DETERMINATION OF THE VINYL-ACETATE CONTENT IN ETHYLENE-VINYL ACETATE COPOLYMERS BY THERMOGRAVIMETRIC ANALYSIS

The dependence of thermal degradation behaviour on vinyl acetate (VA) content of ethylene-vinyl acetate (EVA) copolymers was studied by thermogravimetric analysis (t.g.a.). Among the parameters investigated, the maximum rate of weight loss at the stage of

DSC AND C-13 NMR-STUDIES OF ETHYLENE-PROPENE COPOLYMERS PREPARED BY A HIGHLY-ACTIVE AND STEREOSPECIFIC CATALYST

Ethylene-propene copolymers (EPR) were synthesized at different feed compositions using a highly active and isospecific MgCl2-supported Ti-based catalyst. The thermal behavior of EPR was studied by differential scanning calorimetry, the heterogeneity by f

MOLECULAR CHARACTERISTICS AND CRYSTALLINE-STRUCTURE OF ETHYLENE-DIMETHYLAMINOETHYL-METHACRYLATE COPOLYMERS

The relationship between molecular and crystalline structural characteristics of the ethylene -dimethylaminoethylmethacrylate copolymers (EDAM) was investigated and related to melt flow index MI and average gross content of DAM comonomer, in comparison with low density polyethylene (LDPE) produced by the common high-pressure radical polymerization process. Although the average molecular weight and its distribution are influenced predominantly by the polymerization conditions, DAM-content seems not to depend significantly on molecular weight according to the GPC-FT/IR measurement. Comonomer sequence distributions were determined quantitatively with the C-13-NMR spectra entirely assigned by DEPT and H-1-C-13 COSY techniques. The result suggests the alternating copolymerization tendency and surprisingly coincides with the simulation out-puts based on the assumption of continuous complete mixing reactor model, using Mayo-Lewis equation and the same Q-e values as previously reported on different types of copolymers such as EVA and St.DAM (VA;vinylacetate, St;styrene). It was confirmed by WAXD and SAXS analyses that the crystallinity X(c) and the thickness of lamellar crystal l(c) decreased with increasing DAM-content, whereas the a-lattice and b-lattice dimensions enlarged. X(c) and l(c) can definitely be correlated to the heats of fusion and crystallization measured by DSC. The average size of spherulites measured with light scattering photometry tends to be enlarged with decreasing molecular weight (increasing MI) and DAM-content.

IMPEDANCE STUDY OF THE INTERFACES BETWEEN LITHIUM, POLYANILINE, LITHIUM-DOPED MNO2 AND MODIFIED POLY(ETHYLENE OXIDE) ELECTROLYTE

Impedance study was carried out for the interfaces between lithium, polyaniline (PAn), lithium-doped MnO2 and modified poly(ethylene oxide) (PEO) electrolyte under various' conditions. The interfacial charge-transfer resistances R(ct) on PEO/PAn, R(ct) on PEO/LiMn2O4 increase with depth-of-discharge and decrease after the charge of the cell containing modified PEO as electrolyte. The charge-transfer resistance R(ct) on PEO/PAn is higher than R(ct) on PEO/LiMn2O4 under the same condition, since inserted species and mechanism are different for both cases. In the case of PAn, an additional charge-transfer resistance might be related to the electronic conductivity change in discharge/charge potential range, as it was evident from a voltammetry curve. With increasing cycle numbers, the charge-transfer resistance increases gradually. The impedance results also have shown that at low frequency the diffusion control is dominant in the process of the charge and discharge of Li/PEO/PAn or Li/PEO/LiMn2O4 cell. The diffusion coefficients have been calculated from impedance data.

UNSTEADY DIFFUSION KINETICS OF ZIEGLER-NATTA HETEROGENEOUS CATALYST POLYMERIZATION .4. PREDICTION OF EXPERIMENTAL RESULTS OF PROPYLENE ETHYLENE 1-HEXADECENE TERPOLYMERIZATION

The prediction, based on unsteady diffusion kinetics, of the enhancement of reactivity and incorporation of 1-hexadecene in its copolymerization with propylene on adding a small amount of ethylene (increase from 5,2 mol-% to 10,8 mol-% when 2% of ethylene was added, and to 16,1 mol-% when 5% was added) was verified in the terpolymerization of propylene/1-hexadecene/ethylene on a commercial Solvay-type delta-TiCl3 catalyst. The catalyst efficiency was thus also increased. These augmentations originate from the increase in diffusion coefficient of 1-hexadecene at the catalyst surface when the PP crystallinity decreases on introduction of ethylene. Calculation based on unsteady diffusion kinetics showed that the order of diffusion coefficients ethylene > propylene > 1-hexadecene is reversed as the monomer concentration increases when the monomers are not at their equilibrium concentration. Sequence distribution as determined by means of C-13 NMR revealed a tendency of blocky structure rather than a Bernoullian one. The terpolymer compositions obtained by means of an IR method developed in this work conform rather well with the NMR results. Results in this work not only support the unsteady diffusion kinetics but also provide a new route to prepare olefinic copolymer rubbers with heterogeneous titanium catalysts.

THERMODYNAMICS OF POLY(ETHYLENE OXIDE)-POLY(VINYL ACETATE) BLENDS

Heat-of-mixing data, obtained on blends of poly(ethylene oxide) (PEO) with whole and fractionated poly(vinyl acetate) (PVAc), were used to feed Patterson's theory of polymer-polymer miscibility. Negative values of mixing enthalpy, contact-energy term, interaction'' parameter and excess volume were obtained only for blends with the lowest molecular weight PVAc fraction. These results show that miscibility of PVAc with PEO strongly depends on its molecular weight. The calculated unfavourable excess volume term of the Patterson equation is small in comparison with the absolute value of the interaction term. Therefore, miscibility of PEO and low-molecular-weight PVAc is dictated by the weak specific interactions between different repeat units and by the entropic gain in the mixing process.

MISCIBILITY AND PHASE-BEHAVIOR IN BLENDS OF POLY(HYDROXYETHER OF BISPHENOL-A) WITH POLY(ETHYLENE OXIDE-CO-PROPYLENE OXIDE)

The miscibility of poly(hydroxyether of bisphenol A) (phenoxy) with a series of poly(ethylene oxide-co-propylene oxide) (EPO) has been studied. It was found that the critical copolymer composition for achieving miscibility with phenoxy around 60-degrees-C is about 22 mol % ethylene oxide (EO). Some blends undergo phase separation at elevated temperatures, but there is no maximum in the miscibility window. The mean-field approach has been used to describe this homopolymer/copolymer system. From the miscibility maps and the melting-point depression of the crystallizable component in the blends, the binary interaction energy densities, B(ij), have been calculated for all three pairs. The miscibility of phenoxy with EPO is considered to be caused mainly by the intermolecular hydrogen-bonding interactions between the hydroxyl groups of phenoxy and the ether oxygens of the EO units in the copolymers, while the intramolecular repulsion between EO and propylene oxide units in the copolymers contributes relatively little to the miscibility.

XPS STUDIES ON RADIATION-INDUCED STRUCTURAL-CHANGES IN THE COPOLYMER OF TETRAFLUOROETHYLENE AND ETHYLENE

In this work, the radiation-induced structural changes in the copolymer of tetrafluoroethylene and ethylene (F-40) were studied by X-ray photoelectron spectroscopy (XPS). During irradiation, some CF2 groups in the polymer were found to have been converted into carbon structures that bonded indirectly with fluorine atoms.

SOME NEWER CONCEPTS OF ETHYLENE ALPHA-OLEFIN COPOLYMERIZATION ON HETEROGENEOUS ZIEGLER-NATTA CATALYSTS

Unsteady diffusion kinetic, recently advanced by this laboratory, is applied to the examination of some polymerization and molecular chain structure problems. Hitherto deemed "anomalous" phenomena, such as the faster rate of copolymerization of ethylene/alpha-olefin than the homopolymerization of ethylene and the enrichment in the incorporation of a higher alpha-olefin in its copolymerization with ethylene by a lower alpha-olefin, are reasonably explained by unsteady diffusion of monomers. Molecular chain structure of copolymers, such as compositional heterogeneity and its dependence on comonomer incorporation originates from the difference in diffusion coefficients of the monomers. A copolymer composition equation taking into consideration the unsteady diffusion was developed. In cases where simulated curves were compared with experimental curves, good agreements were found.

SEQUENCE STRUCTURE OF ETHYLENE-VINYL SUBSTITUTED COPOLYMER WITH C-13 NMR .4.

The substituent chemical shift (SCS) has been applied to the assignment of the C-13 NMR spectrum of chlorinated polyethylene (CPE). CPE of different chlorine contents has been employed and their sequence structure discussed. The results show that characteristic of CPE with medium chlorine content is the dichloroethane structure in molecular chain. SCS parameters have been obtained from the C-13 NMR spectra. It was found that the effects of chlorine content and temperature on SCS are negligible, but the substituent parameter S1 reduced by 0.39 ppm when C2Cl4 was added to solvent ODCB.

STRUCTURE AND PROPERTIES OF SEQUENTIALLY POLYMERIZED PROPYLENE-B-[ETHYLENE-CO-PROPYLENE]-B-PROPYLENE COPOLYMERS

The structure and properties of presumed block copolymers of polypropylene (PP) with ethylene-propylene random copolymers (EPR), i.e., PP-EPR and PP-EPR-PP, have been investigated by viscometry, transmission electron microscopy, dynamic mechanical analysis, differential scanning calorimetry, gel permeation chromatography, wide-angle x-ray diffraction, and other techniques testing various mechanical properties. PP-EPR and PP-EPR-PP were synthesized using delta-TiCl3-Et2AlCl as a catalyst system. The results indicate that the intrinsic viscosity of these polymers increases with each block-building step, whereas the intrinsic viscosity of those prepared by chain transfer reaction (strong chain-transfer reagent hydrogen was introduced between block-building steps during polymerization) hardly changes with the reaction time. Compared with PP / EPR blends, PP-EPR-PP block copolymers have lower PP and polyethylene crystallinity, and lower melting and crystallization temperatures of crystalline EPR. Two relaxation peaks of PP and EPR appear in the dynamic spectra of blends. They merge into a very broad relaxation peak with block sequence products of the same composition, indicating good compatibility between PP and EPR in the presence of block copolymers. Varying the PP and EPR content affects the crystallinity, density, and morphological structure of the products, which in turn affects the tensile strength and elongation at break. Because of their superior mechanical properties, sequential polymerization products containing PP-EPR and PP-EPR-PP block copolymers may have potential as compatibilizing agents for isotactic polypropylene and polyethylene blends or as potential heat-resistant thermoplastic elastomers.

RADIATION-INDUCED CROSS-LINKING OF POLY(METHYL METHACRYLATE)-POLY(ETHYLENE OXIDE) BLEND

Radiation-induced crosslinking of poly(methyl methacrylate) (PMMA)-poly(methylene oxide) (PEO) blends was studied. It was found that PMMA in PMMA-PEO blend can be crosslinked in the range of certain doses (1 approximately 20 x 10(4) Gy) and composition (PMMA% = 30 approximately 70) under the absence of oxygen. Moreover, it was also found that the crosslinking degree of PMMA in the blend in which the content of PMMA is 70% is the largest. The crosslinking degree of PMMA in the blend is closely related with the polymer miscibility. The crosslinking degree of the blend prepared at 60-degrees-C is far higher than one at ambient temperature.

SEM STUDY ON FRACTURE-BEHAVIOR OF ETHYLENE/PROPYLENE BLOCK COPOLYMERS AND THEIR BLENDS

The toughening effect of the separate phases of ethylene/propylene block copolymers and their blends was studied by scanning electron microscopy (SEM). The results obtained show that the interfacial adhesion between separate phases and the isotactic polypropene (iPP) matrix in ethylene/propylene block copolymers is strong at room temperature, but poor at low temperature; specimens exhibit tearing of separate phases during fracture at room temperature, but interfacial fracture between separate phases and the iPP matrix at low temperature. From the characteristics of fractographs of ethylene/propylene block copolymers and their blends, it could be concluded that the separate phases improve the toughness of specimens in several ways: they promote the plastic deformation of the iPP, and they can be deformed and fractured themselves during the fracture process. However, it was shown that the plastic deformation processes, such as multiple-crazing, shear yielding, etc. of the matrix are the dominant mechanisms of energy absorption in highly toughened ethylene/propylene block copolymers and their blends. The deformation and fracture of separate phases are only of secondary importance.

CHARACTERIZATION, MORPHOLOGY AND THERMAL-PROPERTIES OF ETHYLENE PROPYLENE BLOCK COPOLYMERS

Characterization, morphology and thermal properties of commercial ethylene-propylene block copolymers have been studied by C-13 nuclear magnetic resonance (n.m.r.) spectroscopy, differential scanning calorimetry (d.s.c.), dynamic mechanical analysis (d.m.a.) and scanning electron microscopy (SEM). The results obtained show that there exists some ethylene-propylene random copolymer in the block copolymers extractable by n-heptane. The possibility of forming PP-b-PE diblock copolymer is questionable on the basis of the effects of residual propene and the chain-transfer reaction in the sequential copolymerization. A difference in the thermal properties between commercial ethylene-propylene block copolymers and PP/PE blends was noticed, which cannot be used to identify PP-b-PE diblock copolymer. The multiphase structure has been confirmed by d.m.a. and SEM, with ethylene-propylene random copolymer and polyethylene forming the domains in the matrix of polypropylene.