Thermal stability of double-ceramic-layer thermal barrier coatings with various coating thickness

Double-ceramic-layer (DCL) coatings with various thickness ratios composed of YSZ (6-8 wt.% Y2O3 + ZrO2) and lanthanum zirconate (LZ, La2Zr2O7) were produced by the atmospheric plasma spraying. Chemical stability of LZ in contact with YSZ in DCL coatings was investigated by calcining powder blends at different temperatures. No obvious reaction was observed when the calcination temperature was lower than 1250 degrees C, implying that LZ and YSZ had good chemical applicability for producing DCL coating. The thermal cycling test indicate that the cycling lives of the DCL coatings are strongly dependent on the thickness ratio of LZ and YSZ, and the coatings with YSZ thickness between 150 and 200 mu m have even longer lives than the single-layer YSZ coating. When the YSZ layer is thinner than 100 mu m, the DCL coatings failed in the LZ layer close to the interface of YSZ layer and LZ layer. For the coatings with the YSZ thickness above 150 mu m, the failure mainly occurs at the interface of the YSZ layer and the bond coat.

A new luminescent material: Li2CaSiO4 : Eu2+

In our study, the Eu2+ doped Li2CaSiO4 phosphors were initially synthesized by high temperature solid state method, and their luminescent properties were also investigated. Eu2+ ions occupied 8-coordinatid distorted dodecahedral Ca sites, leading to strong crystal field splitting. The strong crystal field splitting made the broad excitation band extending from UV to visible region. In addition, the high concentration of Li+ ions in the structure constrained the distortion of the emission centers, then resulted in a small stokes shift, similar to 1100 cm(-1). Under excitation, the Li2CaSiO4:Eu2+ phosphors emitted bluish green light with peak of 480 nm, FWHM of 31 nm and color coordination of (0.06, 0.44). The Eu2+ doped Li2CaSiO4 phosphor would be suitable for bluish green phosphor of white LEDs due to its excellent excitation profile and chromaticity.

Coating nano-hemalite on (Y,Gd)BO3 : Eu3+ phosphors by a facile method

(Y, Gd) BO3:Eu3+ particles coated with nano-hematite were prepared by a facile method I for example (humid) solid phase reaction at room temperature. The resulted hematite-coated (Y, Gd)BO3:Eu3+ particles were characterized by scanning electron microscopy (SEM), energy dispersive spectrometer (EDS) analysis, X-ray diffraction (XRD), X-ray photoelectron spectra (XPS), and photoluminescence spectra (PL). The SEM and EDS analyses indicate that the particles are coated with a very thin layer of iron oxide. XPS results further confirmed that the coating was hematite, and the coating thickness was in nanometer range. XRD patterns showed that either the hematite coating was too thin or the content of hematite was too small, so that the XRD cannot detect it. The emission spectra illustrate that the peak near 580 nm disappears due to the coating of iron oxide, and when the coating is very thin, the ratio of D-5(0)-> F-7(2) to D-5(2)-> F-7(1) of coated particles is higher than that of uncoated ones, which indicates that the color purity of the phosphor is increased by coating nano-hematite.

Co-immobilized microbial biosensor for BOD estimation based on sol-gel derived composite material

A novel type of biochemical oxygen demand (BOD) biosensor was developed for water monitor, based on co-immobilizing of Trichosporon cutaneum and Bacillus subtilis in the sol-gel derived composite material which is composed of silica and the grafting copolymer of poly (vinyl alcohol) and 4-vinylpyridine (PVA-g-P(4-VP)). Factors that influence the performance of the resulting biosensor were examined. The biodegradable substrate spectrum could be expanded by the co-immobilized microorganisms. The biosensor prepared also exhibited good reproducibility and long-term stability. Good agreement was obtained between the results of the sensor BOD measurement and those obtained from conventional BOD5 method for water samples.

A new type of highly efficient luminescent material - The system Al2O3-B2O3 containing Ce3+ and Tb3+ ions

The system Al2O3-B2O3 containing Ce3+ and Tb3+ ions was investigated for the first time. It was found that certain compositions give rise to a new highly efficient green luminescent material.

Coating carbon nanotubes with europium oxide

Carbon nanotubes (CNTS) coating with europium oxide by a simple method is reported in this letter for the first time. The CNTS were refluxed in a solution of nitric acid containing europium nitrate, and the pH value was subsequently ajusted with ammonia solution. At last, the mixture was filtered and annealed. The TEM micrograph showed that the CNTS were covered with a uniform thin layer with thickness of about 15 nm. The XRD results revealed that the CNTS were coated with europium oxide.

Mechanism and life study on polyaniline anti-corrosion coating

Solvent free polyaniline emeraldine base(EB) corrosion protection coating was prepared, employing aliphatic polyamine as solvent of EB as well as hardener of epoxy resin. This coating passed 2000h of salt fog test when the EB loading was about 1 wt%. The interaction between EB and iron indicated that EB acted as a "quasi-catalyst" to cause the formation of densed iron oxide film in the interface.

A hydroxyphenyloxadiazole lithium complex as a highly efficient blue emitter and interface material in organic light-emitting diodes

We synthesized a hydroxyphenyloxadiazole lithium complex (LiOXD) as a blue light-emitting and electron injection/transport material to be used in double-layer organic electroluminescent devices. Devices with the concise configuration of ITO/TPD/LiOXD/Al showed bright blue EL emission centered at 468 nm with a maximum luminance of 2900 cd m(-2). A current efficiency of 3.9 cd A(-1) and power efficiency of 1.1 lm W-1 were obtained. LiOXD was also examined as an interface material. The efficiency of an ITO/NPB/Alq(3)/Al device increased considerably when LiOXD was inserted between Alq(3) and aluminium. The improvement of the device characteristics with LiOXD approached that observed with the dielectric LiF salt.

Encapsulation and luminescence of the nanostructured supramolecular material [Eu(Phen)(4)](NO3)(3)/(CH3)(3)Si-MCM-41

The nanostructured material (NSM) of pure silica MCM-41 molecular sieve was synthesized with tetraethyl orthosilicate (TEOS) as the source of silica and cetyltrimethylammonium bromide (CTMABr) as the template under supersonic wave condition. Then NSM of (CH3)(3)Si-MCM-41 was obtained by introducing trimethylsilyl to MCM-41. (CH3)(3)Si-MCM-41 showed the similar TEM and XRD photographs with the normal crystal of MCM-41 and the diameter of the NSM crystallites with a hexagon shape is of about 10-40 nm. The dispersivity of (CH3)(3)Si-MCM-41 prevails over the NSM of MCM-41 as its hydrophobicity. The fluorescent intensity of (CH3)(3)Si-MCM-41 is 3.4 times as that of the MCM-41. The luminescent functional supramolecular nanostructured material was prepared in EtOH, and characterized by TEM, HRTEM, XRD, TG, IR, and elemental analysis. The results showed that the [Eu(Phen)(4)](NO3)(3) had entered into the channels of nanosized mesoporous sieve of (CH3)(3)Si-MCM-41, forming discrete centers of luminescence. The energy transferring of the host to guest, superficial effect of NSM, quanta tunnel effect, and discrete luminescent center result in the fluorescent intensity of the supramolecule enhancement.

Silicon dioxide coating of CeO2 nanoparticles by solid state reaction at room temperature

The synthesis Of SiO2 coated CeO2 nanoparticles by humid solid state reaction at room. temperature is described. Transmission electron microscope results show that CeO2 Particles were coated with a layer Of SiO2. Binding energy of Ce 3d(5/2) was shifted from 883.8 to 882.8 eV after coating in the XPS Ce 3d spectra. This confirms the chemical bond formation between SiO32- and Ce4+. Because the surface photovoltage property of CeO2 nanoparticles that were used as core materials in the experiment approaches to that of CeO2 macroparticles, peak P2 (electron transition from 0 2p on surface to Ce 4f) disappeared in the surface photovoltage spectrum of CeO2 nanoparticles. Also, the effect Of SiO2 on the electron transition from 0 2p to Ce 4f results in the lowering of surface photovoltage response intensity of P1 peak (electron transition from 0 2p in bulk to Ce 4f).

Luminescence properties of lanthanide complexes doped in hybrid material from tetraethoxysilane and 3-glycidyioxyropyl-trimethoxysilane

Hybrid materials, containing in-situ synthesized lanthanide complexes with intense green light, have been prepared via sol-gel process. The luminescence properties and the decay times of as-synthesized samples were investigated. The excitation spectrum of the samples indicates the formation of complexes between terbium (III) and P-Sulfosalicylic acid. The hybrid materials that contain in-situ synthesized terbium complexes exhibit the characteristic emission bands of the rare earth ions. In addition, the effect of concentration of terbium on the luminescence properties as well as the thermal stability were also studied.

Coating of Y2O3 : Eu3+ particles with alumina by a humid solid state reaction at room temperature

Humid solid state reaction at room temperature was utilized for the first time to coat Y2O3 : Eu3+ particles with alumina. The particles were studied with an X-ray photoelectron spectrometer (XPS), a scanning electron microscope (SEM), and an energy dispersive spectrometer (EDS). XPS results show that the yttrium and europium contents are decreased and that the aluminum content is the highest except for that of oxygen after coating. SEM and EDS results show that particles are coated with a thin shell of alumina.