Effects of crystalline quality on the ultraviolet emission and electrical properties of the ZnO films deposited by magnetron sputtering

The ZnO films were deposited on c-plane sapphire, Si (0 0 1) and MgAl2O4 (1 1 1) substrates in pure Ar ambient at different substrate temperatures ranging from 400 to 750 degrees C by radio frequency magnetron sputtering. X-ray diffraction, photoluminescence and Hall measurements were used to evaluate the growth temperature and the substrate effects on the properties of ZnO films. The results show that the crystalline quality of the ZnO films improves with increasing the temperature up to 600 degrees C, the crystallinity of the films is degraded as the growth temperature increasing further, and the ZnO film with the best crystalline quality is obtained on sapphire at 600 degrees C. The intensity of the photoluminescence and the electrical properties strongly depend on the crystalline quality of the ZnO films. The ZnO films with the better crystallinity have the stronger ultraviolet emission, the higher mobility and the lower residual carrier concentration. The effects of crystallinity on light emission and electrical properties, and the possible origin of the n-type conductivity of the undoped ZnO films are also discussed. (C) 2009 Elsevier B. V. All rights reserved.

Hillocks and hexagonal pits in a thick film grown by HVPE

A GaN film with a thickness of 250 mu m was grown on a GaN/sapphire template in a vertical hydride vapor phase epitaxy (HVPE) reactor. The full-width at half-maximum (FWHM) values of the film were 141 and 498 arcsec for the (0 0 2) and (1 0 2) reflections, respectively. A sharp band-edge emission with a FWHM of 20 meV at 50 K was observed, which corresponded to good crystalline quality of the film. Some almost circular-shaped hillocks located in the spiral growth center were found on the film surface with dimensions of 100 mu m, whose origin was related to screw dislocations and micropipes. Meanwhile, large hexagonal pits also appeared on the film surface, which had six triangular {1 0 (1) over bar 1} facets. The strong emission in the pits was dominated by an impurity-related emission at 377 nm, which could have been a high-concentration oxygen impurity. (c) 2008 Elsevier Ltd. All rights reserved.

Investigation of mode coupling in a microdisk resonator for realizing directional emission

Mode coupling between the whispering-gallery modes (WGMs) is numerically investigated for a two-dimensional microdisk resonator with an output waveguide. The equilateral-polygonal shaped mode patterns can be constructed by mode coupling in the microdisk, and the coupled modes can still keep high quality factors (Q factors). For a microdisk with a diameter of 4.5 mu m and a refractive index of 3.2 connected to a 0.6-mu m-wide output waveguide, the coupled mode at the wavelength of 1490 nm has a Q factor in the order of 10(4), which is ten times larger than those of the uncoupled WGMs, and the output efficiency defined as the ratio of the energy flux confined in the output waveguide to the total radiation energy flux is about 0.65. The mode coupling can be used to realize high efficiency directional-emission microdisk lasers. (C) 2009 Optical Society of America

Holographic fabricated photonic-crystal distributed-feedback quantum cascade laser with near-diffraction-limited beam quality

We demonstrate the fabrication and characterization of photonic-crystal distributed-feedback quantum cascade laser emitting at 4.7 mu m. The tilted rectangular-lattice PCDFB structure was defined using a multi-exposure of two-beam holographic lithography. The devices exhibit the near-diffraction-limited beam emission with the full width at half maximum of the far-field divergence angles about 4.5 degrees and 2.5 degrees for stripe widths of 55 mu m and 95 mu m, respectively. Single-mode emission with a side mode suppression ratio of approximate to 20 dB is achieved in the temperature range (80-210 K). The single-facet output power is above 1 W for a 95 mu m x 2.5 mm laser bar at 85 K in pulsed operation. (C) 2009 Optical Society of America

Full-color emission from In2S3 and ln(2)S(3): Eu3+ nanoparticles

New observations on the luminescence Of In2S3 and europium-doped In2S3 nanoparticles show a green (5 10 nm) emission from In2S3 and In1.8Eu0.2S3 nanoparticles while a blue (425 nm) emission is observed from ln(1.6)Eu(0.4)S(3) nanoparticles. Both the blue and green emissions have large Stokes shifts of 62 and 110 nm, respectively. Excitation with longer-wavelength photons causes the blue emission to shift to a longer wavelength while the green emission wavelength remains unchanged. The lifetimes of both the green and blue emissions are similar to reported values for excitonic recombination. When doped with Eu3+, in addition to the broad blue and green emissions, a red emission near 615 nm attributed to Eu3+ is observed. Temperature dependences on nanoparticle thin films indicate that with increasing temperature, the green emission wavelength remains constant, however, the blue emission shifts toward longer wavelengths. Based on these observations, the blue emission is attributed to exciton recombination and the green emission to Indium interstitial defects. These nanoparticles show full-color emission with high efficiency, fast lifetime decays, and good stability; they are also relatively simple to prepare, thus making them a new type of phosphor with potential applications in lighting, flat-panel displays, and communications.

Luminescence properties of self-assembled InAs/GaAs quantum dots covered by InAlAs and InGaAs combination strain-reducing layer

We report the photoluminescence (PL) and structural properties of self-assembled InAs/GaAs quantum dots (QDs) covered by In0.2Al0.8As and In0.2Ga0.8As combination strain-reducing layer (SRL). By introducing a thin InAlAs layer, the ground state emission wavelength redshifts, and the energy splitting between the ground and first-excited states increases to 85 meV at 10 K. The energy splitting further increases to 92 meV and the temperature dependence of full width at half maximum (FWHM) changes for QDs with different SRL after the multi-stacking. These results are attributed to the fact that the combination layer has different effects on QDs compared to the InGaAs SRL.

Upconversion emission of a Er3+-doped glass microsphere under 633 nm excitation (vol 35, pg 353, 2004)

　

Investigations on V-defects in quaternary AlInGaN epilayers

The characteristics of V-defects in quaternary AlInGaN epilayers and their correlation with fluctuations of the In distribution are investigated. The geometric size of the V-defects is found to depend on the In composition of the alloy. The V-defects are nucleated within the AlInGaN layer and associated with threading dislocations. Line scan cathodoluminescence (CL) shows a redshift of the emission peak and an increase of the half width of the CL spectra as the electron beam approaches the apex of the V-defect. The total redshift decreases with decreasing In mole fraction in the alloy samples. Although the strain reduction may partially contribute to the CL redshift, indium segregation is suggested to be responsible for the V-defect formation and has a main influence on the respective optical properties. (C) 2004 American Institute Of Physics.

A novel extremely broadband superluminescent diode based on symmetric graded tensile-strained bulk InGaAs

A novel broadband superluminescent diode (SLD), which has a symmetric graded tensile-strained bulk InGaAs active region, is developed. The symmetric-graded tensile-strained bulk InGaAs is achieved by changing the group III TMGa source flow only during its growth process by low-pressure metalorganic vapor-phase epitaxy (LP-MOVPE), in which the much different tensile strain is introduced simultaneously. At 200mA injection current, the full width at half maximum (FWHM) of the emission spectrum of the SLID can be up to 122nm, covering the range of 1508-1630nm, and the output power is 11.5mW.

Enhancement of the spectral width of high-power 1.5 mu m integrated superluminescent light source by quantum well intermixing process

A novel type of integrated InGaAsP superluminescent light source was fabricated based on the tilted ridge-waveguide structure with selective-area quantum well (QW) intermixing. The bandgap structure along the length of the device was modified by impurity free vacancy diffusion QW intermixing, The spectral width was broadened from the 16 nm of the normal devices to 37 nm of the QW intermixing enhanced devices at the same output power level. High superluminescent power (210 mW) was obtained under pulsed conditions with a spectral width of 37 nm.

Effect of the InAlAs and InGaAs combination strain-reducing layer on 1.3 mu m emission self-assembled InAs/GaAs quantum dots

Self-assembled InAs quantum dots (QDs) with differing deposition thicknesses covered by InxAl1-xAs (x = 0.2, 0.3) and In0.2Ga0.8As combination strain-reducing layers (CSRLs) were grown by molecular beam epitaxy. Their structural and optical properties were investigated by atomic force microscopy and photoluminescence spectroscopy, respectively. The emission peak position of InAs QDs capped by CSRL can reach 1.34 mum at room temperature with a relatively larger energy splitting of 93 meV between the ground and first excited states.

Upconversion emission of a Er3+-doped glass microsphere under 633 nm excitation

In this work, The TBS glass microspheres doped with Er3+ for morphology-dependent resonances of upconversion emission were designed. The glass sample components are 25TiO(2)-27BaCO(3)-8Ba(NO3)(2)-6ZnO(2)-9CaCO(3)-5H(3)BO(3)-10SiO(2)-7water glass-3Er(2)O(3) (wt%), and the emission spectra of TBS glass and a TBS glass microsphere (about 48 mum in diameter) were measured under 633 nm excitation and discussed. The strong morphology-dependent resonances of upconversion luminescences in the microsphere were observed. The observed resonances could be assigned by using the well-known Lorenz-Mie Formalism. (C) 2003 Elsevier Ltd. All rights reserved.

Luminescence emission originating from nitrogen doping of beta-Ga2O3 nanowires

Nitrogen-doped beta-Ga2O3 nanowires (GaO NWs) were prepared by annealing the as-grown nanowires in an ammonia atmosphere. The optical properties of the nitrogen-doped GaO NWs were studied by measurements of the photoluminescence and phosphorescence decay at the temperature range between 10 and 300 K. The experimental results revealed that nitrogen doping in GaO NWs induced a novel intensive red-light emission around 1.67 eV, with a characteristic decay time around 136 mus at 77 K, much shorter than that of the blue emission (a decay time of 457 mus). The time decay and temperature-dependent luminescence spectra were calculated theoretically based on a donor-acceptor pair model, which is in excellent agreement with the experimental data. This result suggests that the observed novel red-light emission originates from the recombination of an electron trapped on a donor due to oxygen vacancies and a hole trapped on an acceptor due to nitrogen doping.

Mode quality factor based on far-field emission for square resonators

The quality factors of modes in square resonators are calculated based on the far-field emission of the analytical field distribution. The obtained quality factors are in reasonable agreement with those calculated by the finite-difference time-domain (FDTD) technique and Pade approximation method. The emission power in the square diagonal directions for whispering-gallery-like modes in square resonators is zero due to the interference cancellation caused by the odd field distributions relative to the diagonal mirror planes, so they have larger quality factors than the modes with even field distribution.

Fourier series expansion method for gain measurement from amplified spontaneous emission spectra of Fabry-Perot semiconductor lasers

A gain measurement technique, based on Fourier series expansion of periodically extended single fringe of the amplified spontaneous emission spectrum, is proposed for Fabry-Perot semiconductor lasers. The underestimation of gain due to the limited resolution of the measurement system is corrected by a factor related to the system response function. The standard deviations of the gain-reflectivity product under low noise conditions are analyzed for the Fourier series expansion method and compared with those of the Hakki-Paoli method and Cassidy's method. The results show that the Fourier series expansion method is the least sensitive to noise among the three methods. The experiment results obtained by the three methods are also presented and compared.