Efeito cariostático de restaurações adesivas em superfícies radiculares: estudo in vitro

Dental materials that release fluoride have been shown to be effective in caries inhibition around restorations. Adhesive materials would also be effective in caries inhibition by sealing and protecting cavity margins from acidic demineralization. This in vitro study tested the hypothesis that composite restorations with a dentin adhesive system have a caries preventive effect similar to that of an adhesive material with fluoride - glass-ionomer cement - on root surfaces. Twenty roots from extracted sound third molars were embedded in polystyrene resin and ground flat. Standardized cavities were prepared in leveled root surfaces and randomly restored with (a) Chelon-Fil (Espe) or (b) Z100/SingleBond (3M). Baseline indentations were measured at 100, 200 and 300 mum from the occlusal margins of each restoration and the surface microhardness values were obtained using a Knoop diamond indenter. A 2.0 mm wide margin around the restorations was submitted to a pH-cycling model, at 37ºC. After that, surface microhardness was measured again, as it was before. The differences between baseline and final surface microhardness were considered for statistical analysis. The median values of differences were (a): -3.8; -0.3; -1.0; and (b): 3.3; 2.5; 1.7, for the distances of 100, 200 and 300 mum, respectively. The Kruskal-Wallis test did not show statistically significant difference between 100, 200 and 300 mum distances in each tested group. There was no difference between the studied materials at the distances of 200 and 300 mum. Chelon-Fil was statistically different from Z100/SingleBond, at 100 mum (p<0.05). Under the studied conditions, the glass-ionomer cement had a higher caries preventive effect than the composite/dentin adhesive restorations.

O brincar no contexto escolar : significados das brincadeiras realizadas em aulas de educação física e no recreio

Universidade Estadual de Campinas . Faculdade de Educação Física

A influencia dos agentes sociais nos interesses fisico-esportivos do lazer

Universidade Estadual de Campinas. Faculdade de Educação Física

Modelo de inclusão digital para construção do conhecimento em qualidade de vida e atividade fisica

Universidade Estadual de Campinas. Faculdade de Educação Física

Comparação entre o dano muscular de flexores do cotovelo e extensores do joelho em idosos= : Muscle damage comparison between elbow flexors and knee extensors in older adults

Universidade Estadual de Campinas . Faculdade de Educação Física

Watsu : um caminho para a unidade

Universidade Estadual de Campinas . Faculdade de Educação Física

Correlation between metal-ceramic bond strength and coefficient of linear thermal expansion difference

The purpose of this study was to evaluate the metal-ceramic bond strength (MCBS) of 6 metal-ceramic pairs (2 Ni-Cr alloys and 1 Pd-Ag alloy with 2 dental ceramics) and correlate the MCBS values with the differences between the coefficients of linear thermal expansion (CTEs) of the metals and ceramics. Verabond (VB) Ni-Cr-Be alloy, Verabond II (VB2), Ni-Cr alloy, Pors-on 4 (P), Pd-Ag alloy, and IPS (I) and Duceram (D) ceramics were used for the MCBS test and dilatometric test. Forty-eight ceramic rings were built around metallic rods (3.0 mm in diameter and 70.0 mm in length) made from the evaluated alloys. The rods were subsequently embedded in gypsum cast in order to perform a tensile load test, which enabled calculating the CMBS. Five specimens (2.0 mm in diameter and 12.0 mm in length) of each material were made for the dilatometric test. The chromel-alumel thermocouple required for the test was welded into the metal test specimens and inserted into the ceramics. ANOVA and Tukey's test revealed significant differences (p=0.01) for the MCBS test results (MPa), with PI showing higher MCBS (67.72) than the other pairs, which did not present any significant differences. The CTE (10-6 oC-1) differences were: VBI (0.54), VBD (1.33), VB2I (-0.14), VB2D (0.63), PI (1.84) and PD (2.62). Pearson's correlation test (r=0.17) was performed to evaluate of correlation between MCBS and CTE differences. Within the limitations of this study and based on the obtained results, there was no correlation between MCBS and CTE differences for the evaluated metal-ceramic pairs.

Shear bond strength of self-etch and total-etch bonding systems at different dentin depths

The purpose of this study was to evaluate the dentin shear bond strength of four adhesive systems (Adper Single Bond 2, Adper Prompt L-Pop, Magic Bond DE and Self Etch Bond) in regards to buccal and lingual surfaces and dentin depth. Forty extracted third molars had roots removed and crowns bisected in the mesiodistal direction. The buccal and lingual surfaces were fixed in a PVC/acrylic resin ring and were divided into buccal and lingual groups assigned to each selected adhesive. The same specimens prepared for the evaluation of superficial dentin shear resistance were used to evaluate the different depths of dentin. The specimens were identified and abraded at depths of 0.5, 1.0, 1.5 and 2.0 mm. Each depth was evaluated by ISO TR 11405 using an EMIC-2000 machine regulated at 0.5 mm/min with a 200 Kgf load cell. We performed statistical analyses on the results (ANOVA, Tukey and Scheffé tests). Data revealed statistical differences (p < 0.01) in the adhesive and depth variation as well as adhesive/depth interactions. The Adper Single Bond 2 demonstrated the highest mean values of shear bond strength. The Prompt L-Pop product, a self-etching adhesive, revealed higher mean values compared with Magic Bond DE and Self Etch Bond adhesives, a total and self-etching adhesive respectively. It may be concluded that the shear bond strength of dentin is dependent on material (adhesive system), substrate depth and adhesive/depth interaction.

Effect of eugenol-based endodontic sealer on the adhesion of intraradicular posts cemented after different periods

OBJECTIVE: This study evaluated in vitro the influence of an eugenol-based sealer (EndoFill) on the retention of stainless steel prefabricated posts cemented with zinc phosphate and resin-based (Panavia F) cements after different periods of root canal obturation, using the pull-out test. MATERIAL AND METHODS: Sixty upper canines were decoronated and the roots were embedded in resin blocks. The specimens were distributed into 3 groups, according to the period elapsed between canal obturation and post cementation: Group I - immediately; Group II - 72 h and Group III - 4 months. The groups were subdivided according to the type of cement used for post cementation: A - zinc phosphate and B - Panavia F. Following the experimental periods, specimens were subjected to pullout test in an Instron machine with application of tensile force at a crosshead speed of 0.5 mm/min until post dislodgement. The maximum forces required for post removal were recorded (kN) and means were subjected to statistical analysis by 2-way ANOVA and Tukey-Kramer test (α=0.001) RESULTS: There were statistically significant differences (p<0.01) between the posts cemented with zinc phosphate cement (0.2112 kN) and Panavia F (0.0501 kN). However, no statistically significant differences (p>0.05) were found between the three post cementation periods, regardless of the cement. CONCLUSIONS: It was concluded that the eugenol-based sealer influenced the tensile strength of the posts cemented with the resin cement, but had no influence on the time waited between root canal obturation and post space preparation/post cementation.

Adhesion of an endodontic sealer to dentin and gutta-percha: shear and push-out bond strength measurements and SEM analysis

The use of an adequate method for evaluation of the adhesion of root canal filling materials provides more reliable results to allow comparison of the materials and substantiate their clinical choice. The aims of this study were to compare the shear bond strength (SBS) test and push-out test for evaluation of the adhesion of an epoxy-based endodontic sealer (AH Plus) to dentin and gutta-percha, and to assess the failure modes on the debonded surfaces by means of scanning electron microscopy (SEM). Three groups were established (n=7): in group 1, root cylinders obtained from human canines were embedded in acrylic resin and had their canals prepared and filled with sealer; in group 2, longitudinal sections of dentin cylinders were embedded in resin with the canal surface smoothed and turned upwards; in group 3, gutta-percha cylinders were embedded in resin. Polyethylene tubes filled with sealer were positioned on the polished surface of the specimens (groups 2 and 3). The push-out test (group 1) and the SBS test (groups 2 and 3) were performed in an Instron universal testing machine running at crosshead speed of 1 mm/min. Means (±SD) in MPa were: G1 (8.8±1.13), G2 (5.9±1.05) and G3 (3.8±0.55). Statistical analysis by ANOVA and Student's t-test (a=0.05) revealed statistically significant differences (p<0.01) among the groups. SEM analysis showed a predominance of adhesive and mixed failures of AH Plus sealer. The tested surface affected significantly the results with the sealer reaching higher bond strength to dentin than to gutta-percha with the SBS test. The comparison of the employed methodologies showed that the SBS test produced significantly lower bond strength values than the push-out test, was skilful in determining the adhesion of AH Plus sealer to dentin and gutta-percha, and required specimens that could be easily prepared for SEM, presenting as a viable alternative for further experiments.

Heat treatment of a direct composite resin: influence on flexural strength

The purpose of this study was to evaluate the flexural strength of a direct composite, for indirect application, that received heat treatment, with or without investment. One indirect composite was used for comparison. For determination of the heat treatment temperature, thermogravimetric analysis (TGA) and differential scanning calorimetry (DSC) were performed, considering the initial weight loss temperature and glass transition temperature (Tg). Then, after photoactivation (600 mW/cm² - 40 s), the specimens (10 x 2 x 2 mm) were heat-treated following these conditions: 170ºC for 5, 10 or 15 min, embedded or not embedded in investment. Flexural strength was assessed as a means to evaluate the influence of different heat treatment periods and investment embedding on mechanical properties. The data were analyzed by ANOVA and Tukey's test (α = 0.05). TGA showed an initial weight loss temperature of 180ºC and DSC showed a Tg value of 157°C. Heat treatment was conducted in an oven (Flli Manfredi, Italy), after 37°C storage for 48 h. Flexural strength was evaluated after 120 h at 37°C storage. The results showed that different periods and investment embedding presented similar statistical values. Nevertheless, the direct composite resin with treatments presented higher values (178.7 MPa) compared to the indirect composite resin (146.0 MPa) and the same direct composite submitted to photoactivation only (151.7 MPa). Within the limitations of this study, it could be concluded that the heat treatment increased the flexural strength of the direct composite studied, leading to higher mechanical strength compared to the indirect composite.

An in vitro comparison of nickel and chromium release from brackets

This study aimed at comparing amounts of nickel (Ni) and chromium (Cr) released from brackets from different manufacturers in simulated oral environments. 280 brackets were equally divided into 7 groups according to manufacturer. 6 groups of brackets were stainless steel, and 1 group of brackets was made of a cobalt-chromium alloy with low Ni content (0.5%). International standard ISO 10271/2001 was applied to provide test methods. Each bracket was immersed in 0.5 ml of synthetic saliva (SS) or artificial plaque fluid (PF) over a period of 28 days at 37ºC. Solutions were replaced every 7 days, and were analyzed by spectrometry. The Kruskal-Wallis test was applied. Amounts of Ni release in SS (µg L-1 per week) varied between groups from "bellow detection limits" to 694, and from 49 to 5,948.5 in PF. The group of brackets made of cobalt-chromium alloy, with the least nickel content, did not release the least amounts of Ni. Amounts of Cr detected in SS and in PF (µg L-1 per week) were from 1 to 10.4 and from 50.5 to 8,225, respectively. It was therefore concluded that brackets from different manufacturers present different corrosion behavior. Further studies are necessary to determine clinical implications of the findings.

Flexural and diametral tensile strength of composite resins

This study evaluated the flexural strength (sf) and the diametral tensile strength (st) of light-cured composite resins, testing the hypothesis that there is a positive relation between these properties. Twenty specimens were fabricated for each material (Filtek Z250- 3M-Espe; AM- Amelogen, Ultradent; VE- Vit-l-escence, Ultradent; EX- Esthet-X, Dentsply/Caulk), following ISO 4049 and ANSI/ADA 27 specifications and the manufacturers’ instructions. For the st test, cylindrical shaped (4 mm x 6 mm) specimens (n = 10) were placed with their long axes perpendicular to the applied compressive load at a crosshead speed of 1.0 mm/min. The sf was measured using the 3-point bending test, in which bar shaped specimens (n = 10) were tested at a crosshead speed of 0.5 mm/min. Both tests were performed in a universal testing machine (EMIC 2000) recording the fracture load (N). Strength values (MPa) were calculated and statistically analyzed by ANOVA and Tukey (a = 0.05). The mean and standard deviation values (MPa) were Z250-45.06 ± 5.7; AM-35.61 ± 5.4; VE-34.45 ± 7.8; and EX-42.87 ± 6.6 for st; and Z250-126.52 ± 3.3; AM-87.75 ± 3.8; VE-104.66 ± 4.4; and EX-119.48 ± 2.1 for sf. EX and Z250 showed higher st and sf values than the other materials evaluated (p < 0.05), which followed a decreasing trend of mean values. The results confirmed the study hypothesis, showing a positive relation between the material properties examined.

Convecção linearmente organizada na área de Petrolina, semi-árido do Nordeste do Brasil: aspectos em meso e grande escala

É apresentado um estudo sobre sistemas convectivos linearmente organizados e observados por um radar meteorológico banda-C na região semi-árida do Nordeste do Brasil. São analisados três dias (27 a 29) de março de 1985, com ênfase na investigação do papel desempenhado por fatores locais e de grande escala no desenvolvimento dos sistemas. No cenário de grande escala, a área de cobertura do radar foi influenciada por um cavado de ar superior austral no dia 27 e por um vórtice ciclônico de altos níveis no dia 29. A convergência de umidade próxima à superfície favoreceu a atividade convectiva nos dias 27 e 29, enquanto que divergência de umidade próxima à superfície inibiu a atividade convectiva no dia 28. No cenário de mesoescala, foi observado que o aquecimento diurno é um fator importante para a formação de células convectivas, somando-se a ele o papel determinante da orografia na localização dos ecos. De maneira geral, as imagens de radar mostram os sistemas convectivos linearmente organizados em áreas elevadas e núcleos convectivos intensos envolvidos por uma área de precipitação estratiforme. Os resultados indicam que convergência do fluxo de umidade em grande escala e aquecimento radiativo, são fatores determinantes na evolução e desenvolvimento dos ecos na área de estudo.

Pitfalls of artificial grouping and stratification of scientific journals based on their Impact Factor: a case study in Brazilian Zoology

The present contribution explores the impact of the QUALIS metric system for academic evaluation implemented by CAPES (Coordination for the Development of Personnel in Higher Education) upon Brazilian Zoological research. The QUALIS system is based on the grouping and ranking of scientific journals according to their Impact Factor (IF). We examined two main points implied by this system, namely: 1) its reliability as a guideline for authors; 2) if Zoology possesses the same publication profile as Botany and Oceanography, three fields of knowledge grouped by CAPES under the subarea "BOZ" for purposes of evaluation. Additionally, we tested CAPES' recent suggestion that the area of Ecology would represent a fourth field of research compatible with the former three. Our results indicate that this system of classification is inappropriate as a guideline for publication improvement, with approximately one third of the journals changing their strata between years. We also demonstrate that the citation profile of Zoology is distinct from those of Botany and Oceanography. Finally, we show that Ecology shows an IF that is significantly different from those of Botany, Oceanography, and Zoology, and that grouping these fields together would be particularly detrimental to Zoology. We conclude that the use of only one parameter of analysis for the stratification of journals, i.e., the Impact Factor calculated for a comparatively small number of journals, fails to evaluate with accuracy the pattern of publication present in Zoology, Botany, and Oceanography. While such simplified procedure might appeals to our sense of objectivity, it dismisses any real attempt to evaluate with clarity the merit embedded in at least three very distinct aspects of scientific practice, namely: productivity, quality, and specificity.