AgInSbTelSi thin films on glass substrates are prepared by dc magnetron sputtering at room temperature. Using Si underlayer as the thermal diffusion layer, the super-resolution nano-ablation holes with a size of 70nm in the AgInSbTe phase change films are obtained by a far-field focused laser experimental setup, with laser wavelength 405nm and objective-lens numerical aperture 0.90. The nano-ablation formation mechanism is analysed and discussed via the thermal diffusion of sample structures.

Structural change of laser-irradiated Ge2Sb2Te5 films studied by electrical property measurement

Sheet resistance of laser-irradiated Ge2Sb2Te5 thin films prepared by magnetron sputtering was measured by the four-point probe method. With increasing laser power the sheet resistance undergoes an abrupt drop from 10(7) to 10(3) Omega/square at about 580 mW. The abrupt drop in resistance is due to the structural change from amorphous to crystalline state as revealed by X-ray diffraction (XRD) study of the samples around the abrupt change point. Crystallized dots were also formed in the amorphous Ge2Sb2Te5 films by focused short pulse laser-irradiated, the resistivities at the crystallized dots and the non-crystallized area are 3.375 x 10(-3) and 2.725 Omega m, sheet resistance is 3.37 x 10(4) and 2.725 x 10(7) Omega/square respectively, deduced from the I-V Curves that is obtained by conductive atomic force microscope (C-AFM). (C) 2008 Elsevier B.V. All rights reserved.

Laser pulse induced bumps in chalcogenide phase change films

Formation of bumps in chalcogenide phase change thin films during the laser writing process is theoretically and experimentally investigated. The process involves basically fast heating and quenching stages. Circular bumps are formed after cooling, and the shape and size of the bumps depend on various parameters such as temperatures, laser power, beam size, laser pulse duration, etc. In extreme cases, holes are formed at the apex of the bumps. To understand the bumps and their formation is of great interest for data storage. In the present work, a theoretical model is established for the formation process, and the geometric characters of the formed bumps can be analytically and quantitatively evaluated from various parameters involved in the formation. Simulations based on the analytic solution are carried out taking Ag8In14Sb55Te23 as an example. The results are verified with experimental observations of the bumps. (C) 2008 American Institute of Physics.

Reversible Resistance Switching Effect in Amorphous Ge1Sb4Te7 Thin Films without Phase Transformation

We demonstrate a reversible resistance switching effect that does not rely on amorphous-crystalline phase transformation in a nanoscale capacitor-like cell using Ge1Sb4Te7 films as the working material. The polarity and amplitude of the applied electric voltage switches the cell resistance between low- and high-resistance states, as revealed in the current-voltage characteristics of the film by conductive atomic force microscopy (CAFM). This reversible SET/RESET switching effect is induced by voltage pulses and their polarity. The change of electrical resistance due to the switching effect is approximately two orders of magnitude.

Optical properties of dye-doped zirconia films by spectroscopic ellipsometry

The optical properties of zirconia films doped with rhodamine 6G and oxazine 725 by the sol-gel process were investigated using spectroscopic ellipsometry (SE). Accurate refractive index n and the extinction coefficient k were determined using a three-oscillator classical Lorentz model in the wavelength range of 300-800 nm. The derived refractive index of dye-doped films exhibited anomalous dispersion in the absorption region. Wavelength tunable output lasing action yellow and near-infrared wavelength region was achieved by DFB configuration using zirconia films doped with R6G and oxazine 725. (c) 2006 Elsevier B.V. All rights reserved.

Optical properties of zirconia-titania-ORMOSIL films for temperature tuning distributed feedback waveguide lasers

The zirconia-titania-ORMOSIL waveguide thin films with considerable optical quality were prepared by the sol-gel process. The refractive index (n) and the extinction coefficient (k) were determined by a scanning ellipsometer. Wavelength tunable output of distributed feedback waveguide lasing was demonstrated in Rhodamine 6G doped ZrO2 TiO2-ORMOSIL thin films by varying the temperature, and about 5.5 nm wavelength tuning range was achieved around the emission wavelength of 599 nm. The thermal-optic coefficient (dn/dT) of the active ZrO2-TiO2-ORMOSIL films was deduced. (c) 2005 Elsevier B.V. All rights reserved.

Temperature characteristics of optical parameters of phthalocyanine LB films and spin-coated films

The LB films and spin-coated films of tetra-neopentoxy phthalocyanine zinc (TNPPcZn) were prepared and annealed at different temperatures. Their refractive index (n) and extinction coefficient (k) were measured by p-polarized reflectance. The similar value of n and k, as well as similar changing tendency of it and k at varied annealing temperatures, was found between LB films and spin-coated films. In addition, the absorption curves of TNPPcZn LB films and spin-coated films in visible range at different annealing temperature were investigated. The results indicate that the changing tendency of the extinction coefficient of two kinds of TNPPcZn films obtained from two methods mentioned above were coincident. When the annealing temperature increased to 150 degrees C, the monomers of TNPPcZn films transformed to aggregates, n(f) and k(f) of the films increased. Further, n(f) and k(f) decreased as aggregates changed back to monomers again at the annealing temperature of 300 degrees C. The experimental results coincide well with the theoretical analysis. (C) 2004 Elsevier B.V. All rights reserved.

Numerical and experimental analysis on green laser crystallization of amorphous silicon thin films

The effect of laser fluence on the crystallization of amorphous silicon irradiated by a frequency-doubled Nd:YAG laser is studied both theoretically and experimentally. An effective numerical model is set up to predict the melting threshold and the optimized laser fluence for the crystallization of 200-nm-thick amorphous silicon. The variation of the temperature distribution with time and the melt depth is analyzed. Besides the model, the Raman spectra of thin films treated with different fluences are measured to confirm the phase transition and to determine the optimized fluence. The calculating results accord well with those obtained from the experimental data in this research. (C) 2008 Elsevier Ltd. All rights reserved.