Nd, Sm, Eu, Gd, Tb, Dy, Ho, Y, Yb, and In] complex perovskites have been prepared by conventional solid state ceramic route. The dielectric properties (relative permittivity, Er; quality factor, Q; and resonant frequency, rr) of the ceramics have been measured in the frequency range 4-6 GHz using resonance methods. The resonators have relatively high dielectric constant in the range 36-45, high quality factor and small temperature variation of resonant frequency. The dielectric properties are found to depend on the tolerance factor (t), ionic radius (r), and lattice parameter (ap)

The Effect of Glass Additives on the Microwave Dielectric Properties of Ba(Mg 1 /3Ta2/3)03 Ceramics

The effect of glass additives on the densification , phase evolution, microstructure and microwave dielectric properties of Ba(Mg1;3 Ta2i3)03 (BMT) was investigated . Different weight percentages of quenched glass such as B203 , Si02, B203-SiO2, ZnO-B203, 5ZnO-2B2O3, Al203-SiO2, Na20-2B203.10H20, BaO-B203-SiO2, MgO-B203-SiO2, PbO-B203-SiO2 , ZnO-B203-SiO2 and 2MgO-Al203-5SiO2 were added to calcined BMT precursor . The sintering temperature of the glass -added BMT samples were lowered down to 1300 °C compared to solid-state sintering where the temperature was 1650 °C. The formation of high temperature satellite phases such as Ba5Ta4O15 and Ba7Ta6O22 were found to be suppressed by the glass addition . Addition of glass systems such as B203, ZnO-B203, 5ZnO-2B203 and ZnO-B203-SiO2 improved the densification and microwave dielectric properties. Other glasses were found to react with BMT to form low-Q phases which prevented densification . The microwave dielectric properties of undoped BMT with a densification of 93 . 1 % of the theoretical density were Cr = 24 . 8, Tr = 8 ppm/°C and Q„ x f= 80,000 GHz. The BMT doped with 1.0 wt% of B203 has Q„ x f = 124,700GHz, Cr = 24.2, and T f = -1.3 ppm /°C. The unloaded Q factor of 0.2 wt% ZnO-B203-doped BMT was 136,500 GHz while that of 1.0 wt% of 5ZnO-2B203 added ceramic was Q„ x f= 141,800 GHz . The best microwave quality factor was observed for ZnO -B203-SiO2 (ZBS) glass-added ceramics which can act as a perfect liquid-phase medium for the sintering of BMT. The microwave dielectric properties of 0.2wt% ZBS-added BMT dielectric was Q„ x f= 152,800 GHz, F,= 25.5, and Tr = - 1.5 ppm/°C

Photoacoustic Thermal Characterization of Porous Rare-Earth Phosphate Ceramics

The laser induced non-destructive photoacoustic technique has been employed to measure the thermal diffusivity of lanthanum phosphate ceramics prepared by the sol–gel route. The thermal diffusivity value was evaluated by knowing the transition frequency between the thermally thin to thermally thick region from the log–log plot of photoacoustic amplitude versus chopping frequency. Analysis of the data was carried out on the basis of the one-dimensional model of Rosencwaig and Gersho. The present investigation reveals that the sintering temperature has great influence on the propagation of heat carriers and hence on the thermal diffusivity value. The results were interpreted in terms of variations in porosity with sintering temperature as well as with changes in grain size.

Thermal characterization of nanocrystalline porous CePO4 ceramics

A laser-induced photoacoustic technique was employed to investigate thermal transport through nanocrystalline CePO4 samples prepared via the sol–gel route. Evaluation of thermal diffusivity was carried out using the one-dimensional model of Rosencwaig and Gersho for the reflection configuration of the photoacoustic method. Structural analyses of samples revealed that they are nanoporous in nature, possessing micron-sized grains. Analysis of results shows that thermal diffusivity value varies with sintering temperature. Results are explained in terms of the variation in porosity with sintering temperature and the effects of various scattering mechanisms on the propagation of phonons through the nanoporous ceramic matrix. Further analyses confirm that apart from porosity, grain boundary resistance and interface thermal resistance influence the effective value of thermal diffusivity of the samples under investigation.

Thermal characterisation of dye-intercalated K-10 montmorillonite ceramics using photoacoustic technique

Thermal diffusivity (TD) measurements were performed on some industrially important dyes – auramine O (AO), malachite green and methylene blue (MB) – adsorbed K-10 montmorillonites using photoacoustic method. The TD value for the dye-adsorbed clay mineral was observed to change with a variation in dye concentration. The contribution of the dye towards TD was also determined. The repeatedly adsorbed samples with MB and AO exhibited a lower TD than the single-adsorbed samples. TD values of sintered MB samples were also obtained experimentally. These sintered samples exhibit a higher TD, although they show a trend similar to that of non-sintered pellets. A variation in dye concentration and sintering temperature can be used for tuning the TD value of the clay mineral to the desired level.

Thermal transport properties of selected ferroelectrics, mixed valance perovskites and dielectric ceramics using photopyroelectric technique

Photothermal spectroscopy is a group of high sensitivity methods used to measure optical absorption and thermal characteristics of a sample.The basis of photothermal spectroscopy is a photo-induced change in the thermal state of the sample.Light energy absorbed and not lost by subsequent emission results in sample heating.This heating results in a temperature change as well as changes in thermodynamic parameters of the sample which are related to temperature.Measurements of the temperature,pressure,or density changes that occur due to optical absorption are ultimately the basis for the photothermal spectroscopic methods.This is a more direct measure of optical absorption than optical transmission based spectroscopies.Sample heating is a direct consequence of optical absorption and so photothermal spectroscopy signals are directly dependent on light absorption.Scattering and reflection losses do not produce photothermal signals.Subsequently,photothermal spectroscopy more accurately measures optical absorption in scattering solutions,in solids,and at interfaces.This aspect makes it particularly attractive for application to surface and solid absorption studies,and studies in scattering media.

Investigation of dielectric and elastic properties of selected dielectric ceramics and oxide glasses

The dielectric and elastic properties are of considerable significance to the science and technology of matter in the solid state. The study of these properties give information about the magnitude of the forces and nature of the bonding between the atoms. Our aim has been to investigate systematically the effect of doping of an appropriate element on the elastic and dielectric properties of selected dielectric ceramics and oxide glasses. These materials have got wide technological applications due to their interesting electrical, optical, thermal and elastic behaviour. Ultrasound propagation and capacitance measurement techniques have been employed for the systematic investigation of the elastic and dielectric properties of selected number of these materials. Details of the work done and results obtained are presented in this thesis.

Thermal characterisation of dye-intercalated K-10 montmorillonite ceramics using photoacoustic technique

Thermal diffusivity (TD) measurements were performed on some industrially important dyes – auramine O (AO), malachite green and methylene blue (MB) – adsorbed K-10 montmorillonites using photoacoustic method. The TD value for the dye-adsorbed clay mineral was observed to change with a variation in dye concentration. The contribution of the dye towards TD was also determined. The repeatedly adsorbed samples with MB and AO exhibited a lower TD than the single-adsorbed samples. TD values of sintered MB samples were also obtained experimentally. These sintered samples exhibit a higher TD, although they show a trend similar to that of non-sintered pellets. A variation in dye concentration and sintering temperature can be used for tuning the TD value of the clay mineral to the desired level