The acquired enamel pellicle (AEP) is a thin film formed by the selective adsorption of salivary proteins onto the enamel surface of teeth. The AEP forms a critical interface between the mineral phase of teeth (hydroxyapatite) and the oral microbial biofilm. This biofilm is the key feature responsible for the development of dental caries. Fluoride on enamel surface is well known to reduce caries by reducing the solubility of enamel to acid. Information on the effects of fluoride on AEP formation is limited. This study aimed to investigate the effects of fluoride treatment on hydroxyapatite on the subsequent formation of AEP. In addition, this study pioneered the use of label-free quantitative proteomics to better understand the composition of AEP proteins. Hydroxyapatite discs were randomly divided in 4 groups (n = 10 per group). Each disc was exposed to distilled water (control) or sodium fluoride solution (1, 2 or 5%) for 2 hours. Discs were then washed and immersed in human saliva for an additional 2 hours. AEP from each disc was collected and subjected to liquid chromatography electrospray ionization mass spectrometry for protein identification, characterization and quantification. A total of 45 proteins were present in all four groups, 12 proteins were exclusively present in the control group and another 19 proteins were only present in the discs treated with 5% sodium fluoride. Relative proteomic quantification was carried out for the 45 proteins observed in all four groups. Notably, the concentration of important salivary proteins, such as statherin and histatin 1, decrease with increasing levels of fluoride. It suggests that these proteins are repulsed when hydroxyapatite surface is coated with fluoride. Our data demonstrated that treatment of hydroxyapatite with fluoride (at high concentration) qualitatively and quantitatively modulates AEP formation, effects which in turn will likely impact the formation of oral biofilms.

Gold nanoparticle formation in diamond-like carbon using two different methods: Gold ion implantation and co-deposition of gold and carbon

We describe work in which gold nanoparticles were formed in diamond-like carbon (DLC), thereby generating a Au-DLC nanocomposite. A high-quality, hydrogen-free DLC thin film was formed by filtered vacuum arc plasma deposition, into which gold nanoparticles were introduced using two different methods. The first method was gold ion implantation into the DLC film at a number of decreasing ion energies, distributing the gold over a controllable depth range within the DLC. The second method was co-deposition of gold and carbon, using two separate vacuum arc plasma guns with suitably interleaved repetitive pulsing. Transmission electron microscope images show that the size of the gold nanoparticles obtained by ion implantation is 3-5 nm. For the Au-DLC composite obtained by co-deposition, there were two different nanoparticle sizes, most about 2 nm with some 6-7 nm. Raman spectroscopy indicates that the implanted sample contains a smaller fraction of sp(3) bonding for the DLC, demonstrating that some sp(3) bonds are destroyed by the gold implantation. (C) 2012 American Institute of Physics. [http://dx.doi.org/10.1063/1.4757029]

DNA - novel nanomaterial for applications in photonics and in electronics

Functionalization with surfactants and with active molecules of deoxyribonucleic acid (DNA), thin film processing as well as their nonlinear optical and electrical properties are reviewed and discussed. On the basis of a quantum three level model, we show that the anomalous concentration variation of cubic susceptibility chi((3))(-3 omega; omega, omega, omega) in thin films of DNA-CTMA complexes doped with Disperse Red 1 chromophore can be explained by the concentration variation of two-photon resonance contribution. We show also that the DNA complexes, plasticized with glycerol and adequately doped can be processed into self standing conducting membranes with a high electrical conductivity. The measured ionic conductivity at room temperature, depending on dopant used and its concentration, is in the range of 3.5 x 10(-4)-10(-5) S/cm and increases linearly as a function of temperature, reaching 10(-3) S/cm at 358 K for the most conducting sample, obeying predominantly the Arrhenius law. Practical applications of DNA complexes are also described and discussed. (C) 2012 Academie des sciences. Published by Elsevier Masson SAS. All rights reserved.

Polyazomethine with vinylene and phenantridine moieties in the main chain: Synthesis, characterization, opto(electrical) properties and theoretical calculations

The opto(electrical) properties and theoretical calculations of polyazomethine with vinylene and phenantridine moieties in the main chain were investigated in the present study. 2,5-Bis(hexyloxy)-1,4-bis[(2,5-bis(hexyloxy)-4-formyl-phenylenevinylene]benzene was polymerized in solution with 3,8-diamino-6-phenylphenanthridine (PAZ-PV-Ph). The temperatures of 5% weight loss (T-5%) of the polyazomethine was observed at 356 degrees C in nitrogen. Electrochemical properties of thin film of the polymer were studied by differential pulse voltammetry. The HOMO level of the PAZ-PV-Ph was at -4.97 eV. The energy band gap (E-g) was detected of approximately similar to 1.9 eV. Energy band gap (E-gopt) was additionally calculated from absorption spectrum and absorption coefficient alpha. The absorption UV-vis spectra of polyazomethine recorded in solution showed a blue shift in comparison with the solid state. HOMO-LUMO levels and E-g were additionally calculated theoretically by density functional theory and molecular simulations of PAZ-PV-Ph are presented. Current density-voltage (J-U) measurements were performed on ITO/PAZ-PV-Ph/Al, ITO/TiO2/PAZ-PV-Ph/Al and ITO/PEDOT/PAZ-PV-Ph:TiO2/Al devices in the dark and during irradiation with light (under illumination of 1000 W m(-2)). The polymer was tested using AFM technique and roughness (R-a, R-ms) along with skew and kurtosis are presented.

Conductive polymer gas sensor for quantitative detection of methanol in Brazilian sugar-cane spirit

A low-cost chemiresistive gas sensor is described, made by the deposition of a thin film of a conductive polymer, poly(2-dodecanoylsulfanyl-p-phenylenevinylene), doped with dodecylbenzenesulfonic acid (10%, w/w), onto interdigitated electrodes. The sensor exhibits linear electrical conductance changes in function of the concentration of methanol present in sugar-cane spirit in the range between 0.05% and 4.0%. Since the sensor is cheap, easy to fabricate, durable, presents low power consumption, and is not sensitive to ethanol, acetic acid or water, it can be used in portable equipments for monitoring methanol levels in distilled alcoholic beverages such as Brazilian sugar-cane spirit (cachaca). (C) 2011 Elsevier Ltd. All rights reserved.

Morphology and topography analysis of mesoporous titania templated by micrometric latex sphere arrays

In this work, mesoporous titania is prepared by templating latex sphere arrays with four different sphere diameters at the micrometric scale (phi > 1 mu m). The mesoporous titania homogeneously covers the latex spheres and substrate, forming a thin coating characterized by N-2 adsorption isotherm, small angle X-rays scattering, atomic force, field emission and transmission electronic microscopies. Mesoporous titania has been templated into different shapes such as hollow particles and monoliths according to the amount of sol used to fill the voids of the close packed latex spheres. Titania topography strongly depends on the adsorption of polymeric segments over latex spheres surface, which could be decreased by changing the dimensions of latex spheres (phi = 9.5 mu m) generating a lamellar architecture. Thus, micrometric latex sphere arrays can be used to achieve new surface patterns for mesoporous materials via a fast and inexpensive chemical route for construction of functional devices in different technological fields such as energy conversion, inclusion chemistry and biomaterials. (C) 2011 Elsevier Inc. All rights reserved.

Synthesis, characterisation, luminescence and defect centres in solution combustion synthesised CaZrO3:Tb3+ phosphor

Tb3+ doped CaZrO3 has been prepared by an easy solution combustion synthesis method. The combustion derived powder was investigated by X-ray diffraction, Fourier-transform infrared spectrometry and scanning electron microscopy techniques. A room temperature photoluminescence study showed that the phosphors can be efficiently excited by 251 nm light with a weak emission in the blue and orange region and a strong emission in green light region. CaZrO3:Tb3+ exhibits three thermoluminescence (TL) glow peaks at 126 degrees C, 200 degrees C and 480 degrees C. Electron Spin Resonance (ESR) studies were carried out to study the defect centres induced in the phosphor by gamma irradiation and also to identify the centres responsible for the TL peaks. The room temperature ESR spectrum of irradiated phosphor appears to be a superposition of two distinct centres. One of the centres (centre I) with principal g-value 2.0233 is identified as an O- ion. Centre II with an axial symmetric g-tensor with principal values g(parallel to) = 1.9986 and g(perpendicular to) = 2.0023 is assigned to an F+ centre (singly ionised oxygen vacancy). An additional defect centre is observed during thermal annealing experiments and this centre (assigned to F+ centre) seems to originate from an F centre (oxygen vacancy with two electrons). The F centre and also the F+ centre appear to correlate with the observed high temperature TL peak in CaZrO3:Tb3+ phosphor. (c) 2012 Elsevier B.V. All rights reserved.

Focusing surface plasmons on Er3+ ions through gold planar plasmonic lenses

Gold plasmonic lenses consisting of a planar concentric rings-groove with different periods were milled with a focused gallium ion beam on a gold thin film deposited onto an Er3+-doped tellurite glass. The plasmonic lenses were vertically illuminated with an argon ion laser highly focused by means of a 50x objective lens. The focusing mechanism of the plasmonic lenses is explained using a coherent interference model of surface plasmon-polariton (SPP) generation on the circular grating due to the incident field. As a result, phase modulation can be accomplished by the groove gap, similar to a nanoslit array with different widths. This focusing allows a high confinement of SPPs that can excite the Er3+ ions of the glass. The Er3+ luminescence spectra were measured in the far-field (500-750 nm wavelength range), where we could verify the excitation yield via the plasmonic lens on the Er3+ ions. We analyze the influence of the geometrical parameters on the luminescence spectra. The variation of these parameters results in considerable changes of the luminescence spectra.

Redes neurais artificiais na previsão da inflação: aplicação como ferramenta de apoio à análise de decisões financeiras em organizações de pequeno porte

As estimações das taxas de inflação são de fundamental importância para os gestores, pois as decisões de investimento estão intimamente ligadas a elas. Contudo, o comportamento inflacionário tende a ser não linear e até mesmo caótico, tornando difícil a sua correta estimação. Essa característica do fenômeno pode tornar imprecisos os modelos mais simples de previsão, acessíveis às pequenas organizações, uma vez que muitos deles necessitam de grandes manipulações de dados e/ou softwares especializados. O presente artigo tem por objetivo avaliar, por meio de análise formal estatística, a eficácia das redes neurais artificiais (RNA) na previsão da inflação, dentro da realidade de organizações de pequeno porte. As RNA são ferramentas adequadas para mensurar os fenômenos inflacionários, por se tratar de aproximações de funções polinomiais, capazes de lidar com fenômenos não lineares. Para esse processo, foram selecionados três modelos básicos de redes neurais artificiais Multi Layer Perceptron, passíveis de implementação a partir de planilhas eletrônicas de código aberto. Os três modelos foram testados a partir de um conjunto de variáveis independentes sugeridas por Bresser-Pereira e Nakano (1984), com defasagem de um, seis e doze meses. Para tal, foram utilizados testes de Wilcoxon, coeficiente de determinação R² e o percentual de erro médio dos modelos. O conjunto de dados foi dividido em dois, sendo um grupo usado para treinamento das redes neurais artificiais, enquanto outro grupo era utilizado para verificar a capacidade de predição dos modelos e sua capacidade de generalização. Com isso, o trabalho concluiu que determinados modelos de redes neurais artificiais têm uma razoável capacidade de predição da inflação no curto prazo e se constituem em uma alternativa razoável para esse tipo de mensuração.

Structural changes and dynamic behaviour of vanadium oxide-based catalysts for gas-phase selective oxidations

Selective oxidation is one of the simplest functionalization methods and essentially all monomers used in manufacturing artificial fibers and plastics are obtained by catalytic oxidation processes. Formally, oxidation is considered as an increase in the oxidation number of the carbon atoms, then reactions such as dehydrogenation, ammoxidation, cyclization or chlorination are all oxidation reactions. In this field, most of processes for the synthesis of important chemicals used vanadium oxide-based catalysts. These catalytic systems are used either in the form of multicomponent mixed oxides and oxysalts, e.g., in the oxidation of n-butane (V/P/O) and of benzene (supported V/Mo/O) to maleic anhydride, or in the form of supported metal oxide, e.g., in the manufacture of phthalic anhydride by o-xylene oxidation, of sulphuric acid by oxidation of SO2, in the reduction of NOx with ammonia and in the ammoxidation of alkyl aromatics. In addition, supported vanadia catalysts have also been investigated for the oxidative dehydrogenation of alkanes to olefins , oxidation of pentane to maleic anhydride and the selective oxidation of methanol to formaldehyde or methyl formate [1]. During my PhD I focused my work on two gas phase selective oxidation reactions. The work was done at the Department of Industrial Chemistry and Materials (University of Bologna) in collaboration with Polynt SpA. Polynt is a leader company in the development, production and marketing of catalysts for gas-phase oxidation. In particular, I studied the catalytic system for n-butane oxidation to maleic anhydride (fluid bed technology) and for o-xylene oxidation to phthalic anhydride. Both reactions are catalyzed by systems based on vanadium, but catalysts are completely different. Part A is dedicated to the study of V/P/O catalyst for n-butane selective oxidation, while in the Part B the results of an investigation on TiO2-supported V2O5, catalyst for o-xylene oxidation are showed. In Part A, a general introduction about the importance of maleic anhydride, its uses, the industrial processes and the catalytic system are reported. The reaction is the only industrial direct oxidation of paraffins to a chemical intermediate. It is produced by n-butane oxidation either using fixed bed and fluid bed technology; in both cases the catalyst is the vanadyl pyrophosphate (VPP). Notwithstanding the good performances, the yield value didn’t exceed 60% and the system is continuously studied to improve activity and selectivity. The main open problem is the understanding of the real active phase working under reaction conditions. Several articles deal with the role of different crystalline and/or amorphous vanadium/phosphorous (VPO) compounds. In all cases, bulk VPP is assumed to constitute the core of the active phase, while two different hypotheses have been formulated concerning the catalytic surface. In one case the development of surface amorphous layers that play a direct role in the reaction is described, in the second case specific planes of crystalline VPP are assumed to contribute to the reaction pattern, and the redox process occurs reversibly between VPP and VOPO4. Both hypotheses are supported also by in-situ characterization techniques, but the experiments were performed with different catalysts and probably under slightly different working conditions. Due to complexity of the system, these differences could be the cause of the contradictions present in literature. Supposing that a key role could be played by P/V ratio, I prepared, characterized and tested two samples with different P/V ratio. Transformation occurring on catalytic surfaces under different conditions of temperature and gas-phase composition were studied by means of in-situ Raman spectroscopy, trying to investigate the changes that VPP undergoes during reaction. The goal is to understand which kind of compound constituting the catalyst surface is the most active and selective for butane oxidation reaction, and also which features the catalyst should possess to ensure the development of this surface (e.g. catalyst composition). On the basis of results from this study, it could be possible to project a new catalyst more active and selective with respect to the present ones. In fact, the second topic investigated is the possibility to reproduce the surface active layer of VPP onto a support. In general, supportation is a way to improve mechanical features of the catalysts and to overcome problems such as possible development of local hot spot temperatures, which could cause a decrease of selectivity at high conversion, and high costs of catalyst. In literature it is possible to find different works dealing with the development of supported catalysts, but in general intrinsic characteristics of VPP are worsened due to the chemical interaction between active phase and support. Moreover all these works deal with the supportation of VPP; on the contrary, my work is an attempt to build-up a V/P/O active layer on the surface of a zirconia support by thermal treatment of a precursor obtained by impregnation of a V5+ salt and of H3PO4. In-situ Raman analysis during the thermal treatment, as well as reactivity tests are used to investigate the parameters that may influence the generation of the active phase. Part B is devoted to the study of o-xylene oxidation of phthalic anhydride; industrially, the reaction is carried out in gas-phase using as catalysts a supported system formed by V2O5 on TiO2. The V/Ti/O system is quite complex; different vanadium species could be present on the titania surface, as a function of the vanadium content and of the titania surface area: (i) V species which is chemically bound to the support via oxo bridges (isolated V in octahedral or tetrahedral coordination, depending on the hydration degree), (ii) a polymeric species spread over titania, and (iii) bulk vanadium oxide, either amorphous or crystalline. The different species could have different catalytic properties therefore changing the relative amount of V species can be a way to optimize the catalytic performances of the system. For this reason, samples containing increasing amount of vanadium were prepared and tested in the oxidation of o-xylene, with the aim of find a correlations between V/Ti/O catalytic activity and the amount of the different vanadium species. The second part deals with the role of a gas-phase promoter. Catalytic surface can change under working conditions; the high temperatures and a different gas-phase composition could have an effect also on the formation of different V species. Furthermore, in the industrial practice, the vanadium oxide-based catalysts need the addition of gas-phase promoters in the feed stream, that although do not have a direct role in the reaction stoichiometry, when present leads to considerable improvement of catalytic performance. Starting point of my investigation is the possibility that steam, a component always present in oxidation reactions environment, could cause changes in the nature of catalytic surface under reaction conditions. For this reason, the dynamic phenomena occurring at the surface of a 7wt% V2O5 on TiO2 catalyst in the presence of steam is investigated by means of Raman spectroscopy. Moreover a correlation between the amount of the different vanadium species and catalytic performances have been searched. Finally, the role of dopants has been studied. The industrial V/Ti/O system contains several dopants; the nature and the relative amount of promoters may vary depending on catalyst supplier and on the technology employed for the process, either a single-bed or a multi-layer catalytic fixed-bed. Promoters have a quite remarkable effect on both activity and selectivity to phthalic anhydride. Their role is crucial, and the proper control of the relative amount of each component is fundamental for the process performance. Furthermore, it can not be excluded that the same promoter may play different role depending on reaction conditions (T, composition of gas phase..). The reaction network of phthalic anhydride formation is very complex and includes several parallel and consecutive reactions; for this reason a proper understanding of the role of each dopant cannot be separated from the analysis of the reaction scheme. One of the most important promoters at industrial level, which is always present in the catalytic formulations is Cs. It is known that Cs plays an important role on selectivity to phthalic anhydride, but the reasons of this phenomenon are not really clear. Therefore the effect of Cs on the reaction scheme has been investigated at two different temperature with the aim of evidencing in which step of the reaction network this promoter plays its role.

Trasmission and Reflection (ATR)Far-Infrared Spectroscopy Applied in the Analysis of Cultural Heritage Materials

FIR spectroscopy is an alternative way of collecting spectra of many inorganic pigments and corrosion products found on art objects, which is not normally observed in the MIR region. Most FIR spectra are traditionally collected in transmission mode but as a real novelty it is now also possible to record FIR spectra in ATR (Attenuated Total Reflectance) mode. In FIR transmission we employ polyethylene (PE) for preparation of pellets by embedding the sample in PE. Unfortunately, the preparation requires heating of the PE in order to produces at transparent pellet. This will affect compounds with low melting points, especially those with structurally incorporated water. Another option in FIR transmission is the use of thin films. We test the use of polyethylene thin film (PETF), both commercial and laboratory-made PETF. ATR collection of samples is possible in both the MIR and FIR region on solid, powdery or liquid samples. Changing from the MIR to the FIR region is easy as it simply requires the change of detector and beamsplitter (which can be performed within a few minutes). No preparation of the sample is necessary, which is a huge advantage over the PE transmission method. The most obvious difference, when comparing transmission with ATR, is the distortion of band shape (which appears asymmetrical in the lower wavenumber region) and intensity differences. However, the biggest difference can be the shift of strong absorbing bands moving to lower wavenumbers in ATR mode. The sometimes huge band shift necessitates the collection of standard library spectra in both FIR transmission and ATR modes, provided these two methods of collecting are to be employed for analyses of unknown samples. Standard samples of 150 pigment and corrosion compounds are thus collected in both FIR transmission and ATR mode in order to build up a digital library of spectra for comparison with unknown samples. XRD, XRF and Raman spectroscopy assists us in confirming the purity or impurity of our standard samples. 24 didactic test tables, with known pigment and binder painted on the surface of a limestone tablet, are used for testing the established library and different ways of collecting in ATR and transmission mode. In ATR, micro samples are scratched from the surface and examined in both the MIR and FIR region. Additionally, direct surface contact of the didactic tablets with the ATR crystal are tested together with water enhanced surface contact. In FIR transmission we compare the powder from our test tablet on the laboratory PETF and embedded in PE. We also compare the PE pellets collected using a 4x beam condenser, focusing the IR beam area from 8 mm to 2 mm. A few samples collected from a mural painting in a Nepalese temple, corrosion products collected from archaeological Chinese bronze objects and samples from a mural paintings in an Italian abbey, are examined by ATR or transmission spectroscopy.

Modeling surface-atmosphere exchange of trace gases and energy within and above the Amazon rain forest

Die vorliegende Dissertation untersucht die biogeochemischen Vorgänge in der Vegetationsschicht (Bestand) und die Rückkopplungen zwischen physiologischen und physikalischen Umweltprozessen, die das Klima und die Chemie der unteren Atmosphäre beeinflussen. Ein besondere Schwerpunkt ist die Verwendung theoretischer Ansätze zur Quantifizierung des vertikalen Austauschs von Energie und Spurengasen (Vertikalfluss) unter besonderer Berücksichtigung der Wechselwirkungen der beteiligten Prozesse. Es wird ein differenziertes Mehrschicht-Modell der Vegetation hergeleitet, implementiert, für den amazonischen Regenwald parametrisiert und auf einen Standort in Rondonia (Südwest Amazonien) angewendet, welches die gekoppelten Gleichungen zur Energiebilanz der Oberfläche und CO2-Assimilation auf der Blattskala mit einer Lagrange-Beschreibung des Vertikaltransports auf der Bestandesskala kombiniert. Die hergeleiteten Parametrisierungen beinhalten die vertikale Dichteverteilung der Blattfläche, ein normalisiertes Profil der horizontalen Windgeschwindigkeit, die Lichtakklimatisierung der Photosynthesekapazität und den Austausch von CO2 und Wärme an der Bodenoberfläche. Desweiteren werden die Berechnungen zur Photosynthese, stomatären Leitfähigkeit und der Strahlungsabschwächung im Bestand mithilfe von Feldmessungen evaluiert. Das Teilmodell zum Vertikaltransport wird im Detail unter Verwendung von 222-Radon-Messungen evaluiert. Die ``Vorwärtslösung'' und der ``inverse Ansatz'' des Lagrangeschen Dispersionsmodells werden durch den Vergleich von beobachteten und vorhergesagten Konzentrationsprofilen bzw. Bodenflüssen bewertet. Ein neuer Ansatz wird hergeleitet, um die Unsicherheiten des inversen Ansatzes aus denjenigen des Eingabekonzentrationsprofils zu quantifizieren. Für nächtliche Bedingungen wird eine modifizierte Parametrisierung der Turbulenz vorgeschlagen, welche die freie Konvektion während der Nacht im unteren Bestand berücksichtigt und im Vergleich zu früheren Abschätzungen zu deutlich kürzeren Aufenthaltszeiten im Bestand führt. Die vorhergesagte Stratifizierung des Bestandes am Tage und in der Nacht steht im Einklang mit Beobachtungen in dichter Vegetation. Die Tagesgänge der vorhergesagten Flüsse und skalaren Profile von Temperatur, H2O, CO2, Isopren und O3 während der späten Regen- und Trockenzeit am Rondonia-Standort stimmen gut mit Beobachtungen überein. Die Ergebnisse weisen auf saisonale physiologische Änderungen hin, die sich durch höhere stomatäre Leitfähigkeiten bzw. niedrigere Photosyntheseraten während der Regen- und Trockenzeit manifestieren. Die beobachteten Depositionsgeschwindigkeiten für Ozon während der Regenzeit überschreiten diejenigen der Trockenzeit um 150-250%. Dies kann nicht durch realistische physiologische Änderungen erklärt werden, jedoch durch einen zusätzlichen cuticulären Aufnahmemechanismus, möglicherweise an feuchten Oberflächen. Der Vergleich von beobachteten und vorhergesagten Isoprenkonzentrationen im Bestand weist auf eine reduzierte Isoprenemissionskapazität schattenadaptierter Blätter und zusätzlich auf eine Isoprenaufnahme des Bodens hin, wodurch sich die globale Schätzung für den tropischen Regenwald um 30% reduzieren würde. In einer detaillierten Sensitivitätsstudie wird die VOC Emission von amazonischen Baumarten unter Verwendung eines neuronalen Ansatzes in Beziehung zu physiologischen und abiotischen Faktoren gesetzt. Die Güte einzelner Parameterkombinationen bezüglich der Vorhersage der VOC Emission wird mit den Vorhersagen eines Modells verglichen, das quasi als Standardemissionsalgorithmus für Isopren dient und Licht sowie Temperatur als Eingabeparameter verwendet. Der Standardalgorithmus und das neuronale Netz unter Verwendung von Licht und Temperatur als Eingabeparameter schneiden sehr gut bei einzelnen Datensätzen ab, scheitern jedoch bei der Vorhersage beobachteter VOC Emissionen, wenn Datensätze von verschiedenen Perioden (Regen/Trockenzeit), Blattentwicklungsstadien, oder gar unterschiedlichen Spezies zusammengeführt werden. Wenn dem Netzwerk Informationen über die Temperatur-Historie hinzugefügt werden, reduziert sich die nicht erklärte Varianz teilweise. Eine noch bessere Leistung wird jedoch mit physiologischen Parameterkombinationen erzielt. Dies verdeutlicht die starke Kopplung zwischen VOC Emission und Blattphysiologie.

Synthese und Selbstorganisation von Perylendiimid-Oligonucleotid-Konjugaten

Im Rahmen dieser Arbeit wurde eine Methode entwickelt, Perylendiimidfarbstoffe mit Oligonucleotiden in der Lösung zu verknüpfen. Das Ziel der Arbeit war die nicht-kovalente Synthese von Perylendiimid-DNA- und Protein- supramolekularen Strukturen. Dabei werden die molekularen Erkennungseigenschaften von DNA und Proteinen zunutze gemacht. Insgesamt drei Themenbereiche wurden dabei betrachtet: 1. Synthese und Hybridisierung von symmetrischen und asymmetrischen Perylendiimid-bis(oligonucleotid)-konjugaten für die Bildung supramolekularer Strukturen, 2. Erzeugung von Oberflächenstrukturen auf der Basis von Streptavidin-Perylendiimid-Komplexen, 3. Synthese wasserlöslicher Rylenfarbstoffe für Anwendungen in biologischen Systemen. Zur Synthese und Hybridisierung von Perylendiimid-Oligonucleotid-Konjugaten wurde eine neue Idee verfolgt und erfolgreich realisiert. Dabei handelt es sich um die Synthese von Perylendiimid-DNA-Polymeren durch nicht-kovalente Bindungen. Die Basis des entwickelten Konzepts ist die Ausnutzung der Erkennungseigenschaften der DNA, um Perylendiimidmoleküle in eine lineare Makrostruktur zu organisieren, was sonst nur durch komplizierte chemische Polymersynthese zugänglich wäre. Die Selbstorganisation von zwei komplementären Perylendiimid-bis(oligonucleotid)-konjugaten (PODN1 und PODN2), die an der 5`-Position verknüpft sind, führte zu einem linearen Perylendiimid-DNA-Polymer in der Form von …ABABABAB…., das mit Hilfe von Gelelektrophorese charakterisiert wurde. Eindrucksvoll war auch die erfolgreiche Kopplung des hydrophoben Perylendiimids mit zwei unterschiedlichen Oligonucleotidsequenzen in der Lösung, um asymmetrische Perylendiimid-bis(oligonucleotid)-konjugate zu synthetisieren. Mit solchen asymmetrischen Konjugaten konnte die programmierbare Selbstorganisation der Perylendiimid-Oligonucleotide zu einer definierten Polymerstruktur realisiert werden. Die Synthese von PDI-(biotin)2 wurde vorgestellt. Durch die spezifische Erkennungseigenschaft zwischen Biotin und Streptavidin ist es möglich, eine Oberflächenstruktur zu bilden. Die Immobilisierungsexperimente zeigten, dass das PDI (biotin)2 Streptavidin erkennen und binden kann. Dabei konnte eine multischichtige Nanostruktur (5 Doppelschichten) auf einer Goldoberfläche.

Präparation, Charakterisierung und elektronische Eigenschaften von dünnen Schichten des Hochtemperatursupraleiters HgReBa 2 Ca n-1 Cu n O y

Ziel dieser Arbeit war die Pr"{a}paration, Charakterisierung und Untersuchung der elektronischen Eigenschaften von d"{u}nnen Schichten des Hochtemperatursupraleiters HgReBa$_{2}$Ca$_{n-1}$Cu$_{n}$O$_{y}$, die mittels gepulster Laser-Deposition hergestellt wurden. Die HgRe1212-Filme zeigen in der AC-Suszeptibilit"{a}t einen scharfen "{U}bergang in die supraleitende Phase bei 124 K mit einer "{U}bergangsbreite von 2 K. Die resistiven "{U}berg"{a}nge der Proben wurden mit zunehmender St"{a}rke des externen Magnetfeldes breiter. Aus der Steigung der Arrheniusplots konnte die Aktivierungsenergie f"{u}r verschiedene Feldst"{a}rken bestimmt werden. Weiterhin wurde die Winkelabh"{a}ngigkeit des Depinning-Feldes $B_{dp}(theta)$ der Filme gemessen. Hieraus wurde ein Anisotropiewert von $gamma$ = 7.7 bei 105 K ermittelt. Dies ist relevant, um den f"{u}r Anwendungen wichtigen Bereich im $T$-$B$-$theta$-Phasenraum des Materials absch"{a}tzen zu k"{o}nnen. Die kritische Stromdichte $J_{c}$ der d"{u}nnen Filme aus HgRe-1212 wurde mit Hilfe eines SQUID-Magnetometers gemessen. Die entsprechenden $M$-$H$ Kurven bzw. das magnetische Moment dieser Filme wurde f"{u}r einen weiten Temperatur- und Feldbereich mit einem magnetischen Feld senkrecht zum Film aufgenommen. F"{u}r einen HgRe-1212-Film konnte bei 5 K eine kritische Stromdichte von 1.2 x 10$^{7}$ A/cm$^{2}$ und etwa 2 x 10$^{6}$ A/cm$^{2}$ bei 77 K ermittelt werden. Es wurde die Magnetfeld- und die Temperaturabh"{a}ngigkeit des Hall-Effekts im normalleitenden und im Mischzustand in Magnetfeldern senkrecht zur $ab$-Ebene bis zu 12 T gemessen. Oberhalb der kritischen Temperatur $T_{c}$ steigt der longitudinale spezifische Widerstand $rho_{xx}$ linear mit der Temperatur, w"{a}hrend der spezifische Hall-Widerstand $rho_{yx}$ sich umgekehrt proportional zur Temperatur "{a}ndert. In der N"{a}he von $T_{c}$ und in Feldern kleiner als 3 T wurde eine doppelte Vorzeichen"{a}nderung des spezifischen Hall-Widerstandes beobachtet. Der Hall-Winkel im Normalzustand, cot $theta_{H}= alpha T^{2} + beta$, folgt einer universellen $textit{T }^{2}$-Abh"{a}ngigkeit in allen magnetischen Feldern. In der N"{a}he des Nullwiderstand-Zustandes h"{a}ngt der spezifische Hall-Widerstand $rho_{yx}$ "{u}ber ein Potenzgesetz mit dem longitudinalen Widerstand $rho_{xx}$ zusammen. Das Skalenverhalten zwischen $rho_{yx}$ und $rho_{xx}$ weist eine starke Feld-Abh"{a}ngigkeit auf. Der Skalenexponent $beta$ in der Gleichung $rho_{yx}$ =A $rho_{xx}^{beta}$ steigt von 1.0 bis 1.7, w"{a}hrend das Feld von 1.0 bis 12 T zunimmt.

Grating coupled surface plasmon enhanced fluorescence spectroscopy

Over the last three decades, sensors based on the phenomenon of surface plasmon resonance have proven particularly suitable for real time thin film characterization, gas detection, biomolecular interaction examination and to supplement electrochemical methods. Systems based on prism coupling have been combined with fluorescence detection under the name of surface plasmon fluorescence spectroscopy to increase sensitivity even further. Alternatively, metal gratings can be employed to match photons for plasmon resonance. The real time monitoring of binding reactions not yet been reported in the combination of fluorescence detection and grating coupling. Grating-based systems promise more competitive products, because of reduced operating costs, and offer benefits for device engineering. This thesis is comprised of a comprehensive study of the suitability of grating coupling for fluorescence based analyte detection. Fundamental properties of grating coupled surface plasmon fluorescence spectroscopy are described, as well as issues related to the commercial realization of the method. Several new experimental techniques are introduced and demonstrated in order to optimize performance in certain areas and improve upon capabilities in respect to prism-based systems. Holographically fabricated gratings are characterized by atomic force microscopy and optical methods, aided by simulations and profile parameters responsible for efficient coupling are analyzed. The directional emission of fluorophores immobilized on a grating surface is studied in detail, including the magnitude and geometry of the fluorescence emission pattern for different grating constants and polarizations. Additionally, the separation between the minimum of the reflected intensity and the maximum fluorescence excitation position is examined. One of the key requirements for the commercial feasibility of grating coupling is the cheap and faithful mass production of disposable samples from a given master grating. The replication of gratings is demonstrated by a simple hot embossing method with good reproducibility to address this matter. The in-situ fluorescence detection of analyte immobilization and affinity measurements using grating coupling are described for the first time. The physical factors related to the sensitivity of the technique are assessed and the lower limit of detection of the technique is determined for an exemplary assay. Particular attention is paid to the contribution of bulk fluorophores to the total signal in terms of magnitude and polarization of incident and emitted light. Emission from the bulk can be a limiting factor for experiments with certain assay formats. For that reason, a novel optical method, based on the modulation of both polarization and intensity of the incident beam, is introduced and demonstrated to be capable of eliminating this contribution.